Corrosion of Conductor Rolls in the Electrogalvanizing Line at Sidercolor

Autores
Egli, Walter Alfredo; Sere, Pablo Ricardo; Bruno, Sonia; Lazzarino, Héctor
Año de publicación
2012
Idioma
español castellano
Tipo de recurso
documento de conferencia
Estado
versión publicada
Descripción
After some time in service, conductor rolls in the electrogalvanizing line suffer a surface deterioration that has been attributed to a corrosion-erosion process. This process leads to an increase in roughness and finally produces a pattern on the roll surface that is transferred or copied to the electrogalvanized strip surface originating quality defects that lead to rejections in high quality products. To evaluate the conductor rolls in real working condition, a system to determine conductor roll and steel strip electrochemical potentials was designed. An electrochemical experiment that represents in a better way what happens to the conductor roll surface was developed. Different alloys were submitted to this test and then characterized by Scanning electron microscopy (SEM). It was verified that the intensity and the pattern produced by the electrochemical treatment performed in the laboratory and the superficial attack on the discarded conductor roll were almost the same. This work shows some interesting results that help in the understanding of the nature of this specific corrosion mechanism. A method to evaluate the corrosion resistance of new materials for conductor rolls is also presented. Different alloys were evaluated using this technique.
Los rodillos conductores en la línea de electrocincado de Sidercolor presentan luego de determinado período de trabajo un fenómeno de deterioro al cual históricamente se le ha asignado un origen corrosivo-erosivo que modifica el aspecto y la rugosidad de su superficie. Este proceso genera un dibujo que termina transfiriéndose a la chapa cincada causando un defecto cualitativo no apto para productos de alta calidad superficial. Para resolver el problema, se analizaron las posibles causas y se diseñó un sistema de medición del potencial electroquímico en la superficie de los rodillos conductores para diferentes condiciones de proceso. Los resultados se utilizaron para el diseño de un ensayo electroquímico para simular lo que le ocurre a la superficie del rodillo en operación. Se seleccionaron diferentes aleaciones, se sometieron al ensayo y se caracterizaron por microscopía electrónica (SEM-EDAX). Se comparó la intensidad y morfología del ataque electroquímico realizado en laboratorio con lo que se observa en los rodillos descartados en la línea. Este trabajo muestra resultados que permiten comprender la naturaleza de este fenómeno de corrosión. Se presenta también una nueva herramienta para evaluar la aptitud de los materiales de construcción de estos rodillos desde el punto de vista de su resistencia a la corrosión para este uso específico. Finalmente se proponen aleaciones alternativas para mejorar la respuesta en servicio de los rodillos actuales.
Materia
Físico-Química, Ciencia de los Polímeros, Electroquímica
Corrosión
rodillo conductor
cincado electrolítico
Aleaciones
Nivel de accesibilidad
acceso abierto
Condiciones de uso
http://creativecommons.org/licenses/by-nc-nd/4.0/
Repositorio
CIC Digital (CICBA)
Institución
Comisión de Investigaciones Científicas de la Provincia de Buenos Aires
OAI Identificador
oai:digital.cic.gba.gob.ar:11746/10229

id CICBA_1fe33a7306f0c508349bb9b02464f56a
oai_identifier_str oai:digital.cic.gba.gob.ar:11746/10229
network_acronym_str CICBA
repository_id_str 9441
network_name_str CIC Digital (CICBA)
spelling Corrosion of Conductor Rolls in the Electrogalvanizing Line at SidercolorEgli, Walter AlfredoSere, Pablo RicardoBruno, SoniaLazzarino, HéctorFísico-Química, Ciencia de los Polímeros, ElectroquímicaCorrosiónrodillo conductorcincado electrolíticoAleacionesAfter some time in service, conductor rolls in the electrogalvanizing line suffer a surface deterioration that has been attributed to a corrosion-erosion process. This process leads to an increase in roughness and finally produces a pattern on the roll surface that is transferred or copied to the electrogalvanized strip surface originating quality defects that lead to rejections in high quality products. To evaluate the conductor rolls in real working condition, a system to determine conductor roll and steel strip electrochemical potentials was designed. An electrochemical experiment that represents in a better way what happens to the conductor roll surface was developed. Different alloys were submitted to this test and then characterized by Scanning electron microscopy (SEM). It was verified that the intensity and the pattern produced by the electrochemical treatment performed in the laboratory and the superficial attack on the discarded conductor roll were almost the same. This work shows some interesting results that help in the understanding of the nature of this specific corrosion mechanism. A method to evaluate the corrosion resistance of new materials for conductor rolls is also presented. Different