Corrosion of Painted Galvanneal Steel

Autores
Seré, Pablo Ricardo; Deyá, Marta Cecilia; Elsner, Cecilia Inés; Di Sarli, Alejandro Ramón
Año de publicación
2015
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
The annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel thermally treated. The result is a coating formed by Fe-Zn phases. Its main advantage over the conventional galvanized steel is the absence of the characteristic spangles affecting these coatings and the presence of iron providing better weldability than the pure zinc coating. In this work, the corrosion behavior of pre-treated and painted with environmentally friendly schemes, conventionally hot-dip galvanized, and annealing galvanized (Galvanneal) steel were studied. A Ɣ-mercaptopropyltrimethoxysilane (MTMO) pre-treatment was applied. A waterborne polyurethane paint developed at CIDEPINT was used. Assays were performed in the salt spray and controlled humidity chambers. The metal-paint adhesion was determined by Tape Test. The systems deterioration was evaluated by means of periodical visual inspections, optic and electron microscopes, EDXS, and electrochemical impedance measurements. The MTMO showed to be a good adhesion promoter for the systems exposed to the present testing conditions.
Centro de Investigación y Desarrollo en Tecnología de Pinturas (CIDEPINT)
Materia
Ingeniería Química
Galvanneal
Galvanized steel
Corrosion
Paint
Duplex system
Nivel de accesibilidad
acceso abierto
Condiciones de uso
http://creativecommons.org/licenses/by-nc-nd/4.0/
Repositorio
SEDICI (UNLP)
Institución
Universidad Nacional de La Plata
OAI Identificador
oai:sedici.unlp.edu.ar:10915/81564
Acceder
id SEDICI_b51a2e3dd22437e2599c51664dbb5603
oai_identifier_str oai:sedici.unlp.edu.ar:10915/81564
network_acronym_str SEDICI
repository_id_str 1329
network_name_str SEDICI (UNLP)
spelling Corrosion of Painted Galvanneal SteelSeré, Pablo RicardoDeyá, Marta CeciliaElsner, Cecilia InésDi Sarli, Alejandro RamónIngeniería QuímicaGalvannealGalvanized steelCorrosionPaintDuplex systemThe annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel thermally treated. The result is a coating formed by Fe-Zn phases. Its main advantage over the conventional galvanized steel is the absence of the characteristic spangles affecting these coatings and the presence of iron providing better weldability than the pure zinc coating. In this work, the corrosion behavior of pre-treated and painted with environmentally friendly schemes, conventionally hot-dip galvanized, and annealing galvanized (Galvanneal) steel were studied. A Ɣ-mercaptopropyltrimethoxysilane (MTMO) pre-treatment was applied. A waterborne polyurethane paint developed at CIDEPINT was used. Assays were performed in the salt spray and controlled humidity chambers. The metal-paint adhesion was determined by Tape Test. The systems deterioration was evaluated by means of periodical visual inspections, optic and electron microscopes, EDXS, and electrochemical impedance measurements. The MTMO showed to be a good adhesion promoter for the systems exposed to the present testing conditions.Centro de Investigación y Desarrollo en Tecnología de Pinturas (CIDEPINT)2015info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionArticulohttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdf1-10http://sedici.unlp.edu.ar/handle/10915/81564enginfo:eu-repo/semantics/altIdentifier/issn/2211-8128info:eu-repo/semantics/altIdentifier/doi/10.1016/j.mspro.2015.04.042info:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-nd/4.0/Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0)reponame:SEDICI (UNLP)instname:Universidad Nacional de La Platainstacron:UNLP2025-09-29T11:15:06Zoai:sedici.unlp.edu.ar:10915/81564Institucionalhttp://sedici.unlp.edu.ar/Universidad públicaNo correspondehttp://sedici.unlp.edu.ar/oai/snrdalira@sedici.unlp.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:13292025-09-29 11:15:06.848SEDICI (UNLP) - Universidad Nacional de La Platafalse
dc.title.none.fl_str_mv Corrosion of Painted Galvanneal Steel
title Corrosion of Painted Galvanneal Steel
spellingShingle Corrosion of Painted Galvanneal Steel
Seré, Pablo Ricardo
Ingeniería Química
Galvanneal
Galvanized steel
Corrosion
Paint
Duplex system
