Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting

Autores
Pozo Lopez, Gabriela del Valle; Condo, Adriana Maria; Limandri, Silvina Paola; Mutal, Ruben Hector; Winkler, Elin Lilian; Urreta, Silvia Elena; Fabietti, Luis Maria Rodolfo
Año de publicación
2019
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Ni2MnGa cylinders and tubes are solidified in water chilled copper molds, a few millimeters in external diameter and 5 cm long, by the suction casting technique. At room temperature, all samples are in cubic austenitic phase. Microstructure and crystallographic texture of the as-cast rods and tubes are characterized by XRD, SEM, EBSD and TEM. Because of the heat extraction geometry samples exhibit a strong texture, with the [100] direction preferentially oriented in the radial direction, together with a random distribution on the long axis. This texture is more marked in the tubes. XRD and TEM results indicate that the major austenitic phase is fcc, with L21 order. A minority volume of the equilibrium B2′ disordered phase is detected by the presence of two close Curie temperatures in cylinders and tubes 2 mm in external diameter, but not when this diameter is near 1 mm. Precipitates of the stable compounds α-Mn(S,Se), with a NaCl-type structure, and monoclinic P4S5 are observed in all the samples. Cylinders and tubes in austenitic phase are magnetically soft. Hysteresis loops in martensitic phase exhibit local steps associated to a magnetization mechanism involving twin boundary displacement, indicating that a field-induced variant reordering takes place. The switching field Hsw, corresponding to the magnetization step observed, is identified as the field at which twin boundaries become mobile. The measured values of 0.37 T–0.49 T are consistent with those corresponding to the onset of Type I twin boundaries displacement in 5 M martensite, with an equivalent threshold stress of 1 MP.
Fil: Pozo Lopez, Gabriela del Valle. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; Argentina
Fil: Condo, Adriana Maria. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comision Nacional de Energía Atómica. Gerencia de Área Investigaciones y Aplicaciones no Nucleares. Gerencia de Física (Centro Atómico Bariloche). División Física de Metales; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina
Fil: Limandri, Silvina Paola. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; Argentina
Fil: Mutal, Ruben Hector. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; Argentina
Fil: Winkler, Elin Lilian. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comision Nacional de Energía Atómica. Gerencia de Área Investigaciones y Aplicaciones no Nucleares. Gerencia de Física (Centro Atómico Bariloche). División Resonancias Magnéticas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina
Fil: Urreta, Silvia Elena. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; Argentina
Fil: Fabietti, Luis Maria Rodolfo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; Argentina
Materia
FERROMAGNETIC SHAPE–MEMORY ALLOYS
MAGNETIC PROPERTIES
MARTENSITIC TRANSFORMATION
MICROSTRUCTURE
NI2MNGA
SUCTION CASTING
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/124379
Acceder
id CONICETDig_033af3e1fe7b482ed245e407963692d6
oai_identifier_str oai:ri.conicet.gov.ar:11336/124379
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction castingPozo Lopez, Gabriela del ValleCondo, Adriana MariaLimandri, Silvina PaolaMutal, Ruben HectorWinkler, Elin LilianUrreta, Silvia ElenaFabietti, Luis Maria RodolfoFERROMAGNETIC SHAPE–MEMORY ALLOYSMAGNETIC PROPERTIESMARTENSITIC TRANSFORMATIONMICROSTRUCTURENI2MNGASUCTION CASTINGhttps://purl.org/becyt/ford/1.3https://purl.org/becyt/ford/1Ni2MnGa cylinders and tubes are solidified in water chilled copper molds, a few millimeters in external diameter and 5 cm long, by the suction casting technique. At room temperature, all samples are in cubic austenitic phase. Microstructure and crystallographic texture of the as-cast rods and tubes are characterized by XRD, SEM, EBSD and TEM. Because of the heat extraction geometry samples exhibit a strong texture, with the [100] direction preferentially oriented in the radial direction, together with a random distribution on the long axis. This texture is more marked in the tubes. XRD and TEM results indicate that the major austenitic phase is fcc, with L21 order. A minority volume of the equilibrium B2′ disordered phase is detected by the presence of two close Curie temperatures in cylinders and tubes 2 mm in external diameter, but not when this diameter is near 1 mm. Precipitates of the stable compounds α-Mn(S,Se), with a NaCl-type structure, and monoclinic P4S5 are observed in all the samples. Cylinders and tubes in austenitic phase are magnetically soft. Hysteresis loops in martensitic phase exhibit local steps associated to a magnetization mechanism involving twin boundary displacement, indicating that a field-induced variant reordering takes place. The switching field Hsw, corresponding to the magnetization step observed, is identified as the field at which twin boundaries become mobile. The measured values of 0.37 T–0.49 T are consistent with those corresponding to the onset of Type I twin boundaries displacement in 5 M martensite, with an equivalent threshold stress of 1 MP.Fil: Pozo Lopez, Gabriela del Valle. