Characterization and catalytic activity of zirconium dioxide prepared by sol-gel
- Autores
- Davies, Lilian Emilia; Bonini, Norberto Alejandro; Locatelli, Silvano; Gonzo, Elio Emilio
- Año de publicación
- 2005
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- Zirconia samples prepared from Zr(n-OC3H7)4 and ZrOCl2 were characterized by XRD,BET surface area, TG-DTA, TEM/SEM, FTIR, and D2O exchange. Oxides obtained from the alkoxide contain two types of hydroxyl groups at 3704 and 3597 cm-1, which do not exchange with D2O. Those obtained from ZrOCl2 produced three types of hydroxyl groups at 3774, 3733 and 3671 cm-1, which do exchange with D2O. Surface acidity was determined by FTIR of adsorbed lutidine. Only Lewis acid sites were found on samples from ZrOCl2 hydrolysis. FTIR spectra of calcined samples exhibited strong absorption bands in the 1800 to 1000 cm-1 region,which are ascribed to various types of carbonate and bicarbonate species. These ones are strongly adsorbed on the surface oxide and they are removed only after 3 hours at 600 ºC in stream of H2. Samples derive from the alkoxide precursor restore the original carbonate species after exposure to O2 at 600ºC. Catalytic activity for i-propanol dehydration/dehydrogenation showed the absence of basic centers and an intermediate dehydration activity between that of silica and alumina.
Fil: Davies, Lilian Emilia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina
Fil: Bonini, Norberto Alejandro. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina
Fil: Locatelli, Silvano. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina
Fil: Gonzo, Elio Emilio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina - Materia
-
Zirconium oxide
zirconia
acidity
FTIR, 2,6-lutidine - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/67162
Ver los metadatos del registro completo
id |
CONICETDig_e3c7dbf80e9a24f531ea419c1b354305 |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/67162 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Characterization and catalytic activity of zirconium dioxide prepared by sol-gelDavies, Lilian EmiliaBonini, Norberto AlejandroLocatelli, SilvanoGonzo, Elio EmilioZirconium oxidezirconiaacidityFTIR, 2,6-lutidinehttps://purl.org/becyt/ford/1.4https://purl.org/becyt/ford/1Zirconia samples prepared from Zr(n-OC3H7)4 and ZrOCl2 were characterized by XRD,BET surface area, TG-DTA, TEM/SEM, FTIR, and D2O exchange. Oxides obtained from the alkoxide contain two types of hydroxyl groups at 3704 and 3597 cm-1, which do not exchange with D2O. Those obtained from ZrOCl2 produced three types of hydroxyl groups at 3774, 3733 and 3671 cm-1, which do exchange with D2O. Surface acidity was determined by FTIR of adsorbed lutidine. Only Lewis acid sites were found on samples from ZrOCl2 hydrolysis. FTIR spectra of calcined samples exhibited strong absorption bands in the 1800 to 1000 cm-1 region,which are ascribed to various types of carbonate and bicarbonate species. These ones are strongly adsorbed on the surface oxide and they are removed only after 3 hours at 600 ºC in stream of H2. Samples derive from the alkoxide precursor restore the original carbonate species after exposure to O2 at 600ºC. Catalytic activity for i-propanol dehydration/dehydrogenation showed the absence of basic centers and an intermediate dehydration activity between that of silica and alumina.Fil: Davies, Lilian Emilia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; ArgentinaFil: Bonini, Norberto Alejandro. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; ArgentinaFil: Locatelli, Silvano. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; ArgentinaFil: Gonzo, Elio Emilio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; ArgentinaPlapiqui2005-03info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/67162Davies, Lilian Emilia; Bonini, Norberto Alejandro; Locatelli, Silvano; Gonzo, Elio Emilio; Characterization and catalytic activity of zirconium dioxide prepared by sol-gel; Plapiqui; Latin American Applied Research; 35; 1; 3-2005; 23-280327-07931851-8796CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://ref.scielo.org/sds8xkinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:14:09Zoai:ri.conicet.gov.ar:11336/67162instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:14:09.823CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Characterization and catalytic activity of zirconium dioxide prepared by sol-gel |
title |
Characterization and catalytic activity of zirconium dioxide prepared by sol-gel |
spellingShingle |
Characterization and catalytic activity of zirconium dioxide prepared by sol-gel Davies, Lilian Emilia Zirconium oxide zirconia acidity FTIR, 2,6-lutidine |
title_short |
Characterization and catalytic activity of zirconium dioxide prepared by sol-gel |
