Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41

Autores
Fellenz, Nicolás Antonio; Marchetti, Sergio Gustavo; Bengoa, Jose Fernando; Mercader, Roberto Carlos; Stewart, Silvana Jacqueline
Año de publicación
2006
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
A solid of 7.7 wt% iron-loaded MCM-41 was obtained by impregnating the mesoporous material with an Fe-carrying organic salt after subjecting the matrix to a silylation treatment. The Mössbauer and magnetic results show that the as-prepared composite is mainly made up of fine Fe3O4 particles that display a superparamagnetic relaxation at room temperature and block at ≈42 K. A percentage of ≈24% of the iron-containing phases is magnetically blocked at room temperature, and belongs to Fe3O4 that undergoes the Verwey transition. In addition, there is a minor Fe(III) phase that remains paramagnetic down to 4.2 K. © 2006 Elsevier B.V. All rights reserved.
Fil: Fellenz, Nicolás Antonio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Marchetti, Sergio Gustavo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Bengoa, Jose Fernando. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Mercader, Roberto Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina
Fil: Stewart, Silvana Jacqueline. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina
Materia
Chemical Synthesis
Fe3o4
Magnetic Nanoarrays Synthesis
Magnetically Ordered Materials
Mcm-41
Nanofabrications
Nanoparticles Magnetism
Nanostructures
Silylated Mcm-41
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/57688
Acceder
id CONICETDig_f1a891175fb9f31fbbe62afaa7f007a3
oai_identifier_str oai:ri.conicet.gov.ar:11336/57688
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41Fellenz, Nicolás AntonioMarchetti, Sergio GustavoBengoa, Jose FernandoMercader, Roberto CarlosStewart, Silvana JacquelineChemical SynthesisFe3o4Magnetic Nanoarrays SynthesisMagnetically Ordered MaterialsMcm-41NanofabricationsNanoparticles MagnetismNanostructuresSilylated Mcm-41https://purl.org/becyt/ford/1.3https://purl.org/becyt/ford/1A solid of 7.7 wt% iron-loaded MCM-41 was obtained by impregnating the mesoporous material with an Fe-carrying organic salt after subjecting the matrix to a silylation treatment. The Mössbauer and magnetic results show that the as-prepared composite is mainly made up of fine Fe3O4 particles that display a superparamagnetic relaxation at room temperature and block at ≈42 K. A percentage of ≈24% of the iron-containing phases is magnetically blocked at room temperature, and belongs to Fe3O4 that undergoes the Verwey transition. In addition, there is a minor Fe(III) phase that remains paramagnetic down to 4.2 K. © 2006 Elsevier B.V. All rights reserved.Fil: Fellenz, Nicolás Antonio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; ArgentinaFil: Marchetti, Sergio Gustavo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; ArgentinaFil: Bengoa, Jose Fernando. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; ArgentinaFil: Mercader, Roberto Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; ArgentinaFil: Stewart, Silvana Jacqueline. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; ArgentinaElsevier Science2006-11info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/57688Fellenz, Nicolás Antonio; Marchetti, Sergio Gustavo; Bengoa, Jose Fernando; Mercader, Roberto Carlos; Stewart, Silvana Jacqueline; Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41; Elsevier Science; Journal of Magnetism and Magnetic Materials; 306; 1; 11-2006; 30-340304-8853CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1016/j.jmmm.2006.02.101info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0304885306004136info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T09:50:09Zoai:ri.conicet.gov.ar:11336/57688instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 09:50:09.447CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41
title Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41
spellingShingle Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41
Fellenz, Nicolás Antonio
Chemical Synthesis
Fe3o4
Magnetic Nanoarrays Synthesis
Magnetically Ordered Materials
Mcm-41
Nanofabrications
Nanoparticles Magnetism
Nanostructures
Silylated Mcm-41
