Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing
- Autores
- Fernández Scudeller, Federico; Martinez, Ricardo Antonio
- Año de publicación
- 2015
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- This paper aims to characterize the behaviour of austempered ductile iron (ADI) under cyclic load bearing and its surface in contact with water.The first part is devoted to verifying the drop in Ultimate tensile strength and theelongation that takes place when ADI tensile samples are tested submerged in water as compared to values obtained in dry condition.Focus of this work is placed on crack initiation and propagation when submerged SEN(B) samples are tested applying cyclic loads.Different test stages of fissure nucleation and propagation on the lateral face of thesample were documented by microscopic imaging during the test, thereby allowing to characterize the manner in which failure occurred.The resulting fracture surfaces were analysed by scanning electron microscopy (SEM),and possible fracture mechanisms are discussed.The main contributions of this work include characteristic values of the time of crack initiation, crack growth rate and a methodology to study some particularities of the operating fracture mechanisms based on lateral observations and fracture surface images.
Fil: Fernández Scudeller, Federico. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Mar del Plata. Instituto de Investigación En Ciencia y Tecnología de Materiales (i); Argentina. Universidad Nacional de Mar del Plata. Facultad de Ingeniería; Argentina
Fil: Martinez, Ricardo Antonio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Mar del Plata. Instituto de Investigación en Ciencia y Tecnología de Materiales (i); Argentina. Universidad Nacional de Mar del Plata. Facultad de Ingeniería; Argentina - Materia
-
Adi
Water
Embrittlement
Fatiga
Cracks
Cyclic Load - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/10115
Ver los metadatos del registro completo
id |
CONICETDig_75b984d0a597b912d38dacf80e5767f5 |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/10115 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearingFernández Scudeller, FedericoMartinez, Ricardo AntonioAdiWaterEmbrittlementFatigaCracksCyclic Loadhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2This paper aims to characterize the behaviour of austempered ductile iron (ADI) under cyclic load bearing and its surface in contact with water.The first part is devoted to verifying the drop in Ultimate tensile strength and theelongation that takes place when ADI tensile samples are tested submerged in water as compared to values obtained in dry condition.Focus of this work is placed on crack initiation and propagation when submerged SEN(B) samples are tested applying cyclic loads.Different test stages of fissure nucleation and propagation on the lateral face of thesample were documented by microscopic imaging during the test, thereby allowing to characterize the manner in which failure occurred.The resulting fracture surfaces were analysed by scanning electron microscopy (SEM),and possible fracture mechanisms are discussed.The main contributions of this work include characteristic values of the time of crack initiation, crack growth rate and a methodology to study some particularities of the operating fracture mechanisms based on lateral observations and fracture surface images.Fil: Fernández Scudeller, Federico. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Mar del Plata. Instituto de Investigación En Ciencia y Tecnología de Materiales (i); Argentina. Universidad Nacional de Mar del Plata. Facultad de Ingeniería; ArgentinaFil: Martinez, Ricardo Antonio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Mar del Plata. Instituto de Investigación en Ciencia y Tecnología de Materiales (i); Argentina. Universidad Nacional de Mar del Plata. Facultad de Ingeniería; ArgentinaWiley2015-12-29info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/10115Fernández Scudeller, Federico; Martinez, Ricardo Antonio; Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing; Wiley; Fatigue; 39; 3; 29-12-2015; 346-3561460-2695enginfo:eu-repo/semantics/altIdentifier/url/http://onlinelibrary.wiley.com/doi/10.1111/ffe.12360/abstractinfo:eu-repo/semantics/altIdentifier/doi/10.1111/ffe.12360info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T10:11:58Zoai:ri.conicet.gov.ar:11336/10115instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 10:11:58.516CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing |
title |
Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing |
spellingShingle |
Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing Fernández Scudeller, Federico Adi Water Embrittlement Fatiga Cracks Cyclic Load |
title_short |
Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing |
title_full |
Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing |
title_fullStr |
Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing |
title_full_unstemmed |
Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing |
title_sort |
Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing |
dc.creator.none.fl_str_mv |
Fernández Scudeller, Federico Martinez, Ricardo Antonio |
author |
Fernández Scudeller, Federico |
author_facet |
Fernández Scudeller, Federico Martinez, Ricardo Antonio |
author_role |
author |
author2 |
Martinez, Ricardo Antonio |
author2_role |
author |
dc.subject.none.fl_str_mv |
Adi Water Embrittlement Fatiga Cracks Cyclic Load |
topic |
Adi Water Embrittlement Fatiga Cracks Cyclic Load |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
This paper aims to characterize the behaviour of austempered ductile iron (ADI) under cyclic load bearing and its surface in contact with water.The first part is devoted to verifying the drop in Ultimate tensile strength and theelongation that takes place when ADI tensile samples are tested submerged in water as compared to values obtained in dry condition.Focus of this work is placed on crack initiation and propagation when submerged SEN(B) samples are tested applying cyclic loads.Different test stages of fissure nucleation and propagation on the lateral face of thesample were documented by microscopic imaging during the test, thereby allowing to characterize the manner in which failure occurred.The resulting fracture surfaces were analysed by scanning electron microscopy (SEM),and possible fracture mechanisms are discussed.The main contributions of this work include characteristic values of the time of crack initiation, crack growth rate and a methodology to study some particularities of the operating fracture mechanisms based on lateral observations and fracture surface images. Fil: Fernández Scudeller, Federico. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Mar del Plata. Instituto de Investigación En Ciencia y Tecnología de Materiales (i); Argentina. Universidad Nacional de Mar del Plata. Facultad de Ingeniería; Argentina Fil: Martinez, Ricardo Antonio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Mar del Plata. Instituto de Investigación en Ciencia y Tecnología de Materiales (i); Argentina. Universidad Nacional de Mar del Plata. Facultad de Ingeniería; Argentina |
description |
This paper aims to characterize the behaviour of austempered ductile iron (ADI) under cyclic load bearing and its surface in contact with water.The first part is devoted to verifying the drop in Ultimate tensile strength and theelongation that takes place when ADI tensile samples are tested submerged in water as compared to values obtained in dry condition.Focus of this work is placed on crack initiation and propagation when submerged SEN(B) samples are tested applying cyclic loads.Different test stages of fissure nucleation and propagation on the lateral face of thesample were documented by microscopic imaging during the test, thereby allowing to characterize the manner in which failure occurred.The resulting fracture surfaces were analysed by scanning electron microscopy (SEM),and possible fracture mechanisms are discussed.The main contributions of this work include characteristic values of the time of crack initiation, crack growth rate and a methodology to study some particularities of the operating fracture mechanisms based on lateral observations and fracture surface images. |
publishDate |
2015 |
dc.date.none.fl_str_mv |
2015-12-29 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/10115 Fernández Scudeller, Federico; Martinez, Ricardo Antonio; Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing; Wiley; Fatigue; 39; 3; 29-12-2015; 346-356 1460-2695 |
url |
http://hdl.handle.net/11336/10115 |
identifier_str_mv |
Fernández Scudeller, Federico; Martinez, Ricardo Antonio; Evaluation of environmentally assisted fracture of austempered ductile iron (ADI) under cyclic load bearing; Wiley; Fatigue; 39; 3; 29-12-2015; 346-356 1460-2695 |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/url/http://onlinelibrary.wiley.com/doi/10.1111/ffe.12360/abstract info:eu-repo/semantics/altIdentifier/doi/10.1111/ffe.12360 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Wiley |
publisher.none.fl_str_mv |
Wiley |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1842270179845734400 |
score |
13.13397 |