Degradation of polycaprolactone/starch blends and composites with sisal fibre

Autores
Di Franco, C.R.; Cyras, Viviana Paola; Busalmen, Juan Pablo; Ruseckaite, Roxana Alejandra; Vázquez, A.
Año de publicación
2004
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
The susceptibility of polycaprolactone/starch (PCL/S) and sisal fibre-reinforced polycaprolactone/starch blends (SF-PCL/S) to different degrading environments was evaluated. The composites and the unfilled matrix showed hydrolytic stability at pH 7.2 at two different temperatures (25 °C and 40 °C). Fibres were stable under hydrolytic conditions and seemed to favour the entrance of water and then, the swelling and the hydrolysis of the starch (the most bio-available component). At higher fibre content, the composites become more hydrolytically stable probably due to the presence of a fibre–fibre physical network. Microbial attack in biotic aqueous medium was evidenced by the presence of a biofilm, especially on the fibre surface. In soil burial, PCL/S and 15%SF–PCL/S were degraded to about 50% of the initial mass. The weight loss pattern showed by the composite was associated with the presence of strong fibre–fibre and fibre–matrix interactions, which are absent in the neat matrix.
Fil: Di Franco, C.R.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Cyras, Viviana Paola. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Busalmen, Juan Pablo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Ruseckaite, Roxana Alejandra. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Vázquez, A.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Materia
DEGRADATION
HYDROLYSIS
POLYCAPROLACTONE
SISAL FIBRE
SOIL BURIAL
STARCH
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/94395
Acceder
id CONICETDig_8e57c61ccfad73d57c1cc989bfd4f76d
oai_identifier_str oai:ri.conicet.gov.ar:11336/94395
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Degradation of polycaprolactone/starch blends and composites with sisal fibreDi Franco, C.R.Cyras, Viviana PaolaBusalmen, Juan PabloRuseckaite, Roxana AlejandraVázquez, A.DEGRADATIONHYDROLYSISPOLYCAPROLACTONESISAL FIBRESOIL BURIALSTARCHhttps://purl.org/becyt/ford/2.4https://purl.org/becyt/ford/2The susceptibility of polycaprolactone/starch (PCL/S) and sisal fibre-reinforced polycaprolactone/starch blends (SF-PCL/S) to different degrading environments was evaluated. The composites and the unfilled matrix showed hydrolytic stability at pH 7.2 at two different temperatures (25 °C and 40 °C). Fibres were stable under hydrolytic conditions and seemed to favour the entrance of water and then, the swelling and the hydrolysis of the starch (the most bio-available component). At higher fibre content, the composites become more hydrolytically stable probably due to the presence of a fibre–fibre physical network. Microbial attack in biotic aqueous medium was evidenced by the presence of a biofilm, especially on the fibre surface. In soil burial, PCL/S and 15%SF–PCL/S were degraded to about 50% of the initial mass. The weight loss pattern showed by the composite was associated with the presence of strong fibre–fibre and fibre–matrix interactions, which are absent in the neat matrix.Fil: Di Franco, C.R.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Cyras, Viviana Paola. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Busalmen, Juan Pablo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Ruseckaite, Roxana Alejandra. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Vázquez, A.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaElsevier2004-10info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/94395Di Franco, C.R.; Cyras, Viviana Paola; Busalmen, Juan Pablo; Ruseckaite, Roxana Alejandra; Vázquez, A.; Degradation of polycaprolactone/starch blends and composites with sisal fibre; Elsevier; Polymer Degradation And Stability; 86; 1; 10-2004; 95-1030141-3910CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0141391004000795info:eu-repo/semantics/altIdentifier/doi/10.1016/j.polymdegradstab.2004.02.009info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-17T11:24:57Zoai:ri.conicet.gov.ar:11336/94395instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-17 11:24:57.367CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Degradation of polycaprolactone/starch blends and composites with sisal fibre
title Degradation of polycaprolactone/starch blends and composites with sisal fibre
spellingShingle Degradation of polycaprolactone/starch blends and composites with sisal fibre
Di Franco, C.R.
