Influencia del raleo sobre las características anatómicas y las propiedades físicas y mecánicas de la madera de Pinus taeda L. de la región NE de la Argentina.

Autores
Winck, Rosa Ángela
Año de publicación
2013
Idioma
español castellano
Tipo de recurso
tesis de maestría
Estado
versión aceptada
Colaborador/a o director/a de tesis
Area, María Cristina
Suirezs, Teresa María
Descripción
Fil: Winck, Rosa Ángela. Universidad Nacional de Misiones. Facultad de Ciencias Exactas, Químicas y Naturales. Maestría en Ciencias de la Madera, Celulosa y Papel; Argentina.
La región NE de la Argentina se caracteriza por el cultivo de especies forestales de rápido crecimiento con la finalidad de atender a los diferentes mercados de madera. El Pinus taeda constituye una de las especies de mayor importancia, debido a su alta tasa de crecimiento y a las características de la madera, que la hace apta para variados usos industriales. Se estima que la materia prima resultante de estas plantaciones podría presentar un alto porcentaje de leño juvenil, baja densidad, bajo valor de módulo de elasticidad, bajo módulo de rotura y alto valor de ángulo micro-fibrilar, lo que influiría negativamente en las propiedades tecnológicas de la madera. Con el objeto de evaluar la influencia del tratamiento silvicultural de raleo sobre las propiedades anatómicas, físicas y mecánicas de la madera de Pinus taeda de 20 años de edad proveniente de una plantación con densidad inicial de 1960 plantas/ha, sobre la que se aplicaron diferentes intensidades de raleo (0%, 50%, 75% y 87,5% de la densidad inicial). La plantación estaba ubicada en el Departamento Iguazú, provincia de Misiones, Argentina. De esta plantación se tomaron muestras a 1,30 m de altura y a diferentes distancias radiales de un total de 24 árboles, con 6 ejemplares por cada tratamiento de raleo. Se realizaron las mediciones de las distintas variables y se alcanzaron los siguientes resultados, los valores de resistencia a la flexión, densidad básica de la troza y longitud de traqueidas fueron similares para los tratamientos de raleo de 0%, 50% y 75%. Mientras que para el tratamiento más fuerte, con 87,5% de raleo, estas propiedades fueron negativamente afectadas, a excepción de la longitud de traqueidas que fue mayor para este tratamiento. Los valores de resistencia a la compresión paralela a las fibras y la densidad básica a 1,30 m de altura, disminuyeron para intensidades de raleo iguales o mayores al 75%. El tratamiento sin raleo presentó mayor valor medio de contracción volumétrica (11%), debido a que las traqueidas presentaron mayor proporción de leño tardío y mayor espesor de pared. Los tratamientos con 0% y 50% de raleo favorecieron la obtención de mejores valores de espesor de pared y ángulo microfibrilar. Las propiedades anatómicas, físicas y mecánicas mejoraron sustancialmente en la dirección que va desde la médula hacia la corteza, independientemente de la intensidad de raleo. Se concluye que con 50% de raleo se logró optimizar todas las propiedades de la madera evaluadas en este trabajo, que con un raleo igual a 75% algunas propiedades fueron afectadas, y que con raleo de 87,5% todas las propiedades sufrieron cambios significativos. Se determinaron asociaciones moderadas para el ángulo microfibrilar con la densidad básica a 1,30 m y con la densidad básica media de la 2º troza, como así también con los módulos de elasticidad y de rotura a la flexión estática y a la compresión paralela a las fibras. También se determinó que la longitud de traqueidas está fuertemente relacionada con el tamaño del árbol y con la longitud de la copa verde.
