Comparative analysis of TiO<sub>2</sub> layers grown by pulsed laser deposition at atmospheric pressure and pyrolitic nebulization

Autores
Tejerina, Matías Rubén; Gamba, Martina; Ponce Cabrera, L.; Alvira, Fernando Carlos
Año de publicación
2018
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
TiO2 layers and nanolayers are widely studied due to its technological applications. This material could be used in solar cells, transmission, emission or selective reflection, among other applications. In this paper, we show a characterization of layers of TiO2 grown by two different methods, Pulsed Laser Deposition (PLD) at atmospheric pressure and spray pyrolysis (SP). The samples were characterized by SEM, EDS, AFM, XRD and Raman Spectrometry.
Las nanocapas cerámicas son ampliamente estudiadas por su interés en aplicaciones tecnológicas. Estos recubrimientos pueden conformar celdas solares, superficies de transmisión, emisión o reflexión selectiva de luz, entre otras tantas aplicaciones. En este trabajo se presenta una comparación entre películas delgadas de TiO2 depositadas por ablación láser pulsado (PLD) y por nebulización pirolítica (sol-gel spray-pyrolisis, SP). La caracterización de las nanocapas se realizó empleando diversas técnicas como microscopía electrónica de barrido (SEM), espectrometría de dispersión de energía de Rayos X (EDS), microscopia de Fuerza Atómica (AFM), Difracción de Rayos X y espectroscopia Raman.
Facultad de Ciencias Exactas
Centro de Tecnología de Recursos Minerales y Cerámica
Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas
Materia
Ciencias Exactas
Ingeniería
TiO2 layers
spray pyrolysis
air pulsed laser deposition
capas TiO2
spray pirólisis
PLD en aire
Nivel de accesibilidad
acceso abierto
Condiciones de uso
http://creativecommons.org/licenses/by-nc-nd/4.0/
Repositorio
SEDICI (UNLP)
Institución
Universidad Nacional de La Plata
OAI Identificador
oai:sedici.unlp.edu.ar:10915/104455
Acceder
id SEDICI_13c16b0efc3e810ca9ec177c9a4252c3
oai_identifier_str oai:sedici.unlp.edu.ar:10915/104455
network_acronym_str SEDICI
repository_id_str 1329
network_name_str SEDICI (UNLP)
spelling Comparative analysis of TiO<sub>2</sub> layers grown by pulsed laser deposition at atmospheric pressure and pyrolitic nebulizationEstudio comparativo de capas de TiO<sub>2</sub> depositadas por PLD a presión atmosférica y nebulización pirolíticaTejerina, Matías RubénGamba, MartinaPonce Cabrera, L.Alvira, Fernando CarlosCiencias ExactasIngenieríaTiO2 layersspray pyrolysisair pulsed laser depositioncapas TiO2spray pirólisisPLD en aireTiO<sub>2</sub> layers and nanolayers are widely studied due to its technological applications. This material could be used in solar cells, transmission, emission or selective reflection, among other applications. In this paper, we show a characterization of layers of TiO<sub>2</sub> grown by two different methods, Pulsed Laser Deposition (PLD) at atmospheric pressure and spray pyrolysis (SP). The samples were characterized by SEM, EDS, AFM, XRD and Raman Spectrometry.Las nanocapas cerámicas son ampliamente estudiadas por su interés en aplicaciones tecnológicas. Estos recubrimientos pueden conformar celdas solares, superficies de transmisión, emisión o reflexión selectiva de luz, entre otras tantas aplicaciones. En este trabajo se presenta una comparación entre películas delgadas de TiO<sub>2</sub> depositadas por ablación láser pulsado (PLD) y por nebulización pirolítica (sol-gel spray-pyrolisis, SP). La caracterización de las nanocapas se realizó empleando diversas técnicas como microscopía electrónica de barrido (SEM), espectrometría de dispersión de energía de Rayos X (EDS), microscopia de Fuerza Atómica (AFM), Difracción de Rayos X y espectroscopia Raman.Facultad de Ciencias ExactasCentro de Tecnología de Recursos Minerales y CerámicaInstituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas2018-12info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionArticulohttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfhttp://sedici.unlp.edu.ar/handle/10915/104455enginfo:eu-repo/semantics/altIdentifier/url/http://hdl.handle.net/11336/97913info:eu-repo/semantics/altIdentifier/url/https://www.sedoptica.es/Menu_Volumenes/ficha.php?id=1053info:eu-repo/semantics/altIdentifier/issn/2171-8814info:eu-repo/semantics/altIdentifier/doi/10.7149/OPA.51.4.50301info:eu-repo/semantics/altIdentifier/hdl/11336/97913info:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-nd/4.0/Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0)reponame:SEDICI (UNLP)instname:Universidad Nacional de La Platainstacron:UNLP2025-09-03T10:55:00Zoai:sedici.unlp.edu.ar:10915/104455Institucionalhttp://sedici.unlp.edu.ar/Universidad públicaNo correspondehttp://sedici.unlp.edu.ar/oai/snrdalira@sedici.unlp.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:13292025-09-03 10:55:01.216SEDICI (UNLP) - Universidad Nacional de La Platafalse
dc.title.none.fl_str_mv Comparative analysis of TiO<sub>2</sub> layers grown by pulsed laser deposition at atmospheric pressure and pyrolitic nebulization
Estudio comparativo de capas de TiO<sub>2</sub> depositadas por PLD a presión atmosférica y nebulización pirolítica
title Comparative analysis of TiO<sub>2</sub> layers grown by pulsed laser deposition at atmospheric pressure and pyrolitic nebulization
spellingShingle Comparative analysis of TiO<sub>2</sub> layers grown by pulsed laser deposition at atmospheric pressure and pyrolitic nebulization
Tejerina, Matías Rubén
Ciencias Exactas
Ingeniería
TiO2 layers
spray pyrolysis
air pulsed laser deposition
capas TiO2
spray pirólisis
PLD en aire
title_short Comparative analysis of TiO<sub>2</sub> layers grown by pulsed laser deposition at atmospheric pressure and pyrolitic nebulization
title_full Comparative analysis of TiO<sub>2</sub> layers grown by pulsed laser deposition at atmospheric pressure and pyrolitic nebulization
title_fullStr Comparative analysis of TiO<sub>2</sub> layers grown by pulsed laser deposition at atmospheric pressure and pyrolitic nebulization
title_full_unstemmed Comparative analysis of TiO<sub>2</sub> layers grown by pulsed laser deposition at atmospheric pressure and pyrolitic nebulization
title_sort Comparative analysis of TiO<sub>2</sub> layers grown by pulsed laser deposition at atmospheric pressure and pyrolitic nebulization
dc.creator.none.fl_str_mv Tejerina, Matías Rubén
Gamba, Martina
Ponce Cabrera, L.