alloys were evaluated using this technique.Los rodillos conductores en la línea de electrocincado de Sidercolor presentan luego de determinado período de trabajo un fenómeno de deterioro al cual históricamente se le ha asignado un origen corrosivo-erosivo que modifica el aspecto y la rugosidad de su superficie. Este proceso genera un dibujo que termina transfiriéndose a la chapa cincada causando un defecto cualitativo no apto para productos de alta calidad superficial. Para resolver el problema, se analizaron las posibles causas y se diseñó un sistema de medición del potencial electroquímico en la superficie de los rodillos conductores para diferentes condiciones de proceso. Los resultados se utilizaron para el diseño de un ensayo electroquímico para simular lo que le ocurre a la superficie del rodillo en operación. Se seleccionaron diferentes aleaciones, se sometieron al ensayo y se caracterizaron por microscopía electrónica (SEM-EDAX). Se comparó la intensidad y morfología del ataque electroquímico realizado en laboratorio con lo que se observa en los rodillos descartados en la línea. Este trabajo muestra resultados que permiten comprender la naturaleza de este fenómeno de corrosión. Se presenta también una nueva herramienta para evaluar la aptitud de los materiales de construcción de estos rodillos desde el punto de vista de su resistencia a la corrosión para este uso específico. Finalmente se proponen aleaciones alternativas para mejorar la respuesta en servicio de los rodillos actuales.2012info:eu-repo/semantics/conferenceObjectinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_5794info:ar-repo/semantics/documentoDeConferenciaapplication/pdfhttps://digital.cic.gba.gob.ar/handle/11746/10229spainfo:eu-repo/semantics/altIdentifier/hdl/10915/78738info:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-nd/4.0/reponame:CIC Digital (CICBA)instname:Comisión de Investigaciones Científicas de la Provincia de Buenos Airesinstacron:CICBA2025-09-29T13:40:20Zoai:digital.cic.gba.gob.ar:11746/10229Institucionalhttp://digital.cic.gba.gob.arOrganismo científico-tecnológicoNo correspondehttp://digital.cic.gba.gob.ar/oai/snrdmarisa.degiusti@sedici.unlp.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:94412025-09-29 13:40:20.566CIC Digital (CICBA) - Comisión de Investigaciones Científicas de la Provincia de Buenos Airesfalse
dc.title.none.fl_str_mv Corrosion of Conductor Rolls in the Electrogalvanizing Line at Sidercolor
title Corrosion of Conductor Rolls in the Electrogalvanizing Line at Sidercolor
spellingShingle Corrosion of Conductor Rolls in the Electrogalvanizing Line at Sidercolor
Egli, Walter Alfredo
Físico-Química, Ciencia de los Polímeros, Electroquímica
Corrosión
rodillo conductor
cincado electrolítico
Aleaciones
title_short Corrosion of Conductor Rolls in the Electrogalvanizing Line at Sidercolor
title_full Corrosion of Conductor Rolls in the Electrogalvanizing Line at Sidercolor
title_fullStr Corrosion of Conductor Rolls in the Electrogalvanizing Line at Sidercolor
title_full_unstemmed Corrosion of Conductor Rolls in the Electrogalvanizing Line at Sidercolor
title_sort Corrosion of Conductor Rolls in the Electrogalvanizing Line at Sidercolor
dc.creator.none.fl_str_mv Egli, Walter Alfredo
Sere, Pablo Ricardo
Bruno, Sonia
Lazzarino, Héctor
author Egli, Walter Alfredo
author_facet Egli, Walter Alfredo
Sere, Pablo Ricardo
Bruno, Sonia
Lazzarino, Héctor
author_role author
author2 Sere, Pablo Ricardo
Bruno, Sonia
Lazzarino, Héctor
author2_role author
author
author
dc.subject.none.fl_str_mv Físico-Química, Ciencia de los Polímeros, Electroquímica
Corrosión
rodillo conductor
cincado electrolítico
Aleaciones
topic Físico-Química, Ciencia de los Polímeros, Electroquímica
Corrosión
rodillo conductor
cincado electrolítico
Aleaciones
dc.description.none.fl_txt_mv After some time in service, conductor rolls in the electrogalvanizing line suffer a surface deterioration that has been attributed to a corrosion-erosion process. This process leads to an increase in roughness and finally produces a pattern on the roll surface that is transferred or copied to the electrogalvanized strip surface originating quality defects that lead to rejections in high quality products. To evaluate the conductor rolls in real working condition, a system to determine conductor roll and steel strip electrochemical potentials was designed. An electrochemical experiment that represents in a better way what happens to the conductor roll surface was developed. Different alloys were submitted to this test and then characterized by Scanning electron microscopy (SEM). It was verified that the intensity and the pattern produced by the electrochemical treatment performed in the laboratory and the superficial attack on the discarded conductor roll were almost the same. This work shows some interesting results that help in the understanding of the nature of this specific corrosion mechanism. A method to evaluate the corrosion resistance of new materials for conductor rolls is also presented. Different alloys were evaluated using this technique.