Argentine NE region is characteristic for culture of fast growing forest species in order to attend different timber markets. Pinus taeda represents one of the most important species, due to the high growing rate and wood characteristics, which makes it suitable for various industrial uses. It is assumed that the raw material resulting from these plantations could present a high percentage of juvenile wood, low density, low value of modulus of elasticity and modulus of rupture and high micro-fibrillar angle, which would adversely affect technological properties of the wood. With the aim of evaluating the influence of the silvicultural treatment of thinning on the anatomical, physical and mechanical properties of Pinus taeda wood of 20 years of age from a plantation with an initial density of 1960 plants/ha, on which different intensities of thinning where applied (0%, 50%, 75% and 87.5% of the initial density). Plantation was located in the Department Iguazú, of Misiones province, Argentina. From this plantation samples were extracted at 1.30 m height and at different radial distances from a total of 24 trees, with 6 trees for each thinning treatment. The different variables were measured arriving to the following results, the values of bending strength, basic density and tracheids length, were similar for treatments with 0%, 50% and 75 % thinning. However for a stronger 87.5% thinning treatment these properties were adversely affected, except for the length of tracheids which were longer for this treatment. Values of parallel to the fibers compression strength and wood density at 1.30 m height, decreased for thinning intensities equal or greater than 75%. Without thinning treatment showed higher average volumetric shrinkage (11%), because the tracheids had higher proportion of late wood and thicker walls. Treatments with 0 % and 50% of thinning favored obtaining better values for the wall thickness and the micro-fibrillar angle. Anatomical, physical and mechanical properties were substantially improved in the direction going from pith to bark, regardless of the intensity of thinning. It is concluded that with 50% thinning an improvement in all wood properties evaluated in this work was achieved, with 75 % thinning some properties were affected, and with an 87.5 % thinning all properties have experimented significant changes. Moderate associations were determined for micro-fibrillar angle to basic density at 1.30 m height and with the average basic density of the 2º log, as well as with the modulus of elasticity and modulus of rupture in static bending and in compression parallel to the fibers. It was also found that tracheid length is strongly related to tree size and the length of the green cover of the trees.
Materia
Ciencias de la Vida
Madera
Celulosa
Papel
Tratamiento Silvicultural
Ángulo Microfibrilar
Longitud de Traqueidas
Espesor de Pared
Propiedades de la Madera
Silvicultural Treatment
Micro-Fibril Angle
Length of Tracheids
Wall Thickness
Wood Properties
Nivel de accesibilidad
acceso abierto
Condiciones de uso
Atribución-NoComercial-CompartirIgual 4.0 Internacional
Repositorio
Repositorio Institucional Digital de la Universidad Nacional de Misiones (UNaM)
Institución
Universidad Nacional de Misiones
OAI Identificador
oai:rid.unam.edu.ar:20.500.12219/2479

id RIDUNaM_fb977ef7709b5d27a0df5cacade1d3a9
oai_identifier_str oai:rid.unam.edu.ar:20.500.12219/2479
network_acronym_str RIDUNaM
repository_id_str
network_name_str Repositorio Institucional Digital de la Universidad Nacional de Misiones (UNaM)
spelling Influencia del raleo sobre las características anatómicas y las propiedades físicas y mecánicas de la madera de Pinus taeda L. de la región NE de la Argentina.Winck, Rosa ÁngelaCiencias de la VidaMaderaCelulosaPapelTratamiento SilviculturalÁngulo MicrofibrilarLongitud de TraqueidasEspesor de ParedPropiedades de la MaderaSilvicultural TreatmentMicro-Fibril AngleLength of TracheidsWall ThicknessWood PropertiesFil: Winck, Rosa Ángela. Universidad Nacional de Misiones. Facultad de Ciencias Exactas, Químicas y Naturales. Maestría en Ciencias de la Madera, Celulosa y Papel; Argentina.La región NE de la Argentina se caracteriza por el cultivo de especies forestales de rápido crecimiento con la finalidad de atender a los diferentes mercados de madera. El Pinus taeda constituye una de las especies de mayor importancia, debido a su alta tasa de crecimiento y a las características de la madera, que la hace apta para variados usos industriales. Se estima que la materia prima