Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect

Autores
Pinna, Eliana Guadalupe; Martínez, A.A.; Tunez, Fernando Marcelo; Drajlin Gordón, Diego Sebastián; Rodriguez, M.H.
Año de publicación
2019
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
This work shows the results of a comparative hydrometallurgical study of LiCoO2 leaching, obtained from the cathodesof spent lithium-ion batteries (LIBs), with HF and HF/H2O2. The operational parameters researched were H2O2 and HFconcentrations, solid-liquid ratio, stirring speed, temperature and reaction time. The experimental results indicated that the bestworking conditions, with dissolution values close to 100%, were 348 K, 330 rpm, 30 min, 8 g/L, HF 0.6 M and H2O2 0.7 M.Thermodynamic study of the dissociation of HF in aqueous solution and EH-pH diagrams for Li-H2O, Co-H2O and Li-Co-F-H2Osystems were performed. The results showed the feasibility of extracting and recovering metals contained in the sample.Keywords: LiCoO2, LIBs, reducing agent, thermodynamic
Fil: Pinna, Eliana Guadalupe. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Martínez, A.A.. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; Argentina
Fil: Tunez, Fernando Marcelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Drajlin Gordón, Diego Sebastián. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; Argentina
Fil: Rodriguez, M.H.. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; Argentina
Materia
LiCoO2
LIBs
reducing agent
thermodynamic
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/124915
Acceder
id CONICETDig_81a507c2f0e9f09d6ce5ead51c87a461
oai_identifier_str oai:ri.conicet.gov.ar:11336/124915
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effectLixiviación ácida de licoo2 proveniente de libs: estudio termodinámico y del efecto de un agente reductorPinna, Eliana GuadalupeMartínez, A.A.Tunez, Fernando MarceloDrajlin Gordón, Diego SebastiánRodriguez, M.H.LiCoO2LIBsreducing agentthermodynamichttps://purl.org/becyt/ford/1.4https://purl.org/becyt/ford/1This work shows the results of a comparative hydrometallurgical study of LiCoO2 leaching, obtained from the cathodesof spent lithium-ion batteries (LIBs), with HF and HF/H2O2. The operational parameters researched were H2O2 and HFconcentrations, solid-liquid ratio, stirring speed, temperature and reaction time. The experimental results indicated that the bestworking conditions, with dissolution values close to 100%, were 348 K, 330 rpm, 30 min, 8 g/L, HF 0.6 M and H2O2 0.7 M.Thermodynamic study of the dissociation of HF in aqueous solution and EH-pH diagrams for Li-H2O, Co-H2O and Li-Co-F-H2Osystems were performed. The results showed the feasibility of extracting and recovering metals contained in the sample.Keywords: LiCoO2, LIBs, reducing agent, thermodynamicFil: Pinna, Eliana Guadalupe. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; ArgentinaFil: Martínez, A.A.. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; ArgentinaFil: Tunez, Fernando Marcelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; ArgentinaFil: Drajlin Gordón, Diego Sebastián. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; ArgentinaFil: Rodriguez, M.H.. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; ArgentinaUniversidad Autónoma Metropolitana-Iztapalapa2019-04info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/124915Pinna, Eliana Guadalupe; Martínez, A.A.; Tunez, Fernando Marcelo; Drajlin Gordón, Diego Sebastián; Rodriguez, M.H.; Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect; Universidad Autónoma Metropolitana-Iztapalapa; Revista Mexicana de Ingeniería Química; 18; 2; 4-2019; 441-4491665-2738CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://www.rmiq.org/ojs311/index.php/rmiq/article/view/198info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T10:10:42Zoai:ri.conicet.gov.ar:11336/124915instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 10:10:42.71CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect
Lixiviación ácida de licoo2 proveniente de libs: estudio termodinámico y del efecto de un agente reductor
title Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect
spellingShingle Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect
Pinna, Eliana Guadalupe
LiCoO2
LIBs
reducing agent
thermodynamic
title_short Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect
title_full Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect
title_fullStr Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect
title_full_unstemmed Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect
title_sort Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect
dc.creator.none.fl_str_mv Pinna, Eliana Guadalupe
Martínez, A.A.
