Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates

Autores
Zalduendo, María Mercedes; Steinberg, Paula Yael; Prudente, Tomás; Di Liscia, Emiliano Javier; Morrone, Josefina; Angelome, Paula Cecilia; Huck Iriart, Cristián
Año de publicación
2020
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
In this work, the preparation and thermal evolution of sputtered semicontinuous gold thin films obtained over ordered mesoporous TiO2 films are presented. The controlled surface topography of the ordered mesoporous TiO2 substrate was used as template for obtaining plasmonic hotspots for Surface Enhanced Raman Spectroscopy (SERS) applications. Plasmonic thin film was obtained by Au sputtering when film thickness was under circa 10 nm. Above this value, the porosity effects from the substrate were lost and Raman signal enhancement with it. Moreover, heat treatment was explored in order to obtain gold nanoislands that can also provide very efficient Raman enhancement. Hence, a very straightforward synthesis procedure is presented for sensing application, even for large scale production.
Fil: Zalduendo, María Mercedes. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; Argentina
Fil: Steinberg, Paula Yael. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; Argentina
Fil: Prudente, Tomás. Universidad Nacional de San Martín. Escuela de Ciencia y Tecnología; Argentina
Fil: Di Liscia, Emiliano Javier. Comisión Nacional de Energía Atómica. Gerencia de Área Investigaciones y Aplicaciones No Nucleares. Gerencia Física (CAC). Departamento de Física de la Materia Condensada; Argentina
Fil: Morrone, Josefina. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; Argentina
Fil: Angelome, Paula Cecilia. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; Argentina
Fil: Huck Iriart, Cristián. Universidad Nacional de San Martín. Escuela de Ciencia y Tecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
Materia
MESOPOROUS OXIDE THIN FILMS
PLASMONIC FILMS
SERS
SPUTTERING
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/145176
Acceder
id CONICETDig_86b2c683e02ce1013bf6136e9816f726
oai_identifier_str oai:ri.conicet.gov.ar:11336/145176
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substratesZalduendo, María MercedesSteinberg, Paula YaelPrudente, TomásDi Liscia, Emiliano JavierMorrone, JosefinaAngelome, Paula CeciliaHuck Iriart, CristiánMESOPOROUS OXIDE THIN FILMSPLASMONIC FILMSSERSSPUTTERINGhttps://purl.org/becyt/ford/2.10https://purl.org/becyt/ford/2In this work, the preparation and thermal evolution of sputtered semicontinuous gold thin films obtained over ordered mesoporous TiO2 films are presented. The controlled surface topography of the ordered mesoporous TiO2 substrate was used as template for obtaining plasmonic hotspots for Surface Enhanced Raman Spectroscopy (SERS) applications. Plasmonic thin film was obtained by Au sputtering when film thickness was under circa 10 nm. Above this value, the porosity effects from the substrate were lost and Raman signal enhancement with it. Moreover, heat treatment was explored in order to obtain gold nanoislands that can also provide very efficient Raman enhancement. Hence, a very straightforward synthesis procedure is presented for sensing application, even for large scale production.Fil: Zalduendo, María Mercedes. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; ArgentinaFil: Steinberg, Paula Yael. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; ArgentinaFil: Prudente, Tomás. Universidad Nacional de San Martín. Escuela de Ciencia y Tecnología; ArgentinaFil: Di Liscia, Emiliano Javier. Comisión Nacional de Energía Atómica. Gerencia de Área Investigaciones y Aplicaciones No Nucleares. Gerencia Física (CAC). Departamento de Física de la Materia Condensada; ArgentinaFil: Morrone, Josefina. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; ArgentinaFil: Angelome, Paula Cecilia. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; ArgentinaFil: Huck Iriart, Cristián. Universidad Nacional de San Martín. Escuela de Ciencia y Tecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; ArgentinaSpringer Nature2020-10-10info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/145176Zalduendo, María Mercedes; Steinberg, Paula Yael; Prudente, Tomás; Di Liscia, Emiliano Javier; Morrone, Josefina; et al.; Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates; Springer Nature; SN Applied Sciences; 2; 11; 10-10-2020; 1-102523-39632523-3971CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://link.springer.com/10.1007/s42452-020-03635-9info:eu-repo/semantics/altIdentifier/doi/10.1007/s42452-020-03635-9info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T10:08:16Zoai:ri.conicet.gov.ar:11336/145176instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 10:08:16.88CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates
title Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates
spellingShingle Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates
Zalduendo, María Mercedes