resultante de estas plantaciones podría presentar un alto porcentaje de leño juvenil, baja densidad, bajo valor de módulo de elasticidad, bajo módulo de rotura y alto valor de ángulo micro-fibrilar, lo que influiría negativamente en las propiedades tecnológicas de la madera. Con el objeto de evaluar la influencia del tratamiento silvicultural de raleo sobre las propiedades anatómicas, físicas y mecánicas de la madera de Pinus taeda de 20 años de edad proveniente de una plantación con densidad inicial de 1960 plantas/ha, sobre la que se aplicaron diferentes intensidades de raleo (0%, 50%, 75% y 87,5% de la densidad inicial). La plantación estaba ubicada en el Departamento Iguazú, provincia de Misiones, Argentina. De esta plantación se tomaron muestras a 1,30 m de altura y a diferentes distancias radiales de un total de 24 árboles, con 6 ejemplares por cada tratamiento de raleo. Se realizaron las mediciones de las distintas variables y se alcanzaron los siguientes resultados, los valores de resistencia a la flexión, densidad básica de la troza y longitud de traqueidas fueron similares para los tratamientos de raleo de 0%, 50% y 75%. Mientras que para el tratamiento más fuerte, con 87,5% de raleo, estas propiedades fueron negativamente afectadas, a excepción de la longitud de traqueidas que fue mayor para este tratamiento. Los valores de resistencia a la compresión paralela a las fibras y la densidad básica a 1,30 m de altura, disminuyeron para intensidades de raleo iguales o mayores al 75%. El tratamiento sin raleo presentó mayor valor medio de contracción volumétrica (11%), debido a que las traqueidas presentaron mayor proporción de leño tardío y mayor espesor de pared. Los tratamientos con 0% y 50% de raleo favorecieron la obtención de mejores valores de espesor de pared y ángulo microfibrilar. Las propiedades anatómicas, físicas y mecánicas mejoraron sustancialmente en la dirección que va desde la médula hacia la corteza, independientemente de la intensidad de raleo. Se concluye que con 50% de raleo se logró optimizar todas las propiedades de la madera evaluadas en este trabajo, que con un raleo igual a 75% algunas propiedades fueron afectadas, y que con raleo de 87,5% todas las propiedades sufrieron cambios significativos. Se determinaron asociaciones moderadas para el ángulo microfibrilar con la densidad básica a 1,30 m y con la densidad básica media de la 2º troza, como así también con los módulos de elasticidad y de rotura a la flexión estática y a la compresión paralela a las fibras. También se determinó que la longitud de traqueidas está fuertemente relacionada con el tamaño del árbol y con la longitud de la copa verde.Argentine NE region is characteristic for culture of fast growing forest species in order to attend different timber markets. Pinus taeda represents one of the most important species, due to the high growing rate and wood characteristics, which makes it suitable for various industrial uses. It is assumed that the raw material resulting from these plantations could present a high percentage of juvenile wood, low density, low value of modulus of elasticity and modulus of rupture and high micro-fibrillar angle, which would adversely affect technological properties of the wood. With the aim of evaluating the influence of the silvicultural treatment of thinning on the anatomical, physical and mechanical properties of Pinus taeda wood of 20 years of age from a plantation with an initial density of 1960 plants/ha, on which different intensities of thinning where applied (0%, 50%, 75% and 87.5% of the initial density). Plantation was located in the Department Iguazú, of Misiones province, Argentina. From this plantation samples were extracted at 1.30 m height and at different radial distances from a total of 24 trees, with 6 trees for each thinning treatment. The different variables were measured arriving to the following results, the values of bending strength, basic density and tracheids length, were similar for treatments with 0%, 50% and 75 % thinning. However for a stronger 87.5% thinning treatment these properties were adversely affected, except for the length of tracheids which were longer for this treatment. Values of parallel to the fibers compression strength and wood density at 1.30 m height, decreased for thinning intensities equal or greater than 75%. Without thinning treatment showed higher average volumetric shrinkage (11%), because the tracheids had higher proportion of late wood and thicker walls. Treatments with 0 % and 50% of thinning favored obtaining