Tunez, Fernando Marcelo
Drajlin Gordón, Diego Sebastián
Rodriguez, M.H.
author Pinna, Eliana Guadalupe
author_facet Pinna, Eliana Guadalupe
Martínez, A.A.
Tunez, Fernando Marcelo
Drajlin Gordón, Diego Sebastián
Rodriguez, M.H.
author_role author
author2 Martínez, A.A.
Tunez, Fernando Marcelo
Drajlin Gordón, Diego Sebastián
Rodriguez, M.H.
author2_role author
author
author
author
dc.subject.none.fl_str_mv LiCoO2
LIBs
reducing agent
thermodynamic
topic LiCoO2
LIBs
reducing agent
thermodynamic
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.4
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv This work shows the results of a comparative hydrometallurgical study of LiCoO2 leaching, obtained from the cathodesof spent lithium-ion batteries (LIBs), with HF and HF/H2O2. The operational parameters researched were H2O2 and HFconcentrations, solid-liquid ratio, stirring speed, temperature and reaction time. The experimental results indicated that the bestworking conditions, with dissolution values close to 100%, were 348 K, 330 rpm, 30 min, 8 g/L, HF 0.6 M and H2O2 0.7 M.Thermodynamic study of the dissociation of HF in aqueous solution and EH-pH diagrams for Li-H2O, Co-H2O and Li-Co-F-H2Osystems were performed. The results showed the feasibility of extracting and recovering metals contained in the sample.Keywords: LiCoO2, LIBs, reducing agent, thermodynamic
Fil: Pinna, Eliana Guadalupe. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Martínez, A.A.. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; Argentina
Fil: Tunez, Fernando Marcelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Drajlin Gordón, Diego Sebastián. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; Argentina
Fil: Rodriguez, M.H.. Universidad Nacional de Cuyo. Facultad de Ciencias Exactas y Naturales; Argentina
description This work shows the results of a comparative hydrometallurgical study of LiCoO2 leaching, obtained from the cathodesof spent lithium-ion batteries (LIBs), with HF and HF/H2O2. The operational parameters researched were H2O2 and HFconcentrations, solid-liquid ratio, stirring speed, temperature and reaction time. The experimental results indicated that the bestworking conditions, with dissolution values close to 100%, were 348 K, 330 rpm, 30 min, 8 g/L, HF 0.6 M and H2O2 0.7 M.Thermodynamic study of the dissociation of HF in aqueous solution and EH-pH diagrams for Li-H2O, Co-H2O and Li-Co-F-H2Osystems were performed. The results showed the feasibility of extracting and recovering metals contained in the sample.Keywords: LiCoO2, LIBs, reducing agent, thermodynamic
publishDate 2019
dc.date.none.fl_str_mv 2019-04
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/124915
Pinna, Eliana Guadalupe; Martínez, A.A.; Tunez, Fernando Marcelo; Drajlin Gordón, Diego Sebastián; Rodriguez, M.H.; Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect; Universidad Autónoma Metropolitana-Iztapalapa; Revista Mexicana de Ingeniería Química; 18; 2; 4-2019; 441-449
1665-2738
CONICET Digital
CONICET
url http://hdl.handle.net/11336/124915
identifier_str_mv Pinna, Eliana Guadalupe; Martínez, A.A.; Tunez, Fernando Marcelo; Drajlin Gordón, Diego Sebastián; Rodriguez, M.H.; Acid leaching of licoo2 from libs: thermodynamic study and reducing agent effect; Universidad Autónoma Metropolitana-Iztapalapa; Revista Mexicana de Ingeniería Química; 18; 2; 4-2019; 441-449
1665-2738
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/http://www.rmiq.org/ojs311/index.php/rmiq/article/view/198
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Universidad Autónoma Metropolitana-Iztapalapa
publisher.none.fl_str_mv Universidad Autónoma Metropolitana-Iztapalapa
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842270130815369216
score 13.13397

Publicaciones similares