Tannin-modified soybean protein concentrate for wood adhesive

Autores
Espósito, Leandro Hernan; Ciannamea, Emiliano Manuel; Solabarrieta, Ignacio; Piter, Juan Carlos Jesús; Ruseckaite, Roxana Alejandra; Stefani, Pablo Marcelo
Año de publicación
2022
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Soybean protein concentrate (SPC) modified with condensed mimosa tannin (CT) were employed as eco-friendly and formaldehyde-free adhesives for glued-wood joints. Eucalyptus grandis wood boards free of knots and cracks were used as substrate. Thermogravimetric analysis (TGA) showed that tannin provided higher thermal stability to the adhesive, which allowed expanding the temperature range for hot pressing. Apparent viscosity and dynamic contact angle were measured to evaluate the influence of tannin content on rheological behaviour and the wettability process. A classic shear-thinning behaviour was observed for all the adhesives. Apparent viscosity and equilibrium contact angle reached a maximum value for low CT content. This effect was attributed to the existence of associative interactions between CT and SPC. Bonding quality parameters (wood failure percentage and shear strength) of the glued-wood joints were measured according to EN 302-1:2004 standard. SPC adhesive modified with 1 % w/w CT showed the best performance in dry conditions. These adhesives were suitable for glued-wood joints for indoor environments.
Fil: Espósito, Leandro Hernan. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Ciannamea, Emiliano Manuel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Solabarrieta, Ignacio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Piter, Juan Carlos Jesús. Universidad Tecnológica Nacional; Argentina
Fil: Ruseckaite, Roxana Alejandra. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Stefani, Pablo Marcelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Materia
SOYBEAN PROTEIN CONCENTRATE
MIMOSA TANNIN
RHEOLOGY
WETTABILITY
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/212234
Acceder
id CONICETDig_34494ce07e6604df64b08f2338e46634
oai_identifier_str oai:ri.conicet.gov.ar:11336/212234
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Tannin-modified soybean protein concentrate for wood adhesiveEspósito, Leandro HernanCiannamea, Emiliano ManuelSolabarrieta, IgnacioPiter, Juan Carlos JesúsRuseckaite, Roxana AlejandraStefani, Pablo MarceloSOYBEAN PROTEIN CONCENTRATEMIMOSA TANNINRHEOLOGYWETTABILITYhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Soybean protein concentrate (SPC) modified with condensed mimosa tannin (CT) were employed as eco-friendly and formaldehyde-free adhesives for glued-wood joints. Eucalyptus grandis wood boards free of knots and cracks were used as substrate. Thermogravimetric analysis (TGA) showed that tannin provided higher thermal stability to the adhesive, which allowed expanding the temperature range for hot pressing. Apparent viscosity and dynamic contact angle were measured to evaluate the influence of tannin content on rheological behaviour and the wettability process. A classic shear-thinning behaviour was observed for all the adhesives. Apparent viscosity and equilibrium contact angle reached a maximum value for low CT content. This effect was attributed to the existence of associative interactions between CT and SPC. Bonding quality parameters (wood failure percentage and shear strength) of the glued-wood joints were measured according to EN 302-1:2004 standard. SPC adhesive modified with 1 % w/w CT showed the best performance in dry conditions. These adhesives were suitable for glued-wood joints for indoor environments.Fil: Espósito, Leandro Hernan. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Ciannamea, Emiliano Manuel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Solabarrieta, Ignacio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Piter, Juan Carlos Jesús. Universidad Tecnológica Nacional; ArgentinaFil: Ruseckaite, Roxana Alejandra. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Stefani, Pablo Marcelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaUniversitat politecnica de Valencia2022-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/212234Espósito, Leandro Hernan; Ciannamea, Emiliano Manuel; Solabarrieta, Ignacio; Piter, Juan Carlos Jesús; Ruseckaite, Roxana Alejandra; et al.; Tannin-modified soybean protein concentrate for wood adhesive; Universitat politecnica de Valencia; Journal of Applied Research in Technology & Engineering; 3; 1; 1-2022; 1-72695-8821CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://polipapers.upv.es/index.php/JARTE/article/view/15962info:eu-repo/semantics/altIdentifier/doi/10.4995/jarte.2022.15962info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T09:57:11Zoai:ri.conicet.gov.ar:11336/212234instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 09:57:11.978CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Tannin-modified soybean protein concentrate for wood adhesive
title Tannin-modified soybean protein concentrate for wood adhesive
spellingShingle Tannin-modified soybean protein concentrate for wood adhesive
Espósito, Leandro Hernan
SOYBEAN PROTEIN CONCENTRATE
MIMOSA TANNIN
