Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application

Autores
Villa Perez, Cristian; Mendoza Herrera, Luis Joaquin; Santillán, Jesica María José; Muñetón Arboleda, David; Moreno, Mario Sergio Jesus; Arce, Valeria Beatriz
Año de publicación
2024
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Metal nanostructures have received significant attention in recent years owing to their peculiar physical and chemical properties, which span a wide range of practical applications in a variety of scientific and engineering fields. Herein, we report a study of the optical properties and application in the field enhancement of silver nanoplates (Ag-Nplates) obtained by two-step chemical synthesis. Optical Extinction Spectroscopy (OES), together with a detailed theoretical analysis of the experimental spectra, was used to characterize the size distribution, morphology, and optical spectral behavior of the obtained suspensions. These studies were complemented with shape and size distribution analyses using Transmission Electron Microscopy (TEM). It was observed by both techniques that these characteristics are related to the concentration of silver spherical nanoparticles (Ag-Seeds) added during the synthesis of Ag-Nplates. A decrease in the Ag-Seed amount produces an infrared shift of the main plasmon peak with respect to the neat Ag-Seeds suspension, which is related to the size growth of Ag-Nplates showing size distributions centered in the edge length range of 12-15 nm and 34-36 nm for the experimental spectra, whose plasmon peak positions are at 543 nm (higher Ag-Seeds concentration) and 815 nm (lower Ag-Seed concentration), respectively. The detection of Brilliant Blue (BB) by Surface-Enhanced Raman Spectroscopy (SERS) was successfully probed with the incorporation of Ag-Nplates in an agarose gel.
Fil: Villa Perez, Cristian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina
Fil: Mendoza Herrera, Luis Joaquin. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ciencias Básicas; Argentina
Fil: Santillán, Jesica María José. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ciencias Básicas; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina
Fil: Muñetón Arboleda, David. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ciencias Básicas; Argentina
Fil: Moreno, Mario Sergio Jesus. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche | Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche; Argentina
Fil: Arce, Valeria Beatriz. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina
Materia
SILVER NANOPLATES
SERS
PLASMONIC
CHEMICAL SYNTHESIS
OPTICAL EXTINCTION
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/261445
Acceder
id CONICETDig_0284c1a254a4c861e4c4105803f6e2d6
oai_identifier_str oai:ri.conicet.gov.ar:11336/261445
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS ApplicationVilla Perez, CristianMendoza Herrera, Luis JoaquinSantillán, Jesica María JoséMuñetón Arboleda, DavidMoreno, Mario Sergio JesusArce, Valeria BeatrizSILVER NANOPLATESSERSPLASMONICCHEMICAL SYNTHESISOPTICAL EXTINCTIONhttps://purl.org/becyt/ford/2.10https://purl.org/becyt/ford/2Metal nanostructures have received significant attention in recent years owing to their peculiar physical and chemical properties, which span a wide range of practical applications in a variety of scientific and engineering fields. Herein, we report a study of the optical properties and application in the field enhancement of silver nanoplates (Ag-Nplates) obtained by two-step chemical synthesis. Optical Extinction Spectroscopy (OES), together with a detailed theoretical analysis of the experimental spectra, was used to characterize the size distribution, morphology, and optical spectral behavior of the obtained suspensions. These studies were complemented with shape and size distribution analyses using Transmission Electron Microscopy (TEM). It was observed by both techniques that these characteristics are related to the concentration of silver spherical nanoparticles (Ag-Seeds) added during the synthesis of Ag-Nplates. A decrease in the Ag-Seed amount produces an infrared shift of the main plasmon peak with respect to the neat Ag-Seeds suspension, which is related to the size growth of Ag-Nplates showing size distributions centered in the edge length range of 12-15 nm and 34-36 nm for the experimental spectra, whose plasmon peak positions are at 543 nm (higher Ag-Seeds concentration) and 815 nm (lower Ag-Seed concentration), respectively. The detection of Brilliant Blue (BB) by Surface-Enhanced Raman Spectroscopy (SERS) was successfully probed with the incorporation of Ag-Nplates in an agarose gel.Fil: Villa Perez, Cristian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; ArgentinaFil: Mendoza Herrera, Luis Joaquin. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ciencias Básicas; ArgentinaFil: Santillán, Jesica María José. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ciencias Básicas; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; ArgentinaFil: Muñetón Arboleda, David. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ciencias Básicas; ArgentinaFil: Moreno, Mario Sergio Jesus. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche | Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche; ArgentinaFil: Arce, Valeria Beatriz. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; ArgentinaCornell University2024-12info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/261445Villa Perez, Cristian; Mendoza Herrera, Luis Joaquin; Santillán, Jesica María José; Muñetón Arboleda, David; Moreno, Mario Sergio Jesus; et al.; Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application; Cornell University; arXiv; 12-2024; 1-312331-8422CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.48550/arXiv.2412.19452info:eu-repo/semantics/altIdentifier/arxiv/https://arxiv.org/abs/2412.19452info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-10-22T12:02:55Zoai:ri.conicet.gov.ar:11336/261445instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-10-22 12:02:55.381CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application
title Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application
spellingShingle Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application
Villa Perez, Cristian
SILVER NANOPLATES
SERS
PLASMONIC
