Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres

Autores
Santos, H. S.; Cesio, Ana Maria; Gauna, Matias Roberto; Justo, V. F.; Volzone, Cristina
Año de publicación
2017
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Beidellite clay mineral after intercalation of OH-Cr(III) species were thermally analyzed up to 1350 °C in oxygen and nitrogenatmospheres. OH-Cr-beidellite can be used as a pillared clay precursor for catalysis or as adsorbent applications. However, inthis paper beidellite enriched in chromium were analyzed at different thermal treatments up to high temperature for evaluatingstructural changes for possible future ceramic applications. The structural changes were followed by thermal analysis and X-raydiffraction. The thermal treatment of OH-Cr-beidellite in oxygen and nitrogen atmospheres developed different mineralogicalphases up to 1050 °C, but at higher temperatures, the same phases were developed in both atmosphere treatments. Eskolaitephase (Cr2O3) appeared in the sample after heating at 400 °C in oxygen atmosphere, whereas grimaldite (CrO-OH) in nitrogenatmosphere, maintaining the starting phases. At 1000 °C the raw clay minerals disappeared, as it is knew. At 1050 °C in nitrogenatmosphere, grimaldite was absent and eskolaite appeared. At 1350 °C in the samples calcined in both atmospheres, quartz,cristobalite and mullite as the main phases and in lower contents aluminum oxide and aluminum-chromium oxide [(Al,Cr)2O3]were present.
O mineral de argila de beidelita após intercalação das espécies OH-Cr(III) foi termicamente analisado até 1350 °C em atmosferas de oxigénio e nitrogênio. A OH-Cr-beidelita pode ser utilizada como um precursor de argila pilarizada para catálise ou para aplicações adsorventes. No entanto, neste trabalho, a beidelita enriquecida em cromo foi analisada em diferentes tratamentos térmicos até alta temperatura para avaliação de mudanças estruturais para possíveis aplicações cerâmicas futuras. As alterações estruturais foram acompanhadas por análise térmica e difração de raios X. O tratamento térmico da OH-Cr-beidelita em atmosferas de oxigênio e nitrogênio desenvolveu diferentes fases mineralógicas até 1050 °C, mas em temperaturas mais altas, as mesmas fases foram desenvolvidas em ambas atmosferas. A fase eskolaita (Cr2 O3 ) apareceu na amostra após aquecimento a 400 °C em atmosfera de oxigênio, enquanto grimaldita (CrO-OH) em atmosfera de nitrogênio, mantendo as fases iniciais. Em 1000 °C, os minerais originais da argila desapareceram, como é conhecido. Em 1050 °C em atmosfera de nitrogênio, a grimaldita estava ausente e apareceu eskolaita. Em amostras calcinadas a 1350 °C em ambas as atmosferas, estavam presentes quartzo, cristobolita e mulita como fases principais e em menores teores óxido de alumínio e óxido de alumínio e cromo [(Al,Cr)2 O3 ].
Fil: Santos, H. S.. Universidade de Sao Paulo; Brasil
Fil: Cesio, Ana Maria. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Gauna, Matias Roberto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Justo, V. F.. Universidade de Sao Paulo; Brasil
Fil: Volzone, Cristina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Materia
Beidellite
Chromium
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/66458
Acceder
id CONICETDig_5c5e2cfee7719feaf2a5ce23d2bee6d8
oai_identifier_str oai:ri.conicet.gov.ar:11336/66458
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheresAlterações estruturais de Cr-beidelita tratada até 1350 °C em atmosferas de oxigênio ou nitrogênioSantos, H. S.Cesio, Ana MariaGauna, Matias RobertoJusto, V. F.Volzone, CristinaBeidelliteChromiumhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Beidellite clay mineral after intercalation of OH-Cr(III) species were thermally analyzed up to 1350 °C in oxygen and nitrogenatmospheres. OH-Cr-beidellite can be used as a pillared clay precursor for catalysis or as adsorbent applications. However, inthis paper beidellite enriched in chromium were analyzed at different thermal treatments up to high temperature for evaluatingstructural changes for possible future ceramic applications. The structural changes were followed by thermal analysis and X-raydiffraction. The thermal treatment of OH-Cr-beidellite in oxygen and nitrogen atmospheres developed different mineralogicalphases up to 1050 °C, but at higher temperatures, the same phases were developed in both atmosphere treatments. Eskolaitephase (Cr2O3) appeared in the sample after heating at 400 °C in oxygen atmosphere, whereas grimaldite (CrO-OH) in nitrogenatmosphere, maintaining the starting phases. At 1000 °C the raw clay minerals disappeared, as it is knew. At 1050 °C in nitrogenatmosphere, grimaldite was absent and eskolaite appeared. At 1350 °C in the samples calcined in both atmospheres, quartz,cristobalite and mullite as the main phases