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; ArgentinaFil: Condo, Adriana Maria. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comision Nacional de Energía Atómica. Gerencia de Área Investigaciones y Aplicaciones no Nucleares. Gerencia de Física (Centro Atómico Bariloche). División Física de Metales; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; ArgentinaFil: Limandri, Silvina Paola. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; ArgentinaFil: Mutal, Ruben Hector. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; ArgentinaFil: Winkler, Elin Lilian. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comision Nacional de Energía Atómica. Gerencia de Área Investigaciones y Aplicaciones no Nucleares. Gerencia de Física (Centro Atómico Bariloche). División Resonancias Magnéticas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; ArgentinaFil: Urreta, Silvia Elena. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; ArgentinaFil: Fabietti, Luis Maria Rodolfo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; ArgentinaElsevier Science Inc2019-12info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/124379Pozo Lopez, Gabriela del Valle; Condo, Adriana Maria; Limandri, Silvina Paola; Mutal, Ruben Hector; Winkler, Elin Lilian; et al.; Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting; Elsevier Science Inc; Materials Characterization; 158; 12-2019; 1-35; 1099561044-5803CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/abs/pii/S1044580319322557info:eu-repo/semantics/altIdentifier/doi/10.1016/j.matchar.2019.109956info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T09:55:21Zoai:ri.conicet.gov.ar:11336/124379instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 09:55:22.146CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting
title Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting
spellingShingle Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting
Pozo Lopez, Gabriela del Valle
FERROMAGNETIC SHAPE–MEMORY ALLOYS
MAGNETIC PROPERTIES
MARTENSITIC TRANSFORMATION
MICROSTRUCTURE
NI2MNGA
SUCTION CASTING
title_short Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting
title_full Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting
title_fullStr Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting
title_full_unstemmed Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting
title_sort Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting
dc.creator.none.fl_str_mv Pozo Lopez, Gabriela del Valle
Condo, Adriana Maria
Limandri, Silvina Paola
Mutal, Ruben Hector
Winkler, Elin Lilian
Urreta, Silvia Elena
Fabietti, Luis Maria Rodolfo
author Pozo Lopez, Gabriela del Valle
author_facet Pozo Lopez, Gabriela del Valle
Condo, Adriana Maria
Limandri, Silvina Paola
Mutal, Ruben Hector
Winkler, Elin Lilian
Urreta, Silvia Elena
Fabietti, Luis Maria Rodolfo
author_role author
author2 Condo, Adriana Maria
Limandri, Silvina Paola
Mutal, Ruben Hector
Winkler, Elin Lilian
Urreta, Silvia Elena
Fabietti, Luis Maria Rodolfo
author2_role author
author
author
author
author
author
dc.subject.none.fl_str_mv FERROMAGNETIC SHAPE–MEMORY ALLOYS
MAGNETIC PROPERTIES
MARTENSITIC TRANSFORMATION
MICROSTRUCTURE
NI2MNGA
SUCTION CASTING
topic FERROMAGNETIC SHAPE–MEMORY ALLOYS
MAGNETIC PROPERTIES
MARTENSITIC TRANSFORMATION
MICROSTRUCTURE
NI2MNGA
SUCTION CASTING
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.3
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv Ni2MnGa cylinders and tubes are solidified in water chilled copper molds, a few millimeters in external diameter and 5 cm long, by the suction casting technique. At room temperature, all samples are in cubic austenitic phase. Microstructure and crystallographic texture of the as-cast rods and tubes are characterized by XRD, SEM, EBSD and TEM. Because of the heat extraction geometry samples exhibit a strong texture, with the [100] direction preferentially oriented in the radial direction, together with a random distribution on the long axis. This texture is more marked in the tubes. XRD and TEM results indicate that the major austenitic phase is fcc, with L21 order. A minority volume of the equilibrium B2′ disordered phase is detected by the presence of two close Curie temperatures in cylinders and tubes 2 mm in external diameter, but not when this diameter is near 1 mm. Precipitates of the stable compounds α-Mn(S,Se), with a NaCl-type structure, and monoclinic P4S5 are observed in all the samples. Cylinders and tubes in austenitic phase are magnetically soft. Hysteresis loops in martensitic phase exhibit local steps associated to a magnetization mechanism involving twin boundary displacement, indicating that a field-induced variant reordering takes place. The switching field Hsw, corresponding to the magnetization step observed, is identified as the field at which twin boundaries become mobile. The measured values of 0.37 T–0.49 T are consistent with those corresponding to the onset of Type I twin boundaries displacement in 5 M martensite, with an equivalent threshold stress of 1 MP.
