Corrosion of painted galvanneal steel

Autores
Seré, Pablo Ricardo; Deya, Marta Cecilia; Elsner, Cecilia Ines; Di Sarli, Alejandro Ramón
Año de publicación
2015
Idioma
inglés
Tipo de recurso
documento de conferencia
Estado
versión publicada
Descripción
The annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel thermally treated. The result is a coatingformed by Fe-Zn phases. Its main advantage over the conventional galvanized steel is the absence of the characteristic spanglesaffecting these coatings and the presence of iron providing better weldability than the pure zinc coating. In this work, thecorrosion behavior of pre-treated and painted with environmentally friendly schemes, conventionally hot-dip galvanized, andannealing galvanized (Galvanneal) steel were studied. A g-mercaptopropyltrimethoxysilane (MTMO) pre-treatment was applied.A waterborne polyurethane paint developed at CIDEPINT was used. Assays were performed in the salt spray and controlled humidity chambers. The metal-paint adhesion was determined by Tape Test. The systems deterioration was evaluated by means of periodical visual inspections, optic and electron microscopes, EDXS, and electrochemical impedance measurements. The MTMO showed to be a good adhesion promoter for the systems exposed to the present testing conditions.
Fil: Seré, Pablo Ricardo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
Fil: Deya, Marta Cecilia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
Fil: Elsner, Cecilia Ines. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
Fil: Di Sarli, Alejandro Ramón. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
13º Congreso Internacional en Ciencia y Tecnología de Metalurgia y Materiales, SAM / CONAMET
Puerto Iguazú
Argentina
Sociedad Argentina de Materiales
Sociedad Chilena de Metalurgia y Materiales
Materia
GALVANNEAL
GALVANIZED STEEL
CORROSION
PAINT
DUPLEX SYSTEM
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/232634
Acceder
id CONICETDig_caa634fc27e22da4299f862843d8d599
oai_identifier_str oai:ri.conicet.gov.ar:11336/232634
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Corrosion of painted galvanneal steelSeré, Pablo RicardoDeya, Marta CeciliaElsner, Cecilia InesDi Sarli, Alejandro RamónGALVANNEALGALVANIZED STEELCORROSIONPAINTDUPLEX SYSTEMhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2The annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel thermally treated. The result is a coatingformed by Fe-Zn phases. Its main advantage over the conventional galvanized steel is the absence of the characteristic spanglesaffecting these coatings and the presence of iron providing better weldability than the pure zinc coating. In this work, thecorrosion behavior of pre-treated and painted with environmentally friendly schemes, conventionally hot-dip galvanized, andannealing galvanized (Galvanneal) steel were studied. A g-mercaptopropyltrimethoxysilane (MTMO) pre-treatment was applied.A waterborne polyurethane paint developed at CIDEPINT was used. Assays were performed in the salt spray and controlled humidity chambers. The metal-paint adhesion was determined by Tape Test. The systems deterioration was evaluated by means of periodical visual inspections, optic and electron microscopes, EDXS, and electrochemical impedance measurements. The MTMO showed to be a good adhesion promoter for the systems exposed to the present testing conditions.Fil: Seré, Pablo Ricardo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; ArgentinaFil: Deya, Marta Cecilia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; ArgentinaFil: Elsner, Cecilia Ines. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; ArgentinaFil: Di Sarli, Alejandro Ramón. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina13º Congreso Internacional en Ciencia y Tecnología de Metalurgia y Materiales, SAM / CONAMETPuerto IguazúArgentinaSociedad Argentina de MaterialesSociedad Chilena de Metalurgia y MaterialesElsevier2015info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/conferenceObjectCongresoJournalhttp://purl.org/coar/resource_type/c_5794info:ar-repo/semantics/documentoDeConferenciaapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/232634Corrosion of painted galvanneal steel; 13º Congreso Internacional en Ciencia y Tecnología de Metalurgia y Materiales, SAM / CONAMET; Puerto Iguazú; Argentina; 2015; 1-102211-8128CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S2211812815000437info:eu-repo/semantics/altIdentifier/doi/10.1016/j.mspro.2015.04.042Internacionalinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T09:59:10Zoai:ri.conicet.gov.ar:11336/232634instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 09:59:11.209CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Corrosion of painted galvanneal steel
title Corrosion of painted galvanneal steel
