A new polymorph of GaAsO4

Autores
Tunez, Fernando Marcelo; Andrade Gamboa, Julio José; Gonzalez, Jorge Alberto; Esquivel, Marcelo Ricardo Oscar
Año de publicación
2012
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
At room temperature, the compound GaAsO 4 (gallium arsenate) has a berlinite type structure (AlPO 4, P3 121) and it is the only normal pressure polymorph reported as occurring at all temperatures. By means of a gaseous phase route, GaAsO 4 was obtained in a structure homeotypic with α-cristobalite and was retained at room temperature. Structural Rietveld refinement of this new GaAsO 4 polymorph was performed based on space group C222 1 and refined lattice parameters are a = 7.0592 Å, b = 7.0893 Å, c = 7.0977 Å. Heating up to 1000°C the α-cristobalite homeotype transforms to the stable berlinite type structure and it would invert to the β-cristobalite homeotype at about 530°C.
Fil: Tunez, Fernando Marcelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Andrade Gamboa, Julio José. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; Argentina. Universidad Nacional del Comahue; Argentina
Fil: Gonzalez, Jorge Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Esquivel, Marcelo Ricardo Oscar. Universidad Nacional del Comahue; Argentina. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
Materia
X-TAY DIFRACTION
RIETVELD REFINEMENT
POLYMORFISM
PHASE TRANSFROMATION
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/173504
Acceder
id CONICETDig_0a73d355fa2fcec3f5a1620c148aa5c6
oai_identifier_str oai:ri.conicet.gov.ar:11336/173504
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling A new polymorph of GaAsO4Tunez, Fernando MarceloAndrade Gamboa, Julio JoséGonzalez, Jorge AlbertoEsquivel, Marcelo Ricardo OscarX-TAY DIFRACTIONRIETVELD REFINEMENTPOLYMORFISMPHASE TRANSFROMATIONhttps://purl.org/becyt/ford/1.4https://purl.org/becyt/ford/1At room temperature, the compound GaAsO 4 (gallium arsenate) has a berlinite type structure (AlPO 4, P3 121) and it is the only normal pressure polymorph reported as occurring at all temperatures. By means of a gaseous phase route, GaAsO 4 was obtained in a structure homeotypic with α-cristobalite and was retained at room temperature. Structural Rietveld refinement of this new GaAsO 4 polymorph was performed based on space group C222 1 and refined lattice parameters are a = 7.0592 Å, b = 7.0893 Å, c = 7.0977 Å. Heating up to 1000°C the α-cristobalite homeotype transforms to the stable berlinite type structure and it would invert to the β-cristobalite homeotype at about 530°C.Fil: Tunez, Fernando Marcelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; ArgentinaFil: Andrade Gamboa, Julio José. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; Argentina. Universidad Nacional del Comahue; ArgentinaFil: Gonzalez, Jorge Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; ArgentinaFil: Esquivel, Marcelo Ricardo Oscar. Universidad Nacional del Comahue; Argentina. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; ArgentinaElsevier Science2012-04info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/173504Tunez, Fernando Marcelo; Andrade Gamboa, Julio José; Gonzalez, Jorge Alberto; Esquivel, Marcelo Ricardo Oscar; A new polymorph of GaAsO4; Elsevier Science; Materials Letters; 79; 4-2012; 202-2040167-577XCONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0167577X12004934info:eu-repo/semantics/altIdentifier/doi/10.1016/j.matlet.2012.04.015info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-10-15T14:44:57Zoai:ri.conicet.gov.ar:11336/173504instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-10-15 14:44:57.936CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv A new polymorph of GaAsO4
title A new polymorph of GaAsO4
spellingShingle A new polymorph of GaAsO4
Tunez, Fernando Marcelo
X-TAY DIFRACTION
RIETVELD REFINEMENT
POLYMORFISM
PHASE TRANSFROMATION
title_short A new polymorph of GaAsO4
title_full A new polymorph of GaAsO4
title_fullStr A new polymorph of GaAsO4
title_full_unstemmed A new polymorph of GaAsO4
title_sort A new polymorph of GaAsO4
dc.creator.none.fl_str_mv Tunez, Fernando Marcelo
Andrade Gamboa, Julio José
Gonzalez, Jorge Alberto
Esquivel, Marcelo Ricardo Oscar
author Tunez, Fernando Marcelo
author_facet Tunez, Fernando Marcelo
Andrade Gamboa, Julio José
Gonzalez, Jorge Alberto
Esquivel, Marcelo Ricardo Oscar
author_role author
author2 Andrade Gamboa, Julio José
Gonzalez, Jorge Alberto
Esquivel, Marcelo Ricardo Oscar
author2_role author
author
author
dc.subject.none.fl_str_mv X-TAY DIFRACTION
RIETVELD REFINEMENT
POLYMORFISM
PHASE TRANSFROMATION
topic X-TAY DIFRACTION
RIETVELD REFINEMENT
POLYMORFISM
PHASE TRANSFROMATION
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.4
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv At room temperature, the compound GaAsO 4 (gallium arsenate) has a berlinite type structure (AlPO 4, P3 121) and it is the only normal pressure polymorph reported as occurring at all temperatures. By means of a gaseous phase route, GaAsO 4 was obtained in a structure homeotypic with α-cristobalite and was retained at room temperature. Structural Rietveld refinement of this new GaAsO 4 polymorph was performed based on space group C222 1 and refined lattice parameters are a = 7.0592 Å, b = 7.0893 Å, c = 7.0977 Å. Heating up to 1000°C the α-cristobalite homeotype transforms to the stable berlinite type structure and it would invert to the β-cristobalite homeotype at about 530°C.
Fil: Tunez, Fernando Marcelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Andrade Gamboa, Julio José. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; Argentina. Universidad Nacional del Comahue; Argentina
Fil: Gonzalez, Jorge Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Esquivel, Marcelo Ricardo Oscar. Universidad Nacional del Comahue; Argentina. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
description At room temperature, the compound GaAsO 4 (gallium arsenate) has a berlinite type structure (AlPO 4, P3 121) and it is the only normal pressure polymorph reported as occurring at all temperatures. By means of a gaseous phase route, GaAsO 4 was obtained in a structure homeotypic with α-cristobalite and was retained at room temperature. Structural Rietveld refinement of this new GaAsO 4 polymorph was performed based on space group C222 1 and refined lattice parameters are a = 7.0592 Å, b = 7.0893 Å, c = 7.0977 Å. Heating up to 1000°C the α-cristobalite homeotype transforms to the stable berlinite type structure and it would invert to the β-cristobalite homeotype at about 530°C.
publishDate 2012
dc.date.none.fl_str_mv 2012-04
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/173504
Tunez, Fernando Marcelo; Andrade Gamboa, Julio José; Gonzalez, Jorge Alberto; Esquivel, Marcelo Ricardo Oscar; A new polymorph of GaAsO4; Elsevier Science; Materials Letters; 79; 4-2012; 202-204
0167-577X
CONICET Digital
CONICET
url http://hdl.handle.net/11336/173504
identifier_str_mv Tunez, Fernando Marcelo; Andrade Gamboa, Julio José; Gonzalez, Jorge Alberto; Esquivel, Marcelo Ricardo Oscar; A new polymorph of GaAsO4; Elsevier Science; Materials Letters; 79; 4-2012; 202-204
0167-577X
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0167577X12004934
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.matlet.2012.04.015
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier Science
publisher.none.fl_str_mv Elsevier Science
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1846082960821846016
score 13.22299

Publicaciones similares