Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7

Autores
Cruz Zaragoza, Epifanio; Furetta, C.; Marcazzo, Salvador Julian; Santiago, Martin Alejo; Guarneros, C.; Pacio, M.; Palomino, R.
Año de publicación
2016
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Thermoluminescence (TL) and radioluminescence (RL) properties of polycrystalline lithium tetraborate (Li2B4O7) doped with different concentrations of copper (0.25, 0.5, 1 wt %) under beta irradiation have been investigated. The feasibility of using this borate in radiation dosimetry at low doses has been evaluated. Tissue equivalent Li2B4O7 was prepared by solid state reaction using mixing stoichiometric compositions of lithium carbonate (Li2CO3) and boric acid (H3BO3) and a solution of CuCl2 as dopant. The glow curve of the most efficient copper doped borate (Li2B4O7:Cu 0.5 wt %) shows a main stable peak centered at 225 °C and a second low temperature peak centered at 80 °C. The low temperature peak fades completely after 24 h of storage in darkness and at room temperature or after an annealing at 120 °C for 10 s. The main peak of the Li2B4O7:Cu remains constant. The TL response of Li2B4O7:Cu shows good linearity in the analyzed dose range. The stability and repeatability of RL signals of the borate have been studied and the Li2B4O7:Cu (0.5 wt %) shows the higher RL emission and a stable and repetitive response. Results show that polycrystalline Li2B4O7:Cu has prospects to be used in beta radiation dosimetry.
Fil: Cruz Zaragoza, Epifanio. Universidad Nacional Autónoma de México. Instituto de Ciencias Nucleares; México
Fil: Furetta, C.. Universidad Nacional Autónoma de México. Instituto de Ciencias Nucleares; México
Fil: Marcazzo, Salvador Julian. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ciencias Exactas. Instituto de Fisica Arroyo Seco; Argentina
Fil: Santiago, Martin Alejo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ciencias Exactas. Instituto de Fisica Arroyo Seco; Argentina
Fil: Guarneros, C.. Instituto Politécnico Nacional. Centro de Investigación en Ciencia Aplicada y Tecnología Avanzada; Argentina. Consejo Nacional de Ciencia y Tecnología; México
Fil: Pacio, M.. Benemérita Universidad Autónoma de Puebla; México
Fil: Palomino, R.. Benemérita Universidad Autónoma de Puebla; México
Materia
Dosimeter
Lithium Tetraborate
Radioluminescence
Thermoluminescence
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/58176
Acceder
id CONICETDig_f52fa5423082bf10f3f2f158dfc4ae0b
oai_identifier_str oai:ri.conicet.gov.ar:11336/58176
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7Cruz Zaragoza, EpifanioFuretta, C.Marcazzo, Salvador JulianSantiago, Martin AlejoGuarneros, C.Pacio, M.Palomino, R.DosimeterLithium TetraborateRadioluminescenceThermoluminescencehttps://purl.org/becyt/ford/1.3https://purl.org/becyt/ford/1Thermoluminescence (TL) and radioluminescence (RL) properties of polycrystalline lithium tetraborate (Li2B4O7) doped with different concentrations of copper (0.25, 0.5, 1 wt %) under beta irradiation have been investigated. The feasibility of using this borate in radiation dosimetry at low doses has been evaluated. Tissue equivalent Li2B4O7 was prepared by solid state reaction using mixing stoichiometric compositions of lithium carbonate (Li2CO3) and boric acid (H3BO3) and a solution of CuCl2 as dopant. The glow curve of the most efficient copper doped borate (Li2B4O7:Cu 0.5 wt %) shows a main stable peak centered at 225 °C and a second low temperature peak centered at 80 °C. The low temperature peak fades completely after 24 h of storage in darkness and at room temperature or after an annealing at 120 °C for 10 s. The main peak of the Li2B4O7:Cu remains constant. The TL response of Li2B4O7:Cu shows good linearity in the analyzed dose range. The stability and repeatability of RL signals of the borate have been studied and the Li2B4O7:Cu (0.5 wt %) shows the higher RL emission and a stable and repetitive response. Results show that polycrystalline Li2B4O7:Cu has prospects to be used in beta radiation dosimetry.Fil: Cruz Zaragoza, Epifanio. Universidad Nacional Autónoma de México. Instituto de Ciencias Nucleares; MéxicoFil: Furetta, C.. Universidad Nacional Autónoma de México. Instituto de Ciencias Nucleares; MéxicoFil: Marcazzo, Salvador Julian. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ciencias Exactas. Instituto de Fisica Arroyo Seco; ArgentinaFil: Santiago, Martin Alejo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ciencias Exactas. Instituto de Fisica Arroyo Seco; ArgentinaFil: Guarneros, C.. Instituto Politécnico Nacional. Centro de Investigación en Ciencia Aplicada y Tecnología Avanzada; Argentina. Consejo Nacional de Ciencia y Tecnología; MéxicoFil: Pacio, M.. Benemérita Universidad Autónoma de Puebla; MéxicoFil: Palomino, R.. Benemérita Universidad Autónoma de Puebla; MéxicoElsevier Science2016-11info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/58176Cruz Zaragoza, Epifanio; Furetta, C.; Marcazzo, Salvador Julian; Santiago, Martin Alejo; Guarneros, C.; et al.; Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7; Elsevier Science; Journal of Luminescence; 179; 11-2016; 260-2640022-2313CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0022231315309194info:eu-repo/semantics/altIdentifier/doi/10.1016/j.jlumin.2016.07.003info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T09:51:47Zoai:ri.conicet.gov.ar:11336/58176instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 09:51:48.098CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7
title Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7
spellingShingle Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7
Cruz Zaragoza, Epifanio
Dosimeter
Lithium Tetraborate
Radioluminescence
Thermoluminescence
title_short Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7
title_full Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7
title_fullStr Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7
title_full_unstemmed Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7
title_sort Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7
dc.creator.none.fl_str_mv Cruz Zaragoza, Epifanio
Furetta, C.
