Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route

Autores
Gauna, Matías Roberto; Conconi, María Susana; Suárez, Gustavo; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano
Año de publicación
2018
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
In this work, a simple milling sintering route (pressure less) to process dense zircon ceramics from fine (D₅₀ 0.8 µm) zircon powders is explored. Particularly, the milling time effect (0-120 min) and the maximum sintering temperature (1400-1600 °C) were studied. The sintering grade developed microstructure and Vickers hardness (Hv) were evaluated and correlated. The dissociation of silicate into (monoclinic and tetragonal) zirconia and silica was evaluated by X-ray diffraction followed by the Rietveld method; it was found to be below 10 wt% in all the studied ranges. The sintering was enhanced by the milling pretreatment. No sintering additives were incorporated. Dense zircon (porosity below 1 %) ceramics were obtained by a simple milling-sintering route of this high refractory powder at 100-200 °C below the sintering temperature used with conventional processing routes to obtain equivalent final properties. The Vickers hardness reached: 9.0 GPa.
Centro de Tecnología de Recursos Minerales y Cerámica
Facultad de Ciencias Exactas
Materia
Ciencias Exactas
Química
Zircon
Processing
Milling
Sintering
XRD-Rietveld
Nivel de accesibilidad
acceso abierto
Condiciones de uso
http://creativecommons.org/licenses/by/4.0/
Repositorio
SEDICI (UNLP)
Institución
Universidad Nacional de La Plata
OAI Identificador
oai:sedici.unlp.edu.ar:10915/128588
Acceder
id SEDICI_e56656b39173d6906704e34797e609ef
oai_identifier_str oai:sedici.unlp.edu.ar:10915/128588
network_acronym_str SEDICI
repository_id_str 1329
network_name_str SEDICI (UNLP)
spelling Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering RouteGauna, Matías RobertoConconi, María SusanaSuárez, GustavoAglietti, Esteban FaustoRendtorff Birrer, Nicolás MaximilianoCiencias ExactasQuímicaZirconProcessingMillingSinteringXRD-RietveldIn this work, a simple milling sintering route (pressure less) to process dense zircon ceramics from fine (D₅₀ 0.8 µm) zircon powders is explored. Particularly, the milling time effect (0-120 min) and the maximum sintering temperature (1400-1600 °C) were studied. The sintering grade developed microstructure and Vickers hardness (Hv) were evaluated and correlated. The dissociation of silicate into (monoclinic and tetragonal) zirconia and silica was evaluated by X-ray diffraction followed by the Rietveld method; it was found to be below 10 wt% in all the studied ranges. The sintering was enhanced by the milling pretreatment. No sintering additives were incorporated. Dense zircon (porosity below 1 %) ceramics were obtained by a simple milling-sintering route of this high refractory powder at 100-200 °C below the sintering temperature used with conventional processing routes to obtain equivalent final properties. The Vickers hardness reached: 9.0 GPa.Centro de Tecnología de Recursos Minerales y CerámicaFacultad de Ciencias Exactas2018info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionArticulohttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdf15-28http://sedici.unlp.edu.ar/handle/10915/128588enginfo:eu-repo/semantics/altIdentifier/issn/0350-820Xinfo:eu-repo/semantics/altIdentifier/issn/1820-7413info:eu-repo/semantics/altIdentifier/doi/10.2298/sos1801015ginfo:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by/4.0/Creative Commons Attribution 4.0 International (CC BY 4.0)reponame:SEDICI (UNLP)instname:Universidad Nacional de La Platainstacron:UNLP2025-10-15T11:22:53Zoai:sedici.unlp.edu.ar:10915/128588Institucionalhttp://sedici.unlp.edu.ar/Universidad públicaNo correspondehttp://sedici.unlp.edu.ar/oai/snrdalira@sedici.unlp.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:13292025-10-15 11:22:54.197SEDICI (UNLP) - Universidad Nacional de La Platafalse
dc.title.none.fl_str_mv Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route
title Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route
spellingShingle Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route
Gauna, Matías Roberto
Ciencias Exactas
Química
Zircon
Processing
Milling
Sintering
XRD-Rietveld