and in lower contents aluminum oxide and aluminum-chromium oxide [(Al,Cr)2O3]were present.O mineral de argila de beidelita após intercalação das espécies OH-Cr(III) foi termicamente analisado até 1350 °C em atmosferas de oxigénio e nitrogênio. A OH-Cr-beidelita pode ser utilizada como um precursor de argila pilarizada para catálise ou para aplicações adsorventes. No entanto, neste trabalho, a beidelita enriquecida em cromo foi analisada em diferentes tratamentos térmicos até alta temperatura para avaliação de mudanças estruturais para possíveis aplicações cerâmicas futuras. As alterações estruturais foram acompanhadas por análise térmica e difração de raios X. O tratamento térmico da OH-Cr-beidelita em atmosferas de oxigênio e nitrogênio desenvolveu diferentes fases mineralógicas até 1050 °C, mas em temperaturas mais altas, as mesmas fases foram desenvolvidas em ambas atmosferas. A fase eskolaita (Cr2 O3 ) apareceu na amostra após aquecimento a 400 °C em atmosfera de oxigênio, enquanto grimaldita (CrO-OH) em atmosfera de nitrogênio, mantendo as fases iniciais. Em 1000 °C, os minerais originais da argila desapareceram, como é conhecido. Em 1050 °C em atmosfera de nitrogênio, a grimaldita estava ausente e apareceu eskolaita. Em amostras calcinadas a 1350 °C em ambas as atmosferas, estavam presentes quartzo, cristobolita e mulita como fases principais e em menores teores óxido de alumínio e óxido de alumínio e cromo [(Al,Cr)2 O3 ].Fil: Santos, H. S.. Universidade de Sao Paulo; BrasilFil: Cesio, Ana Maria. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Gauna, Matias Roberto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Justo, V. F.. Universidade de Sao Paulo; BrasilFil: Volzone, Cristina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaAssociação Brasileira de Cerâmica2017-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/66458Santos, H. S.; Cesio, Ana Maria; Gauna, Matias Roberto; Justo, V. F.; Volzone, Cristina; Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres; Associação Brasileira de Cerâmica; Ceramica; 64; 369; 1-2017; 64-680366-69131678-4553CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1590/0366-69132018643692215info:eu-repo/semantics/altIdentifier/url/http://ref.scielo.org/f77q5kinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T09:48:36Zoai:ri.conicet.gov.ar:11336/66458instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 09:48:36.853CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres
Alterações estruturais de Cr-beidelita tratada até 1350 °C em atmosferas de oxigênio ou nitrogênio
title Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres
spellingShingle Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres
Santos, H. S.
Beidellite
Chromium
title_short Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres
title_full Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres
title_fullStr Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres
title_full_unstemmed Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres
title_sort Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres
dc.creator.none.fl_str_mv Santos, H. S.
Cesio, Ana Maria
Gauna, Matias Roberto
Justo, V. F.
Volzone, Cristina
author Santos, H. S.
author_facet Santos, H. S.
Cesio, Ana Maria
Gauna, Matias Roberto
Justo, V. F.
Volzone, Cristina
author_role author
author2 Cesio, Ana Maria
Gauna, Matias Roberto
Justo, V. F.
Volzone, Cristina
author2_role author
author
author
author
dc.subject.none.fl_str_mv Beidellite
Chromium
topic Beidellite
Chromium
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv Beidellite clay mineral after intercalation of OH-Cr(III) species were thermally analyzed up to 1350 °C in oxygen and nitrogenatmospheres. OH-Cr-beidellite can be used as a pillared clay precursor for catalysis or as adsorbent applications. However, inthis paper beidellite enriched in chromium were analyzed at different thermal treatments up to high temperature for evaluatingstructural changes for possible future ceramic applications. The structural changes were followed by thermal analysis and X-raydiffraction. The thermal treatment of OH-Cr-beidellite in oxygen and nitrogen atmospheres developed different mineralogicalphases up to 1050 °C, but at higher temperatures, the same phases were developed in both atmosphere treatments. Eskolaitephase (Cr2O3) appeared in the sample after heating at 400 °C in oxygen atmosphere, whereas grimaldite (CrO-OH) in nitrogenatmosphere, maintaining the starting phases. At 1000 °C the raw clay minerals disappeared, as it is knew. At 1050 °C in nitrogenatmosphere, grimaldite was absent and eskolaite appeared. At 1350 °C in the samples calcined in both atmospheres, quartz,cristobalite and mullite as the main phases and in lower contents aluminum oxide and aluminum-chromium oxide [(Al,Cr)2O3]were present.