title_full |
Characterization and catalytic activity of zirconium dioxide prepared by sol-gel |
title_fullStr |
Characterization and catalytic activity of zirconium dioxide prepared by sol-gel |
title_full_unstemmed |
Characterization and catalytic activity of zirconium dioxide prepared by sol-gel |
title_sort |
Characterization and catalytic activity of zirconium dioxide prepared by sol-gel |
dc.creator.none.fl_str_mv |
Davies, Lilian Emilia Bonini, Norberto Alejandro Locatelli, Silvano Gonzo, Elio Emilio |
author |
Davies, Lilian Emilia |
author_facet |
Davies, Lilian Emilia Bonini, Norberto Alejandro Locatelli, Silvano Gonzo, Elio Emilio |
author_role |
author |
author2 |
Bonini, Norberto Alejandro Locatelli, Silvano Gonzo, Elio Emilio |
author2_role |
author author author |
dc.subject.none.fl_str_mv |
Zirconium oxide zirconia acidity FTIR, 2,6-lutidine |
topic |
Zirconium oxide zirconia acidity FTIR, 2,6-lutidine |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/1.4 https://purl.org/becyt/ford/1 |
dc.description.none.fl_txt_mv |
Zirconia samples prepared from Zr(n-OC3H7)4 and ZrOCl2 were characterized by XRD,BET surface area, TG-DTA, TEM/SEM, FTIR, and D2O exchange. Oxides obtained from the alkoxide contain two types of hydroxyl groups at 3704 and 3597 cm-1, which do not exchange with D2O. Those obtained from ZrOCl2 produced three types of hydroxyl groups at 3774, 3733 and 3671 cm-1, which do exchange with D2O. Surface acidity was determined by FTIR of adsorbed lutidine. Only Lewis acid sites were found on samples from ZrOCl2 hydrolysis. FTIR spectra of calcined samples exhibited strong absorption bands in the 1800 to 1000 cm-1 region,which are ascribed to various types of carbonate and bicarbonate species. These ones are strongly adsorbed on the surface oxide and they are removed only after 3 hours at 600 ºC in stream of H2. Samples derive from the alkoxide precursor restore the original carbonate species after exposure to O2 at 600ºC. Catalytic activity for i-propanol dehydration/dehydrogenation showed the absence of basic centers and an intermediate dehydration activity between that of silica and alumina. Fil: Davies, Lilian Emilia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina Fil: Bonini, Norberto Alejandro. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina Fil: Locatelli, Silvano. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina Fil: Gonzo, Elio Emilio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Salta. Instituto de Investigaciones para la Industria Química. Universidad Nacional de Salta. Facultad de Ingeniería. Instituto de Investigaciones para la Industria Química; Argentina |
description |
Zirconia samples prepared from Zr(n-OC3H7)4 and ZrOCl2 were characterized by XRD,BET surface area, TG-DTA, TEM/SEM, FTIR, and D2O exchange. Oxides obtained from the alkoxide contain two types of hydroxyl groups at 3704 and 3597 cm-1, which do not exchange with D2O. Those obtained from ZrOCl2 produced three types of hydroxyl groups at 3774, 3733 and 3671 cm-1, which do exchange with D2O. Surface acidity was determined by FTIR of adsorbed lutidine. Only Lewis acid sites were found on samples from ZrOCl2 hydrolysis. FTIR spectra of calcined samples exhibited strong absorption bands in the 1800 to 1000 cm-1 region,which are ascribed to various types of carbonate and bicarbonate species. These ones are strongly adsorbed on the surface oxide and they are removed only after 3 hours at 600 ºC in stream of H2. Samples derive from the alkoxide precursor restore the original carbonate species after exposure to O2 at 600ºC. Catalytic activity for i-propanol dehydration/dehydrogenation showed the absence of basic centers and an intermediate dehydration activity between that of silica and alumina. |
publishDate |
2005 |
dc.date.none.fl_str_mv |
2005-03 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/67162 Davies, Lilian Emilia; Bonini, Norberto Alejandro; Locatelli, Silvano; Gonzo, Elio Emilio; Characterization and catalytic activity of zirconium dioxide prepared by sol-gel; Plapiqui; Latin American Applied Research; 35; 1; 3-2005; 23-28 0327-0793 1851-8796 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/67162 |
identifier_str_mv |
Davies, Lilian Emilia; Bonini, Norberto Alejandro; Locatelli, Silvano; Gonzo, Elio Emilio; Characterization and catalytic activity of zirconium dioxide prepared by sol-gel; Plapiqui; Latin American Applied Research; 35; 1; 3-2005; 23-28 0327-0793 1851-8796 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/url/http://ref.scielo.org/sds8xk |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Plapiqui |
publisher.none.fl_str_mv |
Plapiqui |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844614065451696128 |
score |
13.070432 |