Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking

Autores
Fernández, Pablo Andrés; Comin, Romina; Cáceres, Maria Victoria; Salvatierra, Nancy Alicia; Cid, Mariana Paula
Año de publicación
2023
Idioma
inglés
Tipo de recurso
documento de conferencia
Estado
versión publicada
Descripción
Biodegradable scaffolds with three-dimensional porous structure are fundamental components for tissue engineering. Collagen is the main protein of the human extracellular matrix, its structure allows the union, migration and in several cases the differentiation of the cells. However, its use has been limited due to low processability by the means of layer-by-layer technologies. In the present, a simple and economical method is developed for collagen purification from porcine skin using treatments with acidic and salt solutions. This preserves the structure of the fibers unlike normally used enzymatic procedures which denature the protein. A collagen ink was prepared with collagen and hyaluronic acid, which can be homogenously extruded through the bioprinter needle, presenting appropriated viscosity and stability for printing 3D scaffolds. Finally, these structures were lyophilized and crosslinked chemically to improve their physical-chemical properties.
Los andamios biodegradables con estructura tridimensional porosa son la base para la regeneración tisular. El colágeno es el principal constituyente proteico de la matriz extracelular humana y posee una estructura que favorece la unión, migración y en ciertos casos la diferenciación de las células, pero su uso ha sido limitado debido a su difícil procesabilidad mediante tecnologías de construcción capa por capa. Por ello, en el presente trabajo se desarrolla un método sencillo y relativamente económico para la purificación de colágeno tipo I de piel porcina a partir de tratamientos con soluciones ácidas y sales, que preservan la estructura de las fibras a diferencia de procedimientos enzimáticos normalmente usados, que desnaturalizan la proteína. Con el colágeno extraído y ácido hialurónico comercial se preparó una tinta que permitió una extrusión homogénea por la impresora y presentó viscosidad y estabilidad suficientes para la impresión de andamios tridimensionales. Finalmente, las estructuras fueron liofilizadas y entrecruzadas químicamente para mejorar sus propiedades físico-químicas.
Fil: Fernández, Pablo Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; Argentina
Fil: Comin, Romina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; Argentina
Fil: Cáceres, Maria Victoria. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales; Argentina
Fil: Salvatierra, Nancy Alicia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; Argentina
Fil: Cid, Mariana Paula. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; Argentina
XXIII Congreso Argentino de Bioingeniería y XII Jornadas de Ingeniería Clínica
San Juan
Argentina
Sociedad Argentina de Bioingenieria
Universidad Nacional de San Juan
Materia
Collagen
Hyaluronic acid
3D printing
Crosslinking
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/231806
Acceder
id CONICETDig_d521e994cdf9813a9c3467eb68b1944a
oai_identifier_str oai:ri.conicet.gov.ar:11336/231806
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinkingFernández, Pablo AndrésComin, RominaCáceres, Maria VictoriaSalvatierra, Nancy AliciaCid, Mariana PaulaCollagenHyaluronic acid3D printingCrosslinkinghttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Biodegradable scaffolds with three-dimensional porous structure are fundamental components for tissue engineering. Collagen is the main protein of the human extracellular matrix, its structure allows the union, migration and in several cases the differentiation of the cells. However, its use has been limited due to low processability by the means of layer-by-layer technologies. In the present, a simple and economical method is developed for collagen purification from porcine skin using treatments with acidic and salt solutions. This preserves the structure of the fibers unlike normally used enzymatic procedures which denature the protein. A collagen ink was prepared with collagen and hyaluronic acid, which can be homogenously extruded through the bioprinter needle, presenting appropriated viscosity and stability for printing 3D scaffolds. Finally, these structures were lyophilized and crosslinked chemically to improve their physical-chemical properties.Los andamios biodegradables con estructura tridimensional porosa son la base para la regeneración tisular. El colágeno es el principal constituyente proteico de la matriz extracelular humana y posee una estructura que favorece la unión, migración y en ciertos casos la diferenciación de las células, pero su uso ha sido limitado debido a su difícil procesabilidad mediante tecnologías de construcción capa por capa. Por ello, en el presente trabajo se desarrolla un método sencillo y relativamente económico para la purificación de colágeno tipo I de piel porcina a partir de tratamientos con soluciones ácidas y sales, que preservan la estructura de las fibras a diferencia de procedimientos enzimáticos normalmente usados, que desnaturalizan la proteína. Con el colágeno extraído y ácido hialurónico comercial se preparó una tinta que permitió una extrusión homogénea por la impresora y presentó viscosidad y estabilidad suficientes para la impresión de andamios tridimensionales. Finalmente, las estructuras fueron liofilizadas y entrecruzadas químicamente para mejorar sus propiedades físico-químicas.Fil: Fernández, Pablo Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; ArgentinaFil: Comin, Romina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; ArgentinaFil: Cáceres, Maria Victoria. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales; ArgentinaFil: Salvatierra, Nancy Alicia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; ArgentinaFil: Cid, Mariana Paula. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; ArgentinaXXIII Congreso Argentino de Bioingeniería y XII Jornadas de Ingeniería ClínicaSan JuanArgentinaSociedad Argentina de BioingenieriaUniversidad Nacional de San JuanSociedad Argentina de BioingenieriaCañadas, Kyomi ShiratoriMorales, ValentinaLópez Celani, Natalia Martina2023info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/conferenceObjectCongresoBookhttp://purl.org/coar/resource_type/c_5794info:ar-repo/semantics/documentoDeConferenciaapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/231806Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking ; XXIII Congreso Argentino de Bioingeniería y XII Jornadas de Ingeniería Clínica; San Juan; Argentina; 2022; 12-12978-987-27301-1-6CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://sabi2022.unsj.edu.ar/libro-de-resumenes/Internacionalinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T09:43:51Zoai:ri.conicet.gov.ar:11336/231806instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 09:43:51.687CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking
title Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking
spellingShingle Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking
Fernández, Pablo Andrés
Collagen
Hyaluronic acid
3D printing
Crosslinking
title_short Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking
title_full Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking
title_fullStr Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking
title_full_unstemmed Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking
title_sort Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking
dc.creator.none.fl_str_mv Fernández, Pablo Andrés
Comin, Romina
Cáceres, Maria Victoria
Salvatierra, Nancy Alicia
Cid, Mariana Paula
author Fernández, Pablo Andrés
author_facet Fernández, Pablo Andrés
Comin, Romina
Cáceres, Maria Victoria
Salvatierra, Nancy Alicia
Cid, Mariana Paula
author_role author
author2 Comin, Romina
Cáceres, Maria Victoria
Salvatierra, Nancy Alicia
Cid, Mariana Paula
author2_role author
author
author
author
dc.contributor.none.fl_str_mv Cañadas, Kyomi Shiratori
Morales, Valentina
López Celani, Natalia Martina
dc.subject.none.fl_str_mv Collagen
Hyaluronic acid
3D printing
Crosslinking
topic Collagen
Hyaluronic acid
3D printing
Crosslinking
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv Biodegradable scaffolds with three-dimensional porous structure are fundamental components for tissue engineering. Collagen is the main protein of the human extracellular matrix, its structure allows the union, migration and in several cases the differentiation of the cells. However, its use has been limited due to low processability by the means of layer-by-layer technologies. In the present, a simple and economical method is developed for collagen purification from porcine skin using treatments with acidic and salt solutions. This preserves the structure of the fibers unlike normally used enzymatic procedures which denature the protein. A collagen ink was prepared with collagen and hyaluronic acid, which can be homogenously extruded through the bioprinter needle, presenting appropriated viscosity and stability for printing 3D scaffolds. Finally, these structures were lyophilized and crosslinked chemically to improve their physical-chemical properties.
Los andamios biodegradables con estructura tridimensional porosa son la base para la regeneración tisular. El colágeno es el principal constituyente proteico de la matriz extracelular humana y posee una estructura que favorece la unión, migración y en ciertos casos la diferenciación de las células, pero su uso ha sido limitado debido a su difícil procesabilidad mediante tecnologías de construcción capa por capa. Por ello, en el presente trabajo se desarrolla un método sencillo y relativamente económico para la purificación de colágeno tipo I de piel porcina a partir de tratamientos con soluciones ácidas y sales, que preservan la estructura de las fibras a diferencia de procedimientos enzimáticos normalmente usados, que desnaturalizan la proteína. Con el colágeno extraído y ácido hialurónico comercial se preparó una tinta que permitió una extrusión homogénea por la impresora y presentó viscosidad y estabilidad suficientes para la impresión de andamios tridimensionales. Finalmente, las estructuras fueron liofilizadas y entrecruzadas químicamente para mejorar sus propiedades físico-químicas.
Fil: Fernández, Pablo Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; Argentina
Fil: Comin, Romina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; Argentina
Fil: Cáceres, Maria Victoria. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales; Argentina
Fil: Salvatierra, Nancy Alicia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; Argentina
Fil: Cid, Mariana Paula. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Investigaciones Biológicas y Tecnológicas. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas, Físicas y Naturales. Instituto de Investigaciones Biológicas y Tecnológicas; Argentina
XXIII Congreso Argentino de Bioingeniería y XII Jornadas de Ingeniería Clínica
San Juan
Argentina
Sociedad Argentina de Bioingenieria
Universidad Nacional de San Juan
description Biodegradable scaffolds with three-dimensional porous structure are fundamental components for tissue engineering. Collagen is the main protein of the human extracellular matrix, its structure allows the union, migration and in several cases the differentiation of the cells. However, its use has been limited due to low processability by the means of layer-by-layer technologies. In the present, a simple and economical method is developed for collagen purification from porcine skin using treatments with acidic and salt solutions. This preserves the structure of the fibers unlike normally used enzymatic procedures which denature the protein. A collagen ink was prepared with collagen and hyaluronic acid, which can be homogenously extruded through the bioprinter needle, presenting appropriated viscosity and stability for printing 3D scaffolds. Finally, these structures were lyophilized and crosslinked chemically to improve their physical-chemical properties.
publishDate 2023
dc.date.none.fl_str_mv 2023
dc.type.none.fl_str_mv info:eu-repo/semantics/publishedVersion
info:eu-repo/semantics/conferenceObject
Congreso
Book
http://purl.org/coar/resource_type/c_5794
info:ar-repo/semantics/documentoDeConferencia
status_str publishedVersion
format conferenceObject
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/231806
Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking ; XXIII Congreso Argentino de Bioingeniería y XII Jornadas de Ingeniería Clínica; San Juan; Argentina; 2022; 12-12
978-987-27301-1-6
CONICET Digital
CONICET
url http://hdl.handle.net/11336/231806
identifier_str_mv Collagen extraction and purification for scaffold 3D printing using hyaluronic acid and chemical crosslinking ; XXIII Congreso Argentino de Bioingeniería y XII Jornadas de Ingeniería Clínica; San Juan; Argentina; 2022; 12-12
978-987-27301-1-6
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://sabi2022.unsj.edu.ar/libro-de-resumenes/
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.coverage.none.fl_str_mv Internacional
dc.publisher.none.fl_str_mv Sociedad Argentina de Bioingenieria
publisher.none.fl_str_mv Sociedad Argentina de Bioingenieria
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1844613379938844672
score 13.070432

Publicaciones similares