Firing transformations of an argentinean calcareous commercial clay
- Autores
- Serra, Maria Florencia; Conconi, María Susana; Suárez, Gustavo; Aglietti, Esteban Fausto; Rendtorff Birrer, Nicolás Maximiliano
- Año de publicación
- 2013
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- Mineralogical transformations caused by firing are usually studied by XRD methods only semi-quantitatively. In this work the original mineral disappearance and the neo-mineralization were evaluated quantitatively. Furthermore an indirect non crystalline phase quantification was performed under 1100 ºC was also carried out using the quartz content as internal standard. This study specifically discusses the behavior of an Argentinean white calcareous earthenware commercial when subjected to traditional ceramic firing, besides the technological importance of this particular material, it acts as a model for other clay based ceramic materials. Materials were subjected to thermal treatments between 700 ºC and 1100 ºC. A preliminary sintering characterization was carried out by contraction and porosity evolution. Simultaneous thermogravimetric and differential thermal analysis (TG-DTA) was carried out to elucidate the actual temperature at which the chemical changes occur. Finally, a quantitative analysis based on the Rietveld refinement of the X-ray diffraction patterns was performed to characterize the crystalline phases present in both the clay and in the materials obtained after different thermal treatments. The actual chemical reactions are proposed. The phases identified after firing at traditional working temperature (1040 ºC) are quartz, plagioclase, and the Spinel type alumino-silicate, accompanied by the non-diffracting un-reacted metakaolin and some amount of amorphous glassy phase. At intermediate temperatures (900 ºC) the presence of gehlenite was also detected. The carbonates (calcite and dolomite) presence and decomposition were also evaluated and demonstrated to determine the sintering characteristics of this material.
Transformações mineralógicas causadas por queima são estudadas pelo método semiquantitativo de difração de raios X. O desaparecimento do mineral original e o neomineral foram avaliados quantitativamente. Além disso, a quantificação de fase não cristalina foi alcançada acima de 1000 ºC, sendo usado quartzo como padrão. Este estudo descreve um calcário branco argentino comercial, o qual é submetido a uma queima cerâmica tradicional, com base na sua importância tecnológica, ele atua como modelo para outras argilas com base cerâmica. Os materiais foram submetidos a tratamento térmico entre 700 ºC e 1000 ºC. Uma caracterização preliminar da sinterização foi avaliar a evolução da retração e da porosidade. Análise simultânea termogravimétrica e térmica diferencial foi realizada para determinar as temperaturas em que ocorrem mudanças químicas. Finalmente, foi feita uma analise quantitativa com base no refinamento Rietveld dos padrões de difração de raios X, para caracterizar as fases cristalinas na argila e nos materiais obtidos após os tratamentos térmicos. As reações químicas que ocorrem são propostas. As fases identificadas após a queima na temperatura tradicional de trabalho (1040 ºC) são quartzo, plagioclásio, e o espinélio tipo aluminio-silicato, juntamente com metacaulim não detetado e algum teor de fase vítrea. Foi também determinada gehlenita em temperaturas intermediarias (900 ºC). A presença e a decomposição de carbonatos (calcita e dolomita) foram também avaliadas e demonstrada sua atuação nas características da sinterização. - Materia
-
Cerámicos
silicate ceramic processing
structure
X-ray diffraction - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- http://creativecommons.org/licenses/by-nc/4.0/
- Repositorio
- Institución
- Comisión de Investigaciones Científicas de la Provincia de Buenos Aires
- OAI Identificador
- oai:digital.cic.gba.gob.ar:11746/5877
Ver los metadatos del registro completo
id |
CICBA_d16c146b925cb086b5890c88fbf67e5c |
---|---|
oai_identifier_str |
oai:digital.cic.gba.gob.ar:11746/5877 |
network_acronym_str |
CICBA |
repository_id_str |
9441 |
network_name_str |
CIC Digital (CICBA) |
spelling |
Firing transformations of an argentinean calcareous commercial claySerra, Maria FlorenciaConconi, María SusanaSuárez, GustavoAglietti, Esteban FaustoRendtorff Birrer, Nicolás MaximilianoCerámicossilicate ceramic processingstructureX-ray diffractionMineralogical transformations caused by firing are usually studied by XRD methods only semi-quantitatively. In this work the original mineral disappearance and the neo-mineralization were evaluated quantitatively. Furthermore an indirect non crystalline phase quantification was performed under 1100 ºC was also carried out using the quartz content as internal standard. This study specifically discusses the behavior of an Argentinean white calcareous earthenware commercial when subjected to traditional ceramic firing, besides the technological importance of this particular material, it acts as a model for other clay based ceramic materials. Materials were subjected to thermal treatments between 700 ºC and 1100 ºC. A preliminary sintering characterization was carried out by contraction and porosity evolution. Simultaneous thermogravimetric and differential thermal analysis (TG-DTA) was carried out to elucidate the actual temperature at which the chemical changes occur. Finally, a quantitative