DEGRADATION
HYDROLYSIS
POLYCAPROLACTONE
SISAL FIBRE
SOIL BURIAL
STARCH
title_short Degradation of polycaprolactone/starch blends and composites with sisal fibre
title_full Degradation of polycaprolactone/starch blends and composites with sisal fibre
title_fullStr Degradation of polycaprolactone/starch blends and composites with sisal fibre
title_full_unstemmed Degradation of polycaprolactone/starch blends and composites with sisal fibre
title_sort Degradation of polycaprolactone/starch blends and composites with sisal fibre
dc.creator.none.fl_str_mv Di Franco, C.R.
Cyras, Viviana Paola
Busalmen, Juan Pablo
Ruseckaite, Roxana Alejandra
Vázquez, A.
author Di Franco, C.R.
author_facet Di Franco, C.R.
Cyras, Viviana Paola
Busalmen, Juan Pablo
Ruseckaite, Roxana Alejandra
Vázquez, A.
author_role author
author2 Cyras, Viviana Paola
Busalmen, Juan Pablo
Ruseckaite, Roxana Alejandra
Vázquez, A.
author2_role author
author
author
author
dc.subject.none.fl_str_mv DEGRADATION
HYDROLYSIS
POLYCAPROLACTONE
SISAL FIBRE
SOIL BURIAL
STARCH
topic DEGRADATION
HYDROLYSIS
POLYCAPROLACTONE
SISAL FIBRE
SOIL BURIAL
STARCH
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.4
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv The susceptibility of polycaprolactone/starch (PCL/S) and sisal fibre-reinforced polycaprolactone/starch blends (SF-PCL/S) to different degrading environments was evaluated. The composites and the unfilled matrix showed hydrolytic stability at pH 7.2 at two different temperatures (25 °C and 40 °C). Fibres were stable under hydrolytic conditions and seemed to favour the entrance of water and then, the swelling and the hydrolysis of the starch (the most bio-available component). At higher fibre content, the composites become more hydrolytically stable probably due to the presence of a fibre–fibre physical network. Microbial attack in biotic aqueous medium was evidenced by the presence of a biofilm, especially on the fibre surface. In soil burial, PCL/S and 15%SF–PCL/S were degraded to about 50% of the initial mass. The weight loss pattern showed by the composite was associated with the presence of strong fibre–fibre and fibre–matrix interactions, which are absent in the neat matrix.
Fil: Di Franco, C.R.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Cyras, Viviana Paola. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Busalmen, Juan Pablo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Ruseckaite, Roxana Alejandra. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Vázquez, A.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
description The susceptibility of polycaprolactone/starch (PCL/S) and sisal fibre-reinforced polycaprolactone/starch blends (SF-PCL/S) to different degrading environments was evaluated. The composites and the unfilled matrix showed hydrolytic stability at pH 7.2 at two different temperatures (25 °C and 40 °C). Fibres were stable under hydrolytic conditions and seemed to favour the entrance of water and then, the swelling and the hydrolysis of the starch (the most bio-available component). At higher fibre content, the composites become more hydrolytically stable probably due to the presence of a fibre–fibre physical network. Microbial attack in biotic aqueous medium was evidenced by the presence of a biofilm, especially on the fibre surface. In soil burial, PCL/S and 15%SF–PCL/S were degraded to about 50% of the initial mass. The weight loss pattern showed by the composite was associated with the presence of strong fibre–fibre and fibre–matrix interactions, which are absent in the neat matrix.
publishDate 2004
dc.date.none.fl_str_mv 2004-10
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/94395
Di Franco, C.R.; Cyras, Viviana Paola; Busalmen, Juan Pablo; Ruseckaite, Roxana Alejandra; Vázquez, A.; Degradation of polycaprolactone/starch blends and composites with sisal fibre; Elsevier; Polymer Degradation And Stability; 86; 1; 10-2004; 95-103
0141-3910
CONICET Digital
CONICET
url http://hdl.handle.net/11336/94395
identifier_str_mv Di Franco, C.R.; Cyras, Viviana Paola; Busalmen, Juan Pablo; Ruseckaite, Roxana Alejandra; Vázquez, A.; Degradation of polycaprolactone/starch blends and composites with sisal fibre; Elsevier; Polymer Degradation And Stability; 86; 1; 10-2004; 95-103
0141-3910
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0141391004000795
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.polymdegradstab.2004.02.009
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier
publisher.none.fl_str_mv Elsevier
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1843606599905574912
score 13.001348

Publicaciones similares