The aims of this work were: to develop composite, bi-layer and laminated biodegradable films based on gelatin and chitosan, to determine film barrier and mechanical properties and to characterize their microstructure. Gelatin and chitosan concentrations used were 7.5% and 1% (w/w), respectively. Glycerol (0.75%) was added as plasticizer. Physicochemical properties such as moisture content, transparency and color were analyzed. Composite and bi-layer systems showed a compact structure indicating a good compatibility between components. Water vapor permeability (WVP) was independent of film thickness up to 120 μm for gelatin films and 60 μm for chitosan ones. Both, bi-layer and laminated systems resulted effective alternatives to reduce WVP of composite films (at least 42.5%). Bi-layer systems showed better mechanical properties than laminated ones. The resistance at break increased from 54.3 for composite to 77.2 MPa for bi-layer films, whereas elongation at break values of both composite and bi-layer films were similar (2.2–5.7%).
Fil: Rivero, Sandra G. M.. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos; Argentina
Fil: Garcia, Maria Alejandra. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos; Argentina
Fil: Pinotti, Adriana Noemi. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos; Argentina
Materia
BARRIER AND MECHANICAL PROPERTIES
BI-LAYER AND LAMINATED SYSTEMS
BIODEGRADABLE FILMS
CHITOSAN
GELATIN
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/136302
Acceder
id CONICETDig_d98477e5ddbc11530171f3b0110a9b85
oai_identifier_str oai:ri.conicet.gov.ar:11336/136302
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Composite and bi-layer films based on gelatin and chitosanRivero, Sandra G. M.Garcia, Maria AlejandraPinotti, Adriana NoemiBARRIER AND MECHANICAL PROPERTIESBI-LAYER AND LAMINATED SYSTEMSBIODEGRADABLE FILMSCHITOSANGELATINhttps://purl.org/becyt/ford/2.11https://purl.org/becyt/ford/2The aims of this work were: to develop composite, bi-layer and laminated biodegradable films based on gelatin and chitosan, to determine film barrier and mechanical properties and to characterize their microstructure. Gelatin and chitosan concentrations used were 7.5% and 1% (w/w), respectively. Glycerol (0.75%) was added as plasticizer. Physicochemical properties such as moisture content, transparency and color were analyzed. Composite and bi-layer systems showed a compact structure indicating a good compatibility between components. Water vapor permeability (WVP) was independent of film thickness up to 120 μm for gelatin films and 60 μm for chitosan ones. Both, bi-layer and laminated systems resulted effective alternatives to reduce WVP of composite films (at least 42.5%). Bi-layer systems showed better mechanical properties than laminated ones. The resistance at break increased from 54.3 for composite to 77.2 MPa for bi-layer films, whereas elongation at break values of both composite and bi-layer films were similar (2.2–5.7%).Fil: Rivero, Sandra G. M.. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos; ArgentinaFil: Garcia, Maria Alejandra. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos; ArgentinaFil: Pinotti, Adriana Noemi. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos; ArgentinaElsevier2009-02info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/136302Rivero, Sandra G. M.; Garcia, Maria Alejandra; Pinotti, Adriana Noemi; Composite and bi-layer films based on gelatin and chitosan; Elsevier; Journal of Food Engineering; 90; 4; 2-2009; 531-5390260-87741873-5770CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1016/j.jfoodeng.2008.07.021info:eu-repo/semantics/altIdentifier/url/https://bit.ly/3enYgNUinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:32:15Zoai:ri.conicet.gov.ar:11336/136302instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:32:15.625CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Composite and bi-layer films based on gelatin and chitosan
title Composite and bi-layer films based on gelatin and chitosan
spellingShingle Composite and bi-layer films based on gelatin and chitosan
Rivero, Sandra G. M.
BARRIER AND MECHANICAL PROPERTIES
BI-LAYER AND LAMINATED SYSTEMS
BIODEGRADABLE FILMS
CHITOSAN
GELATIN
title_short Composite and bi-layer films based on gelatin and chitosan
title_full Composite and bi-layer films based on gelatin and chitosan
title_fullStr Composite and bi-layer films based on gelatin and chitosan
title_full_unstemmed Composite and bi-layer films based on gelatin and chitosan
title_sort Composite and bi-layer films based on gelatin and chitosan
dc.creator.none.fl_str_mv Rivero, Sandra G. M.