Alvira, Fernando Carlos
author Tejerina, Matías Rubén
author_facet Tejerina, Matías Rubén
Gamba, Martina
Ponce Cabrera, L.
Alvira, Fernando Carlos
author_role author
author2 Gamba, Martina
Ponce Cabrera, L.
Alvira, Fernando Carlos
author2_role author
author
author
dc.subject.none.fl_str_mv Ciencias Exactas
Ingeniería
TiO2 layers
spray pyrolysis
air pulsed laser deposition
capas TiO2
spray pirólisis
PLD en aire
topic Ciencias Exactas
Ingeniería
TiO2 layers
spray pyrolysis
air pulsed laser deposition
capas TiO2
spray pirólisis
PLD en aire
dc.description.none.fl_txt_mv TiO<sub>2</sub> layers and nanolayers are widely studied due to its technological applications. This material could be used in solar cells, transmission, emission or selective reflection, among other applications. In this paper, we show a characterization of layers of TiO<sub>2</sub> grown by two different methods, Pulsed Laser Deposition (PLD) at atmospheric pressure and spray pyrolysis (SP). The samples were characterized by SEM, EDS, AFM, XRD and Raman Spectrometry.
Las nanocapas cerámicas son ampliamente estudiadas por su interés en aplicaciones tecnológicas. Estos recubrimientos pueden conformar celdas solares, superficies de transmisión, emisión o reflexión selectiva de luz, entre otras tantas aplicaciones. En este trabajo se presenta una comparación entre películas delgadas de TiO<sub>2</sub> depositadas por ablación láser pulsado (PLD) y por nebulización pirolítica (sol-gel spray-pyrolisis, SP). La caracterización de las nanocapas se realizó empleando diversas técnicas como microscopía electrónica de barrido (SEM), espectrometría de dispersión de energía de Rayos X (EDS), microscopia de Fuerza Atómica (AFM), Difracción de Rayos X y espectroscopia Raman.
Facultad de Ciencias Exactas
Centro de Tecnología de Recursos Minerales y Cerámica
Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas
description TiO<sub>2</sub> layers and nanolayers are widely studied due to its technological applications. This material could be used in solar cells, transmission, emission or selective reflection, among other applications. In this paper, we show a characterization of layers of TiO<sub>2</sub> grown by two different methods, Pulsed Laser Deposition (PLD) at atmospheric pressure and spray pyrolysis (SP). The samples were characterized by SEM, EDS, AFM, XRD and Raman Spectrometry.
publishDate 2018
dc.date.none.fl_str_mv 2018-12
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
Articulo
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://sedici.unlp.edu.ar/handle/10915/104455
url http://sedici.unlp.edu.ar/handle/10915/104455
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/http://hdl.handle.net/11336/97913
info:eu-repo/semantics/altIdentifier/url/https://www.sedoptica.es/Menu_Volumenes/ficha.php?id=1053
info:eu-repo/semantics/altIdentifier/issn/2171-8814
info:eu-repo/semantics/altIdentifier/doi/10.7149/OPA.51.4.50301
info:eu-repo/semantics/altIdentifier/hdl/11336/97913
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
http://creativecommons.org/licenses/by-nc-nd/4.0/
Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0)
eu_rights_str_mv openAccess
rights_invalid_str_mv http://creativecommons.org/licenses/by-nc-nd/4.0/
Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International (CC BY-NC-ND 4.0)
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:SEDICI (UNLP)
instname:Universidad Nacional de La Plata
instacron:UNLP
reponame_str SEDICI (UNLP)
collection SEDICI (UNLP)
instname_str Universidad Nacional de La Plata
instacron_str UNLP
institution UNLP
repository.name.fl_str_mv SEDICI (UNLP) - Universidad Nacional de La Plata
repository.mail.fl_str_mv alira@sedici.unlp.edu.ar
_version_ 1842260436569817088
score 13.13397

Publicaciones similares