better values for the wall thickness and the micro-fibrillar angle. Anatomical, physical and mechanical properties were substantially improved in the direction going from pith to bark, regardless of the intensity of thinning. It is concluded that with 50% thinning an improvement in all wood properties evaluated in this work was achieved, with 75 % thinning some properties were affected, and with an 87.5 % thinning all properties have experimented significant changes. Moderate associations were determined for micro-fibrillar angle to basic density at 1.30 m height and with the average basic density of the 2º log, as well as with the modulus of elasticity and modulus of rupture in static bending and in compression parallel to the fibers. It was also found that tracheid length is strongly related to tree size and the length of the green cover of the trees.Universidad Nacional de Misiones. Facultad de Ciencias Exactas, Químicas y Naturales. Secretaría de Investigación y Posgrado. Maestría en Ciencias de la Madera, Celulosa y Papel.Area, María CristinaSuirezs, Teresa María2013-10-08info:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/acceptedVersionhttp://purl.org/coar/resource_type/c_bdccinfo:ar-repo/semantics/tesisDeMaestriaapplication/pdfapplication/pdf2 MBhttps://hdl.handle.net/20.500.12219/2479spaARG Posadas (Misiones)2010-2013info:eu-repo/semantics/openAccessAtribución-NoComercial-CompartirIgual 4.0 Internacionalhttp://creativecommons.org/licenses/by-nc-sa/4.0/reponame:Repositorio Institucional Digital de la Universidad Nacional de Misiones (UNaM)instname:Universidad Nacional de Misiones2025-09-29T15:02:29Zoai:rid.unam.edu.ar:20.500.12219/2479instacron:UNAMInstitucionalhttps://rid.unam.edu.ar/Universidad públicahttps://www.unam.edu.ar/https://rid.unam.edu.ar/oai/rsnrdArgentinaopendoar:2025-09-29 15:02:29.797Repositorio Institucional Digital de la Universidad Nacional de Misiones (UNaM) - Universidad Nacional de Misionesfalse
dc.title.none.fl_str_mv Influencia del raleo sobre las características anatómicas y las propiedades físicas y mecánicas de la madera de Pinus taeda L. de la región NE de la Argentina.
title Influencia del raleo sobre las características anatómicas y las propiedades físicas y mecánicas de la madera de Pinus taeda L. de la región NE de la Argentina.
spellingShingle Influencia del raleo sobre las características anatómicas y las propiedades físicas y mecánicas de la madera de Pinus taeda L. de la región NE de la Argentina.
Winck, Rosa Ángela
Ciencias de la Vida
Madera
Celulosa
Papel
Tratamiento Silvicultural
Ángulo Microfibrilar
Longitud de Traqueidas
Espesor de Pared
Propiedades de la Madera
Silvicultural Treatment
Micro-Fibril Angle
Length of Tracheids
Wall Thickness
Wood Properties
title_short Influencia del raleo sobre las características anatómicas y las propiedades físicas y mecánicas de la madera de Pinus taeda L. de la región NE de la Argentina.
title_full Influencia del raleo sobre las características anatómicas y las propiedades físicas y mecánicas de la madera de Pinus taeda L. de la región NE de la Argentina.
title_fullStr Influencia del raleo sobre las características anatómicas y las propiedades físicas y mecánicas de la madera de Pinus taeda L. de la región NE de la Argentina.
title_full_unstemmed Influencia del raleo sobre las características anatómicas y las propiedades físicas y mecánicas de la madera de Pinus taeda L. de la región NE de la Argentina.
title_sort Influencia del raleo sobre las características anatómicas y las propiedades físicas y mecánicas de la madera de Pinus taeda L. de la región NE de la Argentina.
dc.creator.none.fl_str_mv Winck, Rosa Ángela
author Winck, Rosa Ángela
author_facet Winck, Rosa Ángela
author_role author
dc.contributor.none.fl_str_mv Area, María Cristina
Suirezs, Teresa María
dc.subject.none.fl_str_mv Ciencias de la Vida
Madera
Celulosa
Papel
Tratamiento Silvicultural
Ángulo Microfibrilar
Longitud de Traqueidas
Espesor de Pared
Propiedades de la Madera
Silvicultural Treatment
Micro-Fibril Angle
Length of Tracheids
Wall Thickness
Wood Properties
topic Ciencias de la Vida
Madera
Celulosa
Papel
Tratamiento Silvicultural
Ángulo Microfibrilar
Longitud de Traqueidas
Espesor de Pared
Propiedades de la Madera
Silvicultural Treatment
Micro-Fibril Angle
Length of Tracheids
Wall Thickness
Wood Properties
dc.description.none.fl_txt_mv Fil: Winck, Rosa Ángela. Universidad Nacional de Misiones. Facultad de Ciencias Exactas, Químicas y Naturales. Maestría en Ciencias de la Madera, Celulosa y Papel; Argentina.