O mineral de argila de beidelita após intercalação das espécies OH-Cr(III) foi termicamente analisado até 1350 °C em atmosferas de oxigénio e nitrogênio. A OH-Cr-beidelita pode ser utilizada como um precursor de argila pilarizada para catálise ou para aplicações adsorventes. No entanto, neste trabalho, a beidelita enriquecida em cromo foi analisada em diferentes tratamentos térmicos até alta temperatura para avaliação de mudanças estruturais para possíveis aplicações cerâmicas futuras. As alterações estruturais foram acompanhadas por análise térmica e difração de raios X. O tratamento térmico da OH-Cr-beidelita em atmosferas de oxigênio e nitrogênio desenvolveu diferentes fases mineralógicas até 1050 °C, mas em temperaturas mais altas, as mesmas fases foram desenvolvidas em ambas atmosferas. A fase eskolaita (Cr2 O3 ) apareceu na amostra após aquecimento a 400 °C em atmosfera de oxigênio, enquanto grimaldita (CrO-OH) em atmosfera de nitrogênio, mantendo as fases iniciais. Em 1000 °C, os minerais originais da argila desapareceram, como é conhecido. Em 1050 °C em atmosfera de nitrogênio, a grimaldita estava ausente e apareceu eskolaita. Em amostras calcinadas a 1350 °C em ambas as atmosferas, estavam presentes quartzo, cristobolita e mulita como fases principais e em menores teores óxido de alumínio e óxido de alumínio e cromo [(Al,Cr)2 O3 ].
Fil: Santos, H. S.. Universidade de Sao Paulo; Brasil
Fil: Cesio, Ana Maria. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Gauna, Matias Roberto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Justo, V. F.. Universidade de Sao Paulo; Brasil
Fil: Volzone, Cristina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
description Beidellite clay mineral after intercalation of OH-Cr(III) species were thermally analyzed up to 1350 °C in oxygen and nitrogenatmospheres. OH-Cr-beidellite can be used as a pillared clay precursor for catalysis or as adsorbent applications. However, inthis paper beidellite enriched in chromium were analyzed at different thermal treatments up to high temperature for evaluatingstructural changes for possible future ceramic applications. The structural changes were followed by thermal analysis and X-raydiffraction. The thermal treatment of OH-Cr-beidellite in oxygen and nitrogen atmospheres developed different mineralogicalphases up to 1050 °C, but at higher temperatures, the same phases were developed in both atmosphere treatments. Eskolaitephase (Cr2O3) appeared in the sample after heating at 400 °C in oxygen atmosphere, whereas grimaldite (CrO-OH) in nitrogenatmosphere, maintaining the starting phases. At 1000 °C the raw clay minerals disappeared, as it is knew. At 1050 °C in nitrogenatmosphere, grimaldite was absent and eskolaite appeared. At 1350 °C in the samples calcined in both atmospheres, quartz,cristobalite and mullite as the main phases and in lower contents aluminum oxide and aluminum-chromium oxide [(Al,Cr)2O3]were present.
publishDate 2017
dc.date.none.fl_str_mv 2017-01
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/66458
Santos, H. S.; Cesio, Ana Maria; Gauna, Matias Roberto; Justo, V. F.; Volzone, Cristina; Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres; Associação Brasileira de Cerâmica; Ceramica; 64; 369; 1-2017; 64-68
0366-6913
1678-4553
CONICET Digital
CONICET
url http://hdl.handle.net/11336/66458
identifier_str_mv Santos, H. S.; Cesio, Ana Maria; Gauna, Matias Roberto; Justo, V. F.; Volzone, Cristina; Structural changes of Cr-beidellite treated up to 1350 °C in oxygen or nitrogen atmospheres; Associação Brasileira de Cerâmica; Ceramica; 64; 369; 1-2017; 64-68
0366-6913
1678-4553
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1590/0366-69132018643692215
info:eu-repo/semantics/altIdentifier/url/http://ref.scielo.org/f77q5k
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Associação Brasileira de Cerâmica
publisher.none.fl_str_mv Associação Brasileira de Cerâmica
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842268931806461952
score 13.13397

Publicaciones similares