Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel
- Autores
- Dalibon, Eugenia L.; Moscatelli, Mauro; Simison, Silvia Noemi; Escalada, Lisandro; Cabo, Amado; Lasorsa, Carlos Alberto; Brühl, Sonia Patricia
- Año de publicación
- 2015
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- Precipitation hardening stainless steels are used in applications where wear and corrosion resistance are required. To improve the surface properties, thermochemical treatments in combination with hard coatings can be used. In this work, the corrosion behaviour of SiOxNy coatings deposited on nitrided and non-nitrided Corrax® PH stainless steel were evaluated comparing them with the behaviour of samples which were only nitrided (two different conditions of nitrogen percentage in the working gases were used). The microstructure was analyzed. Corrosion behaviour was evaluated by the Salt Spray Fog Test and cyclic potentiodynamic polarization in NaCl solution. Erosion-corrosion tests were conducted. The thickness of the coating was about 1.4 microns, and its hardness was 2300 HV. The film had better erosion and corrosion behaviour when it was deposited on the nitrided steel. This fact demonstrated that the nitrided layer results in a good interface that improves the adhesion and mechanical support.
Fil: Dalibon, Eugenia L.. Universidad Nacional de San Martin. Instituto Sabato; Argentina. Universidad Tecnologica Nacional. Facultad Regional Concepcion del Uruguay; Argentina
Fil: Moscatelli, Mauro. Universidad Tecnologica Nacional. Facultad Regional Concepcion del Uruguay; Argentina
Fil: Simison, Silvia Noemi. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Escalada, Lisandro. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Cabo, Amado. No especifíca;
Fil: Lasorsa, Carlos Alberto. Universidad Tecnologica Nacional. Facultad Regional Haedo; Argentina
Fil: Brühl, Sonia Patricia. Universidad Tecnologica Nacional. Facultad Regional Concepcion del Uruguay; Argentina - Materia
-
AMORPHOUS SILICON
CVD
PH STAINLESS STEEL
CORROSION BEHAVIOUR - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/2886
Ver los metadatos del registro completo
id |
CONICETDig_56ddf80a12a3e33f2949f84222f92265 |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/2886 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steelDalibon, Eugenia L.Moscatelli, MauroSimison, Silvia NoemiEscalada, LisandroCabo, AmadoLasorsa, Carlos AlbertoBrühl, Sonia PatriciaAMORPHOUS SILICONCVDPH STAINLESS STEELCORROSION BEHAVIOURhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Precipitation hardening stainless steels are used in applications where wear and corrosion resistance are required. To improve the surface properties, thermochemical treatments in combination with hard coatings can be used. In this work, the corrosion behaviour of SiOxNy coatings deposited on nitrided and non-nitrided Corrax® PH stainless steel were evaluated comparing them with the behaviour of samples which were only nitrided (two different conditions of nitrogen percentage in the working gases were used). The microstructure was analyzed. Corrosion behaviour was evaluated by the Salt Spray Fog Test and cyclic potentiodynamic polarization in NaCl solution. Erosion-corrosion tests were conducted. The thickness of the coating was about 1.4 microns, and its hardness was 2300 HV. The film had better erosion and corrosion behaviour when it was deposited on the nitrided steel. This fact demonstrated that the nitrided layer results in a good interface that improves the adhesion and mechanical support.Fil: Dalibon, Eugenia L.. Universidad Nacional de San Martin. Instituto Sabato; Argentina. Universidad Tecnologica Nacional. Facultad Regional Concepcion del Uruguay; ArgentinaFil: Moscatelli, Mauro. Universidad Tecnologica Nacional. Facultad Regional Concepcion del Uruguay; ArgentinaFil: Simison, Silvia Noemi. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Escalada, Lisandro. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Cabo, Amado. No especifíca;Fil: Lasorsa, Carlos Alberto. Universidad Tecnologica Nacional. Facultad Regional Haedo; ArgentinaFil: Brühl, Sonia Patricia. Universidad Tecnologica Nacional. Facultad Regional Concepcion del Uruguay; ArgentinaElsevier2015-05info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/2886Dalibon, Eugenia L.; Moscatelli, Mauro; Simison, Silvia Noemi; Escalada, Lisandro; Cabo, Amado; et al.; Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel; Elsevier; Procedia Materials Science; 8; 5-2015; 29-382211-8128engInternational Congress of Science and Technology of Metallurgy and Materials, SAM - CONAMET 2013info:eu-repo/semantics/altIdentifier/doi/10.1016/j.mspro.2015.04.045info:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S2211812815000462info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T09:59:08Zoai:ri.conicet.gov.ar:11336/2886instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 09:59:09.005CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel |
title |
Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel |
spellingShingle |
Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel Dalibon, Eugenia L. AMORPHOUS SILICON CVD PH STAINLESS STEEL CORROSION BEHAVIOUR |
title_short |
Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel |
title_full |
Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel |
title_fullStr |
Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel |
title_full_unstemmed |
Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel |
title_sort |
Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel |
dc.creator.none.fl_str_mv |
Dalibon, Eugenia L. Moscatelli, Mauro Simison, Silvia Noemi Escalada, Lisandro Cabo, Amado Lasorsa, Carlos Alberto Brühl, Sonia Patricia |
author |
Dalibon, Eugenia L. |
author_facet |
Dalibon, Eugenia L. Moscatelli, Mauro Simison, Silvia Noemi Escalada, Lisandro Cabo, Amado Lasorsa, Carlos Alberto Brühl, Sonia Patricia |
author_role |
author |
author2 |
Moscatelli, Mauro Simison, Silvia Noemi Escalada, Lisandro Cabo, Amado Lasorsa, Carlos Alberto Brühl, Sonia Patricia |
author2_role |
author author author author author author |
dc.subject.none.fl_str_mv |
AMORPHOUS SILICON CVD PH STAINLESS STEEL CORROSION BEHAVIOUR |
topic |
AMORPHOUS SILICON CVD PH STAINLESS STEEL CORROSION BEHAVIOUR |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
Precipitation hardening stainless steels are used in applications where wear and corrosion resistance are required. To improve the surface properties, thermochemical treatments in combination with hard coatings can be used. In this work, the corrosion behaviour of SiOxNy coatings deposited on nitrided and non-nitrided Corrax® PH stainless steel were evaluated comparing them with the behaviour of samples which were only nitrided (two different conditions of nitrogen percentage in the working gases were used). The microstructure was analyzed. Corrosion behaviour was evaluated by the Salt Spray Fog Test and cyclic potentiodynamic polarization in NaCl solution. Erosion-corrosion tests were conducted. The thickness of the coating was about 1.4 microns, and its hardness was 2300 HV. The film had better erosion and corrosion behaviour when it was deposited on the nitrided steel. This fact demonstrated that the nitrided layer results in a good interface that improves the adhesion and mechanical support. Fil: Dalibon, Eugenia L.. Universidad Nacional de San Martin. Instituto Sabato; Argentina. Universidad Tecnologica Nacional. Facultad Regional Concepcion del Uruguay; Argentina Fil: Moscatelli, Mauro. Universidad Tecnologica Nacional. Facultad Regional Concepcion del Uruguay; Argentina Fil: Simison, Silvia Noemi. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina Fil: Escalada, Lisandro. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina Fil: Cabo, Amado. No especifíca; Fil: Lasorsa, Carlos Alberto. Universidad Tecnologica Nacional. Facultad Regional Haedo; Argentina Fil: Brühl, Sonia Patricia. Universidad Tecnologica Nacional. Facultad Regional Concepcion del Uruguay; Argentina |
description |
Precipitation hardening stainless steels are used in applications where wear and corrosion resistance are required. To improve the surface properties, thermochemical treatments in combination with hard coatings can be used. In this work, the corrosion behaviour of SiOxNy coatings deposited on nitrided and non-nitrided Corrax® PH stainless steel were evaluated comparing them with the behaviour of samples which were only nitrided (two different conditions of nitrogen percentage in the working gases were used). The microstructure was analyzed. Corrosion behaviour was evaluated by the Salt Spray Fog Test and cyclic potentiodynamic polarization in NaCl solution. Erosion-corrosion tests were conducted. The thickness of the coating was about 1.4 microns, and its hardness was 2300 HV. The film had better erosion and corrosion behaviour when it was deposited on the nitrided steel. This fact demonstrated that the nitrided layer results in a good interface that improves the adhesion and mechanical support. |
publishDate |
2015 |
dc.date.none.fl_str_mv |
2015-05 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/2886 Dalibon, Eugenia L.; Moscatelli, Mauro; Simison, Silvia Noemi; Escalada, Lisandro; Cabo, Amado; et al.; Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel; Elsevier; Procedia Materials Science; 8; 5-2015; 29-38 2211-8128 |
url |
http://hdl.handle.net/11336/2886 |
identifier_str_mv |
Dalibon, Eugenia L.; Moscatelli, Mauro; Simison, Silvia Noemi; Escalada, Lisandro; Cabo, Amado; et al.; Corrosion behaviour of a SiOxNy coated and nitrided PH stainless steel; Elsevier; Procedia Materials Science; 8; 5-2015; 29-38 2211-8128 |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
International Congress of Science and Technology of Metallurgy and Materials, SAM - CONAMET 2013 info:eu-repo/semantics/altIdentifier/doi/10.1016/j.mspro.2015.04.045 info:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S2211812815000462 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-nd/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Elsevier |
publisher.none.fl_str_mv |
Elsevier |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844613757297229824 |
score |
13.070432 |