Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications
- Autores
- Pereda, M. D.; Kang, Kyung Won; Bonetto, Rita Dominga; Llorente, Carlos Luis; Bilmes, Pablo David; Gervasi, Claudio
- Año de publicación
- 2012
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- AISI 316 LVM stainless steel type considered in ASTM F138 and F139 standards for implant devices is widely used, in particular for orthopedic surgery, because it combines good biofunctionality and acceptable biocompatibility at low costs. Adequate interaction of these materials with the human body and its capability to reach the desired service level are determined by the surface preparation. The goal of the present work is to relate the surface roughness parameters with the localized corrosion resistance of AISI 316 LVM stainless steel grit blasted for different times and passivated with nitric acid. At intermediate blasting times the roughness parameters attain an extreme value and this surface condition corresponds with the maximum pitting corrosion resistance.
Fil: Pereda, M. D.. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina
Fil: Kang, Kyung Won. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina
Fil: Bonetto, Rita Dominga. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Llorente, Carlos Luis. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina
Fil: Bilmes, Pablo David. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
Fil: Gervasi, Claudio. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ingeniería Química; Argentina - Materia
-
316 Lvm Stainless Steel
Glass Beads Blasting
Roughness Parameters
Corrosion - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/77888
Ver los metadatos del registro completo
id |
CONICETDig_d6b918a2a8fd8521d9af1b8f595726bd |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/77888 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applicationsPereda, M. D.Kang, Kyung WonBonetto, Rita DomingaLlorente, Carlos LuisBilmes, Pablo DavidGervasi, Claudio316 Lvm Stainless SteelGlass Beads BlastingRoughness ParametersCorrosionAISI 316 LVM stainless steel type considered in ASTM F138 and F139 standards for implant devices is widely used, in particular for orthopedic surgery, because it combines good biofunctionality and acceptable biocompatibility at low costs. Adequate interaction of these materials with the human body and its capability to reach the desired service level are determined by the surface preparation. The goal of the present work is to relate the surface roughness parameters with the localized corrosion resistance of AISI 316 LVM stainless steel grit blasted for different times and passivated with nitric acid. At intermediate blasting times the roughness parameters attain an extreme value and this surface condition corresponds with the maximum pitting corrosion resistance.Fil: Pereda, M. D.. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; ArgentinaFil: Kang, Kyung Won. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; ArgentinaFil: Bonetto, Rita Dominga. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; ArgentinaFil: Llorente, Carlos Luis. Universidad Nacional de La Plata. Facultad de Ingeniería; ArgentinaFil: Bilmes, Pablo David. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; ArgentinaFil: Gervasi, Claudio. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ingeniería Química; ArgentinaElsevier2012-06info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/77888Pereda, M. D.; Kang, Kyung Won; Bonetto, Rita Dominga; Llorente, Carlos Luis; Bilmes, Pablo David; et al.; Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications; Elsevier; Procedia Materials Science; 1; 6-2012; 446-4532211-8128CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1016/j.mspro.2012.06.060info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S2211812812000612info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:29:18Zoai:ri.conicet.gov.ar:11336/77888instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:29:19.092CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications |
title |
Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications |
spellingShingle |
Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications Pereda, M. D. 316 Lvm Stainless Steel Glass Beads Blasting Roughness Parameters Corrosion |
title_short |
Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications |
title_full |
Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications |
title_fullStr |
Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications |
title_full_unstemmed |
Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications |
title_sort |
Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications |
dc.creator.none.fl_str_mv |
Pereda, M. D. Kang, Kyung Won Bonetto, Rita Dominga Llorente, Carlos Luis Bilmes, Pablo David Gervasi, Claudio |
author |
Pereda, M. D. |
author_facet |
Pereda, M. D. Kang, Kyung Won Bonetto, Rita Dominga Llorente, Carlos Luis Bilmes, Pablo David Gervasi, Claudio |
author_role |
author |
author2 |
Kang, Kyung Won Bonetto, Rita Dominga Llorente, Carlos Luis Bilmes, Pablo David Gervasi, Claudio |
author2_role |
author author author author author |
dc.subject.none.fl_str_mv |
316 Lvm Stainless Steel Glass Beads Blasting Roughness Parameters Corrosion |
topic |
316 Lvm Stainless Steel Glass Beads Blasting Roughness Parameters Corrosion |
dc.description.none.fl_txt_mv |
AISI 316 LVM stainless steel type considered in ASTM F138 and F139 standards for implant devices is widely used, in particular for orthopedic surgery, because it combines good biofunctionality and acceptable biocompatibility at low costs. Adequate interaction of these materials with the human body and its capability to reach the desired service level are determined by the surface preparation. The goal of the present work is to relate the surface roughness parameters with the localized corrosion resistance of AISI 316 LVM stainless steel grit blasted for different times and passivated with nitric acid. At intermediate blasting times the roughness parameters attain an extreme value and this surface condition corresponds with the maximum pitting corrosion resistance. Fil: Pereda, M. D.. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina Fil: Kang, Kyung Won. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas; Argentina Fil: Bonetto, Rita Dominga. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina Fil: Llorente, Carlos Luis. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina Fil: Bilmes, Pablo David. Universidad Nacional de La Plata. Facultad de Ingeniería; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina Fil: Gervasi, Claudio. Universidad Nacional de La Plata. Facultad de Ingeniería. Departamento de Ingeniería Química; Argentina |
description |
AISI 316 LVM stainless steel type considered in ASTM F138 and F139 standards for implant devices is widely used, in particular for orthopedic surgery, because it combines good biofunctionality and acceptable biocompatibility at low costs. Adequate interaction of these materials with the human body and its capability to reach the desired service level are determined by the surface preparation. The goal of the present work is to relate the surface roughness parameters with the localized corrosion resistance of AISI 316 LVM stainless steel grit blasted for different times and passivated with nitric acid. At intermediate blasting times the roughness parameters attain an extreme value and this surface condition corresponds with the maximum pitting corrosion resistance. |
publishDate |
2012 |
dc.date.none.fl_str_mv |
2012-06 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/77888 Pereda, M. D.; Kang, Kyung Won; Bonetto, Rita Dominga; Llorente, Carlos Luis; Bilmes, Pablo David; et al.; Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications; Elsevier; Procedia Materials Science; 1; 6-2012; 446-453 2211-8128 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/77888 |
identifier_str_mv |
Pereda, M. D.; Kang, Kyung Won; Bonetto, Rita Dominga; Llorente, Carlos Luis; Bilmes, Pablo David; et al.; Impact of surface treatments on the corrosion resistance of ASTM F138-F139 stainless steel for biomedical applications; Elsevier; Procedia Materials Science; 1; 6-2012; 446-453 2211-8128 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.mspro.2012.06.060 info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S2211812812000612 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-nd/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Elsevier |
publisher.none.fl_str_mv |
Elsevier |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844614298775584768 |
score |
13.070432 |