Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis

Autores
Gauna, Matias Roberto; Rendtorff Birrer, Nicolás Maximiliano; Conconi, María Susana; Suarez, Gustavo; Pasquevich, Gustavo Alberto; Rivas Rojas, Patricia Carolina; Damonte, Laura Cristina
Año de publicación
2017
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
By means of Perturbed Angular Correlation (PAC) analysis the resulting phases during mechano-chemical activation process on zircon (ZrSiO4) commercial fine powder (D50 ≅ 0.8 µm) were accurately identified and characterized. A high energy planetary mill was employed with 850 rpm up to 120 min. The phenomenological macroscopic confirmation of the structural change and mechanical activation consisted in an important enhancement of the sintering behavior of the treated fine zircon powders. Three different well known zircon phases were identified and quantified as a function of the milling time: a fully crystalline phase, an aperiodic phase and a distorted phase. A decrease in the first two phases was accompanied by the appearance of the third one; finally, at long term treatments, a partial dissociation was observed. Particularly the resulting zirconium oxide is a highly distorted one. The results were discussed together with those obtained using XRD, SEM and laser scattering. The XRD only showed the partial dissociation of zircon and failed in the differentiation of its nanoconfigurations observed by PAC. The milling of this hard material can be optimized through the performed characterization strategy.
Fil: Gauna, Matias Roberto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Pasquevich, Gustavo Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina
Fil: Rivas Rojas, Patricia Carolina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Agrarias y Forestales; Argentina
Fil: Damonte, Laura Cristina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina
Materia
MILLING
PERTURBED ANGULAR CORRELATIONS
STRUCTURE
ZIRCON POWDER
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/49132
Acceder
id CONICETDig_05afcb3dd9b454bc9d6701498afa744b
oai_identifier_str oai:ri.conicet.gov.ar:11336/49132
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysisGauna, Matias RobertoRendtorff Birrer, Nicolás MaximilianoConconi, María SusanaSuarez, GustavoPasquevich, Gustavo AlbertoRivas Rojas, Patricia CarolinaDamonte, Laura CristinaMILLINGPERTURBED ANGULAR CORRELATIONSSTRUCTUREZIRCON POWDERhttps://purl.org/becyt/ford/1.3https://purl.org/becyt/ford/1By means of Perturbed Angular Correlation (PAC) analysis the resulting phases during mechano-chemical activation process on zircon (ZrSiO4) commercial fine powder (D50 ≅ 0.8 µm) were accurately identified and characterized. A high energy planetary mill was employed with 850 rpm up to 120 min. The phenomenological macroscopic confirmation of the structural change and mechanical activation consisted in an important enhancement of the sintering behavior of the treated fine zircon powders. Three different well known zircon phases were identified and quantified as a function of the milling time: a fully crystalline phase, an aperiodic phase and a distorted phase. A decrease in the first two phases was accompanied by the appearance of the third one; finally, at long term treatments, a partial dissociation was observed. Particularly the resulting zirconium oxide is a highly distorted one. The results were discussed together with those obtained using XRD, SEM and laser scattering. The XRD only showed the partial dissociation of zircon and failed in the differentiation of its nanoconfigurations observed by PAC. The milling of this hard material can be optimized through the performed characterization strategy.Fil: Gauna, Matias Roberto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Pasquevich, Gustavo Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; ArgentinaFil: Rivas Rojas, Patricia Carolina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Agrarias y Forestales; ArgentinaFil: Damonte, Laura Cristina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; ArgentinaElsevier2017-10info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/49132Gauna, Matias Roberto; Rendtorff Birrer, Nicolás Maximiliano; Conconi, María Susana; Suarez, Gustavo; Pasquevich, Gustavo Alberto; et al.; Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis; Elsevier; Ceramics International; 43; 15; 10-2017; 11929-119340272-8842CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1016/j.ceramint.2017.06.041info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0272884217312439info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-17T10:48:18Zoai:ri.conicet.gov.ar:11336/49132instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-17 10:48:18.811CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis
title Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis
spellingShingle Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis
Gauna, Matias Roberto
MILLING
PERTURBED ANGULAR CORRELATIONS
STRUCTURE
ZIRCON POWDER
title_short Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis
title_full Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis
title_fullStr Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis
title_full_unstemmed Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis
title_sort Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis
dc.creator.none.fl_str_mv Gauna, Matias Roberto
Rendtorff Birrer, Nicolás Maximiliano
Conconi, María Susana
Suarez, Gustavo
Pasquevich, Gustavo Alberto
Rivas Rojas, Patricia Carolina
Damonte, Laura Cristina
author Gauna, Matias Roberto
author_facet Gauna, Matias Roberto
Rendtorff Birrer, Nicolás Maximiliano
Conconi, María Susana
Suarez, Gustavo
Pasquevich, Gustavo Alberto
Rivas Rojas, Patricia Carolina
Damonte, Laura Cristina
author_role author
author2 Rendtorff Birrer, Nicolás Maximiliano
Conconi, María Susana
Suarez, Gustavo
Pasquevich, Gustavo Alberto
Rivas Rojas, Patricia Carolina
Damonte, Laura Cristina
author2_role author
author
author
author
author
author
dc.subject.none.fl_str_mv MILLING
PERTURBED ANGULAR CORRELATIONS
STRUCTURE
ZIRCON POWDER
topic MILLING
PERTURBED ANGULAR CORRELATIONS
STRUCTURE
ZIRCON POWDER
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.3
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv By means of Perturbed Angular Correlation (PAC) analysis the resulting phases during mechano-chemical activation process on zircon (ZrSiO4) commercial fine powder (D50 ≅ 0.8 µm) were accurately identified and characterized. A high energy planetary mill was employed with 850 rpm up to 120 min. The phenomenological macroscopic confirmation of the structural change and mechanical activation consisted in an important enhancement of the sintering behavior of the treated fine zircon powders. Three different well known zircon phases were identified and quantified as a function of the milling time: a fully crystalline phase, an aperiodic phase and a distorted phase. A decrease in the first two phases was accompanied by the appearance of the third one; finally, at long term treatments, a partial dissociation was observed. Particularly the resulting zirconium oxide is a highly distorted one. The results were discussed together with those obtained using XRD, SEM and laser scattering. The XRD only showed the partial dissociation of zircon and failed in the differentiation of its nanoconfigurations observed by PAC. The milling of this hard material can be optimized through the performed characterization strategy.
Fil: Gauna, Matias Roberto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Pasquevich, Gustavo Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina
Fil: Rivas Rojas, Patricia Carolina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Agrarias y Forestales; Argentina
Fil: Damonte, Laura Cristina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina
description By means of Perturbed Angular Correlation (PAC) analysis the resulting phases during mechano-chemical activation process on zircon (ZrSiO4) commercial fine powder (D50 ≅ 0.8 µm) were accurately identified and characterized. A high energy planetary mill was employed with 850 rpm up to 120 min. The phenomenological macroscopic confirmation of the structural change and mechanical activation consisted in an important enhancement of the sintering behavior of the treated fine zircon powders. Three different well known zircon phases were identified and quantified as a function of the milling time: a fully crystalline phase, an aperiodic phase and a distorted phase. A decrease in the first two phases was accompanied by the appearance of the third one; finally, at long term treatments, a partial dissociation was observed. Particularly the resulting zirconium oxide is a highly distorted one. The results were discussed together with those obtained using XRD, SEM and laser scattering. The XRD only showed the partial dissociation of zircon and failed in the differentiation of its nanoconfigurations observed by PAC. The milling of this hard material can be optimized through the performed characterization strategy.
publishDate 2017
dc.date.none.fl_str_mv 2017-10
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/49132
Gauna, Matias Roberto; Rendtorff Birrer, Nicolás Maximiliano; Conconi, María Susana; Suarez, Gustavo; Pasquevich, Gustavo Alberto; et al.; Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis; Elsevier; Ceramics International; 43; 15; 10-2017; 11929-11934
0272-8842
CONICET Digital
CONICET
url http://hdl.handle.net/11336/49132
identifier_str_mv Gauna, Matias Roberto; Rendtorff Birrer, Nicolás Maximiliano; Conconi, María Susana; Suarez, Gustavo; Pasquevich, Gustavo Alberto; et al.; Fine zircon (ZrSiO4) powder mechanical activation, a Perturbed Angular Correlation (PAC) analysis; Elsevier; Ceramics International; 43; 15; 10-2017; 11929-11934
0272-8842
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1016/j.ceramint.2017.06.041
info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0272884217312439
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier
publisher.none.fl_str_mv Elsevier
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1843606080475627520
score 13.000565

Publicaciones similares