Los rodillos conductores en la línea de electrocincado de Sidercolor presentan luego de determinado período de trabajo un fenómeno de deterioro al cual históricamente se le ha asignado un origen corrosivo-erosivo que modifica el aspecto y la rugosidad de su superficie. Este proceso genera un dibujo que termina transfiriéndose a la chapa cincada causando un defecto cualitativo no apto para productos de alta calidad superficial. Para resolver el problema, se analizaron las posibles causas y se diseñó un sistema de medición del potencial electroquímico en la superficie de los rodillos conductores para diferentes condiciones de proceso. Los resultados se utilizaron para el diseño de un ensayo electroquímico para simular lo que le ocurre a la superficie del rodillo en operación. Se seleccionaron diferentes aleaciones, se sometieron al ensayo y se caracterizaron por microscopía electrónica (SEM-EDAX). Se comparó la intensidad y morfología del ataque electroquímico realizado en laboratorio con lo que se observa en los rodillos descartados en la línea. Este trabajo muestra resultados que permiten comprender la naturaleza de este fenómeno de corrosión. Se presenta también una nueva herramienta para evaluar la aptitud de los materiales de construcción de estos rodillos desde el punto de vista de su resistencia a la corrosión para este uso específico. Finalmente se proponen aleaciones alternativas para mejorar la respuesta en servicio de los rodillos actuales.
description After some time in service, conductor rolls in the electrogalvanizing line suffer a surface deterioration that has been attributed to a corrosion-erosion process. This process leads to an increase in roughness and finally produces a pattern on the roll surface that is transferred or copied to the electrogalvanized strip surface originating quality defects that lead to rejections in high quality products. To evaluate the conductor rolls in real working condition, a system to determine conductor roll and steel strip electrochemical potentials was designed. An electrochemical experiment that represents in a better way what happens to the conductor roll surface was developed. Different alloys were submitted to this test and then characterized by Scanning electron microscopy (SEM). It was verified that the intensity and the pattern produced by the electrochemical treatment performed in the laboratory and the superficial attack on the discarded conductor roll were almost the same. This work shows some interesting results that help in the understanding of the nature of this specific corrosion mechanism. A method to evaluate the corrosion resistance of new materials for conductor rolls is also presented. Different alloys were evaluated using this technique.
publishDate 2012
dc.date.none.fl_str_mv 2012
dc.type.none.fl_str_mv info:eu-repo/semantics/conferenceObject
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_5794
info:ar-repo/semantics/documentoDeConferencia
format conferenceObject
status_str publishedVersion
dc.identifier.none.fl_str_mv https://digital.cic.gba.gob.ar/handle/11746/10229
url https://digital.cic.gba.gob.ar/handle/11746/10229
dc.language.none.fl_str_mv spa
language spa
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/hdl/10915/78738
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
http://creativecommons.org/licenses/by-nc-nd/4.0/
eu_rights_str_mv openAccess
rights_invalid_str_mv http://creativecommons.org/licenses/by-nc-nd/4.0/
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:CIC Digital (CICBA)
instname:Comisión de Investigaciones Científicas de la Provincia de Buenos Aires
instacron:CICBA
reponame_str CIC Digital (CICBA)
collection CIC Digital (CICBA)
instname_str Comisión de Investigaciones Científicas de la Provincia de Buenos Aires
instacron_str CICBA
institution CICBA
repository.name.fl_str_mv CIC Digital (CICBA) - Comisión de Investigaciones Científicas de la Provincia de Buenos Aires
repository.mail.fl_str_mv marisa.degiusti@sedici.unlp.edu.ar
_version_ 1844618618209304576
score 13.070432