Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria

Autores
Poggio Fraccari, Eduardo Arístides; Mariño, Fernando Javier; Sorbello, Cecilia; Jobbagy, Matias
Año de publicación
2018
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
The activity of several lanthanide promoted Ceria in CO oxidation was studied. Samples were obtained by a high yield and sustainable method by urea thermal decomposition. Precursors basic carbonates,Ce1-xLnx(OH)CO3, being Ln = La (III), Sm(III), Gd(III), Pr(III) were prepared in the range of compositions 0 to 30 at.%.These precursors were annealed to moderate temperature obtain Ln-Ce mixed oxides, at 450ºC. These exhibit large surface areas up to 120 m2/g. Their catalytic performance revealed good activity towards CO oxidation (COOX) forall samples. However, a different behavior may be observed for Ln content higher than 20 at.%. By the reactor operation in differential conditions, the activation energy for COOX were obtained for all samples. The rise ofactivation energy as a function of Ln(III-IV) content is analyzed in the frame of phase stability and surface segregation
Fil: Poggio Fraccari, Eduardo Arístides. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles. Universidad de Buenos Aires. Facultad de Ingeniería. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles; Argentina
Fil: Mariño, Fernando Javier. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles. Universidad de Buenos Aires. Facultad de Ingeniería. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles; Argentina
Fil: Sorbello, Cecilia. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina
Fil: Jobbagy, Matias. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina
Materia
CERIUM
LANTHANIDES
CARBON MONOXIDE
OXIDATION
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/113393
Acceder
id CONICETDig_1e8d689a88c47820ede503a549c5e98d
oai_identifier_str oai:ri.conicet.gov.ar:11336/113393
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceriaPoggio Fraccari, Eduardo ArístidesMariño, Fernando JavierSorbello, CeciliaJobbagy, MatiasCERIUMLANTHANIDESCARBON MONOXIDEOXIDATIONhttps://purl.org/becyt/ford/2.4https://purl.org/becyt/ford/2https://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2The activity of several lanthanide promoted Ceria in CO oxidation was studied. Samples were obtained by a high yield and sustainable method by urea thermal decomposition. Precursors basic carbonates,Ce1-xLnx(OH)CO3, being Ln = La (III), Sm(III), Gd(III), Pr(III) were prepared in the range of compositions 0 to 30 at.%.These precursors were annealed to moderate temperature obtain Ln-Ce mixed oxides, at 450ºC. These exhibit large surface areas up to 120 m2/g. Their catalytic performance revealed good activity towards CO oxidation (COOX) forall samples. However, a different behavior may be observed for Ln content higher than 20 at.%. By the reactor operation in differential conditions, the activation energy for COOX were obtained for all samples. The rise ofactivation energy as a function of Ln(III-IV) content is analyzed in the frame of phase stability and surface segregationFil: Poggio Fraccari, Eduardo Arístides. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles. Universidad de Buenos Aires. Facultad de Ingeniería. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles; ArgentinaFil: Mariño, Fernando Javier. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles. Universidad de Buenos Aires. Facultad de Ingeniería. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles; ArgentinaFil: Sorbello, Cecilia. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; ArgentinaFil: Jobbagy, Matias. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; ArgentinaWhioce Publishing2018-06info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/113393Poggio Fraccari, Eduardo Arístides; Mariño, Fernando Javier; Sorbello, Cecilia; Jobbagy, Matias; Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria; Whioce Publishing; Materials Science: Materials Review; 6-20182529-7791CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.18063/msmr.v2i3.950info:eu-repo/semantics/altIdentifier/url/http://ojs.whioce.com/index.php/msmr/article/view/950info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-10T13:24:05Zoai:ri.conicet.gov.ar:11336/113393instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-10 13:24:05.832CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria
title Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria
spellingShingle Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria
Poggio Fraccari, Eduardo Arístides
CERIUM
LANTHANIDES
CARBON MONOXIDE
OXIDATION
title_short Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria
title_full Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria
title_fullStr Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria
title_full_unstemmed Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria
title_sort Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria
dc.creator.none.fl_str_mv Poggio Fraccari, Eduardo Arístides
Mariño, Fernando Javier
Sorbello, Cecilia
Jobbagy, Matias
author Poggio Fraccari, Eduardo Arístides
author_facet Poggio Fraccari, Eduardo Arístides
Mariño, Fernando Javier
Sorbello, Cecilia
Jobbagy, Matias
author_role author
author2 Mariño, Fernando Javier
Sorbello, Cecilia
Jobbagy, Matias
author2_role author
author
author
dc.subject.none.fl_str_mv CERIUM
LANTHANIDES
CARBON MONOXIDE
OXIDATION
topic CERIUM
LANTHANIDES
CARBON MONOXIDE
OXIDATION
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.4
https://purl.org/becyt/ford/2
https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv The activity of several lanthanide promoted Ceria in CO oxidation was studied. Samples were obtained by a high yield and sustainable method by urea thermal decomposition. Precursors basic carbonates,Ce1-xLnx(OH)CO3, being Ln = La (III), Sm(III), Gd(III), Pr(III) were prepared in the range of compositions 0 to 30 at.%.These precursors were annealed to moderate temperature obtain Ln-Ce mixed oxides, at 450ºC. These exhibit large surface areas up to 120 m2/g. Their catalytic performance revealed good activity towards CO oxidation (COOX) forall samples. However, a different behavior may be observed for Ln content higher than 20 at.%. By the reactor operation in differential conditions, the activation energy for COOX were obtained for all samples. The rise ofactivation energy as a function of Ln(III-IV) content is analyzed in the frame of phase stability and surface segregation
Fil: Poggio Fraccari, Eduardo Arístides. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles. Universidad de Buenos Aires. Facultad de Ingeniería. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles; Argentina
Fil: Mariño, Fernando Javier. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles. Universidad de Buenos Aires. Facultad de Ingeniería. Instituto de Tecnologías del Hidrogeno y Energias Sostenibles; Argentina
Fil: Sorbello, Cecilia. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina
Fil: Jobbagy, Matias. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina
description The activity of several lanthanide promoted Ceria in CO oxidation was studied. Samples were obtained by a high yield and sustainable method by urea thermal decomposition. Precursors basic carbonates,Ce1-xLnx(OH)CO3, being Ln = La (III), Sm(III), Gd(III), Pr(III) were prepared in the range of compositions 0 to 30 at.%.These precursors were annealed to moderate temperature obtain Ln-Ce mixed oxides, at 450ºC. These exhibit large surface areas up to 120 m2/g. Their catalytic performance revealed good activity towards CO oxidation (COOX) forall samples. However, a different behavior may be observed for Ln content higher than 20 at.%. By the reactor operation in differential conditions, the activation energy for COOX were obtained for all samples. The rise ofactivation energy as a function of Ln(III-IV) content is analyzed in the frame of phase stability and surface segregation
publishDate 2018
dc.date.none.fl_str_mv 2018-06
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/113393
Poggio Fraccari, Eduardo Arístides; Mariño, Fernando Javier; Sorbello, Cecilia; Jobbagy, Matias; Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria; Whioce Publishing; Materials Science: Materials Review; 6-2018
2529-7791
CONICET Digital
CONICET
url http://hdl.handle.net/11336/113393
identifier_str_mv Poggio Fraccari, Eduardo Arístides; Mariño, Fernando Javier; Sorbello, Cecilia; Jobbagy, Matias; Catalytic performance of Ce1-xLnxOy of nanocrystalline Ln (III-IV)-substituted ceria; Whioce Publishing; Materials Science: Materials Review; 6-2018
2529-7791
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.18063/msmr.v2i3.950
info:eu-repo/semantics/altIdentifier/url/http://ojs.whioce.com/index.php/msmr/article/view/950
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Whioce Publishing
publisher.none.fl_str_mv Whioce Publishing
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842981334276898816
score 12.48226

Publicaciones similares