Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study

Autores
Schio, P.; Barturen, Mariana; Milano, Julian; Bonilla, Jorge Fabián; Zheng, Y.; Vidal, F.; De Oliveira, A. J. A.
Año de publicación
2014
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
The magnetic anisotropy of 3-nm wide cobalt nanowires embedded in epitaxial CeO2/SrTiO3(001) layers is investigated by ferromagnetic resonance measurements. The measured magnetic shape and the magnetocrystalline anisotropies confirm that the Co nanowires have their main axes perpendicular to the film surface, and they are composed of hcp Co grains with the c-axes oriented along one of the <111> directions of the CeO2 matrix. The effects of such a peculiar structure on the magnetic anisotropy are addressed experimentally. The results show that the magnetic anisotropy of the wires is dominated by the magnetostatic term. The inhomogeneous structure of the wires leads to an effective magnetocrystalline anisotropy smaller than the bulk value of hcp Co.
Fil: Schio, P.. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Universidade Federal do São Carlos; Brasil
Fil: Barturen, Mariana. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; Argentina
Fil: Milano, Julian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; Argentina
Fil: Bonilla, Jorge Fabián. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina
Fil: Zheng, Y.. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina
Fil: Vidal, F.. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina
Fil: De Oliveira, A. J. A.. Universidade Federal do São Carlos; Brasil
Materia
FERROMAGNETIC RESONANCE
MAGNETIC ANISOTROPY
MAGNETIC NANOWIRES
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/180515
Acceder
id CONICETDig_32eea3d1546112d31d34aeb1cc82b83b
oai_identifier_str oai:ri.conicet.gov.ar:11336/180515
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance studySchio, P.Barturen, MarianaMilano, JulianBonilla, Jorge FabiánZheng, Y.Vidal, F.De Oliveira, A. J. A.FERROMAGNETIC RESONANCEMAGNETIC ANISOTROPYMAGNETIC NANOWIREShttps://purl.org/becyt/ford/1.3https://purl.org/becyt/ford/1The magnetic anisotropy of 3-nm wide cobalt nanowires embedded in epitaxial CeO2/SrTiO3(001) layers is investigated by ferromagnetic resonance measurements. The measured magnetic shape and the magnetocrystalline anisotropies confirm that the Co nanowires have their main axes perpendicular to the film surface, and they are composed of hcp Co grains with the c-axes oriented along one of the <111> directions of the CeO2 matrix. The effects of such a peculiar structure on the magnetic anisotropy are addressed experimentally. The results show that the magnetic anisotropy of the wires is dominated by the magnetostatic term. The inhomogeneous structure of the wires leads to an effective magnetocrystalline anisotropy smaller than the bulk value of hcp Co.Fil: Schio, P.. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Universidade Federal do São Carlos; BrasilFil: Barturen, Mariana. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; ArgentinaFil: Milano, Julian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; ArgentinaFil: Bonilla, Jorge Fabián. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; ArgentinaFil: Zheng, Y.. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; ArgentinaFil: Vidal, F.. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; ArgentinaFil: De Oliveira, A. J. A.. Universidade Federal do São Carlos; BrasilIOP Publishing2014-09info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/180515Schio, P.; Barturen, Mariana; Milano, Julian; Bonilla, Jorge Fabián; Zheng, Y.; et al.; Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study; IOP Publishing; Materials Research Express; 1; 3; 9-2014; 1-122053-1591CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://iopscience.iop.org/article/10.1088/2053-1591/1/3/035015info:eu-repo/semantics/altIdentifier/doi/10.1088/2053-1591/1/3/035015info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T09:58:18Zoai:ri.conicet.gov.ar:11336/180515instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 09:58:18.793CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study
title Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study
spellingShingle Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study
Schio, P.
FERROMAGNETIC RESONANCE
MAGNETIC ANISOTROPY
MAGNETIC NANOWIRES
title_short Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study
title_full Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study
title_fullStr Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study
title_full_unstemmed Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study
title_sort Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study
dc.creator.none.fl_str_mv Schio, P.
