Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance

Autores
Gassa, Liliana Mabel; Salvarezza, Roberto Carlos; Folquer, Maria Eugenia; Gassa, Liliana Mabel; Benitez, Guillermo Alfredo; Vela, Maria Elena; Salvarezza, Roberto Carlos
Año de publicación
2011
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Hard, ductile and adherent nanostructured Ni-W coatings were electrodeposited on carbon steel fromelectrolyte solutions containing sodium tungstate, nickel sulfate and sodium citrate, using different current pulse programs. Current pulse frequency was the dominant factor to define chemical composition,grain size, thickness and hardness. According to the electrodeposition conditions the deposited coatings showed 15-30 at% W, the grain size ranged from 65 to 140 nm, and the hardness varied from 650 to850 Hv. Tungsten carbide also present in the coating contributed to its hardness. The corrosion resistanceof the Ni-W coated steel was tested by potentiodynamic polarization in a neutral medium containingsulphate ions. The Ni-W coating protected the carbon steel from localized corrosion induced by sulphate anions.
Fil: Gassa, Liliana Mabel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Instituto de Química del Noroeste. Universidad Nacional de Tucumán. Facultad de Bioquímica, Química y Farmacia. Instituto de Química del Noroeste; Argentina
Fil: Salvarezza, Roberto Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Instituto de Química del Noroeste. Universidad Nacional de Tucumán. Facultad de Bioquímica, Química y Farmacia. Instituto de Química del Noroeste; Argentina
Fil: Folquer, Maria Eugenia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Instituto de Química del Noroeste. Universidad Nacional de Tucumán. Facultad de Bioquímica, Química y Farmacia. Instituto de Química del Noroeste; Argentina
Fil: Gassa, Liliana Mabel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina
Fil: Benitez, Guillermo Alfredo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina
Fil: Vela, Maria Elena. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina
Fil: Salvarezza, Roberto Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina
Materia
PULSE ELECTRODEPOSITION
Ni-W COATINGS
AFM-XPS
CORROSION RESISTANCE
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/277493
Acceder
id CONICETDig_736fe230cc5886389bf31cfbc98f4cdb
oai_identifier_str oai:ri.conicet.gov.ar:11336/277493
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistanceGassa, Liliana MabelSalvarezza, Roberto CarlosFolquer, Maria EugeniaGassa, Liliana MabelBenitez, Guillermo AlfredoVela, Maria ElenaSalvarezza, Roberto CarlosPULSE ELECTRODEPOSITIONNi-W COATINGSAFM-XPSCORROSION RESISTANCEhttps://purl.org/becyt/ford/1.4https://purl.org/becyt/ford/1Hard, ductile and adherent nanostructured Ni-W coatings were electrodeposited on carbon steel fromelectrolyte solutions containing sodium tungstate, nickel sulfate and sodium citrate, using different current pulse programs. Current pulse frequency was the dominant factor to define chemical composition,grain size, thickness and hardness. According to the electrodeposition conditions the deposited coatings showed 15-30 at% W, the grain size ranged from 65 to 140 nm, and the hardness varied from 650 to850 Hv. Tungsten carbide also present in the coating contributed to its hardness. The corrosion resistanceof the Ni-W coated steel was tested by potentiodynamic polarization in a neutral medium containingsulphate ions. The Ni-W coating protected the carbon steel from localized corrosion induced by sulphate anions.Fil: Gassa, Liliana Mabel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Instituto de Química del Noroeste. Universidad Nacional de Tucumán. Facultad de Bioquímica, Química y Farmacia. Instituto de Química del Noroeste; ArgentinaFil: Salvarezza, Roberto Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Instituto de Química del Noroeste. Universidad Nacional de Tucumán. Facultad de Bioquímica, Química y Farmacia. Instituto de Química del Noroeste; ArgentinaFil: Folquer, Maria Eugenia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Instituto de Química del Noroeste. Universidad Nacional de Tucumán. Facultad de Bioquímica, Química y Farmacia. Instituto de Química del Noroeste; ArgentinaFil: Gassa, Liliana Mabel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; ArgentinaFil: Benitez, Guillermo Alfredo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; ArgentinaFil: Vela, Maria Elena. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; ArgentinaFil: Salvarezza, Roberto Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; ArgentinaPergamon-Elsevier Science Ltd2011-07info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/277493Gassa, Liliana Mabel; Salvarezza, Roberto Carlos; Folquer, Maria Eugenia; Gassa, Liliana Mabel; Benitez, Guillermo Alfredo; et al.; Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance; Pergamon-Elsevier Science Ltd; Electrochimica Acta; 56; 17; 7-2011; 5898-59030013-4686CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S0013468611006918info:eu-repo/semantics/altIdentifier/doi/10.1016/j.electacta.2011.04.119info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-12-23T13:56:23Zoai:ri.conicet.gov.ar:11336/277493instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-12-23 13:56:23.704CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance
title Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance
spellingShingle Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance
Gassa, Liliana Mabel
PULSE ELECTRODEPOSITION
Ni-W COATINGS
AFM-XPS
CORROSION RESISTANCE
title_short Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance
title_full Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance
title_fullStr Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance
title_full_unstemmed Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance
title_sort Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance
dc.creator.none.fl_str_mv Gassa, Liliana Mabel
Salvarezza, Roberto Carlos
Folquer, Maria Eugenia
Gassa, Liliana Mabel
Benitez, Guillermo Alfredo
Vela, Maria Elena
Salvarezza, Roberto Carlos
author Gassa, Liliana Mabel
author_facet Gassa, Liliana Mabel
Salvarezza, Roberto Carlos
Folquer, Maria Eugenia
Benitez, Guillermo Alfredo
Vela, Maria Elena
author_role author
author2 Salvarezza, Roberto Carlos
Folquer, Maria Eugenia
Benitez, Guillermo Alfredo
Vela, Maria Elena
author2_role author
author
author
author
dc.subject.none.fl_str_mv PULSE ELECTRODEPOSITION
Ni-W COATINGS
AFM-XPS
CORROSION RESISTANCE
topic PULSE ELECTRODEPOSITION
Ni-W COATINGS
AFM-XPS
CORROSION RESISTANCE
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.4
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv Hard, ductile and adherent nanostructured Ni-W coatings were electrodeposited on carbon steel fromelectrolyte solutions containing sodium tungstate, nickel sulfate and sodium citrate, using different current pulse programs. Current pulse frequency was the dominant factor to define chemical composition,grain size, thickness and hardness. According to the electrodeposition conditions the deposited coatings showed 15-30 at% W, the grain size ranged from 65 to 140 nm, and the hardness varied from 650 to850 Hv. Tungsten carbide also present in the coating contributed to its hardness. The corrosion resistanceof the Ni-W coated steel was tested by potentiodynamic polarization in a neutral medium containingsulphate ions. The Ni-W coating protected the carbon steel from localized corrosion induced by sulphate anions.
Fil: Gassa, Liliana Mabel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Instituto de Química del Noroeste. Universidad Nacional de Tucumán. Facultad de Bioquímica, Química y Farmacia. Instituto de Química del Noroeste; Argentina
Fil: Salvarezza, Roberto Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Instituto de Química del Noroeste. Universidad Nacional de Tucumán. Facultad de Bioquímica, Química y Farmacia. Instituto de Química del Noroeste; Argentina
Fil: Folquer, Maria Eugenia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tucumán. Instituto de Química del Noroeste. Universidad Nacional de Tucumán. Facultad de Bioquímica, Química y Farmacia. Instituto de Química del Noroeste; Argentina
Fil: Gassa, Liliana Mabel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina
Fil: Benitez, Guillermo Alfredo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina
Fil: Vela, Maria Elena. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina
Fil: Salvarezza, Roberto Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina
description Hard, ductile and adherent nanostructured Ni-W coatings were electrodeposited on carbon steel fromelectrolyte solutions containing sodium tungstate, nickel sulfate and sodium citrate, using different current pulse programs. Current pulse frequency was the dominant factor to define chemical composition,grain size, thickness and hardness. According to the electrodeposition conditions the deposited coatings showed 15-30 at% W, the grain size ranged from 65 to 140 nm, and the hardness varied from 650 to850 Hv. Tungsten carbide also present in the coating contributed to its hardness. The corrosion resistanceof the Ni-W coated steel was tested by potentiodynamic polarization in a neutral medium containingsulphate ions. The Ni-W coating protected the carbon steel from localized corrosion induced by sulphate anions.
publishDate 2011
dc.date.none.fl_str_mv 2011-07
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/277493
Gassa, Liliana Mabel; Salvarezza, Roberto Carlos; Folquer, Maria Eugenia; Gassa, Liliana Mabel; Benitez, Guillermo Alfredo; et al.; Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance; Pergamon-Elsevier Science Ltd; Electrochimica Acta; 56; 17; 7-2011; 5898-5903
0013-4686
CONICET Digital
CONICET
url http://hdl.handle.net/11336/277493
identifier_str_mv Gassa, Liliana Mabel; Salvarezza, Roberto Carlos; Folquer, Maria Eugenia; Gassa, Liliana Mabel; Benitez, Guillermo Alfredo; et al.; Ni-W coatings electrodeposited on carbon steel: Chemical composition, mechanical properties and corrosion resistance; Pergamon-Elsevier Science Ltd; Electrochimica Acta; 56; 17; 7-2011; 5898-5903
0013-4686
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S0013468611006918
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.electacta.2011.04.119
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Pergamon-Elsevier Science Ltd
publisher.none.fl_str_mv Pergamon-Elsevier Science Ltd
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1852335462082936832
score 12.952241

Publicaciones similares