Marcazzo, Salvador Julian
Santiago, Martin Alejo
Guarneros, C.
Pacio, M.
Palomino, R.
author Cruz Zaragoza, Epifanio
author_facet Cruz Zaragoza, Epifanio
Furetta, C.
Marcazzo, Salvador Julian
Santiago, Martin Alejo
Guarneros, C.
Pacio, M.
Palomino, R.
author_role author
author2 Furetta, C.
Marcazzo, Salvador Julian
Santiago, Martin Alejo
Guarneros, C.
Pacio, M.
Palomino, R.
author2_role author
author
author
author
author
author
dc.subject.none.fl_str_mv Dosimeter
Lithium Tetraborate
Radioluminescence
Thermoluminescence
topic Dosimeter
Lithium Tetraborate
Radioluminescence
Thermoluminescence
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.3
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv Thermoluminescence (TL) and radioluminescence (RL) properties of polycrystalline lithium tetraborate (Li2B4O7) doped with different concentrations of copper (0.25, 0.5, 1 wt %) under beta irradiation have been investigated. The feasibility of using this borate in radiation dosimetry at low doses has been evaluated. Tissue equivalent Li2B4O7 was prepared by solid state reaction using mixing stoichiometric compositions of lithium carbonate (Li2CO3) and boric acid (H3BO3) and a solution of CuCl2 as dopant. The glow curve of the most efficient copper doped borate (Li2B4O7:Cu 0.5 wt %) shows a main stable peak centered at 225 °C and a second low temperature peak centered at 80 °C. The low temperature peak fades completely after 24 h of storage in darkness and at room temperature or after an annealing at 120 °C for 10 s. The main peak of the Li2B4O7:Cu remains constant. The TL response of Li2B4O7:Cu shows good linearity in the analyzed dose range. The stability and repeatability of RL signals of the borate have been studied and the Li2B4O7:Cu (0.5 wt %) shows the higher RL emission and a stable and repetitive response. Results show that polycrystalline Li2B4O7:Cu has prospects to be used in beta radiation dosimetry.
Fil: Cruz Zaragoza, Epifanio. Universidad Nacional Autónoma de México. Instituto de Ciencias Nucleares; México
Fil: Furetta, C.. Universidad Nacional Autónoma de México. Instituto de Ciencias Nucleares; México
Fil: Marcazzo, Salvador Julian. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ciencias Exactas. Instituto de Fisica Arroyo Seco; Argentina
Fil: Santiago, Martin Alejo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ciencias Exactas. Instituto de Fisica Arroyo Seco; Argentina
Fil: Guarneros, C.. Instituto Politécnico Nacional. Centro de Investigación en Ciencia Aplicada y Tecnología Avanzada; Argentina. Consejo Nacional de Ciencia y Tecnología; México
Fil: Pacio, M.. Benemérita Universidad Autónoma de Puebla; México
Fil: Palomino, R.. Benemérita Universidad Autónoma de Puebla; México
description Thermoluminescence (TL) and radioluminescence (RL) properties of polycrystalline lithium tetraborate (Li2B4O7) doped with different concentrations of copper (0.25, 0.5, 1 wt %) under beta irradiation have been investigated. The feasibility of using this borate in radiation dosimetry at low doses has been evaluated. Tissue equivalent Li2B4O7 was prepared by solid state reaction using mixing stoichiometric compositions of lithium carbonate (Li2CO3) and boric acid (H3BO3) and a solution of CuCl2 as dopant. The glow curve of the most efficient copper doped borate (Li2B4O7:Cu 0.5 wt %) shows a main stable peak centered at 225 °C and a second low temperature peak centered at 80 °C. The low temperature peak fades completely after 24 h of storage in darkness and at room temperature or after an annealing at 120 °C for 10 s. The main peak of the Li2B4O7:Cu remains constant. The TL response of Li2B4O7:Cu shows good linearity in the analyzed dose range. The stability and repeatability of RL signals of the borate have been studied and the Li2B4O7:Cu (0.5 wt %) shows the higher RL emission and a stable and repetitive response. Results show that polycrystalline Li2B4O7:Cu has prospects to be used in beta radiation dosimetry.
publishDate 2016
dc.date.none.fl_str_mv 2016-11
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/58176
Cruz Zaragoza, Epifanio; Furetta, C.; Marcazzo, Salvador Julian; Santiago, Martin Alejo; Guarneros, C.; et al.; Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7; Elsevier Science; Journal of Luminescence; 179; 11-2016; 260-264
0022-2313
CONICET Digital
CONICET
url http://hdl.handle.net/11336/58176
identifier_str_mv Cruz Zaragoza, Epifanio; Furetta, C.; Marcazzo, Salvador Julian; Santiago, Martin Alejo; Guarneros, C.; et al.; Beta radiation induced luminescence of polycrystalline Cu-doped Li2B4O7; Elsevier Science; Journal of Luminescence; 179; 11-2016; 260-264
0022-2313
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0022231315309194
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.jlumin.2016.07.003
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier Science
publisher.none.fl_str_mv Elsevier Science
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1844613591229005824
score 13.070432

Publicaciones similares