Corrosion behaviour of a SiOxNy coated and nitrided ph stainles steel
- Autores
- Dalibón Bähler, Eugenia Laura; Moscatelli, Mauro Nicolás; Simison, Silvia; Escalada, Lisandro; Cabo, Amado; Lasorsa, Carlos; Brühl, Sonia Patricia
- Año de publicación
- 2015
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión aceptada
- Descripción
- Precipitation hardening stainless steels are used in applications where wear and corrosion resistance are required. To improve the surface properties, thermochemical treatments in combination with hard coatings can be used. In this work, the corrosion behaviour of SiOxNy coatings deposited on nitrided and non-nitrided Corrax® PH stainless steel were evaluated comparing them with the behaviour of samples which were only nitrided (two different conditions of nitrogen percentage in the working gases were used). The microstructure was analyzed. Corrosion behaviour was evaluated by the Salt Spray Fog Test and cyclic potentiodynamic polarization in NaCl solution. Erosion-corrosion tests were conducted. The thickness of the coating was about 1.4 microns, and its hardness was 2300 HV. The film had better erosion and corrosion behaviour when it was deposited on the nitrided steel. This fact demonstrated that the nitrided layer results in a good interface that improves the adhesion and mechanical support.
Fil: Dalibón Bähler, Eugenia Laura. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.
Fil: Moscatelli, Mauro Nicolás. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.
Fil: Simison, Silvia. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigación en Ciencia y Tecnología de Materiales; Argentina.
Fil: Escalada, Lisandro. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigación en Ciencia y Tecnología de Materiales; Argentina.
Fil: Cabo, Amado. IONAR SA; Argentina.
Fil: Lasorsa, Carlos. Universidad Tecnológica Nacional. Facultad Regional Haedo; Argentina.
Fil: Brühl, Sonia Patricia. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.
Peer Reviewed - Materia
-
PH steels
PACVD
Corrosion
Plasma nitriding - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- http://creativecommons.org/licenses/by-nc-nd/4.0/
- Repositorio
- Institución
- Universidad Tecnológica Nacional
- OAI Identificador
- oai:ria.utn.edu.ar:20.500.12272/2061
Ver los metadatos del registro completo
id |
RIAUTN_1928a2d9e284846d5e84912c283b3dc4 |
---|---|
oai_identifier_str |
oai:ria.utn.edu.ar:20.500.12272/2061 |
network_acronym_str |
RIAUTN |
repository_id_str |
a |
network_name_str |
Repositorio Institucional Abierto (UTN) |
spelling |
Corrosion behaviour of a SiOxNy coated and nitrided ph stainles steelDalibón Bähler, Eugenia LauraMoscatelli, Mauro NicolásSimison, SilviaEscalada, LisandroCabo, AmadoLasorsa, CarlosBrühl, Sonia PatriciaPH steelsPACVDCorrosionPlasma nitridingPrecipitation hardening stainless steels are used in applications where wear and corrosion resistance are required. To improve the surface properties, thermochemical treatments in combination with hard coatings can be used. In this work, the corrosion behaviour of SiOxNy coatings deposited on nitrided and non-nitrided Corrax® PH stainless steel were evaluated comparing them with the behaviour of samples which were only nitrided (two different conditions of nitrogen percentage in the working gases were used). The microstructure was analyzed. Corrosion behaviour was evaluated by the Salt Spray Fog Test and cyclic potentiodynamic polarization in NaCl solution. Erosion-corrosion tests were conducted. The thickness of the coating was about 1.4 microns, and its hardness was 2300 HV. The film had better erosion and corrosion behaviour when it was deposited on the nitrided steel. This fact demonstrated that the nitrided layer results in a good interface that improves the adhesion and mechanical support.Fil: Dalibón Bähler, Eugenia Laura. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.Fil: Moscatelli, Mauro Nicolás. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.Fil: Simison, Silvia. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigación en Ciencia y Tecnología de Materiales; Argentina.Fil: Escalada, Lisandro. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigación en Ciencia y Tecnología de Materiales; Argentina.Fil: Cabo, Amado. IONAR SA; Argentina.Fil: Lasorsa, Carlos. Universidad Tecnológica Nacional. Facultad Regional Haedo; Argentina.Fil: Brühl, Sonia Patricia. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina.Peer ReviewedElsevier2017-09-19T00:33:51Z2017-09-19T00:33:51Z2015info:eu-repo/semantics/articleinfo:eu-repo/semantics/acceptedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfRevista Elsevier Volume 8, 2015, P. 29-38http://dx.doi.org/doi:/10.1016/j.mspro.2015.04.045http://hdl.handle.net/20.500.12272/2061engenghttp://www.sciencedirect.com/science/article/pii/S2211812815000462?via%3Dihub#!Azzi, M., Benkahoul, M., Klemberg-Sapieha, J. E., Martinu, L., 2010. Corrosion and mechanical properties of duplex-treated 301 stainless steel. Surface and Coatings Technology 205, 1557-1563.Benkahoul, M., Robin, P., Martinu, L., Klemberg-Sapieha, J. E., 2009. Tribological properties of duplex Cr–Si-N coatings on SS410 steel. Surface and Coatings Technology 203, 934-940.Bousser, E., Benkahoul, M., Martinu, L., Klemberg-Sapieha, J. E., 2008, Effect microstructure on erosion resistance of Cr-Si-N coatings. Surface and Coatings Technology 203, 776-780.Brühl, S. P., Charadia, R., Simison, S., Lamas, D. G., Cabo, A., 2010. Corrosion behavior of martensitic and precipitation hardening stainless steels treated by plasma nitriding. Surface and Coatings Technology. 204, 3280-3286.Dalibon, E. L., Lasorsa, C., Cabo, A., Cimetta, J., García, N., Brühl, S. P., 2012. Tribological properties of SiNx films on PH stainless steel with and without nitriding as a pre-treatment. Procedia Materials Science 1, 313–320info:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc-nd/4.0/Dalibón Bähler, Eugenia Laura ; Moscatelli, Mauro ; Simison, Silvia ; Escalada, Lisandro ; Cabo, Amado ; Lasorsa, Carlos ; Brühl, Sonia PatriciaNo comercial con fines académicos.Attribution-NonCommercial-NoDerivatives 4.0 Internacionalreponame:Repositorio Institucional Abierto (UTN)instname:Universidad Tecnológica Nacional2025-09-29T14:29:39Zoai:ria.utn.edu.ar:20.500.12272/2061instacron:UTNInstitucionalhttp://ria.utn.edu.ar/Universidad públicaNo correspondehttp://ria.utn.edu.ar/oaigestionria@rec.utn.edu.ar; fsuarez@rec.utn.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:a2025-09-29 14:29:40.192Repositorio Institucional Abierto (UTN) - Universidad Tecnológica Nacionalfalse |
dc.title.none.fl_str_mv |
Corrosion behaviour of a SiOxNy coated and nitrided ph stainles steel |
title |
Corrosion behaviour of a SiOxNy coated and nitrided ph stainles steel |
spellingShingle |
Corrosion behaviour of a SiOxNy coated and nitrided ph stainles steel Dalibón Bähler, Eugenia Laura PH steels PACVD Corrosion Plasma nitriding |
title_short |
Corrosion behaviour of a SiOxNy coated and nitrided ph stainles steel |
title_full |
Corrosion behaviour of a SiOxNy coated and nitrided ph stainles steel |
title_fullStr |
Corrosion behaviour of a SiOxNy coated and nitrided ph stainles steel |
title_full_unstemmed |
Corrosion behaviour of a SiOxNy coated and nitrided ph stainles steel |
title_sort |
Corrosion behaviour of a SiOxNy coated and nitrided ph stainles steel |
dc.creator.none.fl_str_mv |
Dalibón Bähler, Eugenia Laura Moscatelli, Mauro Nicolás Simison, Silvia Escalada, Lisandro Cabo, Amado Lasorsa, Carlos Brühl, Sonia Patricia |
author |
Dalibón Bähler, Eugenia Laura |
author_facet |
Dalibón Bähler, Eugenia Laura Moscatelli, Mauro Nicolás Simison, Silvia Escalada, Lisandro Cabo, Amado Lasorsa, Carlos Brühl, Sonia Patricia |
author_role |
author |
author2 |
Moscatelli, Mauro Nicolás Simison, Silvia Escalada, Lisandro Cabo, Amado Lasorsa, Carlos Brühl, Sonia Patricia |
author2_role |
author author author author author author |
dc.subject.none.fl_str_mv |
PH steels PACVD Corrosion Plasma nitriding |
topic |
PH steels PACVD Corrosion Plasma nitriding |
dc.description.none.fl_txt_mv |
Precipitation hardening stainless steels are used in applications where wear and corrosion resistance are required. To improve the surface properties, thermochemical treatments in combination with hard coatings can be used. In this work, the corrosion behaviour of SiOxNy coatings deposited on nitrided and non-nitrided Corrax® PH stainless steel were evaluated comparing them with the behaviour of samples which were only nitrided (two different conditions of nitrogen percentage in the working gases were used). The microstructure was analyzed. Corrosion behaviour was evaluated by the Salt Spray Fog Test and cyclic potentiodynamic polarization in NaCl solution. Erosion-corrosion tests were conducted. The thickness of the coating was about 1.4 microns, and its hardness was 2300 HV. The film had better erosion and corrosion behaviour when it was deposited on the nitrided steel. This fact demonstrated that the nitrided layer results in a good interface that improves the adhesion and mechanical support. Fil: Dalibón Bähler, Eugenia Laura. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina. Fil: Moscatelli, Mauro Nicolás. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina. Fil: Simison, Silvia. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigación en Ciencia y Tecnología de Materiales; Argentina. Fil: Escalada, Lisandro. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigación en Ciencia y Tecnología de Materiales; Argentina. Fil: Cabo, Amado. IONAR SA; Argentina. Fil: Lasorsa, Carlos. Universidad Tecnológica Nacional. Facultad Regional Haedo; Argentina. Fil: Brühl, Sonia Patricia. Universidad Tecnológica Nacional. Facultad Regional Concepción del Uruguay. Departamento Ingeniería Electromecánica. Grupo de Ingeniería de Superficies; Argentina. Peer Reviewed |
