Firing transformations of an argentinean calcareous commercial clay
- Autores
- Serra, Maria Florencia; Conconi, María Susana; Suarez, Gustavo; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano
- Año de publicación
- 2013
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- Mineralogical transformations caused by firing are usually studied by XRD methods only semi-quantitatively. In this work the original mineral disappearance and the neo-mineralization were evaluated quantitatively. Furthermore an indirect non crystalline phase quantification was performed under 1100 ºC was also carried out using the quartz content as internal standard. This study specifically discusses the behavior of an Argentinean white calcareous earthenware commercial when subjected to traditional ceramic firing, besides the technological importance of this particular material, it acts as a model for other clay based ceramic materials. Materials were subjected to thermal treatments between 700 ºC and 1100 ºC. A preliminary sintering characterization was carried out by contraction and porosity evolution. Simultaneous thermogravimetric and differential thermal analysis (TG-DTA) was carried out to elucidate the actual temperature at which the chemical changes occur. Finally, a quantitative analysis based on the Rietveld refinement of the X-ray diffraction patterns was performed to characterize the crystalline phases present in both the clay and in the materials obtained after different thermal treatments. The actual chemical reactions are proposed. The phases identified after firing at traditional working temperature (1040 ºC) are quartz, plagioclase, and the Spinel type alumino-silicate, accompanied by the non-diffracting un-reacted metakaolin and some amount of amorphous glassy phase. At intermediate temperatures (900 ºC) the presence of gehlenite was also detected. The carbonates (calcite and dolomite) presence and decomposition were also evaluated and demonstrated to determine the sintering characteristics of this material.
Transformações mineralógicas causadas por queima são estudadas pelo método semiquantitativo de difração de raios X. O desaparecimento do mineral original e o neomineral foram avaliados quantitativamente. Além disso, a quantificação de fase não cristalina foi alcançada acima de 1000 ºC, sendo usado quartzo como padrão. Este estudo descreve um calcário branco argentino comercial, o qual é submetido a uma queima cerâmica tradicional, com base na sua importância tecnológica, ele atua como modelo para outras argilas com base cerâmica. Os materiais foram submetidos a tratamento térmico entre 700 ºC e 1000 ºC. Uma caracterização preliminar da sinterização foi avaliar a evolução da retração e da porosidade. Análise simultânea termogravimétrica e térmica diferencial foi realizada para determinar as temperaturas em que ocorrem mudanças químicas. Finalmente, foi feita uma analise quantitativa com base no refinamento Rietveld dos padrões de difração de raios X, para caracterizar as fases cristalinas na argila e nos materiais obtidos após os tratamentos térmicos. As reações químicas que ocorrem são propostas. As fases identificadas após a queima na temperatura tradicional de trabalho (1040 ºC) são quartzo, plagioclásio, e o espinélio tipo aluminio-silicato, juntamente com metacaulim não detetado e algum teor de fase vítrea. Foi também determinada gehlenita em temperaturas intermediarias (900 ºC). A presença e a decomposição de carbonatos (calcita e dolomita) foram também avaliadas e demonstrada sua atuação nas características da sinterização.
Fil: Serra, Maria Florencia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina
Fil: Conconi, María Susana. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina
Fil: Suarez, Gustavo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina
Fil: Aglietti, Esteban Fausto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina - Materia
-
Ceramica Triaxial
Processamento de Cerâmica de Silicato
Estrutura
Difração de Raios X - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/2171
Ver los metadatos del registro completo
id |
CONICETDig_1fb6c61842ff7ec20d0e51820441c00b |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/2171 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Firing transformations of an argentinean calcareous commercial clayTransformações de queima de uma argila de calcário comercial argentinoSerra, Maria FlorenciaConconi, María SusanaSuarez, GustavoAglietti, Esteban FaustoRendtorff Birrer, Nicolás MaximilianoCeramica TriaxialProcessamento de Cerâmica de SilicatoEstruturaDifração de Raios Xhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Mineralogical transformations caused by firing are usually studied by XRD methods only semi-quantitatively. In this work the original mineral disappearance and the neo-mineralization were evaluated quantitatively. Furthermore an indirect non crystalline phase quantification was performed under 1100 ºC was also carried out using the quartz content as internal standard. This study specifically discusses the behavior of an Argentinean white calcareous earthenware commercial when subjected to traditional ceramic firing, besides the technological importance of this particular material, it acts as a model for other clay based ceramic materials. Materials were subjected to thermal treatments between 700 ºC and 1100 ºC. A preliminary sintering characterization was carried out by contraction and porosity evolution. Simultaneous thermogravimetric and differential thermal analysis (TG-DTA) was carried out to elucidate the actual temperature at which the chemical changes occur. Finally, a quantitative analysis based on the Rietveld refinement of the X-ray diffraction patterns was performed to characterize the crystalline phases present in both the clay and in the materials obtained after different thermal treatments. The