MESOPOROUS OXIDE THIN FILMS
PLASMONIC FILMS
SERS
SPUTTERING
title_short Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates
title_full Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates
title_fullStr Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates
title_full_unstemmed Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates
title_sort Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates
dc.creator.none.fl_str_mv Zalduendo, María Mercedes
Steinberg, Paula Yael
Prudente, Tomás
Di Liscia, Emiliano Javier
Morrone, Josefina
Angelome, Paula Cecilia
Huck Iriart, Cristián
author Zalduendo, María Mercedes
author_facet Zalduendo, María Mercedes
Steinberg, Paula Yael
Prudente, Tomás
Di Liscia, Emiliano Javier
Morrone, Josefina
Angelome, Paula Cecilia
Huck Iriart, Cristián
author_role author
author2 Steinberg, Paula Yael
Prudente, Tomás
Di Liscia, Emiliano Javier
Morrone, Josefina
Angelome, Paula Cecilia
Huck Iriart, Cristián
author2_role author
author
author
author
author
author
dc.subject.none.fl_str_mv MESOPOROUS OXIDE THIN FILMS
PLASMONIC FILMS
SERS
SPUTTERING
topic MESOPOROUS OXIDE THIN FILMS
PLASMONIC FILMS
SERS
SPUTTERING
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.10
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv In this work, the preparation and thermal evolution of sputtered semicontinuous gold thin films obtained over ordered mesoporous TiO2 films are presented. The controlled surface topography of the ordered mesoporous TiO2 substrate was used as template for obtaining plasmonic hotspots for Surface Enhanced Raman Spectroscopy (SERS) applications. Plasmonic thin film was obtained by Au sputtering when film thickness was under circa 10 nm. Above this value, the porosity effects from the substrate were lost and Raman signal enhancement with it. Moreover, heat treatment was explored in order to obtain gold nanoislands that can also provide very efficient Raman enhancement. Hence, a very straightforward synthesis procedure is presented for sensing application, even for large scale production.
Fil: Zalduendo, María Mercedes. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; Argentina
Fil: Steinberg, Paula Yael. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; Argentina
Fil: Prudente, Tomás. Universidad Nacional de San Martín. Escuela de Ciencia y Tecnología; Argentina
Fil: Di Liscia, Emiliano Javier. Comisión Nacional de Energía Atómica. Gerencia de Área Investigaciones y Aplicaciones No Nucleares. Gerencia Física (CAC). Departamento de Física de la Materia Condensada; Argentina
Fil: Morrone, Josefina. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; Argentina
Fil: Angelome, Paula Cecilia. Comisión Nacional de Energía Atómica. Gerencia del Área de Seguridad Nuclear y Ambiente. Gerencia de Química (CAC); Argentina. Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. - Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología; Argentina
Fil: Huck Iriart, Cristián. Universidad Nacional de San Martín. Escuela de Ciencia y Tecnología; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
description In this work, the preparation and thermal evolution of sputtered semicontinuous gold thin films obtained over ordered mesoporous TiO2 films are presented. The controlled surface topography of the ordered mesoporous TiO2 substrate was used as template for obtaining plasmonic hotspots for Surface Enhanced Raman Spectroscopy (SERS) applications. Plasmonic thin film was obtained by Au sputtering when film thickness was under circa 10 nm. Above this value, the porosity effects from the substrate were lost and Raman signal enhancement with it. Moreover, heat treatment was explored in order to obtain gold nanoislands that can also provide very efficient Raman enhancement. Hence, a very straightforward synthesis procedure is presented for sensing application, even for large scale production.
publishDate 2020
dc.date.none.fl_str_mv 2020-10-10
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/145176
Zalduendo, María Mercedes; Steinberg, Paula Yael; Prudente, Tomás; Di Liscia, Emiliano Javier; Morrone, Josefina; et al.; Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates; Springer Nature; SN Applied Sciences; 2; 11; 10-10-2020; 1-10
2523-3963
2523-3971
CONICET Digital
CONICET
url http://hdl.handle.net/11336/145176
identifier_str_mv Zalduendo, María Mercedes; Steinberg, Paula Yael; Prudente, Tomás; Di Liscia, Emiliano Javier; Morrone, Josefina; et al.; Gold semicontinuous thin-film-coated mesoporous TiO2 for SERS substrates; Springer Nature; SN Applied Sciences; 2; 11; 10-10-2020; 1-10
2523-3963
2523-3971
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/http://link.springer.com/10.1007/s42452-020-03635-9
info:eu-repo/semantics/altIdentifier/doi/10.1007/s42452-020-03635-9
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Springer Nature
publisher.none.fl_str_mv Springer Nature
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842270038717890560
score 13.13397

Publicaciones similares