Comparative evaluation of properties of a clay based ceramic shaped via four techniques

Autores
Torres, Camila Irene; Rendtorff Birrer, Nicolás Maximiliano; Cipollone, Mariano; Aglietti, Esteban Fausto; Suárez, Gustavo
Año de publicación
2018
Idioma
español castellano
Tipo de recurso
artículo
Estado
versión publicada
Descripción
The results of qualitative and quantitative properties of clay based ceramic are presented in this work. Four different shaping methods and sintering temperatures were used to understand their influence in the final properties of a ceramic material formulated using kaolinite clay and calcined alumina. This material can be used as a structural ceramic for different applications, and there is no pre-established relation between the forming method and the final sintered properties. Forming methods used to prepare the samples were uniaxial pressing (a batch process that allows application in dry samples), extruding (a continuous process that requires moisture), slip casting (a process that allows to shape complex ceramic ware), and lamination (a batch process that requires moisture). Sintering temperatures were in the range of 1100 and 1400 °C. In order to compare how properties behave as the shaping method and sintering temperature change, textural properties, shrinkage, porosimetry, phase composition and mechanical strength were evaluated and analyzed. Scanning electron microscopy and microtomography were employed for analyzing and comparing the developed microstructures. Differences in the resulting properties are explained in terms of the developed crystalline phases and microstructure.
Resultados das propriedades qualitativas e quantitativas de cerâmica à base de argila são apresentados neste trabalho. Foram utilizados quatro diferentes métodos de conformação e temperaturas de sinterização para entender suas influências nas propriedades finais de um material cerâmico formulado usando argila caulinítica e alumina calcinada. Este material pode ser usado como cerâmica estrutural para diferentes aplicações, e não há relação pré-estabelecida entre o método de conformação e as propriedades sinterizadas finais. Os métodos de conformação utilizados para preparar as amostras foram prensagem uniaxial (processo em batelada que permite a aplicação em amostras secas), extrusão (processo contínuo que requer umidade), colagem (processo que permite moldar produtos cerâmicos complexos) e laminação (processo em batelada que requer umidade). As temperaturas de sinterização foram na faixa de 1100 e 1400 °C. Para comparar como as propriedades se comportam à medida que o método de moldagem e a temperatura de sinterização são alterados, as propriedades de textura, retração, porosimetria, composição de fases e resistência mecânica foram avaliadas e analisadas. Microscopia eletrônica de varredura e microtomografia foram empregadas para analisar e comparar as microestruturas desenvolvidas. As diferenças nas propriedades resultantes são explicadas em termos das fases cristalinas desenvolvidas e da microestrutura.
Centro de Tecnología de Recursos Minerales y Cerámica
Materia
Química
clay based ceramics
shaping
sintering
properties
Nivel de accesibilidad
acceso abierto
Condiciones de uso
http://creativecommons.org/licenses/by-nc-sa/4.0/
Repositorio
SEDICI (UNLP)
Institución
Universidad Nacional de La Plata
OAI Identificador
oai:sedici.unlp.edu.ar:10915/164069

id SEDICI_bc7aa64d9b6782df6bc937410aa76e09
oai_identifier_str oai:sedici.unlp.edu.ar:10915/164069
network_acronym_str SEDICI
repository_id_str 1329
network_name_str SEDICI (UNLP)
spelling Comparative evaluation of properties of a clay based ceramic shaped via four techniquesAvaliação comparative de propriedades de uma cerâmica à base de argila conformada por quatro técnicasTorres, Camila IreneRendtorff Birrer, Nicolás MaximilianoCipollone, MarianoAglietti, Esteban FaustoSuárez, GustavoQuímicaclay based ceramicsshapingsinteringpropertiesThe results of qualitative and quantitative properties of clay based ceramic are presented in this work. Four different shaping methods and sintering temperatures were used to understand their influence in the final properties of a ceramic material formulated using kaolinite clay and calcined alumina. This material can be used as a structural ceramic for different applications, and there is no pre-established relation between the forming method and the final sintered properties. Forming methods used to prepare the samples were uniaxial pressing (a batch process that allows application in dry samples), extruding (a continuous process that requires moisture), slip casting (a process that allows to shape complex ceramic ware), and lamination (a batch process that requires moisture). Sintering temperatures were in the range of 1100 and 1400 °C. In order to compare how properties behave as the shaping method and sintering temperature change, textural properties, shrinkage, porosimetry, phase composition and mechanical strength were evaluated and analyzed. Scanning electron microscopy and microtomography were employed for analyzing and comparing the developed microstructures. Differences in the resulting properties are explained in terms of the developed crystalline phases