actual chemical reactions are proposed. The phases identified after firing at traditional working temperature (1040 ºC) are quartz, plagioclase, and the Spinel type alumino-silicate, accompanied by the non-diffracting un-reacted metakaolin and some amount of amorphous glassy phase. At intermediate temperatures (900 ºC) the presence of gehlenite was also detected. The carbonates (calcite and dolomite) presence and decomposition were also evaluated and demonstrated to determine the sintering characteristics of this material.Transformações mineralógicas causadas por queima são estudadas pelo método semiquantitativo de difração de raios X. O desaparecimento do mineral original e o neomineral foram avaliados quantitativamente. Além disso, a quantificação de fase não cristalina foi alcançada acima de 1000 ºC, sendo usado quartzo como padrão. Este estudo descreve um calcário branco argentino comercial, o qual é submetido a uma queima cerâmica tradicional, com base na sua importância tecnológica, ele atua como modelo para outras argilas com base cerâmica. Os materiais foram submetidos a tratamento térmico entre 700 ºC e 1000 ºC. Uma caracterização preliminar da sinterização foi avaliar a evolução da retração e da porosidade. Análise simultânea termogravimétrica e térmica diferencial foi realizada para determinar as temperaturas em que ocorrem mudanças químicas. Finalmente, foi feita uma analise quantitativa com base no refinamento Rietveld dos padrões de difração de raios X, para caracterizar as fases cristalinas na argila e nos materiais obtidos após os tratamentos térmicos. As reações químicas que ocorrem são propostas. As fases identificadas após a queima na temperatura tradicional de trabalho (1040 ºC) são quartzo, plagioclásio, e o espinélio tipo aluminio-silicato, juntamente com metacaulim não detetado e algum teor de fase vítrea. Foi também determinada gehlenita em temperaturas intermediarias (900 ºC). A presença e a decomposição de carbonatos (calcita e dolomita) foram também avaliadas e demonstrada sua atuação nas características da sinterização.Fil: Serra, Maria Florencia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; ArgentinaFil: Conconi, María Susana. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; ArgentinaFil: Suarez, Gustavo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; ArgentinaFil: Aglietti, Esteban Fausto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; ArgentinaFil: Rendtorff Birrer, Nicolás Maximiliano. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; ArgentinaAssociacao Brasileira de Cerâmica2013-06info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/2171Serra, Maria Florencia; Conconi, María Susana; Suarez, Gustavo; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano; Firing transformations of an argentinean calcareous commercial clay; Associacao Brasileira de Cerâmica; Ceramica; 59; 350; 6-2013; 254-2610366-69131678-4553enginfo:eu-repo/semantics/altIdentifier/url/http://www.scielo.br/scielo.php?pid=S0366-69132013000200010&script=sci_arttextinfo:eu-repo/semantics/altIdentifier/doi/10.1590/S0366-69132013000200010info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:39:01Zoai:ri.conicet.gov.ar:11336/2171instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:39:01.843CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Firing transformations of an argentinean calcareous commercial clay Transformações de queima de uma argila de calcário comercial argentino |
title |
Firing transformations of an argentinean calcareous commercial clay |
spellingShingle |
Firing transformations of an argentinean calcareous commercial clay Serra, Maria Florencia Ceramica Triaxial Processamento de Cerâmica de Silicato Estrutura Difração de Raios X |
title_short |
Firing transformations of an argentinean calcareous commercial clay |
title_full |
Firing transformations of an argentinean calcareous commercial clay |
title_fullStr |
Firing transformations of an argentinean calcareous commercial clay |
title_full_unstemmed |
Firing transformations of an argentinean calcareous commercial clay |
title_sort |
Firing transformations of an argentinean calcareous commercial clay |
dc.creator.none.fl_str_mv |
Serra, Maria Florencia Conconi, María Susana Suarez, Gustavo Aglietti, Esteban Fausto Rendtorff Birrer, Nicolás Maximiliano |
author |
Serra, Maria Florencia |
author_facet |
Serra, Maria Florencia Conconi, María Susana Suarez, Gustavo Aglietti, Esteban Fausto Rendtorff Birrer, Nicolás Maximiliano |
author_role |
author |
author2 |
Conconi, María Susana Suarez, Gustavo Aglietti, Esteban Fausto Rendtorff Birrer, Nicolás Maximiliano |
author2_role |
author author author author |
dc.subject.none.fl_str_mv |
Ceramica Triaxial Processamento de Cerâmica de Silicato Estrutura Difração de Raios X |
topic |
Ceramica Triaxial Processamento de Cerâmica de Silicato Estrutura Difração de Raios X |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
Mineralogical transformations caused by firing are usually studied by XRD methods only semi-quantitatively. In this work the original mineral disappearance and the neo-mineralization were evaluated quantitatively. Furthermore an indirect non crystalline phase quantification was performed under 1100 ºC was also carried out using the quartz content as internal standard. This study specifically discusses the behavior of an Argentinean white calcareous earthenware commercial when subjected to traditional ceramic firing, besides the technological importance of this particular material, it acts as a model for other clay based ceramic materials. Materials were subjected to thermal treatments between 700 ºC and 1100 ºC. A preliminary sintering characterization was carried out by contraction and porosity evolution. Simultaneous thermogravimetric and differential thermal analysis (TG-DTA) was carried out to elucidate the actual temperature