Atmospheric corrosion of painted galvanized and 55% Al-Zn steel sheets: results of 12 years of exposure

Autores
Elsner, Cecilia Inés; Seré, Pablo Ricardo; Di Sarli, Alejandro Ramón
Año de publicación
2012
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Zinc or 55%Al-Zn alloy-coated steel sheets, either bare or covered by different painting systems, have been exposed for 12 years to the action of the urban atmosphere at the CIDEPINT station located in La Plata (34° 50′ South, 57° 53′, West), province of Buenos Aires, Argentina. The samples exposed surface was evaluated through periodical visual inspections, standardized adhesion tests, and electrochemical impedance measurements. The ambient variables monitored were average annual rains and temperatures, time of wetness, sulphur and chloride concentration, relative humidity, and speed and direction of the winds. It was found that in this atmosphere, the corrosion resistance of the bare 55% Al-Zn/steel sheets was higher than of the galvanized steel, and the polyurethane painting system was more protective than the alkyd and epoxy ones, which degraded after 6-7 years of exposure.
Facultad de Ingeniería (FI)
Materia
Ingeniería
Corrosión
Pinturas
Nivel de accesibilidad
acceso abierto
Condiciones de uso
http://creativecommons.org/licenses/by/3.0/
Repositorio
SEDICI (UNLP)
Institución
Universidad Nacional de La Plata
OAI Identificador
oai:sedici.unlp.edu.ar:10915/37225

id SEDICI_c88cb640af0985f831ae90428e444542
oai_identifier_str oai:sedici.unlp.edu.ar:10915/37225
network_acronym_str SEDICI
repository_id_str 1329
network_name_str SEDICI (UNLP)
spelling Atmospheric corrosion of painted galvanized and 55% Al-Zn steel sheets: results of 12 years of exposureElsner, Cecilia InésSeré, Pablo RicardoDi Sarli, Alejandro RamónIngenieríaCorrosiónPinturasZinc or 55%Al-Zn alloy-coated steel sheets, either bare or covered by different painting systems, have been exposed for 12 years to the action of the urban atmosphere at the CIDEPINT station located in La Plata (34° 50′ South, 57° 53′, West), province of Buenos Aires, Argentina. The samples exposed surface was evaluated through periodical visual inspections, standardized adhesion tests, and electrochemical impedance measurements. The ambient variables monitored were average annual rains and temperatures, time of wetness, sulphur and chloride concentration, relative humidity, and speed and direction of the winds. It was found that in this atmosphere, the corrosion resistance of the bare 55% Al-Zn/steel sheets was higher than of the galvanized steel, and the polyurethane painting system was more protective than the alkyd and epoxy ones, which degraded after 6-7 years of exposure.Facultad de Ingeniería (FI)2012info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionArticulohttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfhttp://sedici.unlp.edu.ar/handle/10915/37225enginfo:eu-repo/semantics/altIdentifier/issn/1687-9325info:eu-repo/semantics/altIdentifier/doi/10.1155/2012/419640info:eu-repo/semantics/altIdentifier/hdl/11746/1997info:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by/3.0/Creative Commons Attribution 3.0 Unported (CC BY 3.0)reponame:SEDICI (UNLP)instname:Universidad Nacional de La Platainstacron:UNLP2025-09-29T10:57:07Zoai:sedici.unlp.edu.ar:10915/37225Institucionalhttp://sedici.unlp.edu.ar/Universidad públicaNo correspondehttp://sedici.unlp.edu.ar/oai/snrdalira@sedici.unlp.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:13292025-09-29 10:57:08.242SEDICI (UNLP) - Universidad Nacional de La Platafalse
dc.title.none.fl_str_mv Atmospheric corrosion of painted galvanized and 55% Al-Zn steel sheets: results of 12 years of exposure
title Atmospheric corrosion of painted galvanized and 55% Al-Zn steel sheets: results of 12 years of exposure
spellingShingle Atmospheric corrosion of painted galvanized and 55% Al-Zn steel sheets: results of 12 years of exposure
Elsner, Cecilia Inés
Ingeniería
Corrosión
Pinturas
