Structural and optical properties of ZnO and manganese-doped ZnO

Autores
Gallegos, María Victoria; Peluso, Miguel Andrés; Thomas, Horacio Jorge; Sambeth, Jorge Enrique; Damonte, Laura Cristina
Año de publicación
2016
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
The structural, morphological and optical properties of manganese oxides supported on commercial ZnO,prepared by impregnation with manganese nitrate, were investigated. The nominal compositions of Mnin the samples were 5, 10, 15 and 20%w/w.The X-ray diffraction (XRD) experiments revealed the presenceof the ZnO wurtzite phase in all the samples, and ZnMnO3 was also found in the samples with 15 wt% and20 wt% of Mn. X-ray photoelectron spectroscopy (XPS) showed the presence of Mn2þ and Mn4þ in thexMnZnO samples. The results showed that the Mn2þ ions had substituted the Zn2þ ions withoutchanging the wurtzite structure of ZnO, while Mn4þ might be assigned to the ZnMnO3 impurity phase.The optical band gap was found to be 3.3 eV for undoped ZnO samples and 3.10 eV for Mn-dopedsamples. The lattice defect distribution was investigated using the positron annihilation method. Theresults revealed that the average lifetime is a function of the Mn concentration and the formation of theZnMnO3 phase
Fil: Gallegos, María Victoria. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Peluso, Miguel Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Thomas, Horacio Jorge. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Planta Piloto Multipropósito; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
Fil: Sambeth, Jorge Enrique. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Damonte, Laura Cristina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina
Materia
Mn- ZnO
structural properties
optical properties
XPS
Band Gap Energy
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/42024
Acceder
id CONICETDig_5644f31fbf442c1f2e433dcccdb99556
oai_identifier_str oai:ri.conicet.gov.ar:11336/42024
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Structural and optical properties of ZnO and manganese-doped ZnOGallegos, María VictoriaPeluso, Miguel AndrésThomas, Horacio JorgeSambeth, Jorge EnriqueDamonte, Laura CristinaMn- ZnOstructural propertiesoptical propertiesXPSBand Gap Energyhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2The structural, morphological and optical properties of manganese oxides supported on commercial ZnO,prepared by impregnation with manganese nitrate, were investigated. The nominal compositions of Mnin the samples were 5, 10, 15 and 20%w/w.The X-ray diffraction (XRD) experiments revealed the presenceof the ZnO wurtzite phase in all the samples, and ZnMnO3 was also found in the samples with 15 wt% and20 wt% of Mn. X-ray photoelectron spectroscopy (XPS) showed the presence of Mn2þ and Mn4þ in thexMnZnO samples. The results showed that the Mn2þ ions had substituted the Zn2þ ions withoutchanging the wurtzite structure of ZnO, while Mn4þ might be assigned to the ZnMnO3 impurity phase.The optical band gap was found to be 3.3 eV for undoped ZnO samples and 3.10 eV for Mn-dopedsamples. The lattice defect distribution was investigated using the positron annihilation method. Theresults revealed that the average lifetime is a function of the Mn concentration and the formation of theZnMnO3 phaseFil: Gallegos, María Victoria. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; ArgentinaFil: Peluso, Miguel Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; ArgentinaFil: Thomas, Horacio Jorge. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Planta Piloto Multipropósito; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; ArgentinaFil: Sambeth, Jorge Enrique. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; ArgentinaFil: Damonte, Laura Cristina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; ArgentinaElsevier Science Sa2016-12-29info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/42024Gallegos, María Victoria; Peluso, Miguel Andrés; Thomas, Horacio Jorge; Sambeth, Jorge Enrique; Damonte, Laura Cristina; Structural and optical properties of ZnO and manganese-doped ZnO; Elsevier Science Sa; Journal of Alloys and Compounds; 689; 29-12-2016; 416-4240925-8388CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S0925838816323192info:eu-repo/semantics/altIdentifier/doi/10.1016/j.jallcom.2016.07.283info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-10-22T12:16:43Zoai:ri.conicet.gov.ar:11336/42024instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-10-22 12:16:43.374CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Structural and optical properties of ZnO and manganese-doped ZnO
title Structural and optical properties of ZnO and manganese-doped ZnO
spellingShingle Structural and optical properties of ZnO and manganese-doped ZnO
