Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia

Autores
Aglietti, Esteban Fausto; Suarez, Gustavo; Rendtorff Birrer, Nicolás Maximiliano; Aglietti, Esteban Fausto
Año de publicación
2016
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
In the current paper we present a study of the sinterability of two zirconia (ZrO2) nanopowders with different content of yttrium oxide (Y2O3) 3 and 8 % tetragonal and cubic zirconia, respectively. After sintering between 900-1500ºC, the samples were characterized in terms of their density and porosity using Archimedes technique. Their grain size was evaluated using scanning electron microscope (SEM). Vickers hardness and fracture toughness (KIC) were measured by the indentation method. The results showed that pores are almost eliminated at sintering temperatures higher than 1400ºC and grain size is larger due to the agglomerates formed as a result of grain growth. Vickers hardness evaluated at 1400ºC sintering temperature is greater than that obtained at 1500ºC due to the grain growth produced at this temperature. In addition, we show a correlation between Vickers hardness and the porosity, obtained by evaluating empirical and theoretical models.Keywords: Zirconia, Sintering, Vickers hardness.
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Suarez, Gustavo. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Materia
zirconia
tetragonal
mechanical properties
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/103509
Acceder
id CONICETDig_5b2fc84463b48dbf21060edad3e01255
oai_identifier_str oai:ri.conicet.gov.ar:11336/103509
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconiaAglietti, Esteban FaustoSuarez, GustavoRendtorff Birrer, Nicolás MaximilianoAglietti, Esteban Faustozirconiatetragonalmechanical propertieshttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2In the current paper we present a study of the sinterability of two zirconia (ZrO2) nanopowders with different content of yttrium oxide (Y2O3) 3 and 8 % tetragonal and cubic zirconia, respectively. After sintering between 900-1500ºC, the samples were characterized in terms of their density and porosity using Archimedes technique. Their grain size was evaluated using scanning electron microscope (SEM). Vickers hardness and fracture toughness (KIC) were measured by the indentation method. The results showed that pores are almost eliminated at sintering temperatures higher than 1400ºC and grain size is larger due to the agglomerates formed as a result of grain growth. Vickers hardness evaluated at 1400ºC sintering temperature is greater than that obtained at 1500ºC due to the grain growth produced at this temperature. In addition, we show a correlation between Vickers hardness and the porosity, obtained by evaluating empirical and theoretical models.Keywords: Zirconia, Sintering, Vickers hardness.Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Suarez, Gustavo. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Rendtorff Birrer, Nicolás Maximiliano. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaInt Inst Science Sintering (i I S S)2016-04info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/103509Aglietti, Esteban Fausto; Suarez, Gustavo; Rendtorff Birrer, Nicolás Maximiliano; Aglietti, Esteban Fausto; Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia; Int Inst Science Sintering (i I S S); Science Of Sintering; 48; 1; 4-2016; 119-1300350-820XCONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.2298/SOS1601119Ginfo:eu-repo/semantics/altIdentifier/url/http://www.doiserbia.nb.rs/Article.aspx?ID=0350-820X1601119G#.XqHwbWgzbIUinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:23:56Zoai:ri.conicet.gov.ar:11336/103509instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:23:56.722CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia
title Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia
spellingShingle Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia
Aglietti, Esteban Fausto
zirconia
tetragonal
mechanical properties
title_short Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia
title_full Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia
title_fullStr Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia
title_full_unstemmed Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia
title_sort Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia
dc.creator.none.fl_str_mv Aglietti, Esteban Fausto
Suarez, Gustavo
Rendtorff Birrer, Nicolás Maximiliano
Aglietti, Esteban Fausto
author Aglietti, Esteban Fausto
author_facet Aglietti, Esteban Fausto
Suarez, Gustavo
Rendtorff Birrer, Nicolás Maximiliano
author_role author
author2 Suarez, Gustavo
Rendtorff Birrer, Nicolás Maximiliano
author2_role author
author
dc.subject.none.fl_str_mv zirconia
tetragonal
mechanical properties
topic zirconia
tetragonal
mechanical properties
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv In the current paper we present a study of the sinterability of two zirconia (ZrO2) nanopowders with different content of yttrium oxide (Y2O3) 3 and 8 % tetragonal and cubic zirconia, respectively. After sintering between 900-1500ºC, the samples were characterized in terms of their density and porosity using Archimedes technique. Their grain size was evaluated using scanning electron microscope (SEM). Vickers hardness and fracture toughness (KIC) were measured by the indentation method. The results showed that pores are almost eliminated at sintering temperatures higher than 1400ºC and grain size is larger due to the agglomerates formed as a result of grain growth. Vickers hardness evaluated at 1400ºC sintering temperature is greater than that obtained at 1500ºC due to the grain growth produced at this temperature. In addition, we show a correlation between Vickers hardness and the porosity, obtained by evaluating empirical and theoretical models.Keywords: Zirconia, Sintering, Vickers hardness.
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Suarez, Gustavo. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Aglietti, Esteban Fausto. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
description In the current paper we present a study of the sinterability of two zirconia (ZrO2) nanopowders with different content of yttrium oxide (Y2O3) 3 and 8 % tetragonal and cubic zirconia, respectively. After sintering between 900-1500ºC, the samples were characterized in terms of their density and porosity using Archimedes technique. Their grain size was evaluated using scanning electron microscope (SEM). Vickers hardness and fracture toughness (KIC) were measured by the indentation method. The results showed that pores are almost eliminated at sintering temperatures higher than 1400ºC and grain size is larger due to the agglomerates formed as a result of grain growth. Vickers hardness evaluated at 1400ºC sintering temperature is greater than that obtained at 1500ºC due to the grain growth produced at this temperature. In addition, we show a correlation between Vickers hardness and the porosity, obtained by evaluating empirical and theoretical models.Keywords: Zirconia, Sintering, Vickers hardness.
publishDate 2016
dc.date.none.fl_str_mv 2016-04
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/103509
Aglietti, Esteban Fausto; Suarez, Gustavo; Rendtorff Birrer, Nicolás Maximiliano; Aglietti, Esteban Fausto; Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia; Int Inst Science Sintering (i I S S); Science Of Sintering; 48; 1; 4-2016; 119-130
0350-820X
CONICET Digital
CONICET
url http://hdl.handle.net/11336/103509
identifier_str_mv Aglietti, Esteban Fausto; Suarez, Gustavo; Rendtorff Birrer, Nicolás Maximiliano; Aglietti, Esteban Fausto; Relation between mechanical and textural properties of dense materials of tetragonal and cubic zirconia; Int Inst Science Sintering (i I S S); Science Of Sintering; 48; 1; 4-2016; 119-130
0350-820X
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.2298/SOS1601119G
info:eu-repo/semantics/altIdentifier/url/http://www.doiserbia.nb.rs/Article.aspx?ID=0350-820X1601119G#.XqHwbWgzbIU
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Int Inst Science Sintering (i I S S)
publisher.none.fl_str_mv Int Inst Science Sintering (i I S S)
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1844614235572666368
score 13.070432

Publicaciones similares