Comparative evaluation of properties of a clay based ceramic shaped via four techniques
- Autores
- Torres, Camila Irene; Rendtorff Birrer, Nicolás Maximiliano; Cipollone, M.; Aglietti, Esteban Fausto; Suarez, Gustavo
- Año de publicación
- 2018
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- The results of qualitative and quantitative properties of clay based ceramic are presented in this work. Four different shaping methods and sintering temperatures were used to understand their influence in the final properties of a ceramic material formulated using kaolinite clay and calcined alumina. This material can be used as a structural ceramic for different applications, and there is no pre-established relation between the forming method and the final sintered properties. Forming methods used to prepare the samples were uniaxial pressing (a batch process that allows application in dry samples), extruding (a continuous process that requires moisture), slip casting (a process that allows to shape complex ceramic ware), and lamination (a batch process that requires moisture). Sintering temperatures were in the range of 1100 and 1400 °C. In order to compare how properties behave as the shaping method and sintering temperature change, textural properties, shrinkage, porosimetry, phase composition and mechanical strength were evaluated and analyzed. Scanning electron microscopy and microtomography were employed for analyzing and comparing the developed microstructures. Differences in the resulting properties are explained in terms of the developed crystalline phases and microstructure.
Resultados das propriedades qualitativas e quantitativas de cerâmica à base de argila são apresentados neste trabalho. Foram utilizados quatro diferentes métodos de conformação e temperaturas de sinterização para entender suas influências nas propriedades finais de um material cerâmico formulado usando argila caulinítica e alumina calcinada. Este material pode ser usado como cerâmica estrutural para diferentes aplicações, e não há relação pré-estabelecida entre o método de conformação e as propriedades sinterizadas finais. Os métodos de conformação utilizados para preparar as amostras foram prensagem uniaxial (processo em batelada que permite a aplicação em amostras secas), extrusão (processo contínuo que requer umidade), colagem (processo que permite moldar produtos cerâmicos complexos) e laminação (processo em batelada que requer umidade). As temperaturas de sinterização foram na faixa de 1100 e 1400 °C. Para comparar como as propriedades se comportam à medida que o método de moldagem e a temperatura de sinterização são alterados, as propriedades de textura, retração, porosimetria, composição de fases e resistência mecânica foram avaliadas e analisadas. Microscopia eletrônica de varredura e microtomografia foram empregadas para analisar e comparar as microestruturas desenvolvidas. As diferenças nas propriedades resultantes são explicadas em termos das fases cristalinas desenvolvidas e da microestrutura.
Fil: Torres, Camila Irene. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Cipollone, M.. YPF - Tecnología; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina - Materia
-
CLAY BASED CERAMICS
PROPERTIES
SHAPING
SINTERING - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/102943
Ver los metadatos del registro completo
id |
CONICETDig_20f7aa94b4cce1b574a32086fcb6bb7f |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/102943 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Comparative evaluation of properties of a clay based ceramic shaped via four techniquesAvaliação comparative de propriedades de uma cerâmica à base de argila conformada por quatro técnicasTorres, Camila IreneRendtorff Birrer, Nicolás MaximilianoCipollone, M.Aglietti, Esteban FaustoSuarez, GustavoCLAY BASED CERAMICSPROPERTIESSHAPINGSINTERINGhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2The results of qualitative and quantitative properties of clay based ceramic are presented in this work. Four different shaping methods and sintering temperatures were used to understand their influence in the final properties of a ceramic material formulated using kaolinite clay and calcined alumina. This material can be used as a structural ceramic for different applications, and there is no pre-established relation between the forming method and the final sintered properties. Forming methods used to prepare the samples were uniaxial pressing (a batch process that allows application in dry samples), extruding (a continuous process that requires moisture), slip casting (a process that allows to shape complex ceramic ware), and lamination (a batch process that requires moisture). Sintering temperatures were in the range of 1100 and 1400 °C. In order to compare how properties behave as the shaping method and sintering temperature change, textural properties, shrinkage, porosimetry, phase composition and mechanical strength were evaluated and analyzed. Scanning