at which the chemical changes occur. Finally, a quantitative analysis based on the Rietveld refinement of the X-ray diffraction patterns was performed to characterize the crystalline phases present in both the clay and in the materials obtained after different thermal treatments. The actual chemical reactions are proposed. The phases identified after firing at traditional working temperature (1040 ºC) are quartz, plagioclase, and the Spinel type alumino-silicate, accompanied by the non-diffracting un-reacted metakaolin and some amount of amorphous glassy phase. At intermediate temperatures (900 ºC) the presence of gehlenite was also detected. The carbonates (calcite and dolomite) presence and decomposition were also evaluated and demonstrated to determine the sintering characteristics of this material. Transformações mineralógicas causadas por queima são estudadas pelo método semiquantitativo de difração de raios X. O desaparecimento do mineral original e o neomineral foram avaliados quantitativamente. Além disso, a quantificação de fase não cristalina foi alcançada acima de 1000 ºC, sendo usado quartzo como padrão. Este estudo descreve um calcário branco argentino comercial, o qual é submetido a uma queima cerâmica tradicional, com base na sua importância tecnológica, ele atua como modelo para outras argilas com base cerâmica. Os materiais foram submetidos a tratamento térmico entre 700 ºC e 1000 ºC. Uma caracterização preliminar da sinterização foi avaliar a evolução da retração e da porosidade. Análise simultânea termogravimétrica e térmica diferencial foi realizada para determinar as temperaturas em que ocorrem mudanças químicas. Finalmente, foi feita uma analise quantitativa com base no refinamento Rietveld dos padrões de difração de raios X, para caracterizar as fases cristalinas na argila e nos materiais obtidos após os tratamentos térmicos. As reações químicas que ocorrem são propostas. As fases identificadas após a queima na temperatura tradicional de trabalho (1040 ºC) são quartzo, plagioclásio, e o espinélio tipo aluminio-silicato, juntamente com metacaulim não detetado e algum teor de fase vítrea. Foi também determinada gehlenita em temperaturas intermediarias (900 ºC). A presença e a decomposição de carbonatos (calcita e dolomita) foram também avaliadas e demonstrada sua atuação nas características da sinterização. Fil: Serra, Maria Florencia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina Fil: Conconi, María Susana. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina Fil: Suarez, Gustavo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina Fil: Aglietti, Esteban Fausto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina Fil: Rendtorff Birrer, Nicolás Maximiliano. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico La Plata. Centro Tecnológico de Recursos Minerales y Cerámica (i); Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas; Argentina |
description |
Mineralogical transformations caused by firing are usually studied by XRD methods only semi-quantitatively. In this work the original mineral disappearance and the neo-mineralization were evaluated quantitatively. Furthermore an indirect non crystalline phase quantification was performed under 1100 ºC was also carried out using the quartz content as internal standard. This study specifically discusses the behavior of an Argentinean white calcareous earthenware commercial when subjected to traditional ceramic firing, besides the technological importance of this particular material, it acts as a model for other clay based ceramic materials. Materials were subjected to thermal treatments between 700 ºC and 1100 ºC. A preliminary sintering characterization was carried out by contraction and porosity evolution. Simultaneous thermogravimetric and differential thermal analysis (TG-DTA) was carried out to elucidate the actual temperature at which the chemical changes occur. Finally, a quantitative analysis based on the Rietveld refinement of the X-ray diffraction patterns was performed to characterize the crystalline phases present in both the clay and in the materials obtained after different thermal treatments. The actual chemical reactions are proposed. The phases identified after firing at traditional working temperature (1040 ºC) are quartz, plagioclase, and the Spinel type alumino-silicate, accompanied by the non-diffracting un-reacted metakaolin and some amount of amorphous glassy phase. At intermediate temperatures (900 ºC) the presence of gehlenite was also detected. The carbonates (calcite and dolomite) presence and decomposition were also evaluated and demonstrated to determine the sintering characteristics of this material. |
publishDate |
2013 |
dc.date.none.fl_str_mv |
2013-06 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/2171 Serra, Maria Florencia; Conconi, María Susana; Suarez, Gustavo; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano; Firing transformations of an argentinean calcareous commercial clay; Associacao Brasileira de Cerâmica; Ceramica; 59; 350; 6-2013; 254-261 0366-6913 1678-4553 |
url |
http://hdl.handle.net/11336/2171 |
identifier_str_mv |
Serra, Maria Florencia; Conconi, María Susana; Suarez, Gustavo; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano; Firing transformations of an argentinean calcareous commercial clay; Associacao Brasileira de Cerâmica; Ceramica; 59; 350; 6-2013; 254-261 0366-6913 1678-4553 |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/url/http://www.scielo.br/scielo.php?pid=S0366-69132013000200010&script=sci_arttext info:eu-repo/semantics/altIdentifier/doi/10.1590/S0366-69132013000200010 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Associacao Brasileira de Cerâmica |
publisher.none.fl_str_mv |
Associacao Brasileira de Cerâmica |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844614414416740352 |
score |
13.070432 |