analysis based on the Rietveld refinement of the X-ray diffraction patterns was performed to characterize the crystalline phases present in both the clay and in the materials obtained after different thermal treatments. The actual chemical reactions are proposed. The phases identified after firing at traditional working temperature (1040 ºC) are quartz, plagioclase, and the Spinel type alumino-silicate, accompanied by the non-diffracting un-reacted metakaolin and some amount of amorphous glassy phase. At intermediate temperatures (900 ºC) the presence of gehlenite was also detected. The carbonates (calcite and dolomite) presence and decomposition were also evaluated and demonstrated to determine the sintering characteristics of this material.Transformações mineralógicas causadas por queima são estudadas pelo método semiquantitativo de difração de raios X. O desaparecimento do mineral original e o neomineral foram avaliados quantitativamente. Além disso, a quantificação de fase não cristalina foi alcançada acima de 1000 ºC, sendo usado quartzo como padrão. Este estudo descreve um calcário branco argentino comercial, o qual é submetido a uma queima cerâmica tradicional, com base na sua importância tecnológica, ele atua como modelo para outras argilas com base cerâmica. Os materiais foram submetidos a tratamento térmico entre 700 ºC e 1000 ºC. Uma caracterização preliminar da sinterização foi avaliar a evolução da retração e da porosidade. Análise simultânea termogravimétrica e térmica diferencial foi realizada para determinar as temperaturas em que ocorrem mudanças químicas. Finalmente, foi feita uma analise quantitativa com base no refinamento Rietveld dos padrões de difração de raios X, para caracterizar as fases cristalinas na argila e nos materiais obtidos após os tratamentos térmicos. As reações químicas que ocorrem são propostas. As fases identificadas após a queima na temperatura tradicional de trabalho (1040 ºC) são quartzo, plagioclásio, e o espinélio tipo aluminio-silicato, juntamente com metacaulim não detetado e algum teor de fase vítrea. Foi também determinada gehlenita em temperaturas intermediarias (900 ºC). A presença e a decomposição de carbonatos (calcita e dolomita) foram também avaliadas e demonstrada sua atuação nas características da sinterização.Associacao Brasileira de Cerâmica2013-06info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfhttps://digital.cic.gba.gob.ar/handle/11746/5877enginfo:eu-repo/semantics/altIdentifier/issn/1678-4553info:eu-repo/semantics/openAccesshttp://creativecommons.org/licenses/by-nc/4.0/reponame:CIC Digital (CICBA)instname:Comisión de Investigaciones Científicas de la Provincia de Buenos Airesinstacron:CICBA2025-09-29T13:40:07Zoai:digital.cic.gba.gob.ar:11746/5877Institucionalhttp://digital.cic.gba.gob.arOrganismo científico-tecnológicoNo correspondehttp://digital.cic.gba.gob.ar/oai/snrdmarisa.degiusti@sedici.unlp.edu.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:94412025-09-29 13:40:08.024CIC Digital (CICBA) - Comisión de Investigaciones Científicas de la Provincia de Buenos Airesfalse |
dc.title.none.fl_str_mv |
Firing transformations of an argentinean calcareous commercial clay |
title |
Firing transformations of an argentinean calcareous commercial clay |
spellingShingle |
Firing transformations of an argentinean calcareous commercial clay Serra, Maria Florencia Cerámicos silicate ceramic processing structure X-ray diffraction |
title_short |
Firing transformations of an argentinean calcareous commercial clay |
title_full |
Firing transformations of an argentinean calcareous commercial clay |
title_fullStr |
Firing transformations of an argentinean calcareous commercial clay |
title_full_unstemmed |
Firing transformations of an argentinean calcareous commercial clay |
title_sort |
Firing transformations of an argentinean calcareous commercial clay |
dc.creator.none.fl_str_mv |
Serra, Maria Florencia Conconi, María Susana Suárez, Gustavo Aglietti, Esteban Fausto Rendtorff Birrer, Nicolás Maximiliano |
author |
Serra, Maria Florencia |
author_facet |
Serra, Maria Florencia Conconi, María Susana Suárez, Gustavo Aglietti, Esteban Fausto Rendtorff Birrer, Nicolás Maximiliano |
author_role |
author |
author2 |
Conconi, María Susana Suárez, Gustavo Aglietti, Esteban Fausto Rendtorff Birrer, Nicolás Maximiliano |
author2_role |
author author author author |
dc.subject.none.fl_str_mv |
Cerámicos silicate ceramic processing structure X-ray diffraction |
topic |
Cerámicos silicate ceramic processing structure X-ray diffraction |
dc.description.none.fl_txt_mv |
Mineralogical transformations caused by firing are usually studied by XRD methods only semi-quantitatively. In this work the original mineral disappearance and the neo-mineralization were evaluated quantitatively. Furthermore an indirect non crystalline phase quantification was performed under 1100 ºC was also carried out using the quartz content as internal standard. This study specifically discusses the behavior of an Argentinean white calcareous earthenware commercial when subjected to traditional ceramic firing, besides the technological importance of this particular material, it acts as a model for other clay based ceramic materials. Materials were subjected to thermal treatments between 700 ºC and 1100 ºC. A preliminary sintering characterization was carried out by contraction and porosity evolution. Simultaneous thermogravimetric and differential