electron microscopy and microtomography were employed for analyzing and comparing the developed microstructures. Differences in the resulting properties are explained in terms of the developed crystalline phases and microstructure.Resultados das propriedades qualitativas e quantitativas de cerâmica à base de argila são apresentados neste trabalho. Foram utilizados quatro diferentes métodos de conformação e temperaturas de sinterização para entender suas influências nas propriedades finais de um material cerâmico formulado usando argila caulinítica e alumina calcinada. Este material pode ser usado como cerâmica estrutural para diferentes aplicações, e não há relação pré-estabelecida entre o método de conformação e as propriedades sinterizadas finais. Os métodos de conformação utilizados para preparar as amostras foram prensagem uniaxial (processo em batelada que permite a aplicação em amostras secas), extrusão (processo contínuo que requer umidade), colagem (processo que permite moldar produtos cerâmicos complexos) e laminação (processo em batelada que requer umidade). As temperaturas de sinterização foram na faixa de 1100 e 1400 °C. Para comparar como as propriedades se comportam à medida que o método de moldagem e a temperatura de sinterização são alterados, as propriedades de textura, retração, porosimetria, composição de fases e resistência mecânica foram avaliadas e analisadas. Microscopia eletrônica de varredura e microtomografia foram empregadas para analisar e comparar as microestruturas desenvolvidas. As diferenças nas propriedades resultantes são explicadas em termos das fases cristalinas desenvolvidas e da microestrutura.Fil: Torres, Camila Irene. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Rendtorff Birrer, Nicolás Maximiliano. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Cipollone, M.. YPF - Tecnología; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; ArgentinaFil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaAssociacao Brasileira de Ceramica2018-06info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/102943Torres, Camila Irene; Rendtorff Birrer, Nicolás Maximiliano; Cipollone, M.; Aglietti, Esteban Fausto; Suarez, Gustavo; Comparative evaluation of properties of a clay based ceramic shaped via four techniques; Associacao Brasileira de Ceramica; Ceramica; 64; 370; 6-2018; 176-1820366-69131678-4553CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132018000200176&lng=en&tlng=eninfo:eu-repo/semantics/altIdentifier/doi/10.1590/0366-69132018643702270info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:46:09Zoai:ri.conicet.gov.ar:11336/102943instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:46:09.385CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Comparative evaluation of properties of a clay based ceramic shaped via four techniques Avaliação comparative de propriedades de uma cerâmica à base de argila conformada por quatro técnicas |
title |
Comparative evaluation of properties of a clay based ceramic shaped via four techniques |
spellingShingle |
Comparative evaluation of properties of a clay based ceramic shaped via four techniques Torres, Camila Irene CLAY BASED CERAMICS PROPERTIES SHAPING SINTERING |
title_short |
Comparative evaluation of properties of a clay based ceramic shaped via four techniques |
title_full |
Comparative evaluation of properties of a clay based ceramic shaped via four techniques |
title_fullStr |
Comparative evaluation of properties of a clay based ceramic shaped via four techniques |
title_full_unstemmed |
Comparative evaluation of properties of a clay based ceramic shaped via four techniques |
title_sort |
Comparative evaluation of properties of a clay based ceramic shaped via four techniques |
dc.creator.none.fl_str_mv |
Torres, Camila Irene Rendtorff Birrer, Nicolás Maximiliano Cipollone, M. Aglietti, Esteban Fausto Suarez, Gustavo |
author |
Torres, Camila Irene |
author_facet |
Torres, Camila Irene Rendtorff Birrer, Nicolás Maximiliano Cipollone, M. Aglietti, Esteban Fausto Suarez, Gustavo |
author_role |
author |
author2 |
Rendtorff Birrer, Nicolás Maximiliano Cipollone, M. Aglietti, Esteban Fausto Suarez, Gustavo |
author2_role |
author author author author |
dc.subject.none.fl_str_mv |
CLAY BASED CERAMICS PROPERTIES SHAPING SINTERING |
topic |
CLAY BASED CERAMICS PROPERTIES SHAPING SINTERING |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
