Study of the solidification structure of compacted graphite cast iron

Autores
López, Marcos Gabriel; Rivera, Graciela Leonor; Massone, Juan Miguel; Boeri, Roberto Enrique
Año de publicación
2016
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
This investigation focuses on the study of the solidification mechanism of compacted graphite cast iron (CGI). The solidification macrostructure was revealed in cast samples using a special technique known as direct austempering after solidification (DAAS). The microstructure was revealed by colour etching.The results were compared with earlier investigations of the solidification of spheroidal (SGI) and lamellar (LGI) graphite irons, and show that, similarly to other free graphite cast irons, the solidification of CGI is dominated by the presence of relatively large grains of austenite that can be observed with bareeyes. The CGI cast samples show a typical ingot structure, containing columnar and equiaxed grains, with a narrow columnar to equiaxed transition. The microstructure analysis showed that a dendritic substructure and a large number of eutectic colonies form the grains. Microsegregation is located inside the grains, mostly between secondary dendrite arms. The results indicate that the growth mechanism during solidification of CGI resembles that of LGI, but not the mechanism of SGI.
Fil: López, Marcos Gabriel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Rivera, Graciela Leonor. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Massone, Juan Miguel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Boeri, Roberto Enrique. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Materia
Compacted Graphite Iron
Solidification Structure
Daas Technique
Colour Etching
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/32560
Acceder
id CONICETDig_d91b67172d9e2b8ed1f2fdb96bd6d3fa
oai_identifier_str oai:ri.conicet.gov.ar:11336/32560
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Study of the solidification structure of compacted graphite cast ironLópez, Marcos GabrielRivera, Graciela LeonorMassone, Juan MiguelBoeri, Roberto EnriqueCompacted Graphite IronSolidification StructureDaas TechniqueColour Etchinghttps://purl.org/becyt/ford/2.3https://purl.org/becyt/ford/2This investigation focuses on the study of the solidification mechanism of compacted graphite cast iron (CGI). The solidification macrostructure was revealed in cast samples using a special technique known as direct austempering after solidification (DAAS). The microstructure was revealed by colour etching.The results were compared with earlier investigations of the solidification of spheroidal (SGI) and lamellar (LGI) graphite irons, and show that, similarly to other free graphite cast irons, the solidification of CGI is dominated by the presence of relatively large grains of austenite that can be observed with bareeyes. The CGI cast samples show a typical ingot structure, containing columnar and equiaxed grains, with a narrow columnar to equiaxed transition. The microstructure analysis showed that a dendritic substructure and a large number of eutectic colonies form the grains. Microsegregation is located inside the grains, mostly between secondary dendrite arms. The results indicate that the growth mechanism during solidification of CGI resembles that of LGI, but not the mechanism of SGI.Fil: López, Marcos Gabriel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Rivera, Graciela Leonor. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Massone, Juan Miguel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Boeri, Roberto Enrique. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaTaylor & Francis2016-09-30info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/32560López, Marcos Gabriel; Rivera, Graciela Leonor; Massone, Juan Miguel; Boeri, Roberto Enrique; Study of the solidification structure of compacted graphite cast iron; Taylor & Francis; International Journal Of Cast Metals Research; 29; 5; 30-9-2016; 266-2711364-0461CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1080/13640461.2016.1237099info:eu-repo/semantics/altIdentifier/url/http://www.tandfonline.com/doi/full/10.1080/13640461.2016.1237099info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-10-15T14:43:41Zoai:ri.conicet.gov.ar:11336/32560instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-10-15 14:43:41.679CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Study of the solidification structure of compacted graphite cast iron
title Study of the solidification structure of compacted graphite cast iron
spellingShingle Study of the solidification structure of compacted graphite cast iron
López, Marcos Gabriel
Compacted Graphite Iron
Solidification Structure
Daas Technique