title_short Atmospheric corrosion of painted galvanized and 55% Al-Zn steel sheets: results of 12 years of exposure
title_full Atmospheric corrosion of painted galvanized and 55% Al-Zn steel sheets: results of 12 years of exposure
title_fullStr Atmospheric corrosion of painted galvanized and 55% Al-Zn steel sheets: results of 12 years of exposure
title_full_unstemmed Atmospheric corrosion of painted galvanized and 55% Al-Zn steel sheets: results of 12 years of exposure
title_sort Atmospheric corrosion of painted galvanized and 55% Al-Zn steel sheets: results of 12 years of exposure
dc.creator.none.fl_str_mv Elsner, Cecilia Inés
Seré, Pablo Ricardo
Di Sarli, Alejandro Ramón
author Elsner, Cecilia Inés
author_facet Elsner, Cecilia Inés
Seré, Pablo Ricardo
Di Sarli, Alejandro Ramón
author_role author
author2 Seré, Pablo Ricardo
Di Sarli, Alejandro Ramón
author2_role author
author
dc.subject.none.fl_str_mv Ingeniería
Corrosión
Pinturas
topic Ingeniería
Corrosión
Pinturas
dc.description.none.fl_txt_mv Zinc or 55%Al-Zn alloy-coated steel sheets, either bare or covered by different painting systems, have been exposed for 12 years to the action of the urban atmosphere at the CIDEPINT station located in La Plata (34° 50′ South, 57° 53′, West), province of Buenos Aires, Argentina. The samples exposed surface was evaluated through periodical visual inspections, standardized adhesion tests, and electrochemical impedance measurements. The ambient variables monitored were average annual rains and temperatures, time of wetness, sulphur and chloride concentration, relative humidity, and speed and direction of the winds. It was found that in this atmosphere, the corrosion resistance of the bare 55% Al-Zn/steel sheets was higher than of the galvanized steel, and the polyurethane painting system was more protective than the alkyd and epoxy ones, which degraded after 6-7 years of exposure.
Facultad de Ingeniería (FI)
description Zinc or 55%Al-Zn alloy-coated steel sheets, either bare or covered by different painting systems, have been exposed for 12 years to the action of the urban atmosphere at the CIDEPINT station located in La Plata (34° 50′ South, 57° 53′, West), province of Buenos Aires, Argentina. The samples exposed surface was evaluated through periodical visual inspections, standardized adhesion tests, and electrochemical impedance measurements. The ambient variables monitored were average annual rains and temperatures, time of wetness, sulphur and chloride concentration, relative humidity, and speed and direction of the winds. It was found that in this atmosphere, the corrosion resistance of the bare 55% Al-Zn/steel sheets was higher than of the galvanized steel, and the polyurethane painting system was more protective than the alkyd and epoxy ones, which degraded after 6-7 years of exposure.
publishDate 2012
dc.date.none.fl_str_mv 2012
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
Articulo
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://sedici.unlp.edu.ar/handle/10915/37225
url http://sedici.unlp.edu.ar/handle/10915/37225
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/issn/1687-9325
info:eu-repo/semantics/altIdentifier/doi/10.1155/2012/419640
info:eu-repo/semantics/altIdentifier/hdl/11746/1997
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
http://creativecommons.org/licenses/by/3.0/
Creative Commons Attribution 3.0 Unported (CC BY 3.0)
eu_rights_str_mv openAccess
rights_invalid_str_mv http://creativecommons.org/licenses/by/3.0/
Creative Commons Attribution 3.0 Unported (CC BY 3.0)
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:SEDICI (UNLP)
instname:Universidad Nacional de La Plata
instacron:UNLP
reponame_str SEDICI (UNLP)
collection SEDICI (UNLP)
instname_str Universidad Nacional de La Plata
instacron_str UNLP
institution UNLP
repository.name.fl_str_mv SEDICI (UNLP) - Universidad Nacional de La Plata
repository.mail.fl_str_mv alira@sedici.unlp.edu.ar
_version_ 1844615832307499008
score 13.070432