title_short Corrosion of Painted Galvanneal Steel
title_full Corrosion of Painted Galvanneal Steel
title_fullStr Corrosion of Painted Galvanneal Steel
title_full_unstemmed Corrosion of Painted Galvanneal Steel
title_sort Corrosion of Painted Galvanneal Steel
dc.creator.none.fl_str_mv Seré, Pablo Ricardo
Deyá, Marta Cecilia
Elsner, Cecilia Inés
Di Sarli, Alejandro Ramón
author Seré, Pablo Ricardo
author_facet Seré, Pablo Ricardo
Deyá, Marta Cecilia
Elsner, Cecilia Inés
Di Sarli, Alejandro Ramón
author_role author
author2 Deyá, Marta Cecilia
Elsner, Cecilia Inés
Di Sarli, Alejandro Ramón
author2_role author
author
author
dc.subject.none.fl_str_mv Ingeniería Química
Galvanneal
Galvanized steel
Corrosion
Paint
Duplex system
topic Ingeniería Química
Galvanneal
Galvanized steel
Corrosion
Paint
Duplex system
dc.description.none.fl_txt_mv The annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel thermally treated. The result is a coating formed by Fe-Zn phases. Its main advantage over the conventional galvanized steel is the absence of the characteristic spangles affecting these coatings and the presence of iron providing better weldability than the pure zinc coating. In this work, the corrosion behavior of pre-treated and painted with environmentally friendly schemes, conventionally hot-dip galvanized, and annealing galvanized (Galvanneal) steel were studied. A Ɣ-mercaptopropyltrimethoxysilane (MTMO) pre-treatment was applied. A waterborne polyurethane paint developed at CIDEPINT was used. Assays were performed in the salt spray and controlled humidity chambers. The metal-paint adhesion was determined by Tape Test. The systems deterioration was evaluated by means of periodical visual inspections, optic and electron microscopes, EDXS, and electrochemical impedance measurements. The MTMO showed to be a good adhesion promoter for the systems exposed to the present testing conditions.
Centro de Investigación y Desarrollo en Tecnología de Pinturas (CIDEPINT)
description The annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel thermally treated. The result is a coating formed by Fe-Zn phases. Its main advantage over the conventional galvanized steel is the absence of the characteristic spangles affecting these coatings and the presence of iron providing better weldability than the pure zinc coating. In this work, the corrosion behavior of pre-treated and painted with environmentally friendly schemes, conventionally hot-dip galvanized, and annealing galvanized (Galvanneal) steel were studied. A Ɣ-mercaptopropyltrimethoxysilane (MTMO) pre-treatment was applied. A waterborne polyurethane paint developed at CIDEPINT was used. Assays were performed in the salt spray and controlled humidity chambers. The metal-paint adhesion was determined by Tape Test. The systems deterioration was evaluated by means of periodical visual inspections, optic and electron microscopes, EDXS, and electrochemical impedance measurements. The MTMO showed to be a good adhesion promoter for the systems exposed to the present testing conditions.
publishDate 2015
dc.date.none.fl_str_mv 2015
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
Articulo
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://sedici.unlp.edu.ar/handle/10915/81564
url http://sedici.unlp.edu.ar/handle/10915/81564
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/issn/2211-8128
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.mspro.2015.04.042
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
http://creativecommons.org/licenses/by-nc-nd/4.0/
Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0)
eu_rights_str_mv openAccess
rights_invalid_str_mv http://creativecommons.org/licenses/by-nc-nd/4.0/
Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0)
dc.format.none.fl_str_mv application/pdf
1-10
dc.source.none.fl_str_mv reponame:SEDICI (UNLP)
instname:Universidad Nacional de La Plata
instacron:UNLP
reponame_str SEDICI (UNLP)
collection SEDICI (UNLP)
instname_str Universidad Nacional de La Plata
instacron_str UNLP
institution UNLP
repository.name.fl_str_mv SEDICI (UNLP) - Universidad Nacional de La Plata
repository.mail.fl_str_mv alira@sedici.unlp.edu.ar
_version_ 1844616022593634304
score 13.070432

Publicaciones similares