RHEOLOGY
WETTABILITY
title_short Tannin-modified soybean protein concentrate for wood adhesive
title_full Tannin-modified soybean protein concentrate for wood adhesive
title_fullStr Tannin-modified soybean protein concentrate for wood adhesive
title_full_unstemmed Tannin-modified soybean protein concentrate for wood adhesive
title_sort Tannin-modified soybean protein concentrate for wood adhesive
dc.creator.none.fl_str_mv Espósito, Leandro Hernan
Ciannamea, Emiliano Manuel
Solabarrieta, Ignacio
Piter, Juan Carlos Jesús
Ruseckaite, Roxana Alejandra
Stefani, Pablo Marcelo
author Espósito, Leandro Hernan
author_facet Espósito, Leandro Hernan
Ciannamea, Emiliano Manuel
Solabarrieta, Ignacio
Piter, Juan Carlos Jesús
Ruseckaite, Roxana Alejandra
Stefani, Pablo Marcelo
author_role author
author2 Ciannamea, Emiliano Manuel
Solabarrieta, Ignacio
Piter, Juan Carlos Jesús
Ruseckaite, Roxana Alejandra
Stefani, Pablo Marcelo
author2_role author
author
author
author
author
dc.subject.none.fl_str_mv SOYBEAN PROTEIN CONCENTRATE
MIMOSA TANNIN
RHEOLOGY
WETTABILITY
topic SOYBEAN PROTEIN CONCENTRATE
MIMOSA TANNIN
RHEOLOGY
WETTABILITY
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv Soybean protein concentrate (SPC) modified with condensed mimosa tannin (CT) were employed as eco-friendly and formaldehyde-free adhesives for glued-wood joints. Eucalyptus grandis wood boards free of knots and cracks were used as substrate. Thermogravimetric analysis (TGA) showed that tannin provided higher thermal stability to the adhesive, which allowed expanding the temperature range for hot pressing. Apparent viscosity and dynamic contact angle were measured to evaluate the influence of tannin content on rheological behaviour and the wettability process. A classic shear-thinning behaviour was observed for all the adhesives. Apparent viscosity and equilibrium contact angle reached a maximum value for low CT content. This effect was attributed to the existence of associative interactions between CT and SPC. Bonding quality parameters (wood failure percentage and shear strength) of the glued-wood joints were measured according to EN 302-1:2004 standard. SPC adhesive modified with 1 % w/w CT showed the best performance in dry conditions. These adhesives were suitable for glued-wood joints for indoor environments.
Fil: Espósito, Leandro Hernan. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Ciannamea, Emiliano Manuel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Solabarrieta, Ignacio. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Piter, Juan Carlos Jesús. Universidad Tecnológica Nacional; Argentina
Fil: Ruseckaite, Roxana Alejandra. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Stefani, Pablo Marcelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
description Soybean protein concentrate (SPC) modified with condensed mimosa tannin (CT) were employed as eco-friendly and formaldehyde-free adhesives for glued-wood joints. Eucalyptus grandis wood boards free of knots and cracks were used as substrate. Thermogravimetric analysis (TGA) showed that tannin provided higher thermal stability to the adhesive, which allowed expanding the temperature range for hot pressing. Apparent viscosity and dynamic contact angle were measured to evaluate the influence of tannin content on rheological behaviour and the wettability process. A classic shear-thinning behaviour was observed for all the adhesives. Apparent viscosity and equilibrium contact angle reached a maximum value for low CT content. This effect was attributed to the existence of associative interactions between CT and SPC. Bonding quality parameters (wood failure percentage and shear strength) of the glued-wood joints were measured according to EN 302-1:2004 standard. SPC adhesive modified with 1 % w/w CT showed the best performance in dry conditions. These adhesives were suitable for glued-wood joints for indoor environments.
publishDate 2022
dc.date.none.fl_str_mv 2022-01
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/212234
Espósito, Leandro Hernan; Ciannamea, Emiliano Manuel; Solabarrieta, Ignacio; Piter, Juan Carlos Jesús; Ruseckaite, Roxana Alejandra; et al.; Tannin-modified soybean protein concentrate for wood adhesive; Universitat politecnica de Valencia; Journal of Applied Research in Technology & Engineering; 3; 1; 1-2022; 1-7
2695-8821
CONICET Digital
CONICET
url http://hdl.handle.net/11336/212234
identifier_str_mv Espósito, Leandro Hernan; Ciannamea, Emiliano Manuel; Solabarrieta, Ignacio; Piter, Juan Carlos Jesús; Ruseckaite, Roxana Alejandra; et al.; Tannin-modified soybean protein concentrate for wood adhesive; Universitat politecnica de Valencia; Journal of Applied Research in Technology & Engineering; 3; 1; 1-2022; 1-7
2695-8821
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://polipapers.upv.es/index.php/JARTE/article/view/15962
info:eu-repo/semantics/altIdentifier/doi/10.4995/jarte.2022.15962
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Universitat politecnica de Valencia
publisher.none.fl_str_mv Universitat politecnica de Valencia
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842269446798835712
score 13.13397

Publicaciones similares