Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds
- Autores
- Missana, Liliana Raquel; Moreno Garcia, Maria Florencia; García, L. A.; Aimone, M.; Santiago, O.; Melián Salerno, Emanuel José; Camal Ruggieri, I. N.; Ramallo, M.; Rivero, Guadalupe; Abraham, Gustavo Abel; Feldman, Sara
- Año de publicación
- 2020
- Idioma
- inglés
- Tipo de recurso
- documento de conferencia
- Estado
- versión publicada
- Descripción
- Tissue engineering aims regenerating de novo lost tissue. Our objective was to analyze the biocompatibility of the implant of PCL-nHAp, an electro-spun scaffold prepared by mixtures of a biocompatible and bioabsorbable polyester, poly(caprolactone), and a bioactive ceramic of nanofibrous structure (nanohydroxyapatite particles), in an in vivo model (New Zealand female rabbits). Scaffolds were 5 mm diameter PCL-nHAp discs, superficially modified to increase hydrophilicity by alkaline treatment and sterilized (peracetic acid). Treatments were (I) control, no bone lesion, (II) metaphyseal femoral bone lesion 3 mm deep and 5 mm diameter and PCL-nHAp implant; (III) lesion but no implant (n=6). Rabbit?s clinical evolution was adequate, without affecting gait. No differences in biochemical values (hemograms and transaminases) were detected after 1; 5 and 90 days. Histological studies (90days, 4n) showed that PCL-nHAp scaffold with a corrugated appearance, surrounded, from the outside inwards: A-Hematopoietic bone marrow with megakaryocytes and / or fat with congestive areas; B- few incipiently formed trabeculae, of varied forms;and C- presence of multinucleated giant cells, macrophages, lymphocytes combined with areas of hemorrhage and congestion. An adequate biocompatibility of the scaffolds can be observed, which in its imminent degradation process has not affected the biochemical parameters studied. A non-toxic and biologically active histological response is observed, with moderate levels of inflammation. We believe that longer post-implant periods will allow definitive conclusions.
Fil: Missana, Liliana Raquel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Planta Piloto de Procesos Industriales Microbiológicos; Argentina
Fil: Moreno Garcia, Maria Florencia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Planta Piloto de Procesos Industriales Microbiológicos; Argentina
Fil: García, L. A.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina
Fil: Aimone, M.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina
Fil: Santiago, O.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina
Fil: Melián Salerno, Emanuel José. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina
Fil: Camal Ruggieri, I. N.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina
Fil: Ramallo, M.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina
Fil: Rivero, Guadalupe. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Abraham, Gustavo Abel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Feldman, Sara. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
XXXVI Reunión Anual AAOMM
Ciudad Autónoma de Buenos Aires
Argentina
Asociación Argentina de Osteología y Metabolismo Mineral - Materia
-
biocompatibilidad
nanotecnologia
capronolactona
ingeniería de tejidos - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/131156
Ver los metadatos del registro completo
id |
CONICETDig_dafbfc51816455c4b5fea06a12de5b0b |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/131156 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffoldsBiocompatibilidad posimplante de matrices fibrosas nanocompuestas electrohiladas de policapronolactonaMissana, Liliana RaquelMoreno Garcia, Maria FlorenciaGarcía, L. A.Aimone, M.Santiago, O.Melián Salerno, Emanuel JoséCamal Ruggieri, I. N.Ramallo, M.Rivero, GuadalupeAbraham, Gustavo AbelFeldman, Sarabiocompatibilidadnanotecnologiacapronolactonaingeniería de tejidoshttps://purl.org/becyt/ford/3.3https://purl.org/becyt/ford/3Tissue engineering aims regenerating de novo lost tissue. Our objective was to analyze the biocompatibility of the implant of PCL-nHAp, an electro-spun scaffold prepared by mixtures of a biocompatible and bioabsorbable polyester, poly(caprolactone), and a bioactive ceramic of nanofibrous structure (nanohydroxyapatite particles), in an in vivo model (New Zealand female rabbits). Scaffolds were 5 mm diameter PCL-nHAp discs, superficially modified to increase hydrophilicity by alkaline treatment and sterilized (peracetic acid). Treatments were (I) control, no bone lesion, (II) metaphyseal femoral bone lesion 3 mm deep and 5 mm diameter and PCL-nHAp implant; (III) lesion but no implant (n=6). Rabbit?s clinical evolution was adequate, without affecting gait. No differences in biochemical values (hemograms and transaminases) were detected after 1; 5 and 90 days. Histological studies (90days, 4n) showed that PCL-nHAp scaffold with a corrugated appearance, surrounded, from the outside inwards: A-Hematopoietic bone marrow with megakaryocytes and / or fat with congestive areas; B- few incipiently formed trabeculae, of varied forms;and