Barturen, Mariana
Milano, Julian
Bonilla, Jorge Fabián
Zheng, Y.
Vidal, F.
De Oliveira, A. J. A.
author Schio, P.
author_facet Schio, P.
Barturen, Mariana
Milano, Julian
Bonilla, Jorge Fabián
Zheng, Y.
Vidal, F.
De Oliveira, A. J. A.
author_role author
author2 Barturen, Mariana
Milano, Julian
Bonilla, Jorge Fabián
Zheng, Y.
Vidal, F.
De Oliveira, A. J. A.
author2_role author
author
author
author
author
author
dc.subject.none.fl_str_mv FERROMAGNETIC RESONANCE
MAGNETIC ANISOTROPY
MAGNETIC NANOWIRES
topic FERROMAGNETIC RESONANCE
MAGNETIC ANISOTROPY
MAGNETIC NANOWIRES
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.3
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv The magnetic anisotropy of 3-nm wide cobalt nanowires embedded in epitaxial CeO2/SrTiO3(001) layers is investigated by ferromagnetic resonance measurements. The measured magnetic shape and the magnetocrystalline anisotropies confirm that the Co nanowires have their main axes perpendicular to the film surface, and they are composed of hcp Co grains with the c-axes oriented along one of the <111> directions of the CeO2 matrix. The effects of such a peculiar structure on the magnetic anisotropy are addressed experimentally. The results show that the magnetic anisotropy of the wires is dominated by the magnetostatic term. The inhomogeneous structure of the wires leads to an effective magnetocrystalline anisotropy smaller than the bulk value of hcp Co.
Fil: Schio, P.. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Universidade Federal do São Carlos; Brasil
Fil: Barturen, Mariana. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; Argentina
Fil: Milano, Julian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; Argentina
Fil: Bonilla, Jorge Fabián. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina
Fil: Zheng, Y.. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina
Fil: Vidal, F.. Sorbonne University; Francia. Centre National de la Recherche Scientifique; Francia. Universite de Paris VI. Institut des Nanosciences de Paris; Francia. Laboratorio Internacional Franco-Argentino en Nanociencias; Argentina
Fil: De Oliveira, A. J. A.. Universidade Federal do São Carlos; Brasil
description The magnetic anisotropy of 3-nm wide cobalt nanowires embedded in epitaxial CeO2/SrTiO3(001) layers is investigated by ferromagnetic resonance measurements. The measured magnetic shape and the magnetocrystalline anisotropies confirm that the Co nanowires have their main axes perpendicular to the film surface, and they are composed of hcp Co grains with the c-axes oriented along one of the <111> directions of the CeO2 matrix. The effects of such a peculiar structure on the magnetic anisotropy are addressed experimentally. The results show that the magnetic anisotropy of the wires is dominated by the magnetostatic term. The inhomogeneous structure of the wires leads to an effective magnetocrystalline anisotropy smaller than the bulk value of hcp Co.
publishDate 2014
dc.date.none.fl_str_mv 2014-09
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/180515
Schio, P.; Barturen, Mariana; Milano, Julian; Bonilla, Jorge Fabián; Zheng, Y.; et al.; Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study; IOP Publishing; Materials Research Express; 1; 3; 9-2014; 1-12
2053-1591
CONICET Digital
CONICET
url http://hdl.handle.net/11336/180515
identifier_str_mv Schio, P.; Barturen, Mariana; Milano, Julian; Bonilla, Jorge Fabián; Zheng, Y.; et al.; Magnetic anisotropy of 3nm diameter Co nanowires embedded in CeO2/SrTiO3(001): a ferromagnetic resonance study; IOP Publishing; Materials Research Express; 1; 3; 9-2014; 1-12
2053-1591
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://iopscience.iop.org/article/10.1088/2053-1591/1/3/035015
info:eu-repo/semantics/altIdentifier/doi/10.1088/2053-1591/1/3/035015
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv IOP Publishing
publisher.none.fl_str_mv IOP Publishing
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842269514852466688
score 13.13397

Publicaciones similares