Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering
- Autores
- Martinez, Juan Manuel; Hernández, Maria Florencia; Booth, Raul Fernando Nicolas; Lopez, Paula Virginia; Suarez, Gustavo; Conconi, María Susana; Rendtorff Birrer, Nicolás Maximiliano
- Año de publicación
- 2021
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- Novel 1:1 Yttria partially stabilized zirconia (PSZ) - aluminum borate (AB: Al11B4O33) ceramic composites were prepared and characterized by a simple direct sintering process of PSZ-AB mixtures. Sintering was performed below 1300 °C to minimize the decomposition of borate. Phases were corroborated by XRD. SEM permitted to characterize the microstructure as interlocking needles of AB - rounded by PSZ grains. Porous microstructure configuration was achieved by the proposed processing route. Porosity was within 30% for samples thermally treated at 1200 and 1300 °C. Mechanical behavior was evaluated by diametral compression. A fragile behavior was observed. Both strength and apparent Young modulus were evaluated being ≈30 MPa and ≈3 GPa respectively; values four times higher than the corresponding alumina-AB composite. This is more important when firing at higher temperature. The density of the obtained composites coupled with the mechanical behavior are the main characteristics of this novel composite with potential structural, insulating and filtering applications.
Fil: Martinez, Juan Manuel. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Hernández, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Booth, Raul Fernando Nicolas. Universidad Nacional del Chaco Austral; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
Fil: Lopez, Paula Virginia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina - Materia
-
ALUMINUM BORATE
COMPOSITES
STABILIZED ZIRCONIA - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/181140
Ver los metadatos del registro completo
id |
CONICETDig_cec815c136427cf398c7a527bb8bcb6e |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/181140 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sinteringMartinez, Juan ManuelHernández, Maria FlorenciaBooth, Raul Fernando NicolasLopez, Paula VirginiaSuarez, GustavoConconi, María SusanaRendtorff Birrer, Nicolás MaximilianoALUMINUM BORATECOMPOSITESSTABILIZED ZIRCONIAhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Novel 1:1 Yttria partially stabilized zirconia (PSZ) - aluminum borate (AB: Al11B4O33) ceramic composites were prepared and characterized by a simple direct sintering process of PSZ-AB mixtures. Sintering was performed below 1300 °C to minimize the decomposition of borate. Phases were corroborated by XRD. SEM permitted to characterize the microstructure as interlocking needles of AB - rounded by PSZ grains. Porous microstructure configuration was achieved by the proposed processing route. Porosity was within 30% for samples thermally treated at 1200 and 1300 °C. Mechanical behavior was evaluated by diametral compression. A fragile behavior was observed. Both strength and apparent Young modulus were evaluated being ≈30 MPa and ≈3 GPa respectively; values four times higher than the corresponding alumina-AB composite. This is more important when firing at higher temperature. The density of the obtained composites coupled with the mechanical behavior are the main characteristics of this novel composite with potential structural, insulating and filtering applications.Fil: Martinez, Juan Manuel. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Hernández, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Booth, Raul Fernando Nicolas. Universidad Nacional del Chaco Austral; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; ArgentinaFil: Lopez, Paula Virginia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaInt Inst Science Sintering (i I S S)2021-02info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/181140Martinez, Juan Manuel; Hernández, Maria Florencia; Booth, Raul Fernando Nicolas; Lopez, Paula Virginia; Suarez, Gustavo; et al.; Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering; Int Inst Science Sintering (i I S S); Science Of Sintering; 53; 1; 2-2021; 9-180350-820XCONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://www.doiserbia.nb.rs/img/doi/0350-820X/2021/0350-820X2101009M.pdfinfo:eu-repo/semantics/altIdentifier/doi/10.2298/SOS2101009Minfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T09:55:50Zoai:ri.conicet.gov.ar:11336/181140instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 09:55:51.161CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering |
title |
Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering |
spellingShingle |
Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering Martinez, Juan Manuel ALUMINUM BORATE COMPOSITES STABILIZED ZIRCONIA |
title_short |
Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering |
title_full |
Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering |
title_fullStr |
Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering |
title_full_unstemmed |
Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering |
title_sort |
Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering |
dc.creator.none.fl_str_mv |
Martinez, Juan Manuel Hernández, Maria Florencia Booth, Raul Fernando Nicolas Lopez, Paula Virginia Suarez, Gustavo Conconi, María Susana Rendtorff Birrer, Nicolás Maximiliano |
author |
Martinez, Juan Manuel |
author_facet |
Martinez, Juan Manuel Hernández, Maria Florencia Booth, Raul Fernando Nicolas Lopez, Paula Virginia Suarez, Gustavo Conconi, María Susana Rendtorff Birrer, Nicolás Maximiliano |
author_role |
author |
author2 |
Hernández, Maria Florencia Booth, Raul Fernando Nicolas Lopez, Paula Virginia Suarez, Gustavo Conconi, María Susana Rendtorff Birrer, Nicolás Maximiliano |
author2_role |
author author author author author author |
dc.subject.none.fl_str_mv |
ALUMINUM BORATE COMPOSITES STABILIZED ZIRCONIA |
topic |
ALUMINUM BORATE COMPOSITES STABILIZED ZIRCONIA |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
Novel 1:1 Yttria partially stabilized zirconia (PSZ) - aluminum borate (AB: Al11B4O33) ceramic composites were prepared and characterized by a simple direct sintering process of PSZ-AB mixtures. Sintering was performed below 1300 °C to minimize the decomposition of borate. Phases were corroborated by XRD. SEM permitted to characterize the microstructure as interlocking needles of AB - rounded by PSZ grains. Porous microstructure configuration was achieved by the proposed processing route. Porosity was within 30% for samples thermally treated at 1200 and 1300 °C. Mechanical behavior was evaluated by diametral compression. A fragile behavior was observed. Both strength and apparent Young modulus were evaluated being ≈30 MPa and ≈3 GPa respectively; values four times higher than the corresponding alumina-AB composite. This is more important when firing at higher temperature. The density of the obtained composites coupled with the mechanical behavior are the main characteristics of this novel composite with potential structural, insulating and filtering applications. Fil: Martinez, Juan Manuel. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina Fil: Hernández, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina Fil: Booth, Raul Fernando Nicolas. Universidad Nacional del Chaco Austral; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina Fil: Lopez, Paula Virginia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina Fil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina |
description |
Novel 1:1 Yttria partially stabilized zirconia (PSZ) - aluminum borate (AB: Al11B4O33) ceramic composites were prepared and characterized by a simple direct sintering process of PSZ-AB mixtures. Sintering was performed below 1300 °C to minimize the decomposition of borate. Phases were corroborated by XRD. SEM permitted to characterize the microstructure as interlocking needles of AB - rounded by PSZ grains. Porous microstructure configuration was achieved by the proposed processing route. Porosity was within 30% for samples thermally treated at 1200 and 1300 °C. Mechanical behavior was evaluated by diametral compression. A fragile behavior was observed. Both strength and apparent Young modulus were evaluated being ≈30 MPa and ≈3 GPa respectively; values four times higher than the corresponding alumina-AB composite. This is more important when firing at higher temperature. The density of the obtained composites coupled with the mechanical behavior are the main characteristics of this novel composite with potential structural, insulating and filtering applications. |
publishDate |
2021 |
dc.date.none.fl_str_mv |
2021-02 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/181140 Martinez, Juan Manuel; Hernández, Maria Florencia; Booth, Raul Fernando Nicolas; Lopez, Paula Virginia; Suarez, Gustavo; et al.; Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering; Int Inst Science Sintering (i I S S); Science Of Sintering; 53; 1; 2-2021; 9-18 0350-820X CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/181140 |
identifier_str_mv |
Martinez, Juan Manuel; Hernández, Maria Florencia; Booth, Raul Fernando Nicolas; Lopez, Paula Virginia; Suarez, Gustavo; et al.; Partially stabilized Zirconia (3y-ZrO2) aluminum borate (Al18B4O33) needles composite materials by direct sintering; Int Inst Science Sintering (i I S S); Science Of Sintering; 53; 1; 2-2021; 9-18 0350-820X CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/url/http://www.doiserbia.nb.rs/img/doi/0350-820X/2021/0350-820X2101009M.pdf info:eu-repo/semantics/altIdentifier/doi/10.2298/SOS2101009M |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Int Inst Science Sintering (i I S S) |
publisher.none.fl_str_mv |
Int Inst Science Sintering (i I S S) |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1842269370320945152 |
score |
13.13397 |