and microstructure.Resultados das propriedades qualitativas e quantitativas de cerâmica à base de argila são apresentados neste trabalho. Foram utilizados quatro diferentes métodos de conformação e temperaturas de sinterização para entender suas influências nas propriedades finais de um material cerâmico formulado usando argila caulinítica e alumina calcinada. Este material pode ser usado como cerâmica estrutural para diferentes aplicações, e não há relação pré-estabelecida entre o método de conformação e as propriedades sinterizadas finais. Os métodos de conformação utilizados para preparar as amostras foram prensagem uniaxial (processo em batelada que permite a aplicação em amostras secas), extrusão (processo contínuo que requer umidade), colagem (processo que permite moldar produtos cerâmicos complexos) e laminação (processo em batelada que requer umidade). As temperaturas de sinterização foram na faixa de 1100 e 1400 °C. Para comparar como as propriedades se comportam à medida que o método de moldagem e a temperatura de sinterização são alterados, as propriedades de textura, retração, porosimetria, composição de fases e resistência mecânica foram avaliadas e analisadas. Microscopia eletrônica de varredura e microtomografia foram empregadas para analisar e comparar as microestruturas desenvolvidas. As diferenças nas propriedades resultantes são explicadas em termos das fases cristalinas desenvolvidas e da microestrutura.Centro de Tecnología de Recursos Minerales y Cerámica2018info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionArticulohttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdf176-182http://sedici.unlp.edu.ar/handle/10915/164069spainfo:eu-repo/semantics/altIdentifier/doi/10.1590/0366-69132018643702270info:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-sa/4.0/Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International (CC BY-NC-SA 4.0)reponame:SEDICI (UNLP)instname:Universidad Nacional de La Platainstacron:UNLP2025-09-29T11:43:11Zoai:sedici.unlp.edu.ar:10915/164069Institucionalhttp://sedici.unlp.edu.ar/Universidad públicaNo correspondehttp://sedici.unlp.edu.ar/oai/snrdalira@sedici.unlp.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:13292025-09-29 11:43:11.38SEDICI (UNLP) - Universidad Nacional de La Platafalse
dc.title.none.fl_str_mv Comparative evaluation of properties of a clay based ceramic shaped via four techniques
Avaliação comparative de propriedades de uma cerâmica à base de argila conformada por quatro técnicas
title Comparative evaluation of properties of a clay based ceramic shaped via four techniques
spellingShingle Comparative evaluation of properties of a clay based ceramic shaped via four techniques
Torres, Camila Irene
Química
clay based ceramics
shaping
sintering
properties
title_short Comparative evaluation of properties of a clay based ceramic shaped via four techniques
title_full Comparative evaluation of properties of a clay based ceramic shaped via four techniques
title_fullStr Comparative evaluation of properties of a clay based ceramic shaped via four techniques
title_full_unstemmed Comparative evaluation of properties of a clay based ceramic shaped via four techniques
title_sort Comparative evaluation of properties of a clay based ceramic shaped via four techniques
dc.creator.none.fl_str_mv Torres, Camila Irene
Rendtorff Birrer, Nicolás Maximiliano
Cipollone, Mariano
Aglietti, Esteban Fausto
Suárez, Gustavo
author Torres, Camila Irene
author_facet Torres, Camila Irene
Rendtorff Birrer, Nicolás Maximiliano
Cipollone, Mariano
Aglietti, Esteban Fausto
Suárez, Gustavo
author_role author
author2 Rendtorff Birrer, Nicolás Maximiliano
Cipollone, Mariano
Aglietti, Esteban Fausto
Suárez, Gustavo
author2_role author
author
author
author
dc.subject.none.fl_str_mv Química
clay based ceramics
shaping
sintering
properties
topic Química
clay based ceramics
shaping
sintering
properties
dc.description.none.fl_txt_mv The results of qualitative and quantitative properties of clay based ceramic are presented in this work. Four different shaping methods and sintering temperatures were used to understand their influence in the final properties of a ceramic material formulated using kaolinite clay and calcined alumina. This material can be used as a structural ceramic for different applications, and there is no pre-established relation between the forming method and the final sintered properties. Forming methods used to prepare the samples were uniaxial pressing (a batch process that allows application in dry samples), extruding (a continuous process that requires moisture), slip casting (a process that allows to shape complex ceramic ware), and lamination (a batch process that requires moisture). Sintering temperatures were in the range of 1100 and 1400 °C. In order to compare how properties behave as the shaping method and sintering temperature change, textural properties, shrinkage, porosimetry, phase composition and mechanical strength were evaluated and analyzed. Scanning electron microscopy and microtomography were employed for analyzing and comparing the developed microstructures. Differences in the resulting properties are explained in terms of the developed crystalline phases and microstructure.
