Corrosion of conductor rolls in the electrogalvanizing line at Terniun
- Autores
- Egli, Walter Alfredo; Sere, Pablo Ricardo; Bengoa, Leandro N.; Versino, Florencia; Bruno, Sonia; Lazzarino, Andrés; Espósito, Fernando
- Año de publicación
- 2013
- Idioma
- inglés
- Tipo de recurso
- documento de conferencia
- Estado
- versión publicada
- Descripción
- Conductor rolls in the electrogalvanizing line are made of Duplex Stainless Steel (DSS) and after some time in service they suffer surface deterioration leading to surface defects and rejections in high quality products. Repassivation kinetics and susceptibility to pitting corrosion for the austenitic and ferritic phases were studied. An electrochemical treatment that reproduces the actual industrial corrosive situation was applied to test different alloys in the laboratory. The Hastelloy C22 showed the best performance and was evaluated in the line during a complete production batch. The new roll presented a slight deterioration, much lower than the DSS rolls.
- Materia
-
Ingeniería Química
Corrosión
galvanización - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- http://creativecommons.org/licenses/by-nc-sa/4.0/
- Repositorio
- Institución
- Comisión de Investigaciones Científicas de la Provincia de Buenos Aires
- OAI Identificador
- oai:digital.cic.gba.gob.ar:11746/10223
Ver los metadatos del registro completo
id |
CICBA_848cdfee554e749d68f83b658476cbfb |
---|---|
oai_identifier_str |
oai:digital.cic.gba.gob.ar:11746/10223 |
network_acronym_str |
CICBA |
repository_id_str |
9441 |
network_name_str |
CIC Digital (CICBA) |
spelling |
Corrosion of conductor rolls in the electrogalvanizing line at TerniunEgli, Walter AlfredoSere, Pablo RicardoBengoa, Leandro N.Versino, FlorenciaBruno, SoniaLazzarino, AndrésEspósito, FernandoIngeniería QuímicaCorrosióngalvanizaciónConductor rolls in the electrogalvanizing line are made of Duplex Stainless Steel (DSS) and after some time in service they suffer surface deterioration leading to surface defects and rejections in high quality products. Repassivation kinetics and susceptibility to pitting corrosion for the austenitic and ferritic phases were studied. An electrochemical treatment that reproduces the actual industrial corrosive situation was applied to test different alloys in the laboratory. The Hastelloy C22 showed the best performance and was evaluated in the line during a complete production batch. The new roll presented a slight deterioration, much lower than the DSS rolls.2013info:eu-repo/semantics/conferenceObjectinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_5794info:ar-repo/semantics/documentoDeConferenciaapplication/pdfhttps://digital.cic.gba.gob.ar/handle/11746/10223enginfo:eu-repo/semantics/altIdentifier/hdl/10915/79984info:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-sa/4.0/reponame:CIC Digital (CICBA)instname:Comisión de Investigaciones Científicas de la Provincia de Buenos Airesinstacron:CICBA2025-09-29T13:40:11Zoai:digital.cic.gba.gob.ar:11746/10223Institucionalhttp://digital.cic.gba.gob.arOrganismo científico-tecnológicoNo correspondehttp://digital.cic.gba.gob.ar/oai/snrdmarisa.degiusti@sedici.unlp.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:94412025-09-29 13:40:11.568CIC Digital (CICBA) - Comisión de Investigaciones Científicas de la Provincia de Buenos Airesfalse |
dc.title.none.fl_str_mv |
Corrosion of conductor rolls in the electrogalvanizing line at Terniun |
title |
Corrosion of conductor rolls in the electrogalvanizing line at Terniun |
spellingShingle |
Corrosion of conductor rolls in the electrogalvanizing line at Terniun Egli, Walter Alfredo Ingeniería Química Corrosión galvanización |
title_short |
Corrosion of conductor rolls in the electrogalvanizing line at Terniun |
title_full |
Corrosion of conductor rolls in the electrogalvanizing line at Terniun |
title_fullStr |
Corrosion of conductor rolls in the electrogalvanizing line at Terniun |
title_full_unstemmed |
Corrosion of conductor rolls in the electrogalvanizing line at Terniun |
title_sort |
Corrosion of conductor rolls in the electrogalvanizing line at Terniun |
dc.creator.none.fl_str_mv |
Egli, Walter Alfredo Sere, Pablo Ricardo Bengoa, Leandro N. Versino, Florencia Bruno, Sonia Lazzarino, Andrés Espósito, Fernando |
author |
Egli, Walter Alfredo |
author_facet |
Egli, Walter Alfredo Sere, Pablo Ricardo Bengoa, Leandro N. Versino, Florencia Bruno, Sonia Lazzarino, Andrés Espósito, Fernando |
author_role |
author |
author2 |
Sere, Pablo Ricardo Bengoa, Leandro N. Versino, Florencia Bruno, Sonia Lazzarino, Andrés Espósito, Fernando |
author2_role |
author author author author author author |
dc.subject.none.fl_str_mv |
Ingeniería Química Corrosión galvanización |
topic |
Ingeniería Química Corrosión galvanización |
dc.description.none.fl_txt_mv |
Conductor rolls in the electrogalvanizing line are made of Duplex Stainless Steel (DSS) and after some time in service they suffer surface deterioration leading to surface defects and rejections in high quality products. Repassivation kinetics and susceptibility to pitting corrosion for the austenitic and ferritic phases were studied. An electrochemical treatment that reproduces the actual industrial corrosive situation was applied to test different alloys in the laboratory. The Hastelloy C22 showed the best performance and was evaluated in the line during a complete production batch. The new roll presented a slight deterioration, much lower than the DSS rolls. |
description |
Conductor rolls in the electrogalvanizing line are made of Duplex Stainless Steel (DSS) and after some time in service they suffer surface deterioration leading to surface defects and rejections in high quality products. Repassivation kinetics and susceptibility to pitting corrosion for the austenitic and ferritic phases were studied. An electrochemical treatment that reproduces the actual industrial corrosive situation was applied to test different alloys in the laboratory. The Hastelloy C22 showed the best performance and was evaluated in the line during a complete production batch. The new roll presented a slight deterioration, much lower than the DSS rolls. |
publishDate |
2013 |
dc.date.none.fl_str_mv |
2013 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/conferenceObject info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_5794 info:ar-repo/semantics/documentoDeConferencia |
format |
conferenceObject |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
https://digital.cic.gba.gob.ar/handle/11746/10223 |
url |
https://digital.cic.gba.gob.ar/handle/11746/10223 |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/hdl/10915/79984 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess http://creativecommons.org/licenses/by-nc-sa/4.0/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
http://creativecommons.org/licenses/by-nc-sa/4.0/ |
dc.format.none.fl_str_mv |
application/pdf |
dc.source.none.fl_str_mv |
reponame:CIC Digital (CICBA) instname:Comisión de Investigaciones Científicas de la Provincia de Buenos Aires instacron:CICBA |
reponame_str |
CIC Digital (CICBA) |
collection |
CIC Digital (CICBA) |
instname_str |
Comisión de Investigaciones Científicas de la Provincia de Buenos Aires |
instacron_str |
CICBA |
institution |
CICBA |
repository.name.fl_str_mv |
CIC Digital (CICBA) - Comisión de Investigaciones Científicas de la Provincia de Buenos Aires |
repository.mail.fl_str_mv |
marisa.degiusti@sedici.unlp.edu.ar |
_version_ |
1844618606627782656 |
score |
13.070432 |