thermal analysis (TG-DTA) was carried out to elucidate the actual temperature at which the chemical changes occur. Finally, a quantitative analysis based on the Rietveld refinement of the X-ray diffraction patterns was performed to characterize the crystalline phases present in both the clay and in the materials obtained after different thermal treatments. The actual chemical reactions are proposed. The phases identified after firing at traditional working temperature (1040 ºC) are quartz, plagioclase, and the Spinel type alumino-silicate, accompanied by the non-diffracting un-reacted metakaolin and some amount of amorphous glassy phase. At intermediate temperatures (900 ºC) the presence of gehlenite was also detected. The carbonates (calcite and dolomite) presence and decomposition were also evaluated and demonstrated to determine the sintering characteristics of this material. Transformações mineralógicas causadas por queima são estudadas pelo método semiquantitativo de difração de raios X. O desaparecimento do mineral original e o neomineral foram avaliados quantitativamente. Além disso, a quantificação de fase não cristalina foi alcançada acima de 1000 ºC, sendo usado quartzo como padrão. Este estudo descreve um calcário branco argentino comercial, o qual é submetido a uma queima cerâmica tradicional, com base na sua importância tecnológica, ele atua como modelo para outras argilas com base cerâmica. Os materiais foram submetidos a tratamento térmico entre 700 ºC e 1000 ºC. Uma caracterização preliminar da sinterização foi avaliar a evolução da retração e da porosidade. Análise simultânea termogravimétrica e térmica diferencial foi realizada para determinar as temperaturas em que ocorrem mudanças químicas. Finalmente, foi feita uma analise quantitativa com base no refinamento Rietveld dos padrões de difração de raios X, para caracterizar as fases cristalinas na argila e nos materiais obtidos após os tratamentos térmicos. As reações químicas que ocorrem são propostas. As fases identificadas após a queima na temperatura tradicional de trabalho (1040 ºC) são quartzo, plagioclásio, e o espinélio tipo aluminio-silicato, juntamente com metacaulim não detetado e algum teor de fase vítrea. Foi também determinada gehlenita em temperaturas intermediarias (900 ºC). A presença e a decomposição de carbonatos (calcita e dolomita) foram também avaliadas e demonstrada sua atuação nas características da sinterização. |
description |
Mineralogical transformations caused by firing are usually studied by XRD methods only semi-quantitatively. In this work the original mineral disappearance and the neo-mineralization were evaluated quantitatively. Furthermore an indirect non crystalline phase quantification was performed under 1100 ºC was also carried out using the quartz content as internal standard. This study specifically discusses the behavior of an Argentinean white calcareous earthenware commercial when subjected to traditional ceramic firing, besides the technological importance of this particular material, it acts as a model for other clay based ceramic materials. Materials were subjected to thermal treatments between 700 ºC and 1100 ºC. A preliminary sintering characterization was carried out by contraction and porosity evolution. Simultaneous thermogravimetric and differential thermal analysis (TG-DTA) was carried out to elucidate the actual temperature at which the chemical changes occur. Finally, a quantitative analysis based on the Rietveld refinement of the X-ray diffraction patterns was performed to characterize the crystalline phases present in both the clay and in the materials obtained after different thermal treatments. The actual chemical reactions are proposed. The phases identified after firing at traditional working temperature (1040 ºC) are quartz, plagioclase, and the Spinel type alumino-silicate, accompanied by the non-diffracting un-reacted metakaolin and some amount of amorphous glassy phase. At intermediate temperatures (900 ºC) the presence of gehlenite was also detected. The carbonates (calcite and dolomite) presence and decomposition were also evaluated and demonstrated to determine the sintering characteristics of this material. |
publishDate |
2013 |
dc.date.none.fl_str_mv |
2013-06 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
https://digital.cic.gba.gob.ar/handle/11746/5877 |
url |
https://digital.cic.gba.gob.ar/handle/11746/5877 |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/issn/1678-4553 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess http://creativecommons.org/licenses/by-nc/4.0/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
http://creativecommons.org/licenses/by-nc/4.0/ |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Associacao Brasileira de Cerâmica |
publisher.none.fl_str_mv |
Associacao Brasileira de Cerâmica |
dc.source.none.fl_str_mv |
reponame:CIC Digital (CICBA) instname:Comisión de Investigaciones Científicas de la Provincia de Buenos Aires instacron:CICBA |
reponame_str |
CIC Digital (CICBA) |
collection |
CIC Digital (CICBA) |
instname_str |
Comisión de Investigaciones Científicas de la Provincia de Buenos Aires |
instacron_str |
CICBA |
institution |
CICBA |
repository.name.fl_str_mv |
CIC Digital (CICBA) - Comisión de Investigaciones Científicas de la Provincia de Buenos Aires |
repository.mail.fl_str_mv |
marisa.degiusti@sedici.unlp.edu.ar |
_version_ |
1844618602101080064 |
score |
13.070432 |