Colour Etching
title_short Study of the solidification structure of compacted graphite cast iron
title_full Study of the solidification structure of compacted graphite cast iron
title_fullStr Study of the solidification structure of compacted graphite cast iron
title_full_unstemmed Study of the solidification structure of compacted graphite cast iron
title_sort Study of the solidification structure of compacted graphite cast iron
dc.creator.none.fl_str_mv López, Marcos Gabriel
Rivera, Graciela Leonor
Massone, Juan Miguel
Boeri, Roberto Enrique
author López, Marcos Gabriel
author_facet López, Marcos Gabriel
Rivera, Graciela Leonor
Massone, Juan Miguel
Boeri, Roberto Enrique
author_role author
author2 Rivera, Graciela Leonor
Massone, Juan Miguel
Boeri, Roberto Enrique
author2_role author
author
author
dc.subject.none.fl_str_mv Compacted Graphite Iron
Solidification Structure
Daas Technique
Colour Etching
topic Compacted Graphite Iron
Solidification Structure
Daas Technique
Colour Etching
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.3
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv This investigation focuses on the study of the solidification mechanism of compacted graphite cast iron (CGI). The solidification macrostructure was revealed in cast samples using a special technique known as direct austempering after solidification (DAAS). The microstructure was revealed by colour etching.The results were compared with earlier investigations of the solidification of spheroidal (SGI) and lamellar (LGI) graphite irons, and show that, similarly to other free graphite cast irons, the solidification of CGI is dominated by the presence of relatively large grains of austenite that can be observed with bareeyes. The CGI cast samples show a typical ingot structure, containing columnar and equiaxed grains, with a narrow columnar to equiaxed transition. The microstructure analysis showed that a dendritic substructure and a large number of eutectic colonies form the grains. Microsegregation is located inside the grains, mostly between secondary dendrite arms. The results indicate that the growth mechanism during solidification of CGI resembles that of LGI, but not the mechanism of SGI.
Fil: López, Marcos Gabriel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Rivera, Graciela Leonor. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Massone, Juan Miguel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Boeri, Roberto Enrique. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
description This investigation focuses on the study of the solidification mechanism of compacted graphite cast iron (CGI). The solidification macrostructure was revealed in cast samples using a special technique known as direct austempering after solidification (DAAS). The microstructure was revealed by colour etching.The results were compared with earlier investigations of the solidification of spheroidal (SGI) and lamellar (LGI) graphite irons, and show that, similarly to other free graphite cast irons, the solidification of CGI is dominated by the presence of relatively large grains of austenite that can be observed with bareeyes. The CGI cast samples show a typical ingot structure, containing columnar and equiaxed grains, with a narrow columnar to equiaxed transition. The microstructure analysis showed that a dendritic substructure and a large number of eutectic colonies form the grains. Microsegregation is located inside the grains, mostly between secondary dendrite arms. The results indicate that the growth mechanism during solidification of CGI resembles that of LGI, but not the mechanism of SGI.
publishDate 2016
dc.date.none.fl_str_mv 2016-09-30
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/32560
López, Marcos Gabriel; Rivera, Graciela Leonor; Massone, Juan Miguel; Boeri, Roberto Enrique; Study of the solidification structure of compacted graphite cast iron; Taylor & Francis; International Journal Of Cast Metals Research; 29; 5; 30-9-2016; 266-271
1364-0461
CONICET Digital
CONICET
url http://hdl.handle.net/11336/32560
identifier_str_mv López, Marcos Gabriel; Rivera, Graciela Leonor; Massone, Juan Miguel; Boeri, Roberto Enrique; Study of the solidification structure of compacted graphite cast iron; Taylor & Francis; International Journal Of Cast Metals Research; 29; 5; 30-9-2016; 266-271
1364-0461
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1080/13640461.2016.1237099
info:eu-repo/semantics/altIdentifier/url/http://www.tandfonline.com/doi/full/10.1080/13640461.2016.1237099
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Taylor & Francis
publisher.none.fl_str_mv Taylor & Francis
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1846082943714328576
score 13.22299

Publicaciones similares