Resultados das propriedades qualitativas e quantitativas de cerâmica à base de argila são apresentados neste trabalho. Foram utilizados quatro diferentes métodos de conformação e temperaturas de sinterização para entender suas influências nas propriedades finais de um material cerâmico formulado usando argila caulinítica e alumina calcinada. Este material pode ser usado como cerâmica estrutural para diferentes aplicações, e não há relação pré-estabelecida entre o método de conformação e as propriedades sinterizadas finais. Os métodos de conformação utilizados para preparar as amostras foram prensagem uniaxial (processo em batelada que permite a aplicação em amostras secas), extrusão (processo contínuo que requer umidade), colagem (processo que permite moldar produtos cerâmicos complexos) e laminação (processo em batelada que requer umidade). As temperaturas de sinterização foram na faixa de 1100 e 1400 °C. Para comparar como as propriedades se comportam à medida que o método de moldagem e a temperatura de sinterização são alterados, as propriedades de textura, retração, porosimetria, composição de fases e resistência mecânica foram avaliadas e analisadas. Microscopia eletrônica de varredura e microtomografia foram empregadas para analisar e comparar as microestruturas desenvolvidas. As diferenças nas propriedades resultantes são explicadas em termos das fases cristalinas desenvolvidas e da microestrutura.
Centro de Tecnología de Recursos Minerales y Cerámica
description The results of qualitative and quantitative properties of clay based ceramic are presented in this work. Four different shaping methods and sintering temperatures were used to understand their influence in the final properties of a ceramic material formulated using kaolinite clay and calcined alumina. This material can be used as a structural ceramic for different applications, and there is no pre-established relation between the forming method and the final sintered properties. Forming methods used to prepare the samples were uniaxial pressing (a batch process that allows application in dry samples), extruding (a continuous process that requires moisture), slip casting (a process that allows to shape complex ceramic ware), and lamination (a batch process that requires moisture). Sintering temperatures were in the range of 1100 and 1400 °C. In order to compare how properties behave as the shaping method and sintering temperature change, textural properties, shrinkage, porosimetry, phase composition and mechanical strength were evaluated and analyzed. Scanning electron microscopy and microtomography were employed for analyzing and comparing the developed microstructures. Differences in the resulting properties are explained in terms of the developed crystalline phases and microstructure.
publishDate 2018
dc.date.none.fl_str_mv 2018
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
Articulo
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://sedici.unlp.edu.ar/handle/10915/164069
url http://sedici.unlp.edu.ar/handle/10915/164069
dc.language.none.fl_str_mv spa
language spa
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1590/0366-69132018643702270
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
http://creativecommons.org/licenses/by-nc-sa/4.0/
Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International (CC BY-NC-SA 4.0)
eu_rights_str_mv openAccess
rights_invalid_str_mv http://creativecommons.org/licenses/by-nc-sa/4.0/
Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International (CC BY-NC-SA 4.0)
dc.format.none.fl_str_mv application/pdf
176-182
dc.source.none.fl_str_mv reponame:SEDICI (UNLP)
instname:Universidad Nacional de La Plata
instacron:UNLP
reponame_str SEDICI (UNLP)
collection SEDICI (UNLP)
instname_str Universidad Nacional de La Plata
instacron_str UNLP
institution UNLP
repository.name.fl_str_mv SEDICI (UNLP) - Universidad Nacional de La Plata
repository.mail.fl_str_mv alira@sedici.unlp.edu.ar
_version_ 1844616300912967680
score 13.070432