ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation

Autores
Anson, Marcia; Marchese, Jose; Garis, Eduardo; Ochoa, Nelio Ariel; Pagliero, Cecilia Liliana
Año de publicación
2004
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
The performance of various novel mixed matrix composite (MMC) membranes for separation of CO2 from CH4 was investigated as a function of carbon loading. Acrylonitrile-butadiene-styrene (ABS) copolymer was used as the polymer matrix and two micro-mesoporous activated carbons (AC) were chosen as inorganic fillers. A thorough analysis of the effect of temperature and pressure on the permeation rates of CO2 and CH4 and selective properties of the ABS-AC composite membranes was done. Measurements were made for each system at four different temperatures in the range 20-50 °C, and in the feed pressure range from 2 to 8 × 105 Pa. The ABS-AC membranes showed a simultaneous increase of CO2 gas permeabilities (40-600%) and CO2/CH4 selectivities (40-100%) over the intrinsic ABS permselectivity by increasing the percentage of carbon loaded in the mixed matrix composite membrane.
Fil: Anson, Marcia. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; Argentina
Fil: Marchese, Jose. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich". Universidad Nacional de San Luis. Facultad de Ciencias Físico Matemáticas y Naturales. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich"; Argentina. Universidad de Valladolid; España. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; Argentina
Fil: Garis, Eduardo. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; Argentina
Fil: Ochoa, Nelio Ariel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; Argentina
Fil: Pagliero, Cecilia Liliana. Universidad Nacional de Río Cuarto. Facultad de Ciencias Exactas Fisicoquímicas y Naturales. Instituto de Investigaciones en Tecnologías Energéticas y Materiales Avanzados. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones en Tecnologías Energéticas y Materiales Avanzados; Argentina. Universidad Nacional de Río Cuarto. Facultad de Ingeniería; Argentina
Materia
ABS COPOLYMER
ACTIVATED CARBON
CO2/CH4 SEPARATION
GAS PERMEATION
MIXED MATRIX
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/138669
Acceder
id CONICETDig_9c7787eac1f283e205adea09ac5d0420
oai_identifier_str oai:ri.conicet.gov.ar:11336/138669
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separationAnson, MarciaMarchese, JoseGaris, EduardoOchoa, Nelio ArielPagliero, Cecilia LilianaABS COPOLYMERACTIVATED CARBONCO2/CH4 SEPARATIONGAS PERMEATIONMIXED MATRIXhttps://purl.org/becyt/ford/2.4https://purl.org/becyt/ford/2The performance of various novel mixed matrix composite (MMC) membranes for separation of CO2 from CH4 was investigated as a function of carbon loading. Acrylonitrile-butadiene-styrene (ABS) copolymer was used as the polymer matrix and two micro-mesoporous activated carbons (AC) were chosen as inorganic fillers. A thorough analysis of the effect of temperature and pressure on the permeation rates of CO2 and CH4 and selective properties of the ABS-AC composite membranes was done. Measurements were made for each system at four different temperatures in the range 20-50 °C, and in the feed pressure range from 2 to 8 × 105 Pa. The ABS-AC membranes showed a simultaneous increase of CO2 gas permeabilities (40-600%) and CO2/CH4 selectivities (40-100%) over the intrinsic ABS permselectivity by increasing the percentage of carbon loaded in the mixed matrix composite membrane.Fil: Anson, Marcia. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; ArgentinaFil: Marchese, Jose. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich". Universidad Nacional de San Luis. Facultad de Ciencias Físico Matemáticas y Naturales. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich"; Argentina. Universidad de Valladolid; España. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; ArgentinaFil: Garis, Eduardo. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; ArgentinaFil: Ochoa, Nelio Ariel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; ArgentinaFil: Pagliero, Cecilia Liliana. Universidad Nacional de Río Cuarto. Facultad de Ciencias Exactas Fisicoquímicas y Naturales. Instituto de Investigaciones en Tecnologías Energéticas y Materiales Avanzados. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones en Tecnologías Energéticas y Materiales Avanzados; Argentina. Universidad Nacional de Río Cuarto. Facultad de Ingeniería; ArgentinaElsevier Science2004-11-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/138669Anson, Marcia; Marchese, Jose; Garis, Eduardo; Ochoa, Nelio Ariel; Pagliero, Cecilia Liliana; ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation; Elsevier Science; Journal of Membrane Science; 243; 1-2; 1-11-2004; 19-280376-7388CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/abs/pii/S0376738804003138info:eu-repo/semantics/altIdentifier/doi/10.1016/j.memsci.2004.05.008info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-10-15T14:58:09Zoai:ri.conicet.gov.ar:11336/138669instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-10-15 14:58:09.993CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation
title ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation
spellingShingle ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation
Anson, Marcia
ABS COPOLYMER
ACTIVATED CARBON
CO2/CH4 SEPARATION
GAS PERMEATION
MIXED MATRIX
title_short ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation
title_full ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation
title_fullStr ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation
title_full_unstemmed ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation
title_sort ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation
dc.creator.none.fl_str_mv Anson, Marcia
Marchese, Jose
Garis, Eduardo
Ochoa, Nelio Ariel
Pagliero, Cecilia Liliana
author Anson, Marcia
author_facet Anson, Marcia
Marchese, Jose
Garis, Eduardo
Ochoa, Nelio Ariel
Pagliero, Cecilia Liliana
author_role author
author2 Marchese, Jose
Garis, Eduardo
Ochoa, Nelio Ariel
Pagliero, Cecilia Liliana
author2_role author
author
author
author
dc.subject.none.fl_str_mv ABS COPOLYMER
ACTIVATED CARBON
CO2/CH4 SEPARATION
GAS PERMEATION
MIXED MATRIX
topic ABS COPOLYMER
ACTIVATED CARBON
CO2/CH4 SEPARATION
GAS PERMEATION
MIXED MATRIX
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.4
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv The performance of various novel mixed matrix composite (MMC) membranes for separation of CO2 from CH4 was investigated as a function of carbon loading. Acrylonitrile-butadiene-styrene (ABS) copolymer was used as the polymer matrix and two micro-mesoporous activated carbons (AC) were chosen as inorganic fillers. A thorough analysis of the effect of temperature and pressure on the permeation rates of CO2 and CH4 and selective properties of the ABS-AC composite membranes was done. Measurements were made for each system at four different temperatures in the range 20-50 °C, and in the feed pressure range from 2 to 8 × 105 Pa. The ABS-AC membranes showed a simultaneous increase of CO2 gas permeabilities (40-600%) and CO2/CH4 selectivities (40-100%) over the intrinsic ABS permselectivity by increasing the percentage of carbon loaded in the mixed matrix composite membrane.
Fil: Anson, Marcia. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; Argentina
Fil: Marchese, Jose. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich". Universidad Nacional de San Luis. Facultad de Ciencias Físico Matemáticas y Naturales. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich"; Argentina. Universidad de Valladolid; España. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; Argentina
Fil: Garis, Eduardo. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; Argentina
Fil: Ochoa, Nelio Ariel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina. Universidad Nacional de San Luis. Laboratorio de Ciencias de Superficies y Medios Porosos; Argentina
Fil: Pagliero, Cecilia Liliana. Universidad Nacional de Río Cuarto. Facultad de Ciencias Exactas Fisicoquímicas y Naturales. Instituto de Investigaciones en Tecnologías Energéticas y Materiales Avanzados. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones en Tecnologías Energéticas y Materiales Avanzados; Argentina. Universidad Nacional de Río Cuarto. Facultad de Ingeniería; Argentina
description The performance of various novel mixed matrix composite (MMC) membranes for separation of CO2 from CH4 was investigated as a function of carbon loading. Acrylonitrile-butadiene-styrene (ABS) copolymer was used as the polymer matrix and two micro-mesoporous activated carbons (AC) were chosen as inorganic fillers. A thorough analysis of the effect of temperature and pressure on the permeation rates of CO2 and CH4 and selective properties of the ABS-AC composite membranes was done. Measurements were made for each system at four different temperatures in the range 20-50 °C, and in the feed pressure range from 2 to 8 × 105 Pa. The ABS-AC membranes showed a simultaneous increase of CO2 gas permeabilities (40-600%) and CO2/CH4 selectivities (40-100%) over the intrinsic ABS permselectivity by increasing the percentage of carbon loaded in the mixed matrix composite membrane.
publishDate 2004
dc.date.none.fl_str_mv 2004-11-01
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/138669
Anson, Marcia; Marchese, Jose; Garis, Eduardo; Ochoa, Nelio Ariel; Pagliero, Cecilia Liliana; ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation; Elsevier Science; Journal of Membrane Science; 243; 1-2; 1-11-2004; 19-28
0376-7388
CONICET Digital
CONICET
url http://hdl.handle.net/11336/138669
identifier_str_mv Anson, Marcia; Marchese, Jose; Garis, Eduardo; Ochoa, Nelio Ariel; Pagliero, Cecilia Liliana; ABS copolymer-activated carbon mixed matrix membranes for CO 2/CH4 separation; Elsevier Science; Journal of Membrane Science; 243; 1-2; 1-11-2004; 19-28
0376-7388
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/abs/pii/S0376738804003138
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.memsci.2004.05.008
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier Science
publisher.none.fl_str_mv Elsevier Science
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1846083121106124800
score 13.22299

Publicaciones similares