Fil: Pozo Lopez, Gabriela del Valle. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; Argentina
Fil: Condo, Adriana Maria. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comision Nacional de Energía Atómica. Gerencia de Área Investigaciones y Aplicaciones no Nucleares. Gerencia de Física (Centro Atómico Bariloche). División Física de Metales; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina
Fil: Limandri, Silvina Paola. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; Argentina
Fil: Mutal, Ruben Hector. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; Argentina
Fil: Winkler, Elin Lilian. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comision Nacional de Energía Atómica. Gerencia de Área Investigaciones y Aplicaciones no Nucleares. Gerencia de Física (Centro Atómico Bariloche). División Resonancias Magnéticas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina
Fil: Urreta, Silvia Elena. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; Argentina
Fil: Fabietti, Luis Maria Rodolfo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Instituto de Física Enrique Gaviola. Universidad Nacional de Córdoba. Instituto de Física Enrique Gaviola; Argentina. Universidad Nacional de Córdoba. Facultad de Matemática, Astronomía y Física; Argentina
description Ni2MnGa cylinders and tubes are solidified in water chilled copper molds, a few millimeters in external diameter and 5 cm long, by the suction casting technique. At room temperature, all samples are in cubic austenitic phase. Microstructure and crystallographic texture of the as-cast rods and tubes are characterized by XRD, SEM, EBSD and TEM. Because of the heat extraction geometry samples exhibit a strong texture, with the [100] direction preferentially oriented in the radial direction, together with a random distribution on the long axis. This texture is more marked in the tubes. XRD and TEM results indicate that the major austenitic phase is fcc, with L21 order. A minority volume of the equilibrium B2′ disordered phase is detected by the presence of two close Curie temperatures in cylinders and tubes 2 mm in external diameter, but not when this diameter is near 1 mm. Precipitates of the stable compounds α-Mn(S,Se), with a NaCl-type structure, and monoclinic P4S5 are observed in all the samples. Cylinders and tubes in austenitic phase are magnetically soft. Hysteresis loops in martensitic phase exhibit local steps associated to a magnetization mechanism involving twin boundary displacement, indicating that a field-induced variant reordering takes place. The switching field Hsw, corresponding to the magnetization step observed, is identified as the field at which twin boundaries become mobile. The measured values of 0.37 T–0.49 T are consistent with those corresponding to the onset of Type I twin boundaries displacement in 5 M martensite, with an equivalent threshold stress of 1 MP.
publishDate 2019
dc.date.none.fl_str_mv 2019-12
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/124379
Pozo Lopez, Gabriela del Valle; Condo, Adriana Maria; Limandri, Silvina Paola; Mutal, Ruben Hector; Winkler, Elin Lilian; et al.; Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting; Elsevier Science Inc; Materials Characterization; 158; 12-2019; 1-35; 109956
1044-5803
CONICET Digital
CONICET
url http://hdl.handle.net/11336/124379
identifier_str_mv Pozo Lopez, Gabriela del Valle; Condo, Adriana Maria; Limandri, Silvina Paola; Mutal, Ruben Hector; Winkler, Elin Lilian; et al.; Microstructure and magnetic properties of as-cast Ni2MnGa rods and tubes solidified by suction casting; Elsevier Science Inc; Materials Characterization; 158; 12-2019; 1-35; 109956
1044-5803
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/abs/pii/S1044580319322557
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.matchar.2019.109956
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier Science Inc
publisher.none.fl_str_mv Elsevier Science Inc
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842269340420800512
score 13.13397

Publicaciones similares