Protection of galvanized steel with silanes: its comparison with Chromium(VI)
- Autores
- Seré, Panlo Ricardo; Deya, Marta Cecilia; Egli, Walter Alfredo; Elsner, Cecilia Ines; Di Sarli, Alejandro Ramón
- Año de publicación
- 2014
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- The corrosion behavior of hot dip galvanized steel (HDGS) pre-treated with mercaptopropyltrimethoxysilane and a commercial sulfur-bearing silane was studied. Electrochemical polarization, electrochemical impedance spectroscopy, and electrochemical noise tests showed that silane coatings have a corrosion protection performance similar to the usual hexavalent chromium HDGS passivation treatments. It is also evident that the silane films protect the zinc surface through the formation of an isolating barrier. Through voltamperometric studies it was possible to define an electrochemical porosity of the protective coatings. Based on copper sulfate tests and electrochemical porosity results the films protection capability was evaluated, showing that silane treatments have similar or even better protection performance than standard chromium passivation.
Fil: Seré, Panlo Ricardo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina
Fil: Deya, Marta Cecilia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina
Fil: Egli, Walter Alfredo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina
Fil: Elsner, Cecilia Ines. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina
Fil: Di Sarli, Alejandro Ramón. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina - Materia
-
Silanes
Corrosion
Galvanized Steel
Chromium (Vi)
Zinc - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/11221
Ver los metadatos del registro completo
id |
CONICETDig_99b4e0ad0cf7fa8c0d232bd3036c5f1a |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/11221 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Protection of galvanized steel with silanes: its comparison with Chromium(VI)Seré, Panlo RicardoDeya, Marta CeciliaEgli, Walter AlfredoElsner, Cecilia InesDi Sarli, Alejandro RamónSilanesCorrosionGalvanized SteelChromium (Vi)Zinchttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2The corrosion behavior of hot dip galvanized steel (HDGS) pre-treated with mercaptopropyltrimethoxysilane and a commercial sulfur-bearing silane was studied. Electrochemical polarization, electrochemical impedance spectroscopy, and electrochemical noise tests showed that silane coatings have a corrosion protection performance similar to the usual hexavalent chromium HDGS passivation treatments. It is also evident that the silane films protect the zinc surface through the formation of an isolating barrier. Through voltamperometric studies it was possible to define an electrochemical porosity of the protective coatings. Based on copper sulfate tests and electrochemical porosity results the films protection capability was evaluated, showing that silane treatments have similar or even better protection performance than standard chromium passivation.Fil: Seré, Panlo Ricardo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; ArgentinaFil: Deya, Marta Cecilia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; ArgentinaFil: Egli, Walter Alfredo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; ArgentinaFil: Elsner, Cecilia Ines. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; ArgentinaFil: Di Sarli, Alejandro Ramón. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; ArgentinaSpringer2014-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/11221Seré, Panlo Ricardo; Deya, Marta Cecilia; Egli, Walter Alfredo; Elsner, Cecilia Ines; Di Sarli, Alejandro Ramón; Protection of galvanized steel with silanes: its comparison with Chromium(VI); Springer; Journal Of Materials Engineering And Performance; 23; 1; 1-2014; 342-3481059-94951544-1024enginfo:eu-repo/semantics/altIdentifier/doi/10.1007/s11665-013-0746-1info:eu-repo/semantics/altIdentifier/url/http://link.springer.com/article/10.1007/s11665-013-0746-1info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:07:01Zoai:ri.conicet.gov.ar:11336/11221instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:07:01.507CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Protection of galvanized steel with silanes: its comparison with Chromium(VI) |
title |
Protection of galvanized steel with silanes: its comparison with Chromium(VI) |
spellingShingle |
Protection of galvanized steel with silanes: its comparison with Chromium(VI) Seré, Panlo Ricardo Silanes Corrosion Galvanized Steel Chromium (Vi) Zinc |
title_short |
