Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering

Autores
Bruni, Yesica Lorena; Booth, Raul Fernando Nicolas; Garrido, Liliana Beatriz; Aglietti, Esteban Fausto
Año de publicación
2016
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Composites of the ZrO2-CaO-Al2O3 system exhibit high corrosion resistance and high chemical stability, these being suitable properties for enhanced performance as refractories. In this work composites based on ZrO2-CaAl4O7 (CA2) were developed by reaction sintering of two pure ZrO2 powders with different particle size (d50 = 0.44 μm and d50 = 8 μm) mixed with high-alumina cement. The effects of CaO to ZrO2 molar ratio, particle size of ZrO2 and sintering temperature on densification, c-ZrO2 formation, microstructure and mechanical properties (Vickers hardness, dynamic Young's modulus and compressive strength) were determined. Porosity and mean pore size of composites reduced with decreasing both particle size of ZrO2 and CaO content. The highest compression strength of ∼350 MPa and hardness of 6 GPa corresponded to dense ZrO2-based composite with 15 vol.% CA2 sintered at 1 400°C.
Fil: Bruni, Yesica Lorena. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina
Fil: Booth, Raul Fernando Nicolas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Garrido, Liliana Beatriz. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina
Materia
Calcium Dialuminate
Ceramic Composites
Mechanical Properties
Zirconia
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/49072
Acceder
id CONICETDig_863dd43490a1eb2aea83145afade7a22
oai_identifier_str oai:ri.conicet.gov.ar:11336/49072
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sinteringBruni, Yesica LorenaBooth, Raul Fernando NicolasGarrido, Liliana BeatrizAglietti, Esteban FaustoCalcium DialuminateCeramic CompositesMechanical PropertiesZirconiahttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Composites of the ZrO2-CaO-Al2O3 system exhibit high corrosion resistance and high chemical stability, these being suitable properties for enhanced performance as refractories. In this work composites based on ZrO2-CaAl4O7 (CA2) were developed by reaction sintering of two pure ZrO2 powders with different particle size (d50 = 0.44 μm and d50 = 8 μm) mixed with high-alumina cement. The effects of CaO to ZrO2 molar ratio, particle size of ZrO2 and sintering temperature on densification, c-ZrO2 formation, microstructure and mechanical properties (Vickers hardness, dynamic Young's modulus and compressive strength) were determined. Porosity and mean pore size of composites reduced with decreasing both particle size of ZrO2 and CaO content. The highest compression strength of ∼350 MPa and hardness of 6 GPa corresponded to dense ZrO2-based composite with 15 vol.% CA2 sintered at 1 400°C.Fil: Bruni, Yesica Lorena. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; ArgentinaFil: Booth, Raul Fernando Nicolas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Garrido, Liliana Beatriz. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; ArgentinaCarl Hanser Verlag2016-09info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/49072Bruni, Yesica Lorena; Booth, Raul Fernando Nicolas; Garrido, Liliana Beatriz; Aglietti, Esteban Fausto; Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering; Carl Hanser Verlag; International Journal of Materials Research; 107; 9; 9-2016; 851-8591862-5282CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.3139/146.111404info:eu-repo/semantics/altIdentifier/url/https://www.hanser-elibrary.com/doi/abs/10.3139/146.111404info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-10-22T11:05:37Zoai:ri.conicet.gov.ar:11336/49072instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-10-22 11:05:38.103CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering
title Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering
spellingShingle Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering
Bruni, Yesica Lorena
Calcium Dialuminate
Ceramic Composites
Mechanical Properties
Zirconia
title_short Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering
title_full Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering
title_fullStr Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering
title_full_unstemmed Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering
title_sort Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering
dc.creator.none.fl_str_mv Bruni, Yesica Lorena
Booth, Raul Fernando Nicolas
Garrido, Liliana Beatriz
Aglietti, Esteban Fausto
author Bruni, Yesica Lorena
author_facet Bruni, Yesica Lorena
Booth, Raul Fernando Nicolas
Garrido, Liliana Beatriz
Aglietti, Esteban Fausto
author_role author
author2 Booth, Raul Fernando Nicolas
Garrido, Liliana Beatriz
Aglietti, Esteban Fausto
author2_role author
author
author
dc.subject.none.fl_str_mv Calcium Dialuminate
Ceramic Composites
Mechanical Properties
Zirconia
topic Calcium Dialuminate
Ceramic Composites
Mechanical Properties
Zirconia
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv Composites of the ZrO2-CaO-Al2O3 system exhibit high corrosion resistance and high chemical stability, these being suitable properties for enhanced performance as refractories. In this work composites based on ZrO2-CaAl4O7 (CA2) were developed by reaction sintering of two pure ZrO2 powders with different particle size (d50 = 0.44 μm and d50 = 8 μm) mixed with high-alumina cement. The effects of CaO to ZrO2 molar ratio, particle size of ZrO2 and sintering temperature on densification, c-ZrO2 formation, microstructure and mechanical properties (Vickers hardness, dynamic Young's modulus and compressive strength) were determined. Porosity and mean pore size of composites reduced with decreasing both particle size of ZrO2 and CaO content. The highest compression strength of ∼350 MPa and hardness of 6 GPa corresponded to dense ZrO2-based composite with 15 vol.% CA2 sintered at 1 400°C.
Fil: Bruni, Yesica Lorena. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina
Fil: Booth, Raul Fernando Nicolas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Garrido, Liliana Beatriz. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina
description Composites of the ZrO2-CaO-Al2O3 system exhibit high corrosion resistance and high chemical stability, these being suitable properties for enhanced performance as refractories. In this work composites based on ZrO2-CaAl4O7 (CA2) were developed by reaction sintering of two pure ZrO2 powders with different particle size (d50 = 0.44 μm and d50 = 8 μm) mixed with high-alumina cement. The effects of CaO to ZrO2 molar ratio, particle size of ZrO2 and sintering temperature on densification, c-ZrO2 formation, microstructure and mechanical properties (Vickers hardness, dynamic Young's modulus and compressive strength) were determined. Porosity and mean pore size of composites reduced with decreasing both particle size of ZrO2 and CaO content. The highest compression strength of ∼350 MPa and hardness of 6 GPa corresponded to dense ZrO2-based composite with 15 vol.% CA2 sintered at 1 400°C.
publishDate 2016
dc.date.none.fl_str_mv 2016-09
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/49072
Bruni, Yesica Lorena; Booth, Raul Fernando Nicolas; Garrido, Liliana Beatriz; Aglietti, Esteban Fausto; Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering; Carl Hanser Verlag; International Journal of Materials Research; 107; 9; 9-2016; 851-859
1862-5282
CONICET Digital
CONICET
url http://hdl.handle.net/11336/49072
identifier_str_mv Bruni, Yesica Lorena; Booth, Raul Fernando Nicolas; Garrido, Liliana Beatriz; Aglietti, Esteban Fausto; Densification and mechanical properties of ZrO2-CaAl4O7 composites obtained by reaction sintering; Carl Hanser Verlag; International Journal of Materials Research; 107; 9; 9-2016; 851-859
1862-5282
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.3139/146.111404
info:eu-repo/semantics/altIdentifier/url/https://www.hanser-elibrary.com/doi/abs/10.3139/146.111404
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Carl Hanser Verlag
publisher.none.fl_str_mv Carl Hanser Verlag
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1846781339172339712
score 12.982451

Publicaciones similares