title_short Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route
title_full Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route
title_fullStr Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route
title_full_unstemmed Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route
title_sort Dense Zircon (ZrSiO<SUB>4</SUB>) Ceramics by a Simple Milling-Sintering Route
dc.creator.none.fl_str_mv Gauna, Matías Roberto
Conconi, María Susana
Suárez, Gustavo
Aglietti, Esteban Fausto
Rendtorff Birrer, Nicolás Maximiliano
author Gauna, Matías Roberto
author_facet Gauna, Matías Roberto
Conconi, María Susana
Suárez, Gustavo
Aglietti, Esteban Fausto
Rendtorff Birrer, Nicolás Maximiliano
author_role author
author2 Conconi, María Susana
Suárez, Gustavo
Aglietti, Esteban Fausto
Rendtorff Birrer, Nicolás Maximiliano
author2_role author
author
author
author
dc.subject.none.fl_str_mv Ciencias Exactas
Química
Zircon
Processing
Milling
Sintering
XRD-Rietveld
topic Ciencias Exactas
Química
Zircon
Processing
Milling
Sintering
XRD-Rietveld
dc.description.none.fl_txt_mv In this work, a simple milling sintering route (pressure less) to process dense zircon ceramics from fine (D₅₀ 0.8 µm) zircon powders is explored. Particularly, the milling time effect (0-120 min) and the maximum sintering temperature (1400-1600 °C) were studied. The sintering grade developed microstructure and Vickers hardness (Hv) were evaluated and correlated. The dissociation of silicate into (monoclinic and tetragonal) zirconia and silica was evaluated by X-ray diffraction followed by the Rietveld method; it was found to be below 10 wt% in all the studied ranges. The sintering was enhanced by the milling pretreatment. No sintering additives were incorporated. Dense zircon (porosity below 1 %) ceramics were obtained by a simple milling-sintering route of this high refractory powder at 100-200 °C below the sintering temperature used with conventional processing routes to obtain equivalent final properties. The Vickers hardness reached: 9.0 GPa.
Centro de Tecnología de Recursos Minerales y Cerámica
Facultad de Ciencias Exactas
description In this work, a simple milling sintering route (pressure less) to process dense zircon ceramics from fine (D₅₀ 0.8 µm) zircon powders is explored. Particularly, the milling time effect (0-120 min) and the maximum sintering temperature (1400-1600 °C) were studied. The sintering grade developed microstructure and Vickers hardness (Hv) were evaluated and correlated. The dissociation of silicate into (monoclinic and tetragonal) zirconia and silica was evaluated by X-ray diffraction followed by the Rietveld method; it was found to be below 10 wt% in all the studied ranges. The sintering was enhanced by the milling pretreatment. No sintering additives were incorporated. Dense zircon (porosity below 1 %) ceramics were obtained by a simple milling-sintering route of this high refractory powder at 100-200 °C below the sintering temperature used with conventional processing routes to obtain equivalent final properties. The Vickers hardness reached: 9.0 GPa.
publishDate 2018
dc.date.none.fl_str_mv 2018
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
Articulo
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://sedici.unlp.edu.ar/handle/10915/128588
url http://sedici.unlp.edu.ar/handle/10915/128588
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/issn/0350-820X
info:eu-repo/semantics/altIdentifier/issn/1820-7413
info:eu-repo/semantics/altIdentifier/doi/10.2298/sos1801015g
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
http://creativecommons.org/licenses/by/4.0/
Creative Commons Attribution 4.0 International (CC BY 4.0)
eu_rights_str_mv openAccess
rights_invalid_str_mv http://creativecommons.org/licenses/by/4.0/
Creative Commons Attribution 4.0 International (CC BY 4.0)
dc.format.none.fl_str_mv application/pdf
15-28
dc.source.none.fl_str_mv reponame:SEDICI (UNLP)
instname:Universidad Nacional de La Plata
instacron:UNLP
reponame_str SEDICI (UNLP)
collection SEDICI (UNLP)
instname_str Universidad Nacional de La Plata
instacron_str UNLP
institution UNLP
repository.name.fl_str_mv SEDICI (UNLP) - Universidad Nacional de La Plata
repository.mail.fl_str_mv alira@sedici.unlp.edu.ar
_version_ 1846064284541386752
score 13.22299

Publicaciones similares