Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16
- Autores
- Rivoira, Lorena Paola; Vallés, Verónica Alejandra; Ledesma, Brenda Cecilia Soledad; Ponte, María Virginia; Martinez, Maria Laura; Anunziata, Oscar Alfredo; Beltramone, Andrea Raquel
- Año de publicación
- 2016
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- TiO2-modified mesoporous SBA-16 and titanium-substituted mesoporous SBA-16 were developed and tested in the oxidative desulfurization (ODS) of dibenzothiophene prevailing in liquid fuel. Pure TiO2 was used as reference. The titania-based catalysts were characterized by chemical analysis, XRD, EDX and TEM. The titanium state as tetrahedral (in Ti-SBA-16 sample) or octahedral (in TiO2/SBA-16 sample) coordination surrounding in the silicate matrix was determined by XPS, UV-vis DRS, FTIR, Raman and XANES. We assessed the impact exerted on performance of different reaction variables, including (nature and amount of the active catalytic species, phase system, molar ratio of oxidant H2O2 and DBT, reaction temperature, nature of the substrate and reuse of catalysts). In addition, we carried out a kinetic study and the activation energy was determined. We achieved 90% of S removal from a 0.2 wt.% dibenzothiophene solution at 60 °C in less than 1 h of reaction. The best catalytic results are obtained with high exposed surface of nanometric TiO2 species of TiO2/SBA-16 sample. The activated catalyst is very active in ODS reaction and can be reused four times with no loss in activity.
Fil: Rivoira, Lorena Paola. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina
Fil: Vallés, Verónica Alejandra. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina
Fil: Ledesma, Brenda Cecilia Soledad. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina
Fil: Ponte, María Virginia. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina
Fil: Martinez, Maria Laura. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina
Fil: Anunziata, Oscar Alfredo. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina
Fil: Beltramone, Andrea Raquel. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina - Materia
-
ODS
REACTION KINETICS
TI INCORPORATION METHOD
TI-CONTAINING SBA-16
TIO2 - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/179782
Ver los metadatos del registro completo
id |
CONICETDig_58059c9c99d67f45cecf3a3c2ea67850 |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/179782 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16Rivoira, Lorena PaolaVallés, Verónica AlejandraLedesma, Brenda Cecilia SoledadPonte, María VirginiaMartinez, Maria LauraAnunziata, Oscar AlfredoBeltramone, Andrea RaquelODSREACTION KINETICSTI INCORPORATION METHODTI-CONTAINING SBA-16TIO2https://purl.org/becyt/ford/2.4https://purl.org/becyt/ford/2TiO2-modified mesoporous SBA-16 and titanium-substituted mesoporous SBA-16 were developed and tested in the oxidative desulfurization (ODS) of dibenzothiophene prevailing in liquid fuel. Pure TiO2 was used as reference. The titania-based catalysts were characterized by chemical analysis, XRD, EDX and TEM. The titanium state as tetrahedral (in Ti-SBA-16 sample) or octahedral (in TiO2/SBA-16 sample) coordination surrounding in the silicate matrix was determined by XPS, UV-vis DRS, FTIR, Raman and XANES. We assessed the impact exerted on performance of different reaction variables, including (nature and amount of the active catalytic species, phase system, molar ratio of oxidant H2O2 and DBT, reaction temperature, nature of the substrate and reuse of catalysts). In addition, we carried out a kinetic study and the activation energy was determined. We achieved 90% of S removal from a 0.2 wt.% dibenzothiophene solution at 60 °C in less than 1 h of reaction. The best catalytic results are obtained with high exposed surface of nanometric TiO2 species of TiO2/SBA-16 sample. The activated catalyst is very active in ODS reaction and can be reused four times with no loss in activity.Fil: Rivoira, Lorena Paola. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; ArgentinaFil: Vallés, Verónica Alejandra. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; ArgentinaFil: Ledesma, Brenda Cecilia Soledad. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; ArgentinaFil: Ponte, María Virginia. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; ArgentinaFil: Martinez, Maria Laura. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; ArgentinaFil: Anunziata, Oscar Alfredo. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; ArgentinaFil: Beltramone, Andrea Raquel. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; ArgentinaElsevier Science2016-04info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/179782Rivoira, Lorena Paola; Vallés, Verónica Alejandra; Ledesma, Brenda Cecilia Soledad; Ponte, María Virginia; Martinez, Maria Laura; et al.; Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16; Elsevier Science; Catalysis Today; 271; 4-2016; 102-1130920-5861CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S0920586115005660info:eu-repo/semantics/altIdentifier/doi/10.1016/j.cattod.2015.07.055info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T09:47:21Zoai:ri.conicet.gov.ar:11336/179782instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 09:47:21.343CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16 |
title |
Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16 |
spellingShingle |
Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16 Rivoira, Lorena Paola ODS REACTION KINETICS TI INCORPORATION METHOD TI-CONTAINING SBA-16 TIO2 |
title_short |
Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16 |
title_full |
Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16 |
title_fullStr |
Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16 |
title_full_unstemmed |
Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16 |
title_sort |
Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16 |
dc.creator.none.fl_str_mv |
Rivoira, Lorena Paola Vallés, Verónica Alejandra Ledesma, Brenda Cecilia Soledad Ponte, María Virginia Martinez, Maria Laura Anunziata, Oscar Alfredo Beltramone, Andrea Raquel |
author |
Rivoira, Lorena Paola |
author_facet |
Rivoira, Lorena Paola Vallés, Verónica Alejandra Ledesma, Brenda Cecilia Soledad Ponte, María Virginia Martinez, Maria Laura Anunziata, Oscar Alfredo Beltramone, Andrea Raquel |
author_role |
author |
author2 |
Vallés, Verónica Alejandra Ledesma, Brenda Cecilia Soledad Ponte, María Virginia Martinez, Maria Laura Anunziata, Oscar Alfredo Beltramone, Andrea Raquel |
author2_role |
author author author author author author |
dc.subject.none.fl_str_mv |
ODS REACTION KINETICS TI INCORPORATION METHOD TI-CONTAINING SBA-16 TIO2 |
topic |
ODS REACTION KINETICS TI INCORPORATION METHOD TI-CONTAINING SBA-16 TIO2 |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.4 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
TiO2-modified mesoporous SBA-16 and titanium-substituted mesoporous SBA-16 were developed and tested in the oxidative desulfurization (ODS) of dibenzothiophene prevailing in liquid fuel. Pure TiO2 was used as reference. The titania-based catalysts were characterized by chemical analysis, XRD, EDX and TEM. The titanium state as tetrahedral (in Ti-SBA-16 sample) or octahedral (in TiO2/SBA-16 sample) coordination surrounding in the silicate matrix was determined by XPS, UV-vis DRS, FTIR, Raman and XANES. We assessed the impact exerted on performance of different reaction variables, including (nature and amount of the active catalytic species, phase system, molar ratio of oxidant H2O2 and DBT, reaction temperature, nature of the substrate and reuse of catalysts). In addition, we carried out a kinetic study and the activation energy was determined. We achieved 90% of S removal from a 0.2 wt.% dibenzothiophene solution at 60 °C in less than 1 h of reaction. The best catalytic results are obtained with high exposed surface of nanometric TiO2 species of TiO2/SBA-16 sample. The activated catalyst is very active in ODS reaction and can be reused four times with no loss in activity. Fil: Rivoira, Lorena Paola. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina Fil: Vallés, Verónica Alejandra. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina Fil: Ledesma, Brenda Cecilia Soledad. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina Fil: Ponte, María Virginia. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina Fil: Martinez, Maria Laura. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina Fil: Anunziata, Oscar Alfredo. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina Fil: Beltramone, Andrea Raquel. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación en Nanociencia y Nanotecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba; Argentina |
description |
TiO2-modified mesoporous SBA-16 and titanium-substituted mesoporous SBA-16 were developed and tested in the oxidative desulfurization (ODS) of dibenzothiophene prevailing in liquid fuel. Pure TiO2 was used as reference. The titania-based catalysts were characterized by chemical analysis, XRD, EDX and TEM. The titanium state as tetrahedral (in Ti-SBA-16 sample) or octahedral (in TiO2/SBA-16 sample) coordination surrounding in the silicate matrix was determined by XPS, UV-vis DRS, FTIR, Raman and XANES. We assessed the impact exerted on performance of different reaction variables, including (nature and amount of the active catalytic species, phase system, molar ratio of oxidant H2O2 and DBT, reaction temperature, nature of the substrate and reuse of catalysts). In addition, we carried out a kinetic study and the activation energy was determined. We achieved 90% of S removal from a 0.2 wt.% dibenzothiophene solution at 60 °C in less than 1 h of reaction. The best catalytic results are obtained with high exposed surface of nanometric TiO2 species of TiO2/SBA-16 sample. The activated catalyst is very active in ODS reaction and can be reused four times with no loss in activity. |
publishDate |
2016 |
dc.date.none.fl_str_mv |
2016-04 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/179782 Rivoira, Lorena Paola; Vallés, Verónica Alejandra; Ledesma, Brenda Cecilia Soledad; Ponte, María Virginia; Martinez, Maria Laura; et al.; Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16; Elsevier Science; Catalysis Today; 271; 4-2016; 102-113 0920-5861 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/179782 |
identifier_str_mv |
Rivoira, Lorena Paola; Vallés, Verónica Alejandra; Ledesma, Brenda Cecilia Soledad; Ponte, María Virginia; Martinez, Maria Laura; et al.; Sulfur elimination by oxidative desulfurization with titanium-modified SBA-16; Elsevier Science; Catalysis Today; 271; 4-2016; 102-113 0920-5861 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S0920586115005660 info:eu-repo/semantics/altIdentifier/doi/10.1016/j.cattod.2015.07.055 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf application/pdf application/pdf application/pdf application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Elsevier Science |
publisher.none.fl_str_mv |
Elsevier Science |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844613475548004352 |
score |
13.070432 |