La región NE de la Argentina se caracteriza por el cultivo de especies forestales de rápido crecimiento con la finalidad de atender a los diferentes mercados de madera. El Pinus taeda constituye una de las especies de mayor importancia, debido a su alta tasa de crecimiento y a las características de la madera, que la hace apta para variados usos industriales. Se estima que la materia prima resultante de estas plantaciones podría presentar un alto porcentaje de leño juvenil, baja densidad, bajo valor de módulo de elasticidad, bajo módulo de rotura y alto valor de ángulo micro-fibrilar, lo que influiría negativamente en las propiedades tecnológicas de la madera. Con el objeto de evaluar la influencia del tratamiento silvicultural de raleo sobre las propiedades anatómicas, físicas y mecánicas de la madera de Pinus taeda de 20 años de edad proveniente de una plantación con densidad inicial de 1960 plantas/ha, sobre la que se aplicaron diferentes intensidades de raleo (0%, 50%, 75% y 87,5% de la densidad inicial). La plantación estaba ubicada en el Departamento Iguazú, provincia de Misiones, Argentina. De esta plantación se tomaron muestras a 1,30 m de altura y a diferentes distancias radiales de un total de 24 árboles, con 6 ejemplares por cada tratamiento de raleo. Se realizaron las mediciones de las distintas variables y se alcanzaron los siguientes resultados, los valores de resistencia a la flexión, densidad básica de la troza y longitud de traqueidas fueron similares para los tratamientos de raleo de 0%, 50% y 75%. Mientras que para el tratamiento más fuerte, con 87,5% de raleo, estas propiedades fueron negativamente afectadas, a excepción de la longitud de traqueidas que fue mayor para este tratamiento. Los valores de resistencia a la compresión paralela a las fibras y la densidad básica a 1,30 m de altura, disminuyeron para intensidades de raleo iguales o mayores al 75%. El tratamiento sin raleo presentó mayor valor medio de contracción volumétrica (11%), debido a que las traqueidas presentaron mayor proporción de leño tardío y mayor espesor de pared. Los tratamientos con 0% y 50% de raleo favorecieron la obtención de mejores valores de espesor de pared y ángulo microfibrilar. Las propiedades anatómicas, físicas y mecánicas mejoraron sustancialmente en la dirección que va desde la médula hacia la corteza, independientemente de la intensidad de raleo. Se concluye que con 50% de raleo se logró optimizar todas las propiedades de la madera evaluadas en este trabajo, que con un raleo igual a 75% algunas propiedades fueron afectadas, y que con raleo de 87,5% todas las propiedades sufrieron cambios significativos. Se determinaron asociaciones moderadas para el ángulo microfibrilar con la densidad básica a 1,30 m y con la densidad básica media de la 2º troza, como así también con los módulos de elasticidad y de rotura a la flexión estática y a la compresión paralela a las fibras. También se determinó que la longitud de traqueidas está fuertemente relacionada con el tamaño del árbol y con la longitud de la copa verde.
