Densification of lightweight aluminum borate ceramics by direct sintering of milled powders

Autores
Hernández, Maria Florencia; Suárez, G.; Baudin, C.; Pena Castro, P.; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano
Año de publicación
2018
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Dense aluminum borate (Al 18 B 4 O 33 ) materials were processed by simple milling-sintering of aluminum borate powders obtained by reacting calcined alumina and fine boric acid at temperatures of around 600–800ºC. The effect of milling on the grain size and sintering behavior of the aluminum borate powders was also determined. Sintering began at around 1000°C and was limited by the thermal decomposition (T > 1300 °C) of the borate in to alumina and boron oxide, which volatilize at this temperature. Sub-angular and medium spherical sintered grain microstructures were developed. A hardness of 6 GPa and bulk density below 2.5 g/cm 3 were achieved. The results are accomplished encouraging the structural applications of borate materials.
Fil: Hernández, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Suárez, G.. Instituto de Cerámica y Vidrio de Madrid; España. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Baudin, C.. Instituto de Cerámica y Vidrio de Madrid; España
Fil: Pena Castro, P.. Instituto de Cerámica y Vidrio de Madrid; España
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Materia
ALUMINUM BORATE
PROCESSING
PROPERTIES
SINTERING
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/96463
Acceder
id CONICETDig_47c33da978afcb317a19766c2433126b
oai_identifier_str oai:ri.conicet.gov.ar:11336/96463
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Densification of lightweight aluminum borate ceramics by direct sintering of milled powdersHernández, Maria FlorenciaSuárez, G.Baudin, C.Pena Castro, P.Aglietti, Esteban FaustoRendtorff Birrer, Nicolás MaximilianoALUMINUM BORATEPROCESSINGPROPERTIESSINTERINGhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Dense aluminum borate (Al 18 B 4 O 33 ) materials were processed by simple milling-sintering of aluminum borate powders obtained by reacting calcined alumina and fine boric acid at temperatures of around 600–800ºC. The effect of milling on the grain size and sintering behavior of the aluminum borate powders was also determined. Sintering began at around 1000°C and was limited by the thermal decomposition (T > 1300 °C) of the borate in to alumina and boron oxide, which volatilize at this temperature. Sub-angular and medium spherical sintered grain microstructures were developed. A hardness of 6 GPa and bulk density below 2.5 g/cm 3 were achieved. The results are accomplished encouraging the structural applications of borate materials.Fil: Hernández, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Suárez, G.. Instituto de Cerámica y Vidrio de Madrid; España. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Baudin, C.. Instituto de Cerámica y Vidrio de Madrid; EspañaFil: Pena Castro, P.. Instituto de Cerámica y Vidrio de Madrid; EspañaFil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaTaylor & Francis Ltd2018-10info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/96463Hernández, Maria Florencia; Suárez, G.; Baudin, C.; Pena Castro, P.; Aglietti, Esteban Fausto; et al.; Densification of lightweight aluminum borate ceramics by direct sintering of milled powders; Taylor & Francis Ltd; Journal of Asian Ceramic Societies; 6; 4; 10-2018; 374-3832187-0764CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1080/21870764.2018.1539209info:eu-repo/semantics/altIdentifier/url/https://www.tandfonline.com/doi/full/10.1080/21870764.2018.1539209info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T10:08:56Zoai:ri.conicet.gov.ar:11336/96463instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 10:08:56.92CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Densification of lightweight aluminum borate ceramics by direct sintering of milled powders
title Densification of lightweight aluminum borate ceramics by direct sintering of milled powders
spellingShingle Densification of lightweight aluminum borate ceramics by direct sintering of milled powders
Hernández, Maria Florencia
ALUMINUM BORATE
PROCESSING
PROPERTIES
SINTERING
title_short Densification of lightweight aluminum borate ceramics by direct sintering of milled powders
title_full Densification of lightweight aluminum borate ceramics by direct sintering of milled powders
title_fullStr Densification of lightweight aluminum borate ceramics by direct sintering of milled powders
title_full_unstemmed Densification of lightweight aluminum borate ceramics by direct sintering of milled powders
title_sort Densification of lightweight aluminum borate ceramics by direct sintering of milled powders
dc.creator.none.fl_str_mv Hernández, Maria Florencia
Suárez, G.