Gallegos, María Victoria
Mn- ZnO
structural properties
optical properties
XPS
Band Gap Energy
title_short Structural and optical properties of ZnO and manganese-doped ZnO
title_full Structural and optical properties of ZnO and manganese-doped ZnO
title_fullStr Structural and optical properties of ZnO and manganese-doped ZnO
title_full_unstemmed Structural and optical properties of ZnO and manganese-doped ZnO
title_sort Structural and optical properties of ZnO and manganese-doped ZnO
dc.creator.none.fl_str_mv Gallegos, María Victoria
Peluso, Miguel Andrés
Thomas, Horacio Jorge
Sambeth, Jorge Enrique
Damonte, Laura Cristina
author Gallegos, María Victoria
author_facet Gallegos, María Victoria
Peluso, Miguel Andrés
Thomas, Horacio Jorge
Sambeth, Jorge Enrique
Damonte, Laura Cristina
author_role author
author2 Peluso, Miguel Andrés
Thomas, Horacio Jorge
Sambeth, Jorge Enrique
Damonte, Laura Cristina
author2_role author
author
author
author
dc.subject.none.fl_str_mv Mn- ZnO
structural properties
optical properties
XPS
Band Gap Energy
topic Mn- ZnO
structural properties
optical properties
XPS
Band Gap Energy
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv The structural, morphological and optical properties of manganese oxides supported on commercial ZnO,prepared by impregnation with manganese nitrate, were investigated. The nominal compositions of Mnin the samples were 5, 10, 15 and 20%w/w.The X-ray diffraction (XRD) experiments revealed the presenceof the ZnO wurtzite phase in all the samples, and ZnMnO3 was also found in the samples with 15 wt% and20 wt% of Mn. X-ray photoelectron spectroscopy (XPS) showed the presence of Mn2þ and Mn4þ in thexMnZnO samples. The results showed that the Mn2þ ions had substituted the Zn2þ ions withoutchanging the wurtzite structure of ZnO, while Mn4þ might be assigned to the ZnMnO3 impurity phase.The optical band gap was found to be 3.3 eV for undoped ZnO samples and 3.10 eV for Mn-dopedsamples. The lattice defect distribution was investigated using the positron annihilation method. Theresults revealed that the average lifetime is a function of the Mn concentration and the formation of theZnMnO3 phase
Fil: Gallegos, María Victoria. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Peluso, Miguel Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Thomas, Horacio Jorge. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Planta Piloto Multipropósito; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
Fil: Sambeth, Jorge Enrique. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Damonte, Laura Cristina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina
description The structural, morphological and optical properties of manganese oxides supported on commercial ZnO,prepared by impregnation with manganese nitrate, were investigated. The nominal compositions of Mnin the samples were 5, 10, 15 and 20%w/w.The X-ray diffraction (XRD) experiments revealed the presenceof the ZnO wurtzite phase in all the samples, and ZnMnO3 was also found in the samples with 15 wt% and20 wt% of Mn. X-ray photoelectron spectroscopy (XPS) showed the presence of Mn2þ and Mn4þ in thexMnZnO samples. The results showed that the Mn2þ ions had substituted the Zn2þ ions withoutchanging the wurtzite structure of ZnO, while Mn4þ might be assigned to the ZnMnO3 impurity phase.The optical band gap was found to be 3.3 eV for undoped ZnO samples and 3.10 eV for Mn-dopedsamples. The lattice defect distribution was investigated using the positron annihilation method. Theresults revealed that the average lifetime is a function of the Mn concentration and the formation of theZnMnO3 phase
publishDate 2016
dc.date.none.fl_str_mv 2016-12-29
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/42024
Gallegos, María Victoria; Peluso, Miguel Andrés; Thomas, Horacio Jorge; Sambeth, Jorge Enrique; Damonte, Laura Cristina; Structural and optical properties of ZnO and manganese-doped ZnO; Elsevier Science Sa; Journal of Alloys and Compounds; 689; 29-12-2016; 416-424
0925-8388
CONICET Digital
CONICET
url http://hdl.handle.net/11336/42024
identifier_str_mv Gallegos, María Victoria; Peluso, Miguel Andrés; Thomas, Horacio Jorge; Sambeth, Jorge Enrique; Damonte, Laura Cristina; Structural and optical properties of ZnO and manganese-doped ZnO; Elsevier Science Sa; Journal of Alloys and Compounds; 689; 29-12-2016; 416-424
0925-8388
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S0925838816323192
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.jallcom.2016.07.283
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier Science Sa
publisher.none.fl_str_mv Elsevier Science Sa
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1846782588093464576
score 12.982451

Publicaciones similares