title_short Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41
title_full Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41
title_fullStr Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41
title_full_unstemmed Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41
title_sort Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41
dc.creator.none.fl_str_mv Fellenz, Nicolás Antonio
Marchetti, Sergio Gustavo
Bengoa, Jose Fernando
Mercader, Roberto Carlos
Stewart, Silvana Jacqueline
author Fellenz, Nicolás Antonio
author_facet Fellenz, Nicolás Antonio
Marchetti, Sergio Gustavo
Bengoa, Jose Fernando
Mercader, Roberto Carlos
Stewart, Silvana Jacqueline
author_role author
author2 Marchetti, Sergio Gustavo
Bengoa, Jose Fernando
Mercader, Roberto Carlos
Stewart, Silvana Jacqueline
author2_role author
author
author
author
dc.subject.none.fl_str_mv Chemical Synthesis
Fe3o4
Magnetic Nanoarrays Synthesis
Magnetically Ordered Materials
Mcm-41
Nanofabrications
Nanoparticles Magnetism
Nanostructures
Silylated Mcm-41
topic Chemical Synthesis
Fe3o4
Magnetic Nanoarrays Synthesis
Magnetically Ordered Materials
Mcm-41
Nanofabrications
Nanoparticles Magnetism
Nanostructures
Silylated Mcm-41
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.3
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv A solid of 7.7 wt% iron-loaded MCM-41 was obtained by impregnating the mesoporous material with an Fe-carrying organic salt after subjecting the matrix to a silylation treatment. The Mössbauer and magnetic results show that the as-prepared composite is mainly made up of fine Fe3O4 particles that display a superparamagnetic relaxation at room temperature and block at ≈42 K. A percentage of ≈24% of the iron-containing phases is magnetically blocked at room temperature, and belongs to Fe3O4 that undergoes the Verwey transition. In addition, there is a minor Fe(III) phase that remains paramagnetic down to 4.2 K. © 2006 Elsevier B.V. All rights reserved.
Fil: Fellenz, Nicolás Antonio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Marchetti, Sergio Gustavo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Bengoa, Jose Fernando. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Mercader, Roberto Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina
Fil: Stewart, Silvana Jacqueline. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Física La Plata. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Física La Plata; Argentina
description A solid of 7.7 wt% iron-loaded MCM-41 was obtained by impregnating the mesoporous material with an Fe-carrying organic salt after subjecting the matrix to a silylation treatment. The Mössbauer and magnetic results show that the as-prepared composite is mainly made up of fine Fe3O4 particles that display a superparamagnetic relaxation at room temperature and block at ≈42 K. A percentage of ≈24% of the iron-containing phases is magnetically blocked at room temperature, and belongs to Fe3O4 that undergoes the Verwey transition. In addition, there is a minor Fe(III) phase that remains paramagnetic down to 4.2 K. © 2006 Elsevier B.V. All rights reserved.
publishDate 2006
dc.date.none.fl_str_mv 2006-11
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/57688
Fellenz, Nicolás Antonio; Marchetti, Sergio Gustavo; Bengoa, Jose Fernando; Mercader, Roberto Carlos; Stewart, Silvana Jacqueline; Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41; Elsevier Science; Journal of Magnetism and Magnetic Materials; 306; 1; 11-2006; 30-34
0304-8853
CONICET Digital
CONICET
url http://hdl.handle.net/11336/57688
identifier_str_mv Fellenz, Nicolás Antonio; Marchetti, Sergio Gustavo; Bengoa, Jose Fernando; Mercader, Roberto Carlos; Stewart, Silvana Jacqueline; Synthesis and magnetic characterization of magnetite particles embedded in mesoporous MCM-41; Elsevier Science; Journal of Magnetism and Magnetic Materials; 306; 1; 11-2006; 30-34
0304-8853
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1016/j.jmmm.2006.02.101
info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0304885306004136
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier Science
publisher.none.fl_str_mv Elsevier Science
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842269016068980736
score 13.13397

Publicaciones similares