Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar
- Autores
- Egli, Walter Alfredo; Seré, Pablo Ricardo; Bengoa, Leandro Nicolás; Versino, Florencia; Bruno, Sonia; Lazzarino, Andrés; Espósito, Fernando
- Año de publicación
- 2013
- Idioma
- inglés
- Tipo de recurso
- documento de conferencia
- Estado
- versión publicada
- Descripción
- Conductor rolls in the electrogalvanizing line are made of Duplex Stainless Steel (DSS) and after some time in service they suffer surface deterioration leading to surface defects and rejections in high quality products. Repassivation kinetics and susceptibility to pitting corrosion for the austenitic and ferritic phases were studied. An electrochemical treatment that reproduces the actual industrial corrosive situation was applied to test different alloys in the laboratory. The Hastelloy C22 showed the best performance and was evaluated in the line during a complete production batch. The new roll presented a slight deterioration, much lower than the DSS rolls.
Fil: Egli, Walter Alfredo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
Fil: Seré, Pablo Ricardo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
Fil: Bengoa, Leandro Nicolás. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina
Fil: Versino, Florencia. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina
Fil: Bruno, Sonia. Rede-ar Tenaris Siderca; Argentina
Fil: Lazzarino, Andrés. Ternium Siderar; Argentina
Fil: Espósito, Fernando. Ternium Siderar; Argentina
GALVATECH 2013 & APGalva 2013: 9th International Conference on Zinc and Zinc Alloy Coated Steel Sheet and 2nd AsiaPacific Galvanizing Conference
Beijing
China
The Chinese Society for Metals - Materia
-
CORROSION
CONDUCTOR
ROLL ELECTROGALVANIZING - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/230658
Ver los metadatos del registro completo
id |
CONICETDig_7d16be25220c35e8f2518c1a5e845930 |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/230658 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Corrosion of conductor rolls in the electrogalvanizing line at Ternium SiderarEgli, Walter AlfredoSeré, Pablo RicardoBengoa, Leandro NicolásVersino, FlorenciaBruno, SoniaLazzarino, AndrésEspósito, FernandoCORROSIONCONDUCTORROLL ELECTROGALVANIZINGhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2https://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Conductor rolls in the electrogalvanizing line are made of Duplex Stainless Steel (DSS) and after some time in service they suffer surface deterioration leading to surface defects and rejections in high quality products. Repassivation kinetics and susceptibility to pitting corrosion for the austenitic and ferritic phases were studied. An electrochemical treatment that reproduces the actual industrial corrosive situation was applied to test different alloys in the laboratory. The Hastelloy C22 showed the best performance and was evaluated in the line during a complete production batch. The new roll presented a slight deterioration, much lower than the DSS rolls.Fil: Egli, Walter Alfredo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; ArgentinaFil: Seré, Pablo Ricardo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; ArgentinaFil: Bengoa, Leandro Nicolás. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; ArgentinaFil: Versino, Florencia. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; ArgentinaFil: Bruno, Sonia. Rede-ar Tenaris Siderca; ArgentinaFil: Lazzarino, Andrés. Ternium Siderar; ArgentinaFil: Espósito, Fernando. Ternium Siderar; ArgentinaGALVATECH 2013 & APGalva 2013: 9th International Conference on Zinc and Zinc Alloy Coated Steel Sheet and 2nd AsiaPacific Galvanizing ConferenceBeijingChinaThe Chinese Society for MetalsThe Chinese Society for Metals2013info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/conferenceObjectConferenciaBookhttp://purl.org/coar/resource_type/c_5794info:ar-repo/semantics/documentoDeConferenciaapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/230658Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar; GALVATECH 2013 & APGalva 2013: 9th International Conference on Zinc and Zinc Alloy Coated Steel Sheet and 2nd AsiaPacific Galvanizing Conference; Beijing; China; 2013; 342-347CONICET DigitalCONICETengInternacionalinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:12:17Zoai:ri.conicet.gov.ar:11336/230658instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:12:17.713CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar |
title |
Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar |
spellingShingle |
Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar Egli, Walter Alfredo CORROSION CONDUCTOR ROLL ELECTROGALVANIZING |
title_short |
Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar |
title_full |
Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar |
title_fullStr |
Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar |
title_full_unstemmed |
Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar |
title_sort |
Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar |
dc.creator.none.fl_str_mv |
Egli, Walter Alfredo Seré, Pablo Ricardo Bengoa, Leandro Nicolás Versino, Florencia Bruno, Sonia Lazzarino, Andrés Espósito, Fernando |
author |
Egli, Walter Alfredo |
author_facet |
Egli, Walter Alfredo Seré, Pablo Ricardo Bengoa, Leandro Nicolás Versino, Florencia Bruno, Sonia Lazzarino, Andrés Espósito, Fernando |
author_role |
author |
author2 |
Seré, Pablo Ricardo Bengoa, Leandro Nicolás Versino, Florencia Bruno, Sonia Lazzarino, Andrés Espósito, Fernando |
author2_role |
author author author author author author |
dc.subject.none.fl_str_mv |
CORROSION CONDUCTOR ROLL ELECTROGALVANIZING |
topic |
CORROSION CONDUCTOR ROLL ELECTROGALVANIZING |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
Conductor rolls in the electrogalvanizing line are made of Duplex Stainless Steel (DSS) and after some time in service they suffer surface deterioration leading to surface defects and rejections in high quality products. Repassivation kinetics and susceptibility to pitting corrosion for the austenitic and ferritic phases were studied. An electrochemical treatment that reproduces the actual industrial corrosive situation was applied to test different alloys in the laboratory. The Hastelloy C22 showed the best performance and was evaluated in the line during a complete production batch. The new roll presented a slight deterioration, much lower than the DSS rolls. Fil: Egli, Walter Alfredo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina Fil: Seré, Pablo Ricardo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina Fil: Bengoa, Leandro Nicolás. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Tecnología de Pinturas. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones en Tecnología de Pinturas; Argentina Fil: Versino, Florencia. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina Fil: Bruno, Sonia. Rede-ar Tenaris Siderca; Argentina Fil: Lazzarino, Andrés. Ternium Siderar; Argentina Fil: Espósito, Fernando. Ternium Siderar; Argentina GALVATECH 2013 & APGalva 2013: 9th International Conference on Zinc and Zinc Alloy Coated Steel Sheet and 2nd AsiaPacific Galvanizing Conference Beijing China The Chinese Society for Metals |
description |
Conductor rolls in the electrogalvanizing line are made of Duplex Stainless Steel (DSS) and after some time in service they suffer surface deterioration leading to surface defects and rejections in high quality products. Repassivation kinetics and susceptibility to pitting corrosion for the austenitic and ferritic phases were studied. An electrochemical treatment that reproduces the actual industrial corrosive situation was applied to test different alloys in the laboratory. The Hastelloy C22 showed the best performance and was evaluated in the line during a complete production batch. The new roll presented a slight deterioration, much lower than the DSS rolls. |
publishDate |
2013 |
dc.date.none.fl_str_mv |
2013 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/publishedVersion info:eu-repo/semantics/conferenceObject Conferencia Book http://purl.org/coar/resource_type/c_5794 info:ar-repo/semantics/documentoDeConferencia |
status_str |
publishedVersion |
format |
conferenceObject |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/230658 Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar; GALVATECH 2013 & APGalva 2013: 9th International Conference on Zinc and Zinc Alloy Coated Steel Sheet and 2nd AsiaPacific Galvanizing Conference; Beijing; China; 2013; 342-347 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/230658 |
identifier_str_mv |
Corrosion of conductor rolls in the electrogalvanizing line at Ternium Siderar; GALVATECH 2013 & APGalva 2013: 9th International Conference on Zinc and Zinc Alloy Coated Steel Sheet and 2nd AsiaPacific Galvanizing Conference; Beijing; China; 2013; 342-347 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf application/pdf |
dc.coverage.none.fl_str_mv |
Internacional |
dc.publisher.none.fl_str_mv |
The Chinese Society for Metals |
publisher.none.fl_str_mv |
The Chinese Society for Metals |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844614028564889600 |
score |
13.070432 |