Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure
- Autores
- Elsner, Cecilia Ines; Seré, Pablo Ricardo; Di Sarli, Alejandro Ramón
- Año de publicación
- 2012
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- Zinc or 55%Al-Zn alloy-coated steel sheets, either bare or covered by different painting systems, have been exposed for 12 years to the action of the urban atmosphere at the CIDEPINT station located in La Plata (34° 50′ South, 57° 53′, West), province of Buenos Aires, Argentina. The samples exposed surface was evaluated through periodical visual inspections, standardized adhesion tests, and electrochemical impedance measurements. The ambient variables monitored were average annual rains and temperatures, time of wetness, sulphur and chloride concentration, relative humidity, and speed and direction of the winds. It was found that in this atmosphere, the corrosion resistance of the bare 55% Al-Zn/steel sheets was higher than of the galvanized steel, and the polyurethane painting system was more protective than the alkyd and epoxy ones, which degraded after 6-7 years of exposure.
Fil: Elsner, Cecilia Ines. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina
Fil: Seré, Pablo Ricardo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
Fil: Di Sarli, Alejandro Ramón. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina - Materia
-
coatings
paint
galvanized steel
cincalum - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/82293
Ver los metadatos del registro completo
id |
CONICETDig_ba01934e9e7837dc15974b03fb4ca01b |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/82293 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposureElsner, Cecilia InesSeré, Pablo RicardoDi Sarli, Alejandro Ramóncoatingspaintgalvanized steelcincalumhttps://purl.org/becyt/ford/2.4https://purl.org/becyt/ford/2Zinc or 55%Al-Zn alloy-coated steel sheets, either bare or covered by different painting systems, have been exposed for 12 years to the action of the urban atmosphere at the CIDEPINT station located in La Plata (34° 50′ South, 57° 53′, West), province of Buenos Aires, Argentina. The samples exposed surface was evaluated through periodical visual inspections, standardized adhesion tests, and electrochemical impedance measurements. The ambient variables monitored were average annual rains and temperatures, time of wetness, sulphur and chloride concentration, relative humidity, and speed and direction of the winds. It was found that in this atmosphere, the corrosion resistance of the bare 55% Al-Zn/steel sheets was higher than of the galvanized steel, and the polyurethane painting system was more protective than the alkyd and epoxy ones, which degraded after 6-7 years of exposure.Fil: Elsner, Cecilia Ines. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina. Universidad Nacional de La Plata. Facultad de Ingeniería; ArgentinaFil: Seré, Pablo Ricardo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; ArgentinaFil: Di Sarli, Alejandro Ramón. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; ArgentinaHindawi Publishing Corporation2012-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/82293Elsner, Cecilia Ines; Seré, Pablo Ricardo; Di Sarli, Alejandro Ramón; Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure; Hindawi Publishing Corporation; International Journal of Corrosion; 2012; 1-2012; 1-161687-93251687-9333CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1155/2012/419640info:eu-repo/semantics/altIdentifier/url/https://www.hindawi.com/journals/ijc/2012/419640/info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T09:34:09Zoai:ri.conicet.gov.ar:11336/82293instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 09:34:09.873CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure |
title |
Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure |
spellingShingle |
Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure Elsner, Cecilia Ines coatings paint galvanized steel cincalum |
title_short |
Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure |
title_full |
Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure |
title_fullStr |
Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure |
title_full_unstemmed |
Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure |
title_sort |
Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure |
dc.creator.none.fl_str_mv |
Elsner, Cecilia Ines Seré, Pablo Ricardo Di Sarli, Alejandro Ramón |
author |
Elsner, Cecilia Ines |
author_facet |
Elsner, Cecilia Ines Seré, Pablo Ricardo Di Sarli, Alejandro Ramón |
author_role |
author |
author2 |
Seré, Pablo Ricardo Di Sarli, Alejandro Ramón |
author2_role |
author author |
dc.subject.none.fl_str_mv |
coatings paint galvanized steel cincalum |
topic |
coatings paint galvanized steel cincalum |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.4 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
Zinc or 55%Al-Zn alloy-coated steel sheets, either bare or covered by different painting systems, have been exposed for 12 years to the action of the urban atmosphere at the CIDEPINT station located in La Plata (34° 50′ South, 57° 53′, West), province of Buenos Aires, Argentina. The samples exposed surface was evaluated through periodical visual inspections, standardized adhesion tests, and electrochemical impedance measurements. The ambient variables monitored were average annual rains and temperatures, time of wetness, sulphur and chloride concentration, relative humidity, and speed and direction of the winds. It was found that in this atmosphere, the corrosion resistance of the bare 55% Al-Zn/steel sheets was higher than of the galvanized steel, and the polyurethane painting system was more protective than the alkyd and epoxy ones, which degraded after 6-7 years of exposure. Fil: Elsner, Cecilia Ines. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina Fil: Seré, Pablo Ricardo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina Fil: Di Sarli, Alejandro Ramón. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina |
description |
Zinc or 55%Al-Zn alloy-coated steel sheets, either bare or covered by different painting systems, have been exposed for 12 years to the action of the urban atmosphere at the CIDEPINT station located in La Plata (34° 50′ South, 57° 53′, West), province of Buenos Aires, Argentina. The samples exposed surface was evaluated through periodical visual inspections, standardized adhesion tests, and electrochemical impedance measurements. The ambient variables monitored were average annual rains and temperatures, time of wetness, sulphur and chloride concentration, relative humidity, and speed and direction of the winds. It was found that in this atmosphere, the corrosion resistance of the bare 55% Al-Zn/steel sheets was higher than of the galvanized steel, and the polyurethane painting system was more protective than the alkyd and epoxy ones, which degraded after 6-7 years of exposure. |
publishDate |
2012 |
dc.date.none.fl_str_mv |
2012-01 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/82293 Elsner, Cecilia Ines; Seré, Pablo Ricardo; Di Sarli, Alejandro Ramón; Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure; Hindawi Publishing Corporation; International Journal of Corrosion; 2012; 1-2012; 1-16 1687-9325 1687-9333 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/82293 |
identifier_str_mv |
Elsner, Cecilia Ines; Seré, Pablo Ricardo; Di Sarli, Alejandro Ramón; Atmospheric corrosion of painted galvanized and 55%Al-Zn steel sheets: results of 12 years of exposure; Hindawi Publishing Corporation; International Journal of Corrosion; 2012; 1-2012; 1-16 1687-9325 1687-9333 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/doi/10.1155/2012/419640 info:eu-repo/semantics/altIdentifier/url/https://www.hindawi.com/journals/ijc/2012/419640/ |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Hindawi Publishing Corporation |
publisher.none.fl_str_mv |
Hindawi Publishing Corporation |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844613055838683136 |
score |
13.070432 |