Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether)

Autores
Soulé, Ezequiel Rodolfo; Fine, T.; Borrajo Fernandez, Julio; Williams, Roberto Juan Jose; Pascault, J.P.
Año de publicación
2006
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Phase diagrams of ternary blends of poly(phenylene ether) (PPE, M n = 1.2 and 12 kg mol-1), polystyrene (PS, Mn = 22.5 kg mol-1), and diglycidyl ether of bisphenol A (DGEBA) were experimentally obtained in an extended range of temperatures and fitted with the Flory-Huggins model using three binary interaction parameters. A significant increase in miscibility together with the appearance of an immiscibility loop was found for PPEs with Mn values comprised in the range between 1 and 10 kg mol-1. This enables us to obtain initial homogeneous solutions in regions of high DGEBA concentrations, a possibility that was not previously reported for this ternary blend. This opens new possibilities for the toughening of epoxies replacing a single thermoplastic with a thermoplastic blend where both components (PS and PPE) are completely miscible.
Fil: Soulé, Ezequiel Rodolfo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Fine, T.. Institut National des Sciences Applique´s de Lyon; Francia
Fil: Borrajo Fernandez, Julio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Williams, Roberto Juan Jose. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Pascault, J.P.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Materia
Phase Diagrams
Ternary Systems
Molecular Weight
Blends
Miscibility
Polystyrene
Thermodynamics
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/93060
Acceder
id CONICETDig_53cab4a5989583825bdb2c9d2245023c
oai_identifier_str oai:ri.conicet.gov.ar:11336/93060
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether)Soulé, Ezequiel RodolfoFine, T.Borrajo Fernandez, JulioWilliams, Roberto Juan JosePascault, J.P.Phase DiagramsTernary SystemsMolecular WeightBlendsMiscibilityPolystyreneThermodynamicshttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Phase diagrams of ternary blends of poly(phenylene ether) (PPE, M n = 1.2 and 12 kg mol-1), polystyrene (PS, Mn = 22.5 kg mol-1), and diglycidyl ether of bisphenol A (DGEBA) were experimentally obtained in an extended range of temperatures and fitted with the Flory-Huggins model using three binary interaction parameters. A significant increase in miscibility together with the appearance of an immiscibility loop was found for PPEs with Mn values comprised in the range between 1 and 10 kg mol-1. This enables us to obtain initial homogeneous solutions in regions of high DGEBA concentrations, a possibility that was not previously reported for this ternary blend. This opens new possibilities for the toughening of epoxies replacing a single thermoplastic with a thermoplastic blend where both components (PS and PPE) are completely miscible.Fil: Soulé, Ezequiel Rodolfo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Fine, T.. Institut National des Sciences Applique´s de Lyon; FranciaFil: Borrajo Fernandez, Julio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Williams, Roberto Juan Jose. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Pascault, J.P.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaJohn Wiley & Sons Inc2006-05-06info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/93060Soulé, Ezequiel Rodolfo; Fine, T.; Borrajo Fernandez, Julio; Williams, Roberto Juan Jose; Pascault, J.P.; Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether); John Wiley & Sons Inc; Journal of Applied Polymer Science; 100; 3; 6-5-2006; 1742-17470021-8995CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1002/app.22784info:eu-repo/semantics/altIdentifier/url/https://onlinelibrary.wiley.com/doi/abs/10.1002/app.22784info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T09:52:49Zoai:ri.conicet.gov.ar:11336/93060instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 09:52:49.719CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether)
title Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether)
spellingShingle Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether)
Soulé, Ezequiel Rodolfo
Phase Diagrams
Ternary Systems
Molecular Weight
Blends
Miscibility
Polystyrene
Thermodynamics
title_short Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether)
title_full Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether)
title_fullStr Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether)
title_full_unstemmed Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether)
title_sort Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether)
dc.creator.none.fl_str_mv Soulé, Ezequiel Rodolfo
Fine, T.