C- presence of multinucleated giant cells, macrophages, lymphocytes combined with areas of hemorrhage and congestion. An adequate biocompatibility of the scaffolds can be observed, which in its imminent degradation process has not affected the biochemical parameters studied. A non-toxic and biologically active histological response is observed, with moderate levels of inflammation. We believe that longer post-implant periods will allow definitive conclusions.Fil: Missana, Liliana Raquel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Planta Piloto de Procesos Industriales Microbiológicos; ArgentinaFil: Moreno Garcia, Maria Florencia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Planta Piloto de Procesos Industriales Microbiológicos; ArgentinaFil: García, L. A.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; ArgentinaFil: Aimone, M.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; ArgentinaFil: Santiago, O.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; ArgentinaFil: Melián Salerno, Emanuel José. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; ArgentinaFil: Camal Ruggieri, I. N.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; ArgentinaFil: Ramallo, M.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; ArgentinaFil: Rivero, Guadalupe. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Abraham, Gustavo Abel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Feldman, Sara. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaXXXVI Reunión Anual AAOMMCiudad Autónoma de Buenos AiresArgentinaAsociación Argentina de Osteología y Metabolismo MineralWiley2020info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/conferenceObjectCongresoJournalhttp://purl.org/coar/resource_type/c_5794info:ar-repo/semantics/documentoDeConferenciaapplication/pdfapplication/vnd.openxmlformats-officedocument.wordprocessingml.documentapplication/pdfhttp://hdl.handle.net/11336/131156Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds; XXXVI Reunión Anual AAOMM; Ciudad Autónoma de Buenos Aires; Argentina; 2019; 14-152473-4039CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://asbmr.onlinelibrary.wiley.com/toc/24734039/2020/4/S1info:eu-repo/semantics/altIdentifier/url/http://aaomm.org.ar/congreso-2019/Nacionalinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:03:03Zoai:ri.conicet.gov.ar:11336/131156instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:03:03.809CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds Biocompatibilidad posimplante de matrices fibrosas nanocompuestas electrohiladas de policapronolactona |
title |
Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds |
spellingShingle |
Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds Missana, Liliana Raquel biocompatibilidad nanotecnologia capronolactona ingeniería de tejidos |
title_short |
Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds |
title_full |
Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds |
title_fullStr |
Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds |
title_full_unstemmed |
Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds |
title_sort |
Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds |
dc.creator.none.fl_str_mv |
Missana, Liliana Raquel Moreno Garcia, Maria Florencia García, L. A. Aimone, M. Santiago, O. Melián Salerno, Emanuel José Camal Ruggieri, I. N. Ramallo, M. Rivero, Guadalupe Abraham, Gustavo Abel Feldman, Sara |
author |
Missana, Liliana Raquel |
author_facet |
Missana, Liliana Raquel Moreno Garcia, Maria Florencia García, L. A. Aimone, M. Santiago, O. Melián Salerno, Emanuel José Camal Ruggieri, I. N. Ramallo, M. Rivero, Guadalupe Abraham, Gustavo Abel Feldman, Sara |
author_role |
author |
author2 |
Moreno Garcia, Maria Florencia García, L. A. Aimone, M. Santiago, O. Melián Salerno, Emanuel José Camal Ruggieri, I. N. Ramallo, M. Rivero, Guadalupe Abraham, Gustavo Abel Feldman, Sara |
author2_role |
author author author author author author author author author author |
dc.subject.none.fl_str_mv |
biocompatibilidad nanotecnologia capronolactona ingeniería de tejidos |
topic |
biocompatibilidad nanotecnologia capronolactona ingeniería de tejidos |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/3.3 https://purl.org/becyt/ford/3 |
dc.description.none.fl_txt_mv |