description |
Precipitation hardening stainless steels are used in applications where wear and corrosion resistance are required. To improve the surface properties, thermochemical treatments in combination with hard coatings can be used. In this work, the corrosion behaviour of SiOxNy coatings deposited on nitrided and non-nitrided Corrax® PH stainless steel were evaluated comparing them with the behaviour of samples which were only nitrided (two different conditions of nitrogen percentage in the working gases were used). The microstructure was analyzed. Corrosion behaviour was evaluated by the Salt Spray Fog Test and cyclic potentiodynamic polarization in NaCl solution. Erosion-corrosion tests were conducted. The thickness of the coating was about 1.4 microns, and its hardness was 2300 HV. The film had better erosion and corrosion behaviour when it was deposited on the nitrided steel. This fact demonstrated that the nitrided layer results in a good interface that improves the adhesion and mechanical support. |
publishDate |
2015 |
dc.date.none.fl_str_mv |
2015 2017-09-19T00:33:51Z 2017-09-19T00:33:51Z |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/acceptedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
acceptedVersion |
dc.identifier.none.fl_str_mv |
Revista Elsevier Volume 8, 2015, P. 29-38 http://dx.doi.org/doi:/10.1016/j.mspro.2015.04.045 http://hdl.handle.net/20.500.12272/2061 |
identifier_str_mv |
Revista Elsevier Volume 8, 2015, P. 29-38 |
url |
http://dx.doi.org/doi:/10.1016/j.mspro.2015.04.045 http://hdl.handle.net/20.500.12272/2061 |
dc.language.none.fl_str_mv |
eng eng |
language |
eng |
dc.relation.none.fl_str_mv |
http://www.sciencedirect.com/science/article/pii/S2211812815000462?via%3Dihub#! Azzi, M., Benkahoul, M., Klemberg-Sapieha, J. E., Martinu, L., 2010. Corrosion and mechanical properties of duplex-treated 301 stainless steel. Surface and Coatings Technology 205, 1557-1563. Benkahoul, M., Robin, P., Martinu, L., Klemberg-Sapieha, J. E., 2009. Tribological properties of duplex Cr–Si-N coatings on SS410 steel. Surface and Coatings Technology 203, 934-940. Bousser, E., Benkahoul, M., Martinu, L., Klemberg-Sapieha, J. E., 2008, Effect microstructure on erosion resistance of Cr-Si-N coatings. Surface and Coatings Technology 203, 776-780. Brühl, S. P., Charadia, R., Simison, S., Lamas, D. G., Cabo, A., 2010. Corrosion behavior of martensitic and precipitation hardening stainless steels treated by plasma nitriding. Surface and Coatings Technology. 204, 3280-3286. Dalibon, E. L., Lasorsa, C., Cabo, A., Cimetta, J., García, N., Brühl, S. P., 2012. Tribological properties of SiNx films on PH stainless steel with and without nitriding as a pre-treatment. Procedia Materials Science 1, 313–320 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess http://creativecommons.org/licenses/by-nc-nd/4.0/ Dalibón Bähler, Eugenia Laura ; Moscatelli, Mauro ; Simison, Silvia ; Escalada, Lisandro ; Cabo, Amado ; Lasorsa, Carlos ; Brühl, Sonia Patricia No comercial con fines académicos. Attribution-NonCommercial-NoDerivatives 4.0 Internacional |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
http://creativecommons.org/licenses/by-nc-nd/4.0/ Dalibón Bähler, Eugenia Laura ; Moscatelli, Mauro ; Simison, Silvia ; Escalada, Lisandro ; Cabo, Amado ; Lasorsa, Carlos ; Brühl, Sonia Patricia No comercial con fines académicos. Attribution-NonCommercial-NoDerivatives 4.0 Internacional |
dc.format.none.fl_str_mv |
application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Elsevier |
publisher.none.fl_str_mv |
Elsevier |
dc.source.none.fl_str_mv |
reponame:Repositorio Institucional Abierto (UTN) instname:Universidad Tecnológica Nacional |
reponame_str |
Repositorio Institucional Abierto (UTN) |
collection |
Repositorio Institucional Abierto (UTN) |
instname_str |
Universidad Tecnológica Nacional |
repository.name.fl_str_mv |
Repositorio Institucional Abierto (UTN) - Universidad Tecnológica Nacional |
repository.mail.fl_str_mv |
gestionria@rec.utn.edu.ar; fsuarez@rec.utn.edu.ar |
_version_ |
1844621790326816768 |
score |
12.559606 |