CHEMICAL SYNTHESIS
OPTICAL EXTINCTION
title_short Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application
title_full Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application
title_fullStr Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application
title_full_unstemmed Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application
title_sort Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application
dc.creator.none.fl_str_mv Villa Perez, Cristian
Mendoza Herrera, Luis Joaquin
Santillán, Jesica María José
Muñetón Arboleda, David
Moreno, Mario Sergio Jesus
Arce, Valeria Beatriz
author Villa Perez, Cristian
author_facet Villa Perez, Cristian
Mendoza Herrera, Luis Joaquin
Santillán, Jesica María José
Muñetón Arboleda, David
Moreno, Mario Sergio Jesus
Arce, Valeria Beatriz
author_role author
author2 Mendoza Herrera, Luis Joaquin
Santillán, Jesica María José
Muñetón Arboleda, David
Moreno, Mario Sergio Jesus
Arce, Valeria Beatriz
author2_role author
author
author
author
author
dc.subject.none.fl_str_mv SILVER NANOPLATES
SERS
PLASMONIC
CHEMICAL SYNTHESIS
OPTICAL EXTINCTION
topic SILVER NANOPLATES
SERS
PLASMONIC
CHEMICAL SYNTHESIS
OPTICAL EXTINCTION
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.10
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv Metal nanostructures have received significant attention in recent years owing to their peculiar physical and chemical properties, which span a wide range of practical applications in a variety of scientific and engineering fields. Herein, we report a study of the optical properties and application in the field enhancement of silver nanoplates (Ag-Nplates) obtained by two-step chemical synthesis. Optical Extinction Spectroscopy (OES), together with a detailed theoretical analysis of the experimental spectra, was used to characterize the size distribution, morphology, and optical spectral behavior of the obtained suspensions. These studies were complemented with shape and size distribution analyses using Transmission Electron Microscopy (TEM). It was observed by both techniques that these characteristics are related to the concentration of silver spherical nanoparticles (Ag-Seeds) added during the synthesis of Ag-Nplates. A decrease in the Ag-Seed amount produces an infrared shift of the main plasmon peak with respect to the neat Ag-Seeds suspension, which is related to the size growth of Ag-Nplates showing size distributions centered in the edge length range of 12-15 nm and 34-36 nm for the experimental spectra, whose plasmon peak positions are at 543 nm (higher Ag-Seeds concentration) and 815 nm (lower Ag-Seed concentration), respectively. The detection of Brilliant Blue (BB) by Surface-Enhanced Raman Spectroscopy (SERS) was successfully probed with the incorporation of Ag-Nplates in an agarose gel.
Fil: Villa Perez, Cristian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina
Fil: Mendoza Herrera, Luis Joaquin. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ciencias Básicas; Argentina
Fil: Santillán, Jesica María José. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ciencias Básicas; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina
Fil: Muñetón Arboleda, David. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ciencias Básicas; Argentina
Fil: Moreno, Mario Sergio Jesus. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche | Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche; Argentina
Fil: Arce, Valeria Beatriz. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigaciones Ópticas. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones Ópticas. Universidad Nacional de La Plata. Centro de Investigaciones Ópticas; Argentina
description Metal nanostructures have received significant attention in recent years owing to their peculiar physical and chemical properties, which span a wide range of practical applications in a variety of scientific and engineering fields. Herein, we report a study of the optical properties and application in the field enhancement of silver nanoplates (Ag-Nplates) obtained by two-step chemical synthesis. Optical Extinction Spectroscopy (OES), together with a detailed theoretical analysis of the experimental spectra, was used to characterize the size distribution, morphology, and optical spectral behavior of the obtained suspensions. These studies were complemented with shape and size distribution analyses using Transmission Electron Microscopy (TEM). It was observed by both techniques that these characteristics are related to the concentration of silver spherical nanoparticles (Ag-Seeds) added during the synthesis of Ag-Nplates. A decrease in the Ag-Seed amount produces an infrared shift of the main plasmon peak with respect to the neat Ag-Seeds suspension, which is related to the size growth of Ag-Nplates showing size distributions centered in the edge length range of 12-15 nm and 34-36 nm for the experimental spectra, whose plasmon peak positions are at 543 nm (higher Ag-Seeds concentration) and 815 nm (lower Ag-Seed concentration), respectively. The detection of Brilliant Blue (BB) by Surface-Enhanced Raman Spectroscopy (SERS) was successfully probed with the incorporation of Ag-Nplates in an agarose gel.
publishDate 2024
dc.date.none.fl_str_mv 2024-12
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/261445
Villa Perez, Cristian; Mendoza Herrera, Luis Joaquin; Santillán, Jesica María José; Muñetón Arboleda, David; Moreno, Mario Sergio Jesus; et al.; Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application; Cornell University; arXiv; 12-2024; 1-31
2331-8422
CONICET Digital
CONICET
url http://hdl.handle.net/11336/261445
identifier_str_mv Villa Perez, Cristian; Mendoza Herrera, Luis Joaquin; Santillán, Jesica María José; Muñetón Arboleda, David; Moreno, Mario Sergio Jesus; et al.; Silver Nanoplates: Theoretical and Experimental Characterization. Study of SERS Application; Cornell University; arXiv; 12-2024; 1-31
2331-8422
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.48550/arXiv.2412.19452
info:eu-repo/semantics/altIdentifier/arxiv/https://arxiv.org/abs/2412.19452
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Cornell University
publisher.none.fl_str_mv Cornell University
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1846782368260554752
score 12.982451

Publicaciones similares