Garcia, Maria Alejandra
Pinotti, Adriana Noemi
author Rivero, Sandra G. M.
author_facet Rivero, Sandra G. M.
Garcia, Maria Alejandra
Pinotti, Adriana Noemi
author_role author
author2 Garcia, Maria Alejandra
Pinotti, Adriana Noemi
author2_role author
author
dc.subject.none.fl_str_mv BARRIER AND MECHANICAL PROPERTIES
BI-LAYER AND LAMINATED SYSTEMS
BIODEGRADABLE FILMS
CHITOSAN
GELATIN
topic BARRIER AND MECHANICAL PROPERTIES
BI-LAYER AND LAMINATED SYSTEMS
BIODEGRADABLE FILMS
CHITOSAN
GELATIN
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.11
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv The aims of this work were: to develop composite, bi-layer and laminated biodegradable films based on gelatin and chitosan, to determine film barrier and mechanical properties and to characterize their microstructure. Gelatin and chitosan concentrations used were 7.5% and 1% (w/w), respectively. Glycerol (0.75%) was added as plasticizer. Physicochemical properties such as moisture content, transparency and color were analyzed. Composite and bi-layer systems showed a compact structure indicating a good compatibility between components. Water vapor permeability (WVP) was independent of film thickness up to 120 μm for gelatin films and 60 μm for chitosan ones. Both, bi-layer and laminated systems resulted effective alternatives to reduce WVP of composite films (at least 42.5%). Bi-layer systems showed better mechanical properties than laminated ones. The resistance at break increased from 54.3 for composite to 77.2 MPa for bi-layer films, whereas elongation at break values of both composite and bi-layer films were similar (2.2–5.7%).
Fil: Rivero, Sandra G. M.. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos; Argentina
Fil: Garcia, Maria Alejandra. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos; Argentina
Fil: Pinotti, Adriana Noemi. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Criotecnología de Alimentos. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Criotecnología de Alimentos; Argentina
description The aims of this work were: to develop composite, bi-layer and laminated biodegradable films based on gelatin and chitosan, to determine film barrier and mechanical properties and to characterize their microstructure. Gelatin and chitosan concentrations used were 7.5% and 1% (w/w), respectively. Glycerol (0.75%) was added as plasticizer. Physicochemical properties such as moisture content, transparency and color were analyzed. Composite and bi-layer systems showed a compact structure indicating a good compatibility between components. Water vapor permeability (WVP) was independent of film thickness up to 120 μm for gelatin films and 60 μm for chitosan ones. Both, bi-layer and laminated systems resulted effective alternatives to reduce WVP of composite films (at least 42.5%). Bi-layer systems showed better mechanical properties than laminated ones. The resistance at break increased from 54.3 for composite to 77.2 MPa for bi-layer films, whereas elongation at break values of both composite and bi-layer films were similar (2.2–5.7%).
publishDate 2009
dc.date.none.fl_str_mv 2009-02
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/136302
Rivero, Sandra G. M.; Garcia, Maria Alejandra; Pinotti, Adriana Noemi; Composite and bi-layer films based on gelatin and chitosan; Elsevier; Journal of Food Engineering; 90; 4; 2-2009; 531-539
0260-8774
1873-5770
CONICET Digital
CONICET
url http://hdl.handle.net/11336/136302
identifier_str_mv Rivero, Sandra G. M.; Garcia, Maria Alejandra; Pinotti, Adriana Noemi; Composite and bi-layer films based on gelatin and chitosan; Elsevier; Journal of Food Engineering; 90; 4; 2-2009; 531-539
0260-8774
1873-5770
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1016/j.jfoodeng.2008.07.021
info:eu-repo/semantics/altIdentifier/url/https://bit.ly/3enYgNU
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier
publisher.none.fl_str_mv Elsevier
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1844614335489376256
score 13.070432

Publicaciones similares