Protection of galvanized steel with silanes: its comparison with Chromium(VI) |
title_full |
Protection of galvanized steel with silanes: its comparison with Chromium(VI) |
title_fullStr |
Protection of galvanized steel with silanes: its comparison with Chromium(VI) |
title_full_unstemmed |
Protection of galvanized steel with silanes: its comparison with Chromium(VI) |
title_sort |
Protection of galvanized steel with silanes: its comparison with Chromium(VI) |
dc.creator.none.fl_str_mv |
Seré, Panlo Ricardo Deya, Marta Cecilia Egli, Walter Alfredo Elsner, Cecilia Ines Di Sarli, Alejandro Ramón |
author |
Seré, Panlo Ricardo |
author_facet |
Seré, Panlo Ricardo Deya, Marta Cecilia Egli, Walter Alfredo Elsner, Cecilia Ines Di Sarli, Alejandro Ramón |
author_role |
author |
author2 |
Deya, Marta Cecilia Egli, Walter Alfredo Elsner, Cecilia Ines Di Sarli, Alejandro Ramón |
author2_role |
author author author author |
dc.subject.none.fl_str_mv |
Silanes Corrosion Galvanized Steel Chromium (Vi) Zinc |
topic |
Silanes Corrosion Galvanized Steel Chromium (Vi) Zinc |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
The corrosion behavior of hot dip galvanized steel (HDGS) pre-treated with mercaptopropyltrimethoxysilane and a commercial sulfur-bearing silane was studied. Electrochemical polarization, electrochemical impedance spectroscopy, and electrochemical noise tests showed that silane coatings have a corrosion protection performance similar to the usual hexavalent chromium HDGS passivation treatments. It is also evident that the silane films protect the zinc surface through the formation of an isolating barrier. Through voltamperometric studies it was possible to define an electrochemical porosity of the protective coatings. Based on copper sulfate tests and electrochemical porosity results the films protection capability was evaluated, showing that silane treatments have similar or even better protection performance than standard chromium passivation. Fil: Seré, Panlo Ricardo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina Fil: Deya, Marta Cecilia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina Fil: Egli, Walter Alfredo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina Fil: Elsner, Cecilia Ines. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina Fil: Di Sarli, Alejandro Ramón. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico la Plata. Centro de Investigación y Desarrollo En Tecnología de Pinturas (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina |
description |
The corrosion behavior of hot dip galvanized steel (HDGS) pre-treated with mercaptopropyltrimethoxysilane and a commercial sulfur-bearing silane was studied. Electrochemical polarization, electrochemical impedance spectroscopy, and electrochemical noise tests showed that silane coatings have a corrosion protection performance similar to the usual hexavalent chromium HDGS passivation treatments. It is also evident that the silane films protect the zinc surface through the formation of an isolating barrier. Through voltamperometric studies it was possible to define an electrochemical porosity of the protective coatings. Based on copper sulfate tests and electrochemical porosity results the films protection capability was evaluated, showing that silane treatments have similar or even better protection performance than standard chromium passivation. |
publishDate |
2014 |
dc.date.none.fl_str_mv |
2014-01 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/11221 Seré, Panlo Ricardo; Deya, Marta Cecilia; Egli, Walter Alfredo; Elsner, Cecilia Ines; Di Sarli, Alejandro Ramón; Protection of galvanized steel with silanes: its comparison with Chromium(VI); Springer; Journal Of Materials Engineering And Performance; 23; 1; 1-2014; 342-348 1059-9495 1544-1024 |
url |
http://hdl.handle.net/11336/11221 |
identifier_str_mv |
Seré, Panlo Ricardo; Deya, Marta Cecilia; Egli, Walter Alfredo; Elsner, Cecilia Ines; Di Sarli, Alejandro Ramón; Protection of galvanized steel with silanes: its comparison with Chromium(VI); Springer; Journal Of Materials Engineering And Performance; 23; 1; 1-2014; 342-348 1059-9495 1544-1024 |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/doi/10.1007/s11665-013-0746-1 info:eu-repo/semantics/altIdentifier/url/http://link.springer.com/article/10.1007/s11665-013-0746-1 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf application/pdf application/pdf application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Springer |
publisher.none.fl_str_mv |
Springer |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844613925596823552 |
score |
13.070432 |