Sobre la cinética de curado y la espectroscopía de relajación dieléctrica en compuestos de polibutadieno (BR) con peróxido de dicumilo

• Autores: Marzocca, Angel José; Rodriguez Garraza, A. L.; Sorichetti, Patricio Aníbal; Matteo, Claudia Leda; Mosca, H. O.
• Año de publicación: 2011
• Idioma: español castellano
• Tipo de recurso: artículo
• Fuente: An. (Asoc. Fís. Argent., En línea) 2011;02(23):75-79
• Materia: POLIBUTADIENO; PROPIEDADES DIELECTRICAS; DENSIDAD DE PUENTES; POLYBUTADIENE RUBBER; DIELECTRIC PROPERTIES; CROSSLINKING
• Institución: Universidad Nacional de Buenos Aires. Facultad de Ciencias Exactas y Naturales

Se estudiaron compuestos de polibutadieno con un 38% de estructura cis-1,4 en su configuración molecular, curados con peróxido de dicumilo como reticulante, utilizando dos contenidos en la formulación. Se caracterizó el proceso de curado de los compuestos a partir de curvas reométricas a temperaturas entre 150° C y 180° C, calculándose el tiempo óptimo de curado para cada temperatura ensayada, t100. Se evaluó la cinética de curado utilizando el formalismo de Kamal-Sourour, obteniéndose el orden y la velocidad de reacción para cada temperatura, la energía de activación del proceso de reticulación y su dependencia con la formulación. Se curaron probetas entre 150° C y 180° C al tiempo óptimo de curado a fin de analizar la estructura de reticulación formada. Mediante la técnica de hinchamiento en solvente (swelling) y el formalismo de Flory-Rehner se caracterizaron a estos compuestos según la densidad de puntos de entrecruzamiento (crosslinks) alcanzada en el proceso de curado. Se utilizó espectroscopia de relajación dieléctrica para estudiar la influencia de la temperatura de curado en los compuestos preparados. Estos ensayos se realizaron a temperatura ambiente y frecuencia entre 1 Hz y 30 MHz. Se comparan los resultados con los obtenidos previamente en compuestos similares utilizando azufre/acelerante (TBBS) como sistema de curado Se discute la influencia del tipo de entrecruzamientos formados analizando los resultados de relajación dieléctrica
Polybutadiene rubber compounds with 38% of cis-1,4 structure in its molecular configuration, cured with dicumyl peroxide as crosslinker, and using two types of formulations were studied The cure process of the compounds was analyzed from rheometric data at temperatures between 150°C and 180°C, calculating the optimum cure time for each temperature tested, t100. The cure kinetics was analyzed by means of the Kamal-Sourour’s formalism, obtaining the order and the reaction rate at each temperature, the activation energy of the cure process and its dependence on the formulation Specimens were cured between 150°C and 180°C at the optimum cure time to characterize the crosslink structure. By the swelling technique and the formalism of Flory-Rehner, these compounds were characterized according to the crosslink density achieved in the vulcanization process. Spectroscopy was used to study the dielectric relaxation effect with the cure temperature of the prepared compounds. These tests, performed at room temperature and frequencies between 1 Hz and 30 MHz were compared to results obtained previously in similar compounds using sulfur/accelerator (TBBS) as cure system. The influence of the type of crosslinks formed was analyzing in the frame of the results of the dielectric relaxation.
Fil: Marzocca, Angel José. Universidad Nacional De Buenos Aires. Facultad de Ciencias Exactas y Naturales. Laboratorio de Polímeros y Materiales Compuestos (UBA-FCEyN-LPYMC). Buenos Aires. Argentina
Fil: Rodriguez Garraza, A. L.. Universidad Nacional De Buenos Aires. Facultad de Ciencias Exactas y Naturales. Laboratorio de Polímeros y Materiales Compuestos (UBA-FCEyN-LPYMC). Buenos Aires. Argentina
Fil: Sorichetti, Patricio Aníbal. Universidad de Buenos Aires. Facultad de Ingeniería. Departamento de Física. Laboratorio de Sistemas Líquidos (UBA-FI-LSL). Buenos Aires. Argentina
Fil: Matteo, Claudia Leda. Universidad de Buenos Aires. Facultad de Ingeniería. Departamento de Física. Laboratorio de Sistemas Líquidos (UBA-FI-LSL). Buenos Aires. Argentina
Fil: Mosca, H. O.. Comisión Nacional de Energía Atómica. Centro Atómico Constituyentes.(CAC-CNEA-CONICET). Buenos Aires. Argentina