spellingShingle Corrosion of painted galvanneal steel
Seré, Pablo Ricardo
GALVANNEAL
GALVANIZED STEEL
CORROSION
PAINT
DUPLEX SYSTEM
title_short Corrosion of painted galvanneal steel
title_full Corrosion of painted galvanneal steel
title_fullStr Corrosion of painted galvanneal steel
title_full_unstemmed Corrosion of painted galvanneal steel
title_sort Corrosion of painted galvanneal steel
dc.creator.none.fl_str_mv Seré, Pablo Ricardo
Deya, Marta Cecilia
Elsner, Cecilia Ines
Di Sarli, Alejandro Ramón
author Seré, Pablo Ricardo
author_facet Seré, Pablo Ricardo
Deya, Marta Cecilia
Elsner, Cecilia Ines
Di Sarli, Alejandro Ramón
author_role author
author2 Deya, Marta Cecilia
Elsner, Cecilia Ines
Di Sarli, Alejandro Ramón
author2_role author
author
author
dc.subject.none.fl_str_mv GALVANNEAL
GALVANIZED STEEL
CORROSION
PAINT
DUPLEX SYSTEM
topic GALVANNEAL
GALVANIZED STEEL
CORROSION
PAINT
DUPLEX SYSTEM
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv The annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel thermally treated. The result is a coatingformed by Fe-Zn phases. Its main advantage over the conventional galvanized steel is the absence of the characteristic spanglesaffecting these coatings and the presence of iron providing better weldability than the pure zinc coating. In this work, thecorrosion behavior of pre-treated and painted with environmentally friendly schemes, conventionally hot-dip galvanized, andannealing galvanized (Galvanneal) steel were studied. A g-mercaptopropyltrimethoxysilane (MTMO) pre-treatment was applied.A waterborne polyurethane paint developed at CIDEPINT was used. Assays were performed in the salt spray and controlled humidity chambers. The metal-paint adhesion was determined by Tape Test. The systems deterioration was evaluated by means of periodical visual inspections, optic and electron microscopes, EDXS, and electrochemical impedance measurements. The MTMO showed to be a good adhesion promoter for the systems exposed to the present testing conditions.
Fil: Seré, Pablo Ricardo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
Fil: Deya, Marta Cecilia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
Fil: Elsner, Cecilia Ines. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
Fil: Di Sarli, Alejandro Ramón. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
13º Congreso Internacional en Ciencia y Tecnología de Metalurgia y Materiales, SAM / CONAMET
Puerto Iguazú
Argentina
Sociedad Argentina de Materiales
Sociedad Chilena de Metalurgia y Materiales
description The annealing galvanized steel (Galvanneal) is produced from hot-dip galvanized steel thermally treated. The result is a coatingformed by Fe-Zn phases. Its main advantage over the conventional galvanized steel is the absence of the characteristic spanglesaffecting these coatings and the presence of iron providing better weldability than the pure zinc coating. In this work, thecorrosion behavior of pre-treated and painted with environmentally friendly schemes, conventionally hot-dip galvanized, andannealing galvanized (Galvanneal) steel were studied. A g-mercaptopropyltrimethoxysilane (MTMO) pre-treatment was applied.A waterborne polyurethane paint developed at CIDEPINT was used. Assays were performed in the salt spray and controlled humidity chambers. The metal-paint adhesion was determined by Tape Test. The systems deterioration was evaluated by means of periodical visual inspections, optic and electron microscopes, EDXS, and electrochemical impedance measurements. The MTMO showed to be a good adhesion promoter for the systems exposed to the present testing conditions.
publishDate 2015
dc.date.none.fl_str_mv 2015
dc.type.none.fl_str_mv info:eu-repo/semantics/publishedVersion
info:eu-repo/semantics/conferenceObject
Congreso
Journal
http://purl.org/coar/resource_type/c_5794
info:ar-repo/semantics/documentoDeConferencia
status_str publishedVersion
format conferenceObject
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/232634
Corrosion of painted galvanneal steel; 13º Congreso Internacional en Ciencia y Tecnología de Metalurgia y Materiales, SAM / CONAMET; Puerto Iguazú; Argentina; 2015; 1-10
2211-8128
CONICET Digital
CONICET
url http://hdl.handle.net/11336/232634
identifier_str_mv Corrosion of painted galvanneal steel; 13º Congreso Internacional en Ciencia y Tecnología de Metalurgia y Materiales, SAM / CONAMET; Puerto Iguazú; Argentina; 2015; 1-10
2211-8128
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S2211812815000437
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.mspro.2015.04.042
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.coverage.none.fl_str_mv Internacional
dc.publisher.none.fl_str_mv Elsevier
publisher.none.fl_str_mv Elsevier
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1844613758196908032
score 13.070432

Publicaciones similares