Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route

Autores
Gauna, Matias Roberto; Conconi, María Susana; Suarez, Gustavo; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano
Año de publicación
2018
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
In this work, a simple milling sintering route (pressure less) to process dense zircon ceramics from fine (D50 0.8 μm) zircon powders is explored. Particularly, the milling time effect (0-120 min) and the maximum sintering temperature (1400-1600 °C) were studied. The sintering grade developed microstructure and Vickers hardness (Hv) were evaluated and correlated. The dissociation of silicate into (monoclinic and tetragonal) zirconia and silica was evaluated by X-ray diffraction followed by the Rietveld method; it was found to be below 10 wt% in all the studied ranges. The sintering was enhanced by the milling pretreatment. No sintering additives were incorporated. Dense zircon (porosity below 1 %) ceramics were obtained by a simple milling-sintering route of this high refractory powder at 100-200 °C below the sintering temperature used with conventional processing routes to obtain equivalent final properties. The Vickers hardness reached: 9.0 GPa.
Fil: Gauna, Matias Roberto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Materia
ZIRCIN
PROCESSING
MILLING
SINTERING
XRD-RIETVELD
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/102941
Acceder
id CONICETDig_ddbcd5b9b201e22521c77542aad1d9c0
oai_identifier_str oai:ri.conicet.gov.ar:11336/102941
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Dense zircon (ZrSiO4) ceramics by a simple milling-sintering routeGauna, Matias RobertoConconi, María SusanaSuarez, GustavoAglietti, Esteban FaustoRendtorff Birrer, Nicolás MaximilianoZIRCINPROCESSINGMILLINGSINTERINGXRD-RIETVELDhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2In this work, a simple milling sintering route (pressure less) to process dense zircon ceramics from fine (D50 0.8 μm) zircon powders is explored. Particularly, the milling time effect (0-120 min) and the maximum sintering temperature (1400-1600 °C) were studied. The sintering grade developed microstructure and Vickers hardness (Hv) were evaluated and correlated. The dissociation of silicate into (monoclinic and tetragonal) zirconia and silica was evaluated by X-ray diffraction followed by the Rietveld method; it was found to be below 10 wt% in all the studied ranges. The sintering was enhanced by the milling pretreatment. No sintering additives were incorporated. Dense zircon (porosity below 1 %) ceramics were obtained by a simple milling-sintering route of this high refractory powder at 100-200 °C below the sintering temperature used with conventional processing routes to obtain equivalent final properties. The Vickers hardness reached: 9.0 GPa.Fil: Gauna, Matias Roberto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaInt Inst Science Sintering (i I S S)2018-04info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/102941Gauna, Matias Roberto; Conconi, María Susana; Suarez, Gustavo; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano; Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route; Int Inst Science Sintering (i I S S); Science Of Sintering; 50; 1; 4-2018; 15-280350-820XCONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.2298/SOS1801015Ginfo:eu-repo/semantics/altIdentifier/url/http://www.doiserbia.nb.rs/Article.aspx?ID=0350-820X1801015G#.Xpk_Q8gzbIUinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-11-05T10:16:17Zoai:ri.conicet.gov.ar:11336/102941instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-11-05 10:16:17.798CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route
title Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route
spellingShingle Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route
Gauna, Matias Roberto
ZIRCIN
PROCESSING
MILLING
SINTERING
XRD-RIETVELD
title_short Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route
title_full Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route
title_fullStr Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route
title_full_unstemmed Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route
title_sort Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route
dc.creator.none.fl_str_mv Gauna, Matias Roberto
Conconi, María Susana
Suarez, Gustavo
Aglietti, Esteban Fausto
Rendtorff Birrer, Nicolás Maximiliano
author Gauna, Matias Roberto
author_facet Gauna, Matias Roberto
Conconi, María Susana
Suarez, Gustavo
Aglietti, Esteban Fausto
Rendtorff Birrer, Nicolás Maximiliano
author_role author
author2 Conconi, María Susana
Suarez, Gustavo
Aglietti, Esteban Fausto
Rendtorff Birrer, Nicolás Maximiliano
author2_role author
author
author
author
dc.subject.none.fl_str_mv ZIRCIN
PROCESSING
MILLING
SINTERING
XRD-RIETVELD
topic ZIRCIN
PROCESSING
MILLING
SINTERING
XRD-RIETVELD
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv In this work, a simple milling sintering route (pressure less) to process dense zircon ceramics from fine (D50 0.8 μm) zircon powders is explored. Particularly, the milling time effect (0-120 min) and the maximum sintering temperature (1400-1600 °C) were studied. The sintering grade developed microstructure and Vickers hardness (Hv) were evaluated and correlated. The dissociation of silicate into (monoclinic and tetragonal) zirconia and silica was evaluated by X-ray diffraction followed by the Rietveld method; it was found to be below 10 wt% in all the studied ranges. The sintering was enhanced by the milling pretreatment. No sintering additives were incorporated. Dense zircon (porosity below 1 %) ceramics were obtained by a simple milling-sintering route of this high refractory powder at 100-200 °C below the sintering temperature used with conventional processing routes to obtain equivalent final properties. The Vickers hardness reached: 9.0 GPa.
Fil: Gauna, Matias Roberto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
description In this work, a simple milling sintering route (pressure less) to process dense zircon ceramics from fine (D50 0.8 μm) zircon powders is explored. Particularly, the milling time effect (0-120 min) and the maximum sintering temperature (1400-1600 °C) were studied. The sintering grade developed microstructure and Vickers hardness (Hv) were evaluated and correlated. The dissociation of silicate into (monoclinic and tetragonal) zirconia and silica was evaluated by X-ray diffraction followed by the Rietveld method; it was found to be below 10 wt% in all the studied ranges. The sintering was enhanced by the milling pretreatment. No sintering additives were incorporated. Dense zircon (porosity below 1 %) ceramics were obtained by a simple milling-sintering route of this high refractory powder at 100-200 °C below the sintering temperature used with conventional processing routes to obtain equivalent final properties. The Vickers hardness reached: 9.0 GPa.
publishDate 2018
dc.date.none.fl_str_mv 2018-04
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/102941
Gauna, Matias Roberto; Conconi, María Susana; Suarez, Gustavo; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano; Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route; Int Inst Science Sintering (i I S S); Science Of Sintering; 50; 1; 4-2018; 15-28
0350-820X
CONICET Digital
CONICET
url http://hdl.handle.net/11336/102941
identifier_str_mv Gauna, Matias Roberto; Conconi, María Susana; Suarez, Gustavo; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano; Dense zircon (ZrSiO4) ceramics by a simple milling-sintering route; Int Inst Science Sintering (i I S S); Science Of Sintering; 50; 1; 4-2018; 15-28
0350-820X
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.2298/SOS1801015G
info:eu-repo/semantics/altIdentifier/url/http://www.doiserbia.nb.rs/Article.aspx?ID=0350-820X1801015G#.Xpk_Q8gzbIU
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Int Inst Science Sintering (i I S S)
publisher.none.fl_str_mv Int Inst Science Sintering (i I S S)
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1847977728704249856
score 13.084122

Publicaciones similares