Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy

Autores
Stábile, Franco Matías; Piccico, M.; Serra, Maria Florencia; Rafti, Matias; Suarez, Gustavo; Rendtorff Birrer, Nicolás Maximiliano
Año de publicación
2015
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
In the present work we attempt to describe the results of the thermal behavior analysis of a commercial glaze obtained in a thermal microscope developed by the research group. At the same time, the density and the wetting angle of the glaze with an alumina surface was evaluated. Particularly the sintering temperature, the sphere, semi-sphere and fusion temperatures were also determined. These present characteristic viscosities. Afterward, by means of the de Vogel-Fulcher-Tammann equation, the viscosity as a function of temperature was estimated. In the first part the developed equipment is described together with the image analysis carried out for the in-situ cylindrical samples (2,5 mm of height and diameter). The thermal cycle was up to 1200ºC with a heating rate of 5ºC/min. The developed equipment presents the following characteristics: some problems with the temperature evaluation, it was slightly affected by air currents and difficulties for achieving an adequate parallelism. On the other hand, the potentialities of the equipment for development and study of the thermal behavior of glasses was established.
Fil: Stábile, Franco Matías. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Piccico, M.. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Serra, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rafti, Matias. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Materia
Viscosidad
Temperaturas
Vidrio
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/48977
Acceder
id CONICETDig_ffe676537cc94e0487fdd362811f1202
oai_identifier_str oai:ri.conicet.gov.ar:11336/48977
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage MicroscopyStábile, Franco MatíasPiccico, M.Serra, Maria FlorenciaRafti, MatiasSuarez, GustavoRendtorff Birrer, Nicolás MaximilianoViscosidadTemperaturasVidriohttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2https://purl.org/becyt/ford/1.4https://purl.org/becyt/ford/1In the present work we attempt to describe the results of the thermal behavior analysis of a commercial glaze obtained in a thermal microscope developed by the research group. At the same time, the density and the wetting angle of the glaze with an alumina surface was evaluated. Particularly the sintering temperature, the sphere, semi-sphere and fusion temperatures were also determined. These present characteristic viscosities. Afterward, by means of the de Vogel-Fulcher-Tammann equation, the viscosity as a function of temperature was estimated. In the first part the developed equipment is described together with the image analysis carried out for the in-situ cylindrical samples (2,5 mm of height and diameter). The thermal cycle was up to 1200ºC with a heating rate of 5ºC/min. The developed equipment presents the following characteristics: some problems with the temperature evaluation, it was slightly affected by air currents and difficulties for achieving an adequate parallelism. On the other hand, the potentialities of the equipment for development and study of the thermal behavior of glasses was established.Fil: Stábile, Franco Matías. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Piccico, M.. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Serra, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Rafti, Matias. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaElsevier2015-06info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/48977Stábile, Franco Matías; Piccico, M.; Serra, Maria Florencia; Rafti, Matias; Suarez, Gustavo; et al.; Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy; Elsevier; Procedia Materials Science; 9; 6-2015; 563-5702211-8128CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1016/j.mspro.2015.05.031info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S2211812815002151info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:29:22Zoai:ri.conicet.gov.ar:11336/48977instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:29:23.045CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy
title Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy
spellingShingle Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy
Stábile, Franco Matías
Viscosidad
Temperaturas
Vidrio
title_short Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy
title_full Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy
title_fullStr Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy
title_full_unstemmed Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy
title_sort Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy
dc.creator.none.fl_str_mv Stábile, Franco Matías
Piccico, M.
Serra, Maria Florencia
Rafti, Matias
Suarez, Gustavo
Rendtorff Birrer, Nicolás Maximiliano
author Stábile, Franco Matías
author_facet Stábile, Franco Matías
Piccico, M.
Serra, Maria Florencia
Rafti, Matias
Suarez, Gustavo
Rendtorff Birrer, Nicolás Maximiliano
author_role author
author2 Piccico, M.
Serra, Maria Florencia
Rafti, Matias
Suarez, Gustavo
Rendtorff Birrer, Nicolás Maximiliano
author2_role author
author
author
author
author
dc.subject.none.fl_str_mv Viscosidad
Temperaturas
Vidrio
topic Viscosidad
Temperaturas
Vidrio
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
https://purl.org/becyt/ford/1.4
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv In the present work we attempt to describe the results of the thermal behavior analysis of a commercial glaze obtained in a thermal microscope developed by the research group. At the same time, the density and the wetting angle of the glaze with an alumina surface was evaluated. Particularly the sintering temperature, the sphere, semi-sphere and fusion temperatures were also determined. These present characteristic viscosities. Afterward, by means of the de Vogel-Fulcher-Tammann equation, the viscosity as a function of temperature was estimated. In the first part the developed equipment is described together with the image analysis carried out for the in-situ cylindrical samples (2,5 mm of height and diameter). The thermal cycle was up to 1200ºC with a heating rate of 5ºC/min. The developed equipment presents the following characteristics: some problems with the temperature evaluation, it was slightly affected by air currents and difficulties for achieving an adequate parallelism. On the other hand, the potentialities of the equipment for development and study of the thermal behavior of glasses was established.
Fil: Stábile, Franco Matías. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Piccico, M.. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Serra, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rafti, Matias. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
description In the present work we attempt to describe the results of the thermal behavior analysis of a commercial glaze obtained in a thermal microscope developed by the research group. At the same time, the density and the wetting angle of the glaze with an alumina surface was evaluated. Particularly the sintering temperature, the sphere, semi-sphere and fusion temperatures were also determined. These present characteristic viscosities. Afterward, by means of the de Vogel-Fulcher-Tammann equation, the viscosity as a function of temperature was estimated. In the first part the developed equipment is described together with the image analysis carried out for the in-situ cylindrical samples (2,5 mm of height and diameter). The thermal cycle was up to 1200ºC with a heating rate of 5ºC/min. The developed equipment presents the following characteristics: some problems with the temperature evaluation, it was slightly affected by air currents and difficulties for achieving an adequate parallelism. On the other hand, the potentialities of the equipment for development and study of the thermal behavior of glasses was established.
publishDate 2015
dc.date.none.fl_str_mv 2015-06
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/48977
Stábile, Franco Matías; Piccico, M.; Serra, Maria Florencia; Rafti, Matias; Suarez, Gustavo; et al.; Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy; Elsevier; Procedia Materials Science; 9; 6-2015; 563-570
2211-8128
CONICET Digital
CONICET
url http://hdl.handle.net/11336/48977
identifier_str_mv Stábile, Franco Matías; Piccico, M.; Serra, Maria Florencia; Rafti, Matias; Suarez, Gustavo; et al.; Viscosity and Thermal Evolution of Density and Wetting Angle of a Commercial Glaze by Means of Hot Stage Microscopy; Elsevier; Procedia Materials Science; 9; 6-2015; 563-570
2211-8128
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1016/j.mspro.2015.05.031
info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S2211812815002151
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier
publisher.none.fl_str_mv Elsevier
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1844614299943698432
score 13.070432

Publicaciones similares