The results of qualitative and quantitative properties of clay based ceramic are presented in this work. Four different shaping methods and sintering temperatures were used to understand their influence in the final properties of a ceramic material formulated using kaolinite clay and calcined alumina. This material can be used as a structural ceramic for different applications, and there is no pre-established relation between the forming method and the final sintered properties. Forming methods used to prepare the samples were uniaxial pressing (a batch process that allows application in dry samples), extruding (a continuous process that requires moisture), slip casting (a process that allows to shape complex ceramic ware), and lamination (a batch process that requires moisture). Sintering temperatures were in the range of 1100 and 1400 °C. In order to compare how properties behave as the shaping method and sintering temperature change, textural properties, shrinkage, porosimetry, phase composition and mechanical strength were evaluated and analyzed. Scanning electron microscopy and microtomography were employed for analyzing and comparing the developed microstructures. Differences in the resulting properties are explained in terms of the developed crystalline phases and microstructure. Resultados das propriedades qualitativas e quantitativas de cerâmica à base de argila são apresentados neste trabalho. Foram utilizados quatro diferentes métodos de conformação e temperaturas de sinterização para entender suas influências nas propriedades finais de um material cerâmico formulado usando argila caulinítica e alumina calcinada. Este material pode ser usado como cerâmica estrutural para diferentes aplicações, e não há relação pré-estabelecida entre o método de conformação e as propriedades sinterizadas finais. Os métodos de conformação utilizados para preparar as amostras foram prensagem uniaxial (processo em batelada que permite a aplicação em amostras secas), extrusão (processo contínuo que requer umidade), colagem (processo que permite moldar produtos cerâmicos complexos) e laminação (processo em batelada que requer umidade). As temperaturas de sinterização foram na faixa de 1100 e 1400 °C. Para comparar como as propriedades se comportam à medida que o método de moldagem e a temperatura de sinterização são alterados, as propriedades de textura, retração, porosimetria, composição de fases e resistência mecânica foram avaliadas e analisadas. Microscopia eletrônica de varredura e microtomografia foram empregadas para analisar e comparar as microestruturas desenvolvidas. As diferenças nas propriedades resultantes são explicadas em termos das fases cristalinas desenvolvidas e da microestrutura. Fil: Torres, Camila Irene. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina Fil: Rendtorff Birrer, Nicolás Maximiliano. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina Fil: Cipollone, M.. YPF - Tecnología; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina |
description |
The results of qualitative and quantitative properties of clay based ceramic are presented in this work. Four different shaping methods and sintering temperatures were used to understand their influence in the final properties of a ceramic material formulated using kaolinite clay and calcined alumina. This material can be used as a structural ceramic for different applications, and there is no pre-established relation between the forming method and the final sintered properties. Forming methods used to prepare the samples were uniaxial pressing (a batch process that allows application in dry samples), extruding (a continuous process that requires moisture), slip casting (a process that allows to shape complex ceramic ware), and lamination (a batch process that requires moisture). Sintering temperatures were in the range of 1100 and 1400 °C. In order to compare how properties behave as the shaping method and sintering temperature change, textural properties, shrinkage, porosimetry, phase composition and mechanical strength were evaluated and analyzed. Scanning electron microscopy and microtomography were employed for analyzing and comparing the developed microstructures. Differences in the resulting properties are explained in terms of the developed crystalline phases and microstructure. |
publishDate |
2018 |
dc.date.none.fl_str_mv |
2018-06 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/102943 Torres, Camila Irene; Rendtorff Birrer, Nicolás Maximiliano; Cipollone, M.; Aglietti, Esteban Fausto; Suarez, Gustavo; Comparative evaluation of properties of a clay based ceramic shaped via four techniques; Associacao Brasileira de Ceramica; Ceramica; 64; 370; 6-2018; 176-182 0366-6913 1678-4553 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/102943 |
identifier_str_mv |
Torres, Camila Irene; Rendtorff Birrer, Nicolás Maximiliano; Cipollone, M.; Aglietti, Esteban Fausto; Suarez, Gustavo; Comparative evaluation of properties of a clay based ceramic shaped via four techniques; Associacao Brasileira de Ceramica; Ceramica; 64; 370; 6-2018; 176-182 0366-6913 1678-4553 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/url/http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132018000200176&lng=en&tlng=en info:eu-repo/semantics/altIdentifier/doi/10.1590/0366-69132018643702270 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Associacao Brasileira de Ceramica |
publisher.none.fl_str_mv |
Associacao Brasileira de Ceramica |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844614502565281792 |
score |
13.070432 |