Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry

Autores
Mentasti, Luciana; Martínez Clemente, Nahuel Facundo; Zucchi, Ileana Alicia; Santiago, Martin Alejo; Barreto, Gastón Pablo
Año de publicación
2020
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
YVO4:Eu3+ is a red emitter phosphor commercially available as micrometric powder due to its high luminescence efficiency under electron-beam excitation. Although some published results have demonstrated the potential of using this micrometer material in Fiber Optic Dosimetry systems, there is no information regarding its use on a nanometric scale. In order to obtain a nanometric material with high luminescent efficiency, a simple synthetic combustion method was developed and the results were compared with both, those of a commercial material and those obtained by a typical coprecipitation synthesis. A single crystalline phase was obtained when the combustion route was employed for the preparation meanwhile two crystalline phases were obtained via coprecipitation synthesis. The particle size of YVO4:Eu3+ obtained by combustion route ranges from 55 up to 200 nm. Fourier Transform Infrared Spectroscopy and Thermogravimetric Analysis indicated that annealing at 600 °C promote the degradation of the impurities that remained adsorbed onto nanoparticles surface after the synthesis. However, to improve the Radioluminescence intensity, an annealing process at 1000 °C was required. The method allows obtaining a nanometric material with a scintillation intensity almost twice higher than that of the commercial powder.
Fil: Mentasti, Luciana. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina
Fil: Martínez Clemente, Nahuel Facundo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina
Fil: Zucchi, Ileana Alicia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Santiago, Martin Alejo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina
Fil: Barreto, Gastón Pablo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina
Materia
CHEMICAL SYNTHESIS
CRYSTAL STRUCTURE
LUMINESCENCE
OPTICAL MATERIALS
OPTICAL SPECTROSCOPY
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/143297
Acceder
id CONICETDig_e548f71bf5a5737db5957a156319cd3e
oai_identifier_str oai:ri.conicet.gov.ar:11336/143297
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic DosimetryMentasti, LucianaMartínez Clemente, Nahuel FacundoZucchi, Ileana AliciaSantiago, Martin AlejoBarreto, Gastón PabloCHEMICAL SYNTHESISCRYSTAL STRUCTURELUMINESCENCEOPTICAL MATERIALSOPTICAL SPECTROSCOPYhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2YVO4:Eu3+ is a red emitter phosphor commercially available as micrometric powder due to its high luminescence efficiency under electron-beam excitation. Although some published results have demonstrated the potential of using this micrometer material in Fiber Optic Dosimetry systems, there is no information regarding its use on a nanometric scale. In order to obtain a nanometric material with high luminescent efficiency, a simple synthetic combustion method was developed and the results were compared with both, those of a commercial material and those obtained by a typical coprecipitation synthesis. A single crystalline phase was obtained when the combustion route was employed for the preparation meanwhile two crystalline phases were obtained via coprecipitation synthesis. The particle size of YVO4:Eu3+ obtained by combustion route ranges from 55 up to 200 nm. Fourier Transform Infrared Spectroscopy and Thermogravimetric Analysis indicated that annealing at 600 °C promote the degradation of the impurities that remained adsorbed onto nanoparticles surface after the synthesis. However, to improve the Radioluminescence intensity, an annealing process at 1000 °C was required. The method allows obtaining a nanometric material with a scintillation intensity almost twice higher than that of the commercial powder.Fil: Mentasti, Luciana. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; ArgentinaFil: Martínez Clemente, Nahuel Facundo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; ArgentinaFil: Zucchi, Ileana Alicia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Santiago, Martin Alejo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; ArgentinaFil: Barreto, Gastón Pablo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; ArgentinaElsevier Science SA2020-07-03info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/143297Mentasti, Luciana; Martínez Clemente, Nahuel Facundo; Zucchi, Ileana Alicia; Santiago, Martin Alejo; Barreto, Gastón Pablo; Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry; Elsevier Science SA; Journal of Alloys and Compounds; 829; 3-7-2020; 1-330925-83881873-4669CONICET DigitalCONICETenghttp://hdl.handle.net/11336/235079info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/abs/pii/S0925838820309919info:eu-repo/semantics/altIdentifier/doi/10.1016/j.jallcom.2020.154628info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-11-05T10:52:13Zoai:ri.conicet.gov.ar:11336/143297instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-11-05 10:52:14.138CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry
title Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry
spellingShingle Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry
Mentasti, Luciana
CHEMICAL SYNTHESIS
CRYSTAL STRUCTURE
LUMINESCENCE
OPTICAL MATERIALS
OPTICAL SPECTROSCOPY
title_short Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry
title_full Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry
title_fullStr Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry
title_full_unstemmed Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry
title_sort Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry
dc.creator.none.fl_str_mv Mentasti, Luciana
Martínez Clemente, Nahuel Facundo
Zucchi, Ileana Alicia
Santiago, Martin Alejo
Barreto, Gastón Pablo
author Mentasti, Luciana
author_facet Mentasti, Luciana
Martínez Clemente, Nahuel Facundo
Zucchi, Ileana Alicia
Santiago, Martin Alejo
Barreto, Gastón Pablo
author_role author
author2 Martínez Clemente, Nahuel Facundo
Zucchi, Ileana Alicia
Santiago, Martin Alejo
Barreto, Gastón Pablo
author2_role author
author
author
author
dc.subject.none.fl_str_mv CHEMICAL SYNTHESIS
CRYSTAL STRUCTURE
LUMINESCENCE
OPTICAL MATERIALS
OPTICAL SPECTROSCOPY
topic CHEMICAL SYNTHESIS
CRYSTAL STRUCTURE
LUMINESCENCE
OPTICAL MATERIALS
OPTICAL SPECTROSCOPY
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv YVO4:Eu3+ is a red emitter phosphor commercially available as micrometric powder due to its high luminescence efficiency under electron-beam excitation. Although some published results have demonstrated the potential of using this micrometer material in Fiber Optic Dosimetry systems, there is no information regarding its use on a nanometric scale. In order to obtain a nanometric material with high luminescent efficiency, a simple synthetic combustion method was developed and the results were compared with both, those of a commercial material and those obtained by a typical coprecipitation synthesis. A single crystalline phase was obtained when the combustion route was employed for the preparation meanwhile two crystalline phases were obtained via coprecipitation synthesis. The particle size of YVO4:Eu3+ obtained by combustion route ranges from 55 up to 200 nm. Fourier Transform Infrared Spectroscopy and Thermogravimetric Analysis indicated that annealing at 600 °C promote the degradation of the impurities that remained adsorbed onto nanoparticles surface after the synthesis. However, to improve the Radioluminescence intensity, an annealing process at 1000 °C was required. The method allows obtaining a nanometric material with a scintillation intensity almost twice higher than that of the commercial powder.
Fil: Mentasti, Luciana. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina
Fil: Martínez Clemente, Nahuel Facundo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina
Fil: Zucchi, Ileana Alicia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Santiago, Martin Alejo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina
Fil: Barreto, Gastón Pablo. Universidad Nacional del Centro de la Provincia de Buenos Aires. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Tandil. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires. - Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Investigaciones en Física e Ingeniería del Centro de la Provincia de Buenos Aires; Argentina
description YVO4:Eu3+ is a red emitter phosphor commercially available as micrometric powder due to its high luminescence efficiency under electron-beam excitation. Although some published results have demonstrated the potential of using this micrometer material in Fiber Optic Dosimetry systems, there is no information regarding its use on a nanometric scale. In order to obtain a nanometric material with high luminescent efficiency, a simple synthetic combustion method was developed and the results were compared with both, those of a commercial material and those obtained by a typical coprecipitation synthesis. A single crystalline phase was obtained when the combustion route was employed for the preparation meanwhile two crystalline phases were obtained via coprecipitation synthesis. The particle size of YVO4:Eu3+ obtained by combustion route ranges from 55 up to 200 nm. Fourier Transform Infrared Spectroscopy and Thermogravimetric Analysis indicated that annealing at 600 °C promote the degradation of the impurities that remained adsorbed onto nanoparticles surface after the synthesis. However, to improve the Radioluminescence intensity, an annealing process at 1000 °C was required. The method allows obtaining a nanometric material with a scintillation intensity almost twice higher than that of the commercial powder.
publishDate 2020
dc.date.none.fl_str_mv 2020-07-03
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/143297
Mentasti, Luciana; Martínez Clemente, Nahuel Facundo; Zucchi, Ileana Alicia; Santiago, Martin Alejo; Barreto, Gastón Pablo; Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry; Elsevier Science SA; Journal of Alloys and Compounds; 829; 3-7-2020; 1-33
0925-8388
1873-4669
CONICET Digital
CONICET
url http://hdl.handle.net/11336/143297
identifier_str_mv Mentasti, Luciana; Martínez Clemente, Nahuel Facundo; Zucchi, Ileana Alicia; Santiago, Martin Alejo; Barreto, Gastón Pablo; Development of a simple process to obtain luminescent YVO4:Eu3+ nanoparticles for Fiber Optic Dosimetry; Elsevier Science SA; Journal of Alloys and Compounds; 829; 3-7-2020; 1-33
0925-8388
1873-4669
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv http://hdl.handle.net/11336/235079
info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/abs/pii/S0925838820309919
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.jallcom.2020.154628
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier Science SA
publisher.none.fl_str_mv Elsevier Science SA
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1847978246119882752
score 13.087074

Publicaciones similares