Tissue engineering aims regenerating de novo lost tissue. Our objective was to analyze the biocompatibility of the implant of PCL-nHAp, an electro-spun scaffold prepared by mixtures of a biocompatible and bioabsorbable polyester, poly(caprolactone), and a bioactive ceramic of nanofibrous structure (nanohydroxyapatite particles), in an in vivo model (New Zealand female rabbits). Scaffolds were 5 mm diameter PCL-nHAp discs, superficially modified to increase hydrophilicity by alkaline treatment and sterilized (peracetic acid). Treatments were (I) control, no bone lesion, (II) metaphyseal femoral bone lesion 3 mm deep and 5 mm diameter and PCL-nHAp implant; (III) lesion but no implant (n=6). Rabbit?s clinical evolution was adequate, without affecting gait. No differences in biochemical values (hemograms and transaminases) were detected after 1; 5 and 90 days. Histological studies (90days, 4n) showed that PCL-nHAp scaffold with a corrugated appearance, surrounded, from the outside inwards: A-Hematopoietic bone marrow with megakaryocytes and / or fat with congestive areas; B- few incipiently formed trabeculae, of varied forms;and C- presence of multinucleated giant cells, macrophages, lymphocytes combined with areas of hemorrhage and congestion. An adequate biocompatibility of the scaffolds can be observed, which in its imminent degradation process has not affected the biochemical parameters studied. A non-toxic and biologically active histological response is observed, with moderate levels of inflammation. We believe that longer post-implant periods will allow definitive conclusions. Fil: Missana, Liliana Raquel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Planta Piloto de Procesos Industriales Microbiológicos; Argentina Fil: Moreno Garcia, Maria Florencia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Planta Piloto de Procesos Industriales Microbiológicos; Argentina Fil: García, L. A.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina Fil: Aimone, M.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina Fil: Santiago, O.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina Fil: Melián Salerno, Emanuel José. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina Fil: Camal Ruggieri, I. N.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina Fil: Ramallo, M.. Universidad Nacional de Rosario. Facultad de Ciencias Médicas. Laboratorio de Biología Osteoarticular, Ingeniería Tisular y Terapias Emergentes; Argentina Fil: Rivero, Guadalupe. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina Fil: Abraham, Gustavo Abel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina Fil: Feldman, Sara. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina XXXVI Reunión Anual AAOMM Ciudad Autónoma de Buenos Aires Argentina Asociación Argentina de Osteología y Metabolismo Mineral |
description |
Tissue engineering aims regenerating de novo lost tissue. Our objective was to analyze the biocompatibility of the implant of PCL-nHAp, an electro-spun scaffold prepared by mixtures of a biocompatible and bioabsorbable polyester, poly(caprolactone), and a bioactive ceramic of nanofibrous structure (nanohydroxyapatite particles), in an in vivo model (New Zealand female rabbits). Scaffolds were 5 mm diameter PCL-nHAp discs, superficially modified to increase hydrophilicity by alkaline treatment and sterilized (peracetic acid). Treatments were (I) control, no bone lesion, (II) metaphyseal femoral bone lesion 3 mm deep and 5 mm diameter and PCL-nHAp implant; (III) lesion but no implant (n=6). Rabbit?s clinical evolution was adequate, without affecting gait. No differences in biochemical values (hemograms and transaminases) were detected after 1; 5 and 90 days. Histological studies (90days, 4n) showed that PCL-nHAp scaffold with a corrugated appearance, surrounded, from the outside inwards: A-Hematopoietic bone marrow with megakaryocytes and / or fat with congestive areas; B- few incipiently formed trabeculae, of varied forms;and C- presence of multinucleated giant cells, macrophages, lymphocytes combined with areas of hemorrhage and congestion. An adequate biocompatibility of the scaffolds can be observed, which in its imminent degradation process has not affected the biochemical parameters studied. A non-toxic and biologically active histological response is observed, with moderate levels of inflammation. We believe that longer post-implant periods will allow definitive conclusions. |
publishDate |
2020 |
dc.date.none.fl_str_mv |
2020 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/publishedVersion info:eu-repo/semantics/conferenceObject Congreso Journal http://purl.org/coar/resource_type/c_5794 info:ar-repo/semantics/documentoDeConferencia |
status_str |
publishedVersion |
format |
conferenceObject |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/131156 Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds; XXXVI Reunión Anual AAOMM; Ciudad Autónoma de Buenos Aires; Argentina; 2019; 14-15 2473-4039 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/131156 |
identifier_str_mv |
Post-implant biocompatibility of electro-spunded polycapronolactone nanocomposite fibrous scaffolds; XXXVI Reunión Anual AAOMM; Ciudad Autónoma de Buenos Aires; Argentina; 2019; 14-15 2473-4039 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/url/https://asbmr.onlinelibrary.wiley.com/toc/24734039/2020/4/S1 info:eu-repo/semantics/altIdentifier/url/http://aaomm.org.ar/congreso-2019/ |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/vnd.openxmlformats-officedocument.wordprocessingml.document application/pdf |
dc.coverage.none.fl_str_mv |
Nacional |
dc.publisher.none.fl_str_mv |
Wiley |
publisher.none.fl_str_mv |
Wiley |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844613841644683264 |
score |
13.070432 |