Baudin, C.
Pena Castro, P.
Aglietti, Esteban Fausto
Rendtorff Birrer, Nicolás Maximiliano
author Hernández, Maria Florencia
author_facet Hernández, Maria Florencia
Suárez, G.
Baudin, C.
Pena Castro, P.
Aglietti, Esteban Fausto
Rendtorff Birrer, Nicolás Maximiliano
author_role author
author2 Suárez, G.
Baudin, C.
Pena Castro, P.
Aglietti, Esteban Fausto
Rendtorff Birrer, Nicolás Maximiliano
author2_role author
author
author
author
author
dc.subject.none.fl_str_mv ALUMINUM BORATE
PROCESSING
PROPERTIES
SINTERING
topic ALUMINUM BORATE
PROCESSING
PROPERTIES
SINTERING
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv Dense aluminum borate (Al 18 B 4 O 33 ) materials were processed by simple milling-sintering of aluminum borate powders obtained by reacting calcined alumina and fine boric acid at temperatures of around 600–800ºC. The effect of milling on the grain size and sintering behavior of the aluminum borate powders was also determined. Sintering began at around 1000°C and was limited by the thermal decomposition (T > 1300 °C) of the borate in to alumina and boron oxide, which volatilize at this temperature. Sub-angular and medium spherical sintered grain microstructures were developed. A hardness of 6 GPa and bulk density below 2.5 g/cm 3 were achieved. The results are accomplished encouraging the structural applications of borate materials.
Fil: Hernández, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Suárez, G.. Instituto de Cerámica y Vidrio de Madrid; España. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Baudin, C.. Instituto de Cerámica y Vidrio de Madrid; España
Fil: Pena Castro, P.. Instituto de Cerámica y Vidrio de Madrid; España
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
description Dense aluminum borate (Al 18 B 4 O 33 ) materials were processed by simple milling-sintering of aluminum borate powders obtained by reacting calcined alumina and fine boric acid at temperatures of around 600–800ºC. The effect of milling on the grain size and sintering behavior of the aluminum borate powders was also determined. Sintering began at around 1000°C and was limited by the thermal decomposition (T > 1300 °C) of the borate in to alumina and boron oxide, which volatilize at this temperature. Sub-angular and medium spherical sintered grain microstructures were developed. A hardness of 6 GPa and bulk density below 2.5 g/cm 3 were achieved. The results are accomplished encouraging the structural applications of borate materials.
publishDate 2018
dc.date.none.fl_str_mv 2018-10
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/96463
Hernández, Maria Florencia; Suárez, G.; Baudin, C.; Pena Castro, P.; Aglietti, Esteban Fausto; et al.; Densification of lightweight aluminum borate ceramics by direct sintering of milled powders; Taylor & Francis Ltd; Journal of Asian Ceramic Societies; 6; 4; 10-2018; 374-383
2187-0764
CONICET Digital
CONICET
url http://hdl.handle.net/11336/96463
identifier_str_mv Hernández, Maria Florencia; Suárez, G.; Baudin, C.; Pena Castro, P.; Aglietti, Esteban Fausto; et al.; Densification of lightweight aluminum borate ceramics by direct sintering of milled powders; Taylor & Francis Ltd; Journal of Asian Ceramic Societies; 6; 4; 10-2018; 374-383
2187-0764
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1080/21870764.2018.1539209
info:eu-repo/semantics/altIdentifier/url/https://www.tandfonline.com/doi/full/10.1080/21870764.2018.1539209
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Taylor & Francis Ltd
publisher.none.fl_str_mv Taylor & Francis Ltd
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842270062850867200
score 13.13397

Publicaciones similares