Argentine NE region is characteristic for culture of fast growing forest species in order to attend different timber markets. Pinus taeda represents one of the most important species, due to the high growing rate and wood characteristics, which makes it suitable for various industrial uses. It is assumed that the raw material resulting from these plantations could present a high percentage of juvenile wood, low density, low value of modulus of elasticity and modulus of rupture and high micro-fibrillar angle, which would adversely affect technological properties of the wood. With the aim of evaluating the influence of the silvicultural treatment of thinning on the anatomical, physical and mechanical properties of Pinus taeda wood of 20 years of age from a plantation with an initial density of 1960 plants/ha, on which different intensities of thinning where applied (0%, 50%, 75% and 87.5% of the initial density). Plantation was located in the Department Iguazú, of Misiones province, Argentina. From this plantation samples were extracted at 1.30 m height and at different radial distances from a total of 24 trees, with 6 trees for each thinning treatment. The different variables were measured arriving to the following results, the values of bending strength, basic density and tracheids length, were similar for treatments with 0%, 50% and 75 % thinning. However for a stronger 87.5% thinning treatment these properties were adversely affected, except for the length of tracheids which were longer for this treatment. Values of parallel to the fibers compression strength and wood density at 1.30 m height, decreased for thinning intensities equal or greater than 75%. Without thinning treatment showed higher average volumetric shrinkage (11%), because the tracheids had higher proportion of late wood and thicker walls. Treatments with 0 % and 50% of thinning favored obtaining better values for the wall thickness and the micro-fibrillar angle. Anatomical, physical and mechanical properties were substantially improved in the direction going from pith to bark, regardless of the intensity of thinning. It is concluded that with 50% thinning an improvement in all wood properties evaluated in this work was achieved, with 75 % thinning some properties were affected, and with an 87.5 % thinning all properties have experimented significant changes. Moderate associations were determined for micro-fibrillar angle to basic density at 1.30 m height and with the average basic density of the 2º log, as well as with the modulus of elasticity and modulus of rupture in static bending and in compression parallel to the fibers. It was also found that tracheid length is strongly related to tree size and the length of the green cover of the trees.
description Fil: Winck, Rosa Ángela. Universidad Nacional de Misiones. Facultad de Ciencias Exactas, Químicas y Naturales. Maestría en Ciencias de la Madera, Celulosa y Papel; Argentina.
publishDate 2013
dc.date.none.fl_str_mv 2013-10-08
dc.type.none.fl_str_mv info:eu-repo/semantics/masterThesis
info:eu-repo/semantics/acceptedVersion
http://purl.org/coar/resource_type/c_bdcc
info:ar-repo/semantics/tesisDeMaestria
format masterThesis
status_str acceptedVersion
dc.identifier.none.fl_str_mv https://hdl.handle.net/20.500.12219/2479
url https://hdl.handle.net/20.500.12219/2479
dc.language.none.fl_str_mv spa
language spa
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
Atribución-NoComercial-CompartirIgual 4.0 Internacional
http://creativecommons.org/licenses/by-nc-sa/4.0/
eu_rights_str_mv openAccess
rights_invalid_str_mv Atribución-NoComercial-CompartirIgual 4.0 Internacional
http://creativecommons.org/licenses/by-nc-sa/4.0/
dc.format.none.fl_str_mv application/pdf
application/pdf
2 MB
dc.coverage.none.fl_str_mv ARG Posadas (Misiones)
2010-2013
dc.publisher.none.fl_str_mv Universidad Nacional de Misiones. Facultad de Ciencias Exactas, Químicas y Naturales. Secretaría de Investigación y Posgrado. Maestría en Ciencias de la Madera, Celulosa y Papel.
publisher.none.fl_str_mv Universidad Nacional de Misiones. Facultad de Ciencias Exactas, Químicas y Naturales. Secretaría de Investigación y Posgrado. Maestría en Ciencias de la Madera, Celulosa y Papel.
dc.source.none.fl_str_mv reponame:Repositorio Institucional Digital de la Universidad Nacional de Misiones (UNaM)
instname:Universidad Nacional de Misiones
reponame_str Repositorio Institucional Digital de la Universidad Nacional de Misiones (UNaM)
collection Repositorio Institucional Digital de la Universidad Nacional de Misiones (UNaM)
instname_str Universidad Nacional de Misiones
repository.name.fl_str_mv Repositorio Institucional Digital de la Universidad Nacional de Misiones (UNaM) - Universidad Nacional de Misiones
repository.mail.fl_str_mv
_version_ 1844623287546544128
score 12.559606