Borrajo Fernandez, Julio
Williams, Roberto Juan Jose
Pascault, J.P.
author Soulé, Ezequiel Rodolfo
author_facet Soulé, Ezequiel Rodolfo
Fine, T.
Borrajo Fernandez, Julio
Williams, Roberto Juan Jose
Pascault, J.P.
author_role author
author2 Fine, T.
Borrajo Fernandez, Julio
Williams, Roberto Juan Jose
Pascault, J.P.
author2_role author
author
author
author
dc.subject.none.fl_str_mv Phase Diagrams
Ternary Systems
Molecular Weight
Blends
Miscibility
Polystyrene
Thermodynamics
topic Phase Diagrams
Ternary Systems
Molecular Weight
Blends
Miscibility
Polystyrene
Thermodynamics
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv Phase diagrams of ternary blends of poly(phenylene ether) (PPE, M n = 1.2 and 12 kg mol-1), polystyrene (PS, Mn = 22.5 kg mol-1), and diglycidyl ether of bisphenol A (DGEBA) were experimentally obtained in an extended range of temperatures and fitted with the Flory-Huggins model using three binary interaction parameters. A significant increase in miscibility together with the appearance of an immiscibility loop was found for PPEs with Mn values comprised in the range between 1 and 10 kg mol-1. This enables us to obtain initial homogeneous solutions in regions of high DGEBA concentrations, a possibility that was not previously reported for this ternary blend. This opens new possibilities for the toughening of epoxies replacing a single thermoplastic with a thermoplastic blend where both components (PS and PPE) are completely miscible.
Fil: Soulé, Ezequiel Rodolfo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Fine, T.. Institut National des Sciences Applique´s de Lyon; Francia
Fil: Borrajo Fernandez, Julio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Williams, Roberto Juan Jose. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Pascault, J.P.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
description Phase diagrams of ternary blends of poly(phenylene ether) (PPE, M n = 1.2 and 12 kg mol-1), polystyrene (PS, Mn = 22.5 kg mol-1), and diglycidyl ether of bisphenol A (DGEBA) were experimentally obtained in an extended range of temperatures and fitted with the Flory-Huggins model using three binary interaction parameters. A significant increase in miscibility together with the appearance of an immiscibility loop was found for PPEs with Mn values comprised in the range between 1 and 10 kg mol-1. This enables us to obtain initial homogeneous solutions in regions of high DGEBA concentrations, a possibility that was not previously reported for this ternary blend. This opens new possibilities for the toughening of epoxies replacing a single thermoplastic with a thermoplastic blend where both components (PS and PPE) are completely miscible.
publishDate 2006
dc.date.none.fl_str_mv 2006-05-06
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/93060
Soulé, Ezequiel Rodolfo; Fine, T.; Borrajo Fernandez, Julio; Williams, Roberto Juan Jose; Pascault, J.P.; Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether); John Wiley & Sons Inc; Journal of Applied Polymer Science; 100; 3; 6-5-2006; 1742-1747
0021-8995
CONICET Digital
CONICET
url http://hdl.handle.net/11336/93060
identifier_str_mv Soulé, Ezequiel Rodolfo; Fine, T.; Borrajo Fernandez, Julio; Williams, Roberto Juan Jose; Pascault, J.P.; Phase Diagrams of Blends of Poly(phenylene ether), Polystyrene, and Diglycidyl Ether of Bisphenol A: Influence of the Molar Mass of Poly(phenylene ether); John Wiley & Sons Inc; Journal of Applied Polymer Science; 100; 3; 6-5-2006; 1742-1747
0021-8995
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1002/app.22784
info:eu-repo/semantics/altIdentifier/url/https://onlinelibrary.wiley.com/doi/abs/10.1002/app.22784
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv John Wiley & Sons Inc
publisher.none.fl_str_mv John Wiley